• Current Photovoltaic Research
• /
• v.2 no.3
• /
• pp.110-114
• /
• 2014

We propose a low temperature sol-gel ZnO/Ag nanowire composite thin film to fulfill low temperature and low cost requirements, which are essential criteria in future flexible electronic devices. In this proposed thin film, Ag nanowire plays the role of electrical conduction, and sol-gel ZnO provides a structural medium with a high visible transmittance. Low temperature restriction in the sol-gel fabrication process prevents sufficient oxidation of Zn acetate precursors, which were solved by a post-coating treatment with ultraviolet light irradiation. Composite thin film formation was performed by spin coating methods with a mixed precursor solution or in a sequential manner. We obtained an average visible transmittance larger than 85% and a sheet resistance smaller than $50{\Omega}/sq$. After optimization in a fabricated composite transparent conductive thin film with the thickness around 100 nm. Similar experimental demonstration in a flexible substrate (polyethyleneterephthalate) was successful, which implies a promising application opportunity of this technology.

• Korean Journal of Materials Research
• /
• v.18 no.4
• /
• pp.211-217
• /
• 2008

A $ZrO_2$ coating solution containing $ZrO_2$ photo-catalysis, which is transparent in visible light, was prepared by the hydrolysis of alkoxide, and thin films on the $SiO_2$ glass substrate were formed in a dipcoating method. These thin films were heat-treated at temperatures ranging from $250^{\circ}C-800^{\circ}C$ and their characteristics were subjected to thermal analysis, XRD, spectrometry, SEM, EDS, contact angle measurement, and AFM. Tetragonal $ZrO_2$ phase was found in the thin film heat treated at $450^{\circ}C$, and anatase $TiO_2$ phase was detected in the thin film heat-treated at $600^{\circ}C$ and above. The thickness of the films was approximately 300 nm, and the roughness was 0.66 nm. Thus, the film properties are excellent. The films are super hydrophilic with a contact angle of $4.0^{\circ}$; moreover, they have self-cleaning effect due to the photo catalytic property of anatase $TiO_2$.

• Journal of the Korean Chemical Society
• /
• v.65 no.2
• /
• pp.125-132
• /
• 2021

An electrochromic nickel oxide thin film was fabricated on a flexible PET/ITO substrate using a nanocrystallite- dispersed coating sol and bar coater. Nanocrystalline NiOx of 3-4 nm crystallite size was first synthesized by base precipitation and thermal conversion. This NiOx nanocrystallite powder was mechanically dispersed in an alcoholic solvent mixed with a silane binder to prepare a coating sol for thin film. This sol method is different from the normal sol-gel method in that it does not require the conversion of precursor by heat treatment. Therefore, this method provides a very facile method to prepare NiOx thin films on any kind of substrate and it can be easily applied to mass production. The electrochromic performance of this NiOx thin film on PET/ITO electrode with a thickness of about 400 nm was investigated in a nonaqueous LiClO4 electrolyte solution by cyclic voltammetric and repeated chronoamperometric measurements in conjunction with spectrophotometry. The visible light modulation of 44% and the colorization efficiency of 41 ㎠/C at 550 nm were obtained at the step potentials of -0.8/+1.2 V vs Ag and a duration of 30 s.

• Journal of Ceramic Processing Research
• /
• v.20 no.6
• /
• pp.603-608
• /
• 2019

In this study, the multilayered thin films of (Ba,Sr)TiO3/K(Ta,Nb)O3 were fabricated by the sol-gel and spin coating methods, and their structural and electrical properties were investigated. The specimen showed polycrystalline X-ray diffraction (XRD) characteristics with a tetragonal structure. The average grain size and film thickness for one coating were about 30~40nm and 60nm, respectively. The phase transition temperature of specimen was lower than 10 ℃. The dielectric constant and loss at 20 ℃ of the specimen coated six times were 1,231 and 0.69, respectively. The rate of change in dielectric constant at an applied direct current (DC) voltage of the six times coated thin films was 17.3%/V. The electrocaloric effect was the highest around the temperature at which the remanent polarization rapidly changed. When an electric field of 660kV/cm was applied to the triply coated thin films, the highest electrocaloric property of 4.41 ℃ was observed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.5
• /
• pp.230-234
• /
• 2013

IR cut-off thin films consisted of ATO nanoparticles were successfully fabricated by sol-gel method. The coating solution was synthesized with organic/inorganic hybrid binder and ATO colloidal solution and ATO thin films were coated on a slide glass with the withdrawal speed of 5~40 mm/s. As the withdrawal speed increased from 5 mm/s to 40 mm/s, the thickness of coating thin films also increased from $1.05{\mu}m$ to $4.25{\mu}m$ and the IR cut-off in wavelength of 780~2500 nm increased from 49.5 % to 66.7 %. In addition, the pencil hardness of ATO thin films dried at $80^{\circ}C$ was ca. 5H and the coating films were not removed after a cross cutter tape test because of the hybrid binder synthesized with tetraethylorthosilicate and methyltrimethoxysilane. The surface morphologies, optical properties and film thickness of prepared thin films with a different withdrawal speed were measured by field emission scanning electron microscope (FE-SEM), UV-Vis spectrophotometer, and Dektak.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.7-8
• /
• 2002

It is a time to introduce a concept of lubrication to space systems. Minimum amount of lubricant should be supplied to a contact interface instead of preparing too much lubricant on surfaces of the earth. In situ controllable lubrication method is wanted to overcome unexpected tribo-troubles in space. Tribo-coating, which forms a thin solid film in nm-scale by vacuum deposition during friction, is a promising lubrication method for space.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10a
• /
• pp.57-58
• /
• 2003

Thin coating layer of clay minerals was fabricated on nylon fiber and uv-light resistivity of the clay-coated nylons, schematically shown in Figure 1, were investigated. Clay minerals with higher absorbance protect the nylon fibers more effectively from uv light. The coating process is expected as safe and stable procedure because clay and aqueous dispersion of the clay used for the process is innocuous.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.10 no.1
• /
• pp.35-54
• /
• 1992

Direct electrostatic coating method is simple, low cost and environmentally useful method. We are investigated on the coating of carrier transfer polymer layer on the carrier generate inorganic pigment layer using direct electrostatic coating method. The sample was obtained electrostatic deposite layer by fusing and calendering on the copper phthalocyanine. we could be found several polymer thin film shows good bond properties between film and pigment layer.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.9 no.1
• /
• pp.1-11
• /
• 1991

In this reseach, double-layered photoconductor consist of the carrier generation layer(CGL) of $\varepsilon$ type copper phthalocyanine thin film by an aqueous coating method and the carrier transport layer(CGL) of polyvinyl carbazol(PVK) by spin coating. We inverstigated effect of the surfactant solution and cathod electrolysis to the crystal type of $\varepsilon$-CuPc in CGL with TEM, SEM and X- ray diffraction spectroscopy and studied the mechanism of an aqueous coating for the preparation of CGL. The effect of the washing of CGL about the electrophotographic characteristics of the $\varepsilon$-CuPc/PVK doublelayered photoconductors is studied also.

• Applied Chemistry for Engineering
• /
• v.34 no.1
• /
• pp.30-35
• /
• 2023

The glass bead surface was coated using a TiO₂ sol, after which dry-treated (TB) and calcined (TBc) samples were prepared. Photocatalytic degradation of methylene blue and toluene, as well as characterization of the TiO₂ thin films, were carried out. The TiO₂ thin film of the TB sample had the same shape as the sponge foam, according to FE-SEM, XPS, and FTIR analyses, and contained both amorphous and crystalline TiO₂. On the other hand, crystalline TiO₂ was mainly present in the TiO₂ thin film of the TBc sample, and needle-shaped particles and tiny ones were mixed. The adsorption capacity for methylene blue and the degradation rate of the TBc sample were less than 10 % compared with those of the TB sample, and the adsorption capacity and degradation rate of the TBc sample decreased similarly as the amount of TiO₂ coating increased. The amount of toluene adsorption for the TBc sample (46 mg/g) was smaller than that of the TB sample with the same coating amount, but the degradation rate was similar. In the case of the TB sample, the degradation rate for toluene decreased less than the adsorption capacity as the amount of TiO₂ coating increased. This result is considered to be because, in the non-calcined TB sample, the active site reduction of the crystalline particles occurred less and the specific surface area of the amorphous texture decreased as the amount of TiO₂ coating increased.