• Magazine of the Korea Concrete Institute
• /
• v.11 no.1
• /
• pp.119-127
• /
• 1999

The objective of this study is to simulate the fracture behavior of composite structure bonded with more than 2 different cementitious materials. For this, concrete and cement were stacked and bonded in a direction perpendicular to loading and specimens were tested. Each constituent material of concrete and cement was fabricated independently also, and three point bending and indirect tensile tests were carried out for the acquisition of measured values applicable to the proposed model. As a result of comparing theoretical results and experimental ones, it was found that the proposed model derived from fictitious crack theory can be used to predict the fracture behavior of composite structures on the vases of well agreement with experimental results. It was also noted that the degree of improvement of fracture energies and strengths is greatly dependent on the stacking sequence of layers composing of a composite structure. Thus, it can be concluded that brittleness or ductility of a composite structure can be accomplished by a proper arrangement of layers on one's purpose throughout the proposed analysis.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.77-86
• /
• 2008

The reliability of leaded and lead-free solders of BGA type packages on a printed circuit board was investigated by employing the standard drop test and 4-point bending test. Tested solder joints were examined by optical microscopy to identify associated failure mode. Three-dimensional finite element analysis(FEM) with ANSYS Workbench v.11 was carried out to understand the mechanical behavior of solder joints under the influence of bending or drop impact. The results of numerical analysis are in good agreement with those obtained by experiments. Packages in the center of the PCB experienced higher stress than those in the perimeter of the PCB. The solder joints located in the outermost comer of the package suffered from higher stress than those located in center region. In both drop and bending impact tests, the lead-free solder showed better performances than the leaded solders. The numerical analysis results indicated that stress and strain behavior of solder joint were dependent on various effective parameters.

• Steel and Composite Structures
• /
• v.45 no.3
• /
• pp.467-482
• /
• 2022

One of the major failure modes in composite sandwich structures is the separation between skins and core. In this study, the effect of employing foam filled composite corrugated core on the skin/core debonding (resistance to separation between skin and core) is investigated both experimentally and numerically. To this aim, triangular corrugated core specimens are manufactured and compared with reference specimens only made of PVC foam core in terms of skin/core debonding under bending loading. The corrugated composite laminates are fabricated using the hand layup method. Also, the Vacuumed Infusion Process (VIP) is employed to join the skins to the core with greater quality. Utilizing an End Notched Shear (ENS) fixture, three point bending tests are performed on the manufactured sandwich composite panels. The results reveal that the resistance to separation capacity and flexural stiffness of sandwich composite has been increased about 170% and 76%, respectively by using a triangular corrugated core. The Cohesive Zone Model (CZM) with appropriate cohesive law in ABAQUS finite element software is used to model the progressive face/core interfaces debonding the difference between experimental and numerical results in predicting the maximum born load before the skin/core separation is about 6 % in simple core specimens and 3% in triangular corrugated core specimens.

• Journal of Ocean Engineering and Technology
• /
• v.27 no.2
• /
• pp.69-74
• /
• 2013

In this study, the crack healing effects of $Al_2O_3$ ceramics based on the heat treatment conditions were investigated. The influence of the additive amounts of SiC nanoparticles and the cycling process of indentation-heat treatment on the crack healing effect of $Al_2O_3$ ceramics were also examined. Three-point bending tests were carried out and the morphological changes in the fracture surface were observed by using FE-SEM. As a result, heat-treated samples in a vacuum or air atmosphere showed improved bending strengths compared to un-heat treated samples. This means that cracked specimens can be healed by heat treatment in a vacuum or air atmosphere. The crack healing effect of $Al_2O_3$ ceramics that were heat treated in an air atmosphere was much higher than that of those heat treated in a vacuum. After heat treatment, the $Al_2O_3$ ceramics with 30 wt% SiC nanoparticles showed a higher bending strength than those with 15 wt% SiC. The cyclic indentation and heat treatment did not remarkably affect the crack healing effect. The SEM images showed that the median crack, indenter mark on the surface, and pores in the fracture surface of a specimen almost disappeared after being heat treated in an air atmosphere.

• Composites Research
• /
• v.30 no.2
• /
• pp.158-164
• /
• 2017

The fiber metal laminate is a type of hybrid materials laminated thin metallic sheets with fiber reinforced plastic sheets. The laminate has been researched or applied in automotive and aerospace industries due to their outstanding impact absorbing performance in view of light weight aspect. Specially, the replacement of side-impact beam as the fiber reinforced plastic has been researched actively. The objective of this paper is the primitive investigation in the development of side-door impact beam using the fiber metal laminate. First, the three-point bending simulations were conducted to decide the shape of impact beam using the numerical analysis. Next, two cases impact beam (pure DP 980 and fiber metal laminate) were installed in the side-door, and then the bending tests (according to FMVSS 214S) were simulated using the numerical analysis. It is noted that the side-door impact beam can be replaced with the fiber metal laminate sufficiently based on the numerical analysis results.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.34-37
• /
• 2001

This study developed Fiber/Particle Hybrid MMCs and analyzed their mechanical properties. Using $\textrm{Al}_2\textrm{O}_3f$ and $\textrm{Al}_2\textrm{O}_3p$ with the fiber to particle ratio of 1:1, 1:3, 1:5 hybrid preform and MMCs are fabricated. For the analysis of the mechanical properties, three point bending tests were preformed for the preform and tensile test for the MMCs. The experimental results show that the hybrid MMCs can be successfully fabricated using the equipment of fiber preform fabrication system and squeeze casting method. And as the amount of particle in hybrid MMCs increases, the tensile strength, elastic modulus and the volume fraction of reinforcement increases.

• Computers and Concrete
• /
• v.9 no.1
• /
• pp.51-61
• /
• 2012

According to the results of three-point bending tests of rubberized concrete and plain concrete, the parameters such as total fracture energy ($G_F$), initial fracture energy ($G_f$), and tensile strength ($f_t$) are obtained for concrete material. Using ABAQUS software and a bilinear softening fictitious crack model, the crack propagation process was simulated and compared to the experimental results. It is found that the increase of AE hit count has a similar trend with the increase of energy dissipation in FEM simulation. For two types of concretes, both experimental results and numerical simulation indicate that the rubberized concrete has a better fracture resistance.

• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.135-139
• /
• 2002

Carbon powders (CP) and carbon fiber (CF) were introduced info glass fiber reinforced plastics (FRP) composites to obtain fracture detection function. The composites were evaluated through the relation between a load-displacement curve and an electrical resistance change curve in three point bending test. CP containing FRP (CP-FRP) has a sensitivity of electrical resistance change at much lower load level than CF containing FRP (CF-FRP). In loading-unloading tests, CP-FRP showed a large amount of residual electrical resistance which enables the estimation of loading hysteresis.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.739-744
• /
• 2000

Concrete structures generally have cracks, so for the safety and durability of structures, studies to detect cracks using nondestructive tests have been treated in great deal. In order to assure the reliability of concrete structure, microscopic fracture behavior and internal damage progress of concrete under the loading should be fully understood. The purpose of this study predicts location of initial crack and measures direction of crack propagation for on-line monitoring before the crack really grows in structures by using two-dimensional Acoustic Emission(AE) source location based on rectangular method with three-point bending test. This will allow efficient maintenance of concrete structure through monitoring of internal cracking based on AE method.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.147-150
• /
• 2004

In order to describe the mechanical behavior of highly anisotropic and asymmetric materials such as fiber­reinforced composites, the elastic-plastic constitutive equations were used here based on the recently developed yield criterion and hardening laws. As for the yield criterion, modified Drucker-Prager yield surface was used to represent the orthotropic and asymetric properties of composite materials, while the anisotropic evolution of back­stress was accounted for the hardening behavior. Experimental procedures to obtain the material parameters of the hardening laws and yield surface are presented for 3D Circular Braided Glass Fiber Reinforced Composites. For verification purpose, comparisons of finite element simulations using the elastic-plastic constitutive equations, anisotropic elastic constitutive equations and experiments were performed for the three point bending tests. The results of finite element simulations showed good agreements with experiments, especially for the elastic-plastic constitutive equations with yield criterion considering anisotropy as well as asymmetry and anisotropic back stress evolution rule.