• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.6-13
• /
• 2004

The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of Alloy 600(UNS N06600) was evaluated in 10% sodium hydroxide solution at $315^{\circ}C$. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours with and without inhibitors such as titanium oxide, titanium boride and cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in no inhibitor solution. It was found that the changes of the active-passive transition potentials and the film compositions were related to the resistance to stress corrosion cracking in high temperature caustic solution.

• Korean Journal of Materials Research
• /
• v.16 no.1
• /
• pp.50-57
• /
• 2006

Phase mixtures of Titanium boride, nitride, and carbide powder were produced by the reduction of a mixture of titanium and boron oxides with carbon via a gas-solid phase reaction. Boron oxides produce a vapour phase or decompose to a metal sub-oxide gaseous species when reduced at elevated temperature. The mechanism of BO sub-oxide gas formation from $B_2O_3$ and its subsequent reduction to titanium diboride for the production of uniform size hexagonal platelets is explained. These gaseous phases are critical for the formation of boride, nitride and carbide ceramics. For the production of ceramic phase composite microstructures, the nitrogen partial pressure was the most critical factor. Some calculated equilibrium phase fields has been verified experimentally. The theoretical approach therefore identifies conditions for the formation of phase mixtures. The thermodynamic and kinetic factors that govern the phase constituents are also discussed.

• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.829-834
• /
• 2004

Annealing of $Cu(B)/Ti/SiO_2$ in vacuum has been carried out to investigate the effects of Ti underlayer on microstructure in $Cu(B)/Ti/SiO_2$ structures. For comparison, $Cu(B)/Ti/SiO_2$ structures was also annealed in vacuum. Three different temperature dependence of Cu growth can be seen in $Cu(B)/Ti/SiO_2$; B precipitates- pinned grain growth, abnormal grain growth, normal grain growth. The Ti underlayer having a strong affinity for B atoms reacts with the out-diffused B to the Ti surface and forms titanium boride at the Cu-Ti interface. The formation of titanium boride acts as a sink for the out-diffusion of B atoms. The depletion of boron in grain boundaries of Cu films, as results of the rapid diffusion of B along the grain boundaries and the insufficient segregation of B to the grain boundaries, induces grain boundaries to migrate and causes the abnormal grain growth. The increased bulk diffusion coefficient of B within Cu grains can be responsible for the normal grain growth occurring in the annealed $Cu(B)/Ti/SiO_2\;at\;600^{\circ}C$. In contrast, the $Cu/SiO_2$ structures show only the abnormal growth of grains and their sizes increasing as the temperature increases above $400^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.33 no.4
• /
• pp.464-470
• /
• 1996

Toughening mechanism of boron carbide ceramics by the addition of titanium boride was investigated. Speci-men was prepared by hot pressing of boron carbide with upto 30vol% of titanium boride particulates. Toughness of boron carbide ceramics was increased from 4.7 MPa m1/2 to 6.3 MPa m1/2 with 15 vol% TiB2 addition. But further increase of TiB2 content results in slow decrease of toughness. From microstructure evaluation and crack propagation behavior it is concluded that the major toughening mechanism is crack deflection pheno-mena.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.1
• /
• pp.20-26
• /
• 2001

Titanium boride ($\textrn{TiB}_{x}$) films were deposited on (100) silicon substrates at the substrate temperature of $500^{\circ}C$ by means of the co-evaporation of titanium and boron evaporants during deposition. The co-evaporation method makes it possible to deposit the non-stoichiometric films with different boron-to-titanium ratio($0{\le}B/Ti \le 2.5$). The resistivity increases linearly as the boron-to-titanium ratio in the as-deposited films is increased. The surface roughness of $\textrn{TiB}_{x}$ films is changed as a function of the boron-to-titanium ratio. The XRD spectrum for pure titanium film shows a highly (002) preferred orientation. For B/Ti=0.59 ratio only a single TiB phase that shows a (111) preferred orientation is observed. However, the $\textrn{TiB}_{x}$ phase with the hexagonal structure of the $AlB_2$(C32) type appears as the boron concentration increase, and only a single $\textrn{TiB}_{x}$ phase is observed for $B/Ti \ge 2.0$ ratio. The $\textrn{TiB}_{x}$/Si samples reveal a tensile stress (3~$20{\times}^9$dyn/$\textrm{cm}^2$) in the overall composition of the films, although the magnitude of the residual stresses is depended on the nominal B/Ti ratio.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1099-1106
• /
• 1997

In the present study, the effect of TiB2 addition on the sintering behavior of ZrB2 ceramics was studied with hot pressing under Ar atmosphere. Hot pressing experiments were carried out in graphite dies at the 1$700^{\circ}C$, 180$0^{\circ}C$ under Ar atmosphere. The sintering density increased with increasing TiB2 contents. With the addition of 10wt% TiB2 almost theoretical density could be achieved by hot-pressing at 180$0^{\circ}C$. Zr-Ti-Fe-B compound in liquid phase was observed from the EDS and WDS analysis. It was considered that sinterability was enhanced due to the mass transfer through liquid phase formed at the sintering temperature. In addition of TiB2, transition metal of groups IV, substitutional solid solution could be formed.

• Journal of Powder Materials
• /
• v.23 no.4
• /
• pp.282-286
• /
• 2016

A sintered body of $TiB_2$-reinforced iron matrix composite ($Fe-TiB_2$) is fabricated by pressureless-sintering of a mixture of titanium hydride ($TiH_2$) and iron boride (FeB) powders. The powder mixture is prepared in a planetary ball-mill at 700 rpm for 3 h and then pressurelessly sintered at 1300, 1350 and $1400^{\circ}C$ for 0-2 h. The optimal sintering temperature for high densities (above 95% relative density) is between 1350 and $1400^{\circ}C$, where the holding time can be varied from 0.25 to 2 h. A maximum relative density of 96.0% is obtained from the ($FeB+TiH_2$) powder compacts sintered at $1400^{\circ}C$ for 2 h. Sintered compacts have two main phases of Fe and $TiB_2$ along with traces of TiB, which seems to be formed through the reaction of TiB2 formed at lower temperatures during the heating stage with the excess Ti that is intentionally added to complete the reaction for $TiB_2$ formation. Nearly fully densified sintered compacts show a homogeneous microstructure composed of fine $TiB_2$ particulates with submicron sizes and an Fe-matrix. A maximum hardness of 71.2 HRC is obtained from the specimen sintered at $1400^{\circ}C$ for 0.5 h, which is nearly equivalent to the HRC of conventional WC-Co hardmetals containing 20 wt% Co.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.91.2-91.2
• /
• 2012

The TiB2-reinforced iron matrix nanocomposite (Fe-TiB2) was in-situ fabricated from titanium hydride (TiH2) and iron boride (FeB) powders by a simple and cost-effective process that combines the mechanical activation (MA) and a subsequent heat treatment (HT). Effect of milling factors and synthesized temperatures on the formation of the nanocomposite were presented and discussed. A differential thermal analyser (DSC-TG) was employed for examination of thermal behavior of MAed powders. Phases of the nanocomposite were confirmed by X-ray diffraction analysis (XRD). The morphologies and microstructure of nanocomposite were investigated by field emission-scanning electron microscopy (FE-SEM) and energy-dispersive X-ray spectroscopy (EDS). Phase composition and distribution were analyzed by electron probe X-ray microanalysis (EPMA). Results showed that TiB2 particles formed in nanoscale were uniformly distributed in alloyed Fe matrix.

• Journal of Powder Materials
• /
• v.20 no.3
• /
• pp.221-227
• /
• 2013

$TiB_2$-reinforced iron matrix composite (Fe-$TiB_2$) powder was in-situ fabricated from titanium hydride ($TiH_2$) and iron boride (FeB) powders by the mechanical activation and a subsequent reaction. Phase formation of the composite powder was identified by X-ray diffraction (XRD). The morphology and phase composition were observed and measured by field emission-scanning electron microscopy (FE-SEM) and energy-dispersive X-ray spectroscopy (EDS), respectively. The results showed that $TiB_2$ particles formed in nanoscale were uniformly distributed in Fe matrix. $Fe_2B$ phase existed due to an incomplete reaction of Ti and FeB. Effect of milling process and synthesis temperature on the formation of composite were discussed.

• Composites Research
• /
• v.31 no.4
• /
• pp.117-121
• /
• 2018

Various ceramic particulate such as TiC, $TiB_2$, $Al_2O_3$ reinforced SUS431 matrix composites were successfully fabricated by a novel liquid pressing infiltration process. Microstructures of the SUS431 composite were analyzed to determine manufacturability of composites. $Al_2O_3$-SUS431 composite had lots of defects due to poor wettability between the $Al_2O_3$ and steel matrix. On the other hand, TiC was uniformly dispersed in the SUS431 matrix than $TiB_2$ and $Al_2O_3$ due to good wettability and interfacial properties.