The ultrastructural characteristics of shear fracture surfaces of laminated wood prepared from major four Korea wood specimens were examined. Commercial urea and urethan resin were used as adhesives for laminated woods of both homospecies and heterospecies. The morphology of fracture surface was observed using an optical microscopy and scanning electron microscopy. Three anatomical failure types were recognized : intercell failure, intrawall failure and transwall failure. In dry specimen, failure occurred mainly in woods. Laminated woods of softwoods showed mostly intrawall failure and transwall failure of tracheids, and them of hardwoods indicated mainly intrawall failure and interwall failure. Laminated woods prepared with urethan resin showed coarse fracture surface, on the other hand, those prepared with an urea formaldehyde resin had clean surface. In wet specimen, failure occurred dominantly in glue line. Intrawall failure and flags were characterized in laminated wood prepared with urethan resin. In heterospecies laminated woods, failure was occurred mainly in softwood. Consequently, fracture morphology of laminated wood may be influenced by adhesives, moisture content, species and anatomical characteristics.

• Journal of the Korean Wood Science and Technology
• /
• 제39권4호
• /
• pp.351-358
• /
• 2011

인장이상재를 갖는 활엽수재의 파괴특성을 이해하기 위해 신갈나무재의 전단시험 및 휨시험을 통하여 파괴단면을 관찰하였다. 육안적으로 관찰한 결과 전단시편의 경우 정상재보다 인장이상재 시편에서 더 많은 섬유의 보풀이 관찰되었고, 함수율 30% 시편의 전단면이 10%보다 거칠고 많은 섬유의 보풀이 관찰되었다. 휨시험에 의해 파괴된 인장이상재는 정상재에 비해 목섬유가 굵고 길게 드러나 있는 것이 관찰되었다. SEM 관찰 결과 방사면 전단파괴시 정상재와 인장이상재의 목섬유는 벽내파괴에 의한 파괴형태를 보여주고 있으며, 방사유세포는 벽절단파괴에 가까운 형태로 파괴되었다. 접선면 전단파괴시 목섬유는 벽내파괴에 의한 파괴형태를 보여주고 있고 인장이상재의 목섬유의 파괴부분이 더 거칠었다. 방사유세포는 양 시편 모두 벽절단파괴에 의한 파괴 형태를 보여주었으며, 인장이상재의 방사유세포에서 절단면이 비교적 깨끗한 것으로 나타났다. 휨시험에 의한 목섬유 파면의 형태는 정상재의 목섬유에 비하여 인장이상재가 파괴 시 끝이 무디고 깨끗하게 끊어진 모습을 보여주었다.