• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.416-416
• /
• 2016

Organic-inorganic metal halide perovskite solar cells have received attention because it has a number of advantages with excellent light harvesting, high carrier mobility, and facile solution processability and also recorded recently power conversion efficiency (PCEs) of over 20%. The major issue on perovskite solar cells have been reached the limit of small area laboratory scale devices produced using fabrication techniques such as spin coating and physical vapor deposition which are incompatible with low-cost and large area fabrication of perovskite solar cells using printing and coating techniques. To solution these problems, we have investigated the feasibility of achieving fully printable perovskite solar cells by the blade-coating technique. The blade-coating fabrication has been widely used to fabricate organic solar cells (OSCs) and is proven to be a simple, environment-friendly, and low-cost method for the solution-processed photovoltaic. Moreover, the film morphology control in the blade-coating method is much easier than the spray coating and roll-to-roll printing; high-quality photoactive layers with controllable thickness can be performed by using a precisely polished blade with low surface roughness and coating gap control between blade and coating substrate[1]. In order to fabricate perovskite devices with good efficiency, one of the main factors in printed electronic processing is the fabrication of thin films with controlled morphology, high surface coverage and minimum pinholes for high performance, printed thin film perovskite solar cells. Charge dissociation efficiency, charge transport and diffusion length of charge species are dependent on the crystallinity of the film [2]. We fabricated the printed perovskite solar cells with large area and flexible by the bar-coating. The morphology of printed film could be closely related with the condition of the bar-coating technique such as coating speed, concentration and amount of solution, drying condition, and suitable film thickness was also studied by using the optical analysis with SEM. Electrical performance of printed devices is gives hysteresis and efficiency distribution.

• Tribology and Lubricants
• /
• 제27권3호
• /
• pp.147-155
• /
• 2011

The ceramic coatings are excellent materials of cutting tools and sliding parts. To evaluate the wear characteristics of very thin ceramic coated layer, it is very important to investigate its wear process microscopically. An effective method for investigating the wear of a thin layer is the observation of wear process in microscopic detail using in-situ system. In this study, using the SEM Tribosystem as in-situ system, the microscopic wear mode of TiN coatings was investigated in repeated sliding. As results, four modes were observed for TiN coatings: Ploughing, powder formation, flake formation and coating delimitation. The observation of the microscopic wear by in-situ system can clarify the allowable stress of TiN coating.

• 한국세라믹학회지
• /
• 제34권1호
• /
• pp.37-44
• /
• 1997

졸겔법중 딥코팅법을 이용하여 조성비 2Fe/Ba=5.25 졸로부터 바륨페라이트 박막을 제조하였다. 졸의 겔화과정은 4단계로 구분할 수 있으며, 8$0^{\circ}C$에서 90분간 반응시켜 제조한 졸이 코팅용 졸로서 가장 적합한 특성을 나타내었다. 박막층에 형성된 침상 형태의 입자들은 기판에 수평 하게 위치하고 있었으며, 박막 두께가 증가함에 따라 그 경향은 증가하였다. 침상형 입자의 자화용이축 방향은 장축 방향이었다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2002년도 추계학술대회 논문집
• /
• pp.659-662
• /
• 2002

SL(Stereolithography) part is made by piling up thin layers which causes the stair stepping effect at the surface of SL parts. This effect brings about excessive surface roughness and requires additional post-process finishing such as abrasive techniques that are detrimental to part geometry and time consuming. Hence a wax coating and grinding post-process is proposed to improve the surface quality of SL part. The wax that has suitable properties for the proposed post-process is coated all over the part surface. By grinding the thin layer of coated on the SL part only, the surface roughness can be improved without any damage on the part. From the experimental results, This approach is considered to be very practical fur die casting with RT(Rapid Tooling) techniques.

• 한국세라믹학회지
• /
• 제32권4호
• /
• pp.516-524
• /
• 1995

In this study, to prepare the dielectric (Ba, Sr)TiO3 thin films by the sol-gel process, Titaminum (IV) sio-propoxide (Ti[OCH(CH3)2]4), Ba and Sr acetate were used for sol and thin films were prepared by dip-coating process. Stability of sol decreased with the increase of Sr, and thickness of thin films were obtained 0.13~0.17${\mu}{\textrm}{m}$ by 1 coating cycle. Transmittance of amorphous thin films heated at 500 and 55$0^{\circ}C$ was very good, and crystallization tendency of thin films according to heat-treatment temperature and crystallization characteristics of thin films heated at 11$0^{\circ}C$ for 3 hrs were analysed. As a result, good perovskite structure was obtained higher than 100$0^{\circ}C$, and tetragonality of thin film was decreased but pyrochlore was formed with increasing Sr. In case of addition to substitute 0.4mol% Sr for Ba, dielectric constant was 288 and loss factor (tan $\delta$) was 0.04.

• 한국세라믹학회지
• /
• 제33권11호
• /
• pp.1195-1202
• /
• 1996

To prepare the dielectric thin films of (Pb1-xSrx)TiO3 (x=0.1, 0.2, 0.3, 0.35, 0.5) by the sol-gel process titanium (IV) isopropoxide (Ti[OCH(CH3)2]4) and Pb Sr, acetate were used therefore the thin films were fabricated by dip-coating method. Stability of the sol decreased with addition of Sr content thin films could be fabricated up to 35mol% Over this range precipitation of sol occured thin films couldn't be obtained. Transmittance of thin films at visible range decreased with the increase of heat-treatment temperature but exhibited transmit-tance above 60% in all case. Moreover transmittance of thin films at visible range slightly increased with of addition of Sr,. When thin film containing 30 mol% srontium was heated at 600℃ the best perovskite phase was obtained. The dielectric constant (ε) was 280 and dielectric loss factor (tan δ) was 0.021 and curie tempera-ture (Tc) decreased with the increase of addition of Sr.

• 한국재료학회지
• /
• 제24권3호
• /
• pp.145-151
• /
• 2014

Solution-based Sb-doped $SnO_2$ (ATO) transparent conductive oxides using a low-temperature process were fabricated by an electrospray technique followed by spin coating. We demonstrated their structural, chemical, morphological, electrical, and optical properties by means of X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, atomic force microscopy, Hall effect measurement system, and UV-Vis spectrophotometry. In order to investigate optimum electrical and optical properties at low-temperature annealing, we systemically coated two layer, four layer, and six layers of ATO sol-solution using spin-coating on the electrosprayed ATO thin films. The resistivity and optical transmittance of the ATO thin films decreased as the thickness of ATO sol-layer increased. Then, the ATO thin films with two sol-layers exhibited superb figure of merit compared to the other samples. The performance improvement in a low temperature process ($300^{\circ}C$) can be explained by the effect of enhanced carrier concentration due to the improved densification of the ATO thin films causing the optimum sol-layer coating. Therefore, the solution-based ATO thin films prepared at $300^{\circ}C$C exhibited the superb electrical (${\sim}7.25{\times}10^{-3}{\Omega}{\cdot}cm$) and optical transmittance (~83.1 %) performances.

• 한국표면공학회지
• /
• 제50권5호
• /
• pp.345-351
• /
• 2017

A double-layered anti-reflective coating with hydrophilic/abrasion-resistant properties was studied using anatase titanium dioxide($TiO_2$) and silicon oxycarbide($SiO_xC_y$) thin film. $TiO_2$ and $SiO_xC_y$ thin films were sequentially deposited on a glass substrate by DC sputtering and PECVD, respectively. The optical properties were measured by UV-Vis-NIR spectrophotometer. The abrasion-resistance and the hydrophilicity were observed by a taber abrasion tester and a contact angle analyzer, respectively. The $TiO_2/SiO_xC_y$ double-layer thin film had an average transmittance of 91.3%, which was improved by 10% in the visible light region (400 to 800 nm) than that of the $TiO_2$ single-layer thin film. The contact angle of $TiO_2/SiO_xC_y$ film was $6.9^{\circ}$ right after UV exposure. After 9 days from the exposure, the contact angle was $10.2^{\circ}$, which was $33^{\circ}$ lower than that of the $TiO_2$ single-layer film. By the abrasion test, $SiO_xC_y$ film showed a superior abrasion-resistance to the $TiO_2$ film. Consequently, the $TiO_2/SiO_xC_y$ double-layer film has achieved superior anti-reflection, hydrophilicity, and abrasion resistance over the $TiO_2$ or $SiO_xC_y$ single-layer film.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2011년도 춘계학술대회
• /
• pp.676-677
• /
• 2011

초경합금 성형용 코어를 이용한 고온 압축 성형방식으로 제작되기 때문에 성형용 코어의 초정밀 연산 가공 및 코어면 코팅 기술 개발이 시급한 상황이다. 따라서 본 연구에서는 성형용 초경합금 코어의 연삭가공을 수행하고, 가공 완료된 성형용 코어의 가공면에 Re-Ir 코팅을 수해, 측정을 통하여 코팅면의 마찰 계수 변화에 대한 연구를 수행하였다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 추계학술대회 논문집
• /
• pp.467-471
• /
• 2005

In this paper, experimental methods about the flow behavior of thin polymer film by various edge patterns in the spin coating process for stable cover layer coating of a blu-ray disc is described. The blu-ray disc, a next-generation optical disc format over 25GB, consists of a 1.1m thick substrate and a 0.1mm tick cover layer. Generally, cover layer on the blu-ray disc is made by the polymer spin coating process. However, it is hard to secure sufficient coating uniformity around the rim on the cover layer. In order to get the uniform thickness deviation and to minimize the bead around the rim, the edge of the disc substrate can be modified into various patterns, such as normal plain, trench, step and chamfer pattern, etc, around the rim on the disc and experimented with various parameters, such as surface tension, viscosity, coating time, temperature and rotation speed, etc. And the optimal shape of the rim was tried to get by 3 dimensional computer simulation of the polymer expulsion process.