• 한국주조공학회지
• /
• 제18권6호
• /
• pp.593-603
• /
• 1998

Commercial ductile iron was coated with titanium and aluminum powders by low pressure plasma spraying and then irradiated with a $CO_2$ laser to produce anti-corrosive TiC composite layer. TiC carbides were precipitated homogeneously in a laser alloyed layer by in-situ reaction between carbon existed in the base metal and titanium with thermal sprayed coating. The formation of gas pores and brittle limited mixing zone with ledeburite microstructure in TiC composite layer were surpressed by the complementary alloying of aluminum. The hardness of TiC composite layer obtained by addition of titanium and aluminum was between 600 and 660 Hv, which was three times as high as the hardness of ferritic ductile iron. From the results of isothermal oxidation at 1123k for 24 hours in air, high temperature oxidation resistance of the TiC composite layer with aluminum was improved and doubled when compared with the TiC composite layer without aluminum.

• Maxillofacial Plastic and Reconstructive Surgery
• /
• 제37권
• /
• pp.6.1-6.9
• /
• 2015

Orthognathic surgery requires stable fixation for uneventful healing of osteotomized bony segments and optimal remodeling. Titanium plates and screws have been accepted as the gold standard for rigid fixation in orthognathic surgery. Although titanium osteofixation is the most widely used approach, the use of bioabsorbable devices has been increasing recently. Biodegradation of bioabsorbable devices eliminates the need for a second operation to remove metal plates and screws. However, long-term stability and relapse frequency in bioabsorbable osteofixation are still insufficiently studied, especially in cases of segmental movements of great magnitude or segmental movements to a position where bony resistance exists. This paper reviews the background, techniques, and complications of bioabsorbable osteofixation and compares bioabsorbable and titanium osteofixation in orthognathic surgery in terms of skeletal stability.

• 한국산업융합학회 논문집
• /
• 제8권1호
• /
• pp.25-29
• /
• 2005

Titanium specially has high specific strength, excellent mechanical properties as fatigue strength and fracture ductility, good corrosion resistance, and therefore are broadly applied to the various fields. It is required the developmennt for the skills of wire-cut electrical discharge machining(WEDM), but the WEDMed surface was found to be worst due to the attached components of wire. Therefore precision maching method like lapping is necessary for getting high quilty surface. Roughness of lapped surface, surface hardness to each process depth and improved method of surface shape were stuided experimentally, by changing of grain size of diamond lap material and lapping pressure with constant speed in lapping process.

• 한국표면공학회지
• /
• 제24권4호
• /
• pp.196-205
• /
• 1991

Multi-level thin films are very important in ULSI applications because of their high electromigration resistance. This study presents the effects of titanium, titanium nitride and titanium tungsten underlayers of the stability of multi-aluminum thin films during isothermal annealing. High purity Al(99.999%) films have been electron-beam evaporated on Ti, TiN, TiW films formed on SiO2/Si (P-type(100))-wafer substrates by RF-sputtering in Ar gas ambient. The hillock growth was increased with annealing temperatures. Growth of hillocks was observed during isothermal annealing of the thin films by scanning electron microscopy. The hillock growth was believed to appear due to the recrystallization process driven by stress relaxation during isothermal annealing. Thermomigration damage was also presented in thin films by grain boundary grooving processes. It is shown that underlayers of Al/TiN/SiO2, Al/TiW/SiO2 thin films are preferrable to Al/SiO2 thin film metallization.

• 한국주조공학회지
• /
• 제11권6호
• /
• pp.482-490
• /
• 1991

This study presents the wear characteristics of Ti alloys (Pure Ti, Ti-6Al-4V, Ti-5Al-2.5Sn) fabricated by centrifugal precision casting in an Ohara dental titanium casting machine. It was found that the hardness of the surface region is higher than that of the interior region. It is considered that the oxygen adsorption in the surface region during casting, leads to the interstitial solid solution hardening. Wear resistance incerases in the order of pure Ti, Ti-6Al-4V, Ti-5Al-2.5Sn alloys. The interior hardness value increases in the same order. The specific wear rate increases with applied load and increases monotonously with sliding speed. The Fe transfer from the counterpart material was observed on the worn surface of the Ti-5Al-2.5Sn alloy. Oxidative wear occurs at low sliding speeds and mechanical fracture wear occurs at high sliding speeds.

• Corrosion Science and Technology
• /
• 제9권1호
• /
• pp.8-11
• /
• 2010

During PEO (plasma-electrolytic-oxidation) treatment of titanium, the relationship between the thickness of oxide film and the measured electrical information was investigated. A simple real time monitoring method based on the electrical information being gathered during PEO treatment is proposed. The proposed method utilizes the current flowing from a high frequency voltage source to calculate the resistance of an oxide film, which is converted into the thickness of an oxide film. This monitoring method can be implemented in PEO system in which an oxide film is grown by constant or pulsed voltage/current sources.

• 한국재료학회지
• /
• 제15권1호
• /
• pp.37-41
• /
• 2005

Stainless steel fibers with a diameter of $17\;{\mu}m$ and 630 nm were produced from stainless steel wires by the drawing/annealing/exfolitation process. The suitable sheath material to draw the core stainless steel wires to fibers was the Cu coating. The low melting metal of Zn was not a suitable sheath coating. Also, an attempt was made to produce $20\;{\mu}m{\Phi}Ti$ fibers from the core titanium wires. The main obstacles in producing Ti fibers were their resistance to deformation owing to the Ti's hop structure, and high reactivity of Ti with the exfolitation solution.

• 대한치과보철학회지
• /
• 제45권2호
• /
• pp.169-181
• /
• 2007

Statement of problem: Titanium is well known as a proper metal for the dental restorations, because it has an excellent biocompatibility, resistance to corrosion, and mechanical property. However, adhesion between titanium and dental porcelains is related to the diffusion of oxygen to the reaction layers formed on cast-titanium surfaces during porcelain firing and those oxidized layers make the adhesion difficult to be formed. Many studies using mechanical, chemical and physical methods to enhance the titanium-ceramic adhesion have been actively performed. Purpose: This study meant to comparatively analyse the adhesion characteristics depending on different titanium surface coatings after coating the casts and wrought titanium surfaces with Au and TiN. Material and method: In this study, the titanium specimens (CP-Ti, Grade 2, Kobe still Co. Japan) were categorized into cast and wrought titanium. The wrought titanium was cast by using the MgO-based investment(Selevest CB, Selec). The cast and wrought titanium were treated with Au coating($ParaOne^{(R)}$., Gold Ion Sputter, Model PS-1200) and TiN coating(ATEC system, Korea) and the ultra low fusing dental porcelain was fused and fired onto the samples. Biaxial flection test was done on the fired samples and the porcelain was separated. The adhesion characteristics of porcelain and titanium after firing and the specimen surfaces before and after the porcelain fracture test were observed with SEM. The atomic percent of Si on all sample surfaces was comparatively analysed by EDS. In addition, the constituents of specimen surface layers after the porcelain fracture and the formed compound were evaluated by X-ray diffraction diagnosis. Result: The results of this study were obtained as follows : 1. The surface characteristics of cast and wrought titanium after surface treatment(Au, TiN, $Al_2O_3$ sandblasting) were similar and each cast and wrought titanium showed similar bonding characteristics. 2. Before and after the biaxial flection test, the highest atomic weight change of Si component was found in $Al_2O_3$ sandblasted wrought titanium(28.6at.% $\rightarrow$ 8.3at.%). On the other hand, the least change was seen in Au-Pd-In alloy(24.5at.% $\rightarrow$ 9.1at.%). 3. Much amount of Si components was uniformly distributed in Au and TiN coated titanium, but less amount of Si's was unevenly dispersed on Al2O3 sandblasting surfaces. 4. In X-ray diffraction diagnosis after porcelain debonding, we could see $Au_2Ti$ compound and TiN coating layers on Au and TiN coated surfaces and $TiO_2$, typical oxide of titanium, on all titanium surfaces. 5. Debonding of porcelain on cast and wrought titanium surface after the biaxial flection is considered as a result of adhesion deterioration between coating layers and titanium surfaces. We found that there are both adhesive failure and cohesive failure at the same time. Conclusion: These results showed that the titanium-ceramic adhesion could be improved by coating cast and wrought titanium surfaces with Au and TiN when making porcelain fused to metal crowns. In order to use porcelain fused to titanium clinically, it is considered that coating technique to enhance the bonding strength between coating kKlayers and titanium surfaces should be developed first.

• Journal of Electrochemical Science and Technology
• /
• 제8권4호
• /
• pp.294-306
• /
• 2017

Stainless steels and titanium alloys are widely used in the medical industry as replacement materials. These materials may be affected by the conditions and type of environment. In the same manner, soft drinks are widely consumed products. It is of interest for dental industry to know the behavior of medical-grade alloys when these are in contact with soft drinks, since any excessive ion release can suppose a risk for human health. In the present study, the electrochemical behavior of three stainless steel alloys and pure titanium was analyzed using three types of cola soft drinks as electrolyte. The objective of this study was to evaluate the response of these metallic materials in each type of solution (cola standard, light and zero). Different electrochemical techniques were used for the evaluation of the alloys, namely potentiodynamic polarization, linear polarization, and open-circuit potential measurements. The corrosion resistance of the stainless-steel alloys and titanium in the cola soft drinks was provided by the formation of a stable passive film formed by metal oxides. Scanning electron microscopy was used as a complementary technique to reveal corrosion phenomena at the surface of the materials evaluated.

• 한국산업융합학회 논문집
• /
• 제10권4호
• /
• pp.201-206
• /
• 2007

Most of the fatigue fractures of various machine structures start at discontinuities or small defects. In this study property of crack growth of titanium alloy was also analyzed to investigate the difference compared with the carbon steel. Titanium alloy has very high specific strength, and the material is widely utilized in advanced engineering fields such as aerospace, atomic energy and ocean development because of its excellence in corrosion and heat resistance. Generally the machine structures experience irregular loadings rather than periodic forces. The prediction of the fatigue life therefore has been analyzed to provide fundamentals of the design and estimation of the machine structures under irregular loading conditions.