• Journal of Mechanical Science and Technology
• /
• v.20 no.5
• /
• pp.675-680
• /
• 2006

This is a study of fatigue strength of weld deposits with transverse cracks in plate up to 50 mm thick. It is concerned with the fatigue properties of welds already with transverse cracks. A previous study of transverse crack occurrence, location and microstructure in accordance with welding conditions was published in the Welding Journal (Lee et al., 1998). A fatigue crack develops as a result of stress concentration and extends with each load cycle until fatigue occurs, or until the cyclic loads are transferred to redundant members. The fatigue performance of a member is more dependent on the localized state of stress than the static strength of the base metal or the weld metal. Fatigue specimens were machined to have transverse cracks located on the surface and inside the specimen. Evaluation of fatigue strength depending on location of transverse cracks was then performed. When transverse cracks were propagated in a quarter-or half-circle shape, the specimen broke at low cycle in the presence of a surface crack. However, when the crack was inside the specimen, it propagated in a circular or elliptical shape and the specimen showed high fatigue strength, enough to reach the fatigue limit within tolerance of design stresses.

• Transactions of Materials Processing
• /
• v.27 no.2
• /
• pp.100-106
• /
• 2018

In the continuous casting process, the incidence of transverse surface cracks on the piece may occur by multiple and diverse variables. It is noted that mathematical models may predict only the occurance of the transverse surface cracks, but can require a lot of time (more than three days) to produce a result with this process. This study applied neural networks to predict whether the cracks on the piece surface occurs or does not occur. The computation time was shortened to three minutes, making it applicable to an on-line program, which predicts the non-cracks or cracks of the piece surface in the actual continuous casting process. In addition, the operating conditions to prevent the occurrence of the transverse surface cracks, using decision boundaries were also suggested.

• Advanced Composite Materials
• /
• v.16 no.1
• /
• pp.45-61
• /
• 2007

This paper describes a damage accumulation mechanism in cross-ply CFRP laminates $[0_2/90_2]_{2S}$ subjected to out-of-plane loading. Drop-weight impact and static indentation tests were carried out, and induced damage was observed by ultrasonic C-scan and an optical microscope. Both tests gave essentially the same results for damage modes, sizes, and load-deformation history. First, a crack occurred in the bottom $0^{\circ}$ layer accompanying some delamination along the crack caused by bending stress. Then, transverse cracks occurred in the middle $90^{\circ}$ layer with decreasing contact force between the specimen and the indenter. Measured local strains near the impact point showed that the stress state changed from a bending dominant state to an in-plane tensile dominant state. A cohesive interface element was used to simulate the propagation of multiple delaminations and transverse cracks under static indentation. Two types of analytical models are considered, one with multiple delaminations and the other with both multiple delaminations and transverse cracks. The damage obtained for the model with only multiple delaminations was quite different from that obtained from the experiment. However, the results obtained from the model with both delaminations and transverse cracks well explain the characteristics of the damage obtained in the experiment. The existence of the transverse cracks is essential to form the characteristic impact damage.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.5-14
• /
• 1999

Free vibration characteristics of a cantilevered laminated composite beam with multiple non-propagating transverse open cracks are investigated. In the present analysis a special ply-angle distribution referred to as asymmetric stiffness configuration inducing the elastic coupling between chord-wise bending and extension is considered. The multiple open cracks are modelled as equivalent rotational springs whose spring constants are calculated based on the fracture mechanics of composite material structures. Governing equations of a composite beam with open cracks are derived via Hamilton's Principle and Timoshenko beam theory encompassing transverse shear and rotary inertia effect is adopted. The effects of various parameters such as the ply angle, fiber volume fraction, crack numbers, crack positions and crack depthes on the free vibration characteristics of the beam with multiple cracks are highlighted. The numerical results show that the existence of the multiple cracks in an anisotropic composite beam affects the free vibration characteristics in a more complex fashion compared with the beam with a single crack.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.57-67
• /
• 1999

Welding is widely applicable and reliable process and is mainly adopted for fabricating heavy structures. Recently, weld metal transverse cracks in butt and fillet weld joint is a serious problem, and they must be eliminated for improving weld joint reliability. The weld metal transverse crack susceptibility of butt and fillet joint was carried out by cantilever type tensile crack testing jig and CTS test. In this view of point, this study investigated the potential factors for weld metal transverse crack. The main results obtained were as follows: 1. The content o fdiffusible hydrogen in weld metal played an important role for weld metal transverse cracks. 2. From cantilever type tensile crack tests, it was pointed out that the higher the diffusible hydrogen content and tensile restraint, the more susceptible to weld metal transverse craking. 3. The TSN(thermal severity number) and diffusible hydrogen were important factors for determining weld metal transverse cracks in fillet weld joints.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.405-408
• /
• 2009

Edge cracks in cold rolling always influence to the quality of productions, while the "V" shaped cracks were propagated by passing the roll gap. We set up the sizes and shapes of initial cracks in simulation according to the references from real productions. Different to in hot rolling, the cracks in cold rolling couldn't be reduced from propagation automatically after generated, even if these could be reduced by changing the process parameters. In this paper, we described the affections of process parameters on the propagation of edge cracks, such as reduction ratio and tension. We predicted that the dependence of the cracks propagations of changing of process conditions and expected to gain the smaller edge cracks. By raising the reduction ratio, the cracks were propagated increasingly in both transverse and rolling directions. And as tension raise, the cracks became propagated in both directions in which transverse direction was less effectively.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.49-56
• /
• 1999

Welding is a reliable process and is mainly adopted for fabricating heavy structures. Recently, transverse cracks in the weld metal is serious problem, and they affect cost, efficiency, safety and joint reliability for various welded structures. In this view of point, this study investigated the potential factors for weld metal transverse crack. The main results obtained are as follows; 1) The content of diffusible hydrogen in the commercial flux cored are welding wire was remarkable change by manufacturer. 2) The diffusible hydrogen content was thd main factor for weld metal transverse cracks. 3) Weld metal was immune to transverse cracking under the condition of low diffusible hydrogen content of high restraint condition. 4) The factors for weld metal transverse crack would be the content of diffusible hydrogen and restraint of weld joint.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.56-64
• /
• 1997

Macrostructural characteristic of the transverse cracks and fatigue behavior were studied for EH 32 TMCP 50mm thick plate welded with FACW under the variation in preheat and interpass temperatures. Transverse cracks were detected in specimen welded with preheat and interpass temperature below $30^{\circ}C$, but cracks were not detected in the specimens welded with preheat and interpass temperatures at the range of $100~120^{\circ}C$.C. The location of crack formation was found to strongly depend upon the thickness of weld layers as regard to the plate thickness.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.5 no.2
• /
• pp.217-227
• /
• 2002

Theoretical and experimental free vibration characteristics of cantilevered laminated composite beams with single or multiple transverse non-propagating open cracks are investigated. The presence of intrinsic cracks in beams modifies the flexibility and in turn free vibration characteristics of the structures, and the existence of the multiple cracks in an anisotropic composite beam affects the free vibration characteristics in a more complex fashion compared with the beam with a single crack. Also the experimental results are well coincide with the numerical results in the decrease of natural frequencies and the transformation of mode shapes because of intrinsic cracks in the composite or aluminum beams. It is revealed that non-destructive crack detection(NDT) or vibration based inspection(VBI) is possible by analyzing the free vibration responses of cracked composite beams.

• Journal of the Korea Concrete Institute
• /
• v.13 no.5
• /
• pp.499-506
• /
• 2001

Eight direct tension tests were conducted to study the bond characteristics and crack behavior in high-strength concrete axial members. The main variable was the concrete strength up to 61-63 MPa. The specimens consisted of two different types of the short specimens modeled the part between transverse cracks and the long specimens having numerous transverse cracks. The results obtained show that the bond strength increases in proportion to compressive strength. Thereby, in high-strength concrete the length of stress-disturbed region is shortened and the space of adjacent transverse cracks become smaller. Although the concrete strength varies from 25 MPa to 61 MPa, the split cracking loads remain constant, while transverse cracking loads vary as variation of concrete tensile strength. Accordingly, the current code provisions for development length may need reconsideration in high-strength concrete members, and it is recommended that either thicker cover or transverse reinforcement should be additionally provided for high-strength concrete members.