• Applied Chemistry for Engineering
• /
• v.10 no.5
• /
• pp.778-783
• /
• 1999

The effect of carbon fiber orientation on the tribological properties of carbon fiber/epoxy composites used as a reflecting material for the electromagnetic wave has been investigated. It was found that the carbon fiber/epoxy composite which slides normal to prepreg lay-up direction had less friction and wear that those slides parallel to prepreg fiber lay-up direction due to the increase of delamination between carbon fiber and epoxy. Composite with unidirectional orientation($0/0^{\circ}$) had higher tribological properties than those with multidirectional orientation($0/45/90/-45^{\circ}$ and $0/90^{\circ}$) when the sliding direction was normal to prepreg lay-up direction. This was caused by the debonding between carbon fiber and epoxy which is proportional to contact area between the sliding surface and carbon fiber. Opposite results have been found when the sliding direction was parallel to prepreg lay-up direction due tot he tensile force applied on carbon fiber. In addition, it was shown that wear factor increased with increasing sliding velocity but the friction coefficient did not depend upon the sliding velocity.

• Carbon letters
• /
• v.14 no.1
• /
• pp.22-26
• /
• 2013

The effects of heat treatment temperature (HTT) of polyacrylonitrile-based carbon fiber (CF) on the mechanical, thermal, and tribological properties of C/C composites were investigated. It was found that HTT (graphitization) of CF affects the thermal conductivity and mechanical and tribological characteristics of C/C composites. Thermal treatment of fibers at temperatures up to $2800^{\circ}C$ led to a decrease of the wear rate and the friction coefficient of C/C composite-based discs from 7.0 to 1.1 ${\mu}m$/stop and from 0.356 to 0.269, respectively. The friction surface morphology and friction mechanism strongly depended on the mechanical properties of the CFs. The relief of the friction surface of composites based on CFs with final graphitization was also modified, compared to that of composites based on initial fibers. This phenomenon could be explained by modification of the abrasive wear resistance of reinforcement fibers and consequently modification of the friction and wearing properties of composites. Correlation of the graphitization temperature with the increased flexural and compressive strength, apparent density, and thermal conductivity of the composites was also demonstrated.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.6
• /
• pp.391-399
• /
• 1997

To figure out wheher the tribological properties of a hras-coating layer can be imporved by ion implantatio, TiN-coated SKD 11 61 were implanted with nitrogen ion and their wear peoperties were examined systematically. The amount of nitrgen ione implanted on the coating layer was $2 \times 10^{15},\;10^{16},\;10^{17},\;and\;10^{18}\;ions/\textrm{cm}^2$, respectively. X-ray diffraction revealed theintensity of the peaks belong TiN tended to increase as the ion dose increased, which implied that the implantation promoted the formation of TiN in the coated later. Howeverthe hardensity of the specimens increased then decreased again as the ion dose increased, resulting in a obvious drop of the hardness for the ion does of $2 \times 10^{18}\;ions/\textrm{cm}^2$<\TEX>. While the adhesion of the coated layer of SKD 61 was excllent regrdless of the implatation, the adhesion of the later of SKD 11 was apparently improved by the implantation. The overall wear properties of SKD 11 was better than that of SKD 61, and the best result was yielded at the ion dose of $2 \times 10^{15}\;ions/\textrm{cm}^2$<\TEX>.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.5
• /
• pp.439-445
• /
• 2005

The tribological properties of ceramics are very important in the application to engineering ceramic parts such as seal rings, pump parts, meter parts, and so on. In this study, the effects of each other purity on the mechanical and tribological properties of alumina and zirconia ceramics were investigated. Sliding distance, sliding speed, contact load. friction coefficient, the amount of worn out material at a certain time, and the prepared composites were measured. Crystalline phases and microstructure were examined with XRD and SEM. We obtained the good properties of friction coefficient and wear resistance at the purity 99.7$\%$ of alumina. However, The purity 95$\%$ were great at the wear amount of worn out material.

• Tribology and Lubricants
• /
• v.25 no.1
• /
• pp.61-65
• /
• 2009

Tribological properties of the semi-metallic friction materials containing different solid lubricants (graphite, $WS_2$, $MoS_2$) were investigated. The friction materials were fabricated with an experimental formulation and tested with gray cast iron disks. Results showed that graphite contributed to stabilize the friction coefficient during run-in processes. Also, graphite provided better fade resistance than that of $WS_2$ and $MoS_2$. At intermediate temperature ranges, however, friction materials with $WS_2$ or $MoS_2$ maintained higher friction effectiveness than that of graphite. On the other hand, friction materials containing $MoS_2$ showed increased wear rates than that with graphite or $WS_2$. Friction materials with proper combinations of two solid lubricants showed better friction and wear properties than that of the friction materials containing single solid lubricant.

• Korean Journal of Materials Research
• /
• v.31 no.6
• /
• pp.339-344
• /
• 2021

Composite materials offer distinct and unique properties that are not naturally inherited in the individual materials that make them. One of the most attractive composites to manufacture is the aluminum alloy matrix composite, because it usually combines easiness of availability, light weight, strength, and other favorable properties. In the current work, Powder Metallurgy Method (PMM) is used to prepare Al2024 matrix composites reinforced with different mixing ratios of yttrium oxide (Y₂O₃) particles. The tests performed on the composites include physical, mechanical, and tribological, as well as microstructure analysis via optical microscope. The results show that the experimental density slightly decreases while the porosity increases when the reinforcement ratio increases within the selected range of 0 ~ 20 wt%. Besides this, the yield strength, tensile strength, and Vickers hardness increase up to a 10 wt% Y₂O₃ ratio, after which they decline. Moreover, the wear results show that the composite follows the same paradigm for strength and hardness. It is concluded that this composite is ideal for application when higher strength is required from aluminum composites, as well as lighter weight up to certain values of Y₂O₃ ratio.

• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.149-155
• /
• 2011

We investigated tribological characteristics of diamond-like carbon (DLC) in a condition with carbon nanotube (CNT) content of 1wt% in aqueous solution. Si-DLC films were deposited by radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) process on Al6061 aluminum alloy. In this study, the deposition of DLC films was carried out in vacuum with a chamber pressure of 10-5 to 10-3 Torr achieved by mechanical pump followed by turbo molecular pump. The surface adsorbed oxygen on the Aluminum substrates was removed by passing Ar gas for 10 minutes. The RF power was maintained at 500W throughout the experiment. A buffer layer of HMDSO was deposited on the substrate to improve the adhesion of DLC coating. At this point CH4 gas was introduced in the chamber using gas flow controller and DLC coating was deposited on the buffer layer along with HMDSO for 50 min. The thickness of 1 ${\mu}m$ was obtained for DLC films on aluminum substrates The tribological properties of as synthesized DLC films were analyzed by wear test in the presence of dry air, water and lubricant such as CNT ink.

• Journal of Mechanical Science and Technology
• /
• v.17 no.9
• /
• pp.1276-1286
• /
• 2003

The performance of porous bearing under different lubricants and lubricating conditions was experimentally investigated in this study. In order to carry out the experiments, a new test rig was designed to determine the tribological properties of based sintered bronze journal bearings that were manufactured by powder metallurgy (P/M) techniques. To determine the effects of lubricating conditions with and without oil supplement (OS) on the tribological characteristics of these bearings under static loading and periodic loadings, some experiments were carried out using different lubricants. In the tests, pure base oil (SAE 20W50), two fully formulated commercial engine oils (SAE20W50) and lubricating oils with commercial additive concentration ratio of 3％ were used. The worn surfaces of test bearings were examined using optical microscopy. Experimental results showed that the change in friction coefficient was more stable and in smaller magnitude under static loading than that of periodic loading. In addition, the friction coefficient and the wear rate conducted with base oil resulted in higher values than those of fully formulated oils with and without OS lubricating conditions. The experimental results obtained in this study indicated that the correct selection of lubricant and suitable running conditions were very important on the tribological characteristics of porous bearings.

• Journal of Power System Engineering
• /
• v.14 no.4
• /
• pp.50-55
• /
• 2010

In order to investigate tribological effects of nano copper particles impregnated(CuN) on surface polytetrafluoroethylene(PTFE) on sealing wear and an experimental study was carried out to determine the wear behavior of copper nano-particles impregnation two kind thickness in super critical $CO_2$ liquid. Experimental results showed that the friction coefficients of CuN PTFE at the low sliding speed(0.44m/s) and the oil temperature ($60^{\circ}C$) were higher than that of virgin PTFE. And a thin nano copper particles impreganated thickness was formed on the surface in the PTFE and the specimen with this treatment has much better friction properties than the original one. Fortunately, at the high load(80 N) and the oil temperature, the friction coefficient of CuN PTFE was lower than that of virgin PTFE. This evidenced the load carrying capacity of CuN PTFE was much better than that of virgin PTFE under the high load condition(80 N) specially. Therefore, it can be concluded that the friction coefficient variation of CuN PTFE is very small but its wear rate decreases greatly with increase in sliding speed.

• The Korean Journal of Ceramics
• /
• v.3 no.1
• /
• pp.47-51
• /
• 1997

The dense sintered bodies of Si/SiC composite with various Si contents could be fabricated by changing the green density in the forming process. The Si/SiC/graphite composites with various graphite contents could be also fabricated by changing a graphite content in the starting composition. Their mechanical and tribological properties were characterized and wear mechanism was also studided. The hardness and strength of the Si/SiC and the Si/SiC/graphite were decreased with increasing the contents of free Si and graphite, respectively. However, the friction coefficient and specific wear rate had no specific relations to their hardness and strength. Adhesion of free Si was a main factor to determine a wear resistance of the Si/SiC composite. In the case of the Si/SiC/graphite, solid lubricationl and liquid reservoir of the graphite particles played the main role of the reduction of the friction force. In the torque test to estimate the possibility of practical of practical applications, the value of torque between the Al2O3 disk and Si/SiC/graphite disk was 1/6 lower compared with two $Al_2O_3$ disks on the basis of 100,000 cycles.