• Applied Science and Convergence Technology
• /
• 제26권4호
• /
• pp.62-65
• /
• 2017

Passivation of surface defects by the formation of chemically inert structure at the surface of $TiO_2$ nanocrystals can be potentially useful in enhancing their photocatalytic activity. In this regard, we have studied the surface chemical states of $TiO_2$ surfaces prepared by a treatment in the afterglow of $N_2$ microwave plasma using X-ray photoemission spectroscopy (XPS). We find that nitrogen is incorporated into the surface after the treatment up to a few atomic percent. Interestingly, the surface oxynitride layer is found to be chemically stable when it's in contact with water at room temperature (RT). The surface nitrogen species were also found to be thermally stable upon annealing up to $150^{\circ}C$ in the atmospheric pressure. Thus, we conclude that the treatment of oxide materials such as $TiO_2$ in the afterglow of $N_2$ plasma can be effective way to passivate the surface with nitrogen species.

• 자원리싸이클링
• /
• 제18권4호
• /
• pp.24-30
• /
• 2009

희토류 원소를 기반으로한 알루미늄산 형광체에 담지된 산화티탄은 졸겔방법 으로 제조되었다. 이렇게 제조된 산화티탄 나노입자의 재료물성을 분석하기 위해 XRD, FT-IR, DRS UV-Vis, TEM 측정을 실시하였다. 형광체에 담지된 산화티탄 입자의 소결 전후의 XRD분석결과는 600도 이상의 온도에서 아나타제에서 루틸로 상변화가 일어나지 않았다. 600도 이상의 온도에서 지속적인(장시간) 열처리 후에도 형광체에 담지된 산화티탄이 결정화도가 높은 아나타제로 존재 하는 것은 형광체 지지체와 담지된 산화티탄의 서로 다른 결정입계에 의하여 결정성장과 상변화에 필요한 치밀화가 억제되기 때문으로 판단된다. DRS측정결과 형광체에 담지된 산화티탄은 산화티탄이 없는 형광체에 비하여 보다 긴 장파로 쉬프트한 것은 밴드갭 에너지의 환원을 나타낸다. 이러한 형광체에 담지된 산화티탄의 FT-IR 스펙트럼은 피크의 위치가 더 높은 파수로 이동하였다. 이것은 산화티탄 입자와 지지체 사이의 공유결합이 관계하기 때문 이라 판단된다. TEM 이미지는 형광체 지지체에 다른 입자 크기로 담지되어 있는 산화티탄의 분산, 결정화 및 입자 형상을 나타낸다.