Temperature increase during OLED operation can significantly degrade the device lifetime. By using top-emission OLEDs fabricated on glass and silicon substrates that have different thermal conductivities, we found that efficient heat dissipation and corresponding lifetime improvement can be obtained by making a direct contact between the OLED anode and the high thermally-conductive silicon substrate. We describe substrate-dependent OLED heat dissipation behavior and OLED lifetime improvement by using infrared camera images and constant current stress test methods.

• 한국안전학회지
• /
• 제13권3호
• /
• pp.88-95
• /
• 1998

In this paper, we investigated the change of wettability, surface potential decay and dielectric properties caused by ultraviolet-treated, thermal-treated and discharge-treated FRP(fiber reinforced plastics) respectively for finding out the influence of dry treatments effected to electrical characteristics on the surface of polymer composites. For the change of wettability, the contact angle of thermal-treated specimen with the high temperature of $200^{\circ}C$ increased. But that of UV-treated and discharge- treated specimen decreased. The characteristic of surface potential decay shows the tendency of the remarkable decrease on UV-treated and discharge-treated specimens, but no difference on thermal-treated specimen compared with untreated one. Also, for the dielectric properties, it shows the increase at large on the treated specimens and especially, the remarkable increase on thermal-treated one.

• Composites Research
• /
• 제33권5호
• /
• pp.268-274
• /
• 2020

이 연구에서는 에폭시 수지에 나노 실리카 입자의 농도가 열화 거동에 미치는 영향에 대해 알아보았다. 약 12 nm 크기의 실리카 입자를 에폭시 수지에 세가지 무게비로 섞은 나노 복합소재를 제작하여 열중량분석(Thermogravimetric Analysis, TGA)을 이용하여 여섯 가지의 서로 다른 승온률 하에서 열화거동 변화를 분석하였다. 등변환법(Isoconversional Method)에 기초한 Friedman, Flynn-Wall-Ozawa, Kissinger 그리고 DAEM(Distributed Activation Energy Method) 방식으로 활성화에너지를 정량적으로 계산하였다. 계산 결과에 의하면 순수 에폭시와 비교했을 때, 실리카 입자가 함유될 경우 활성화에너지가 상승한다는 것을 확인할 수 있었다. 그러나 10%와 18%의 활성화에너지 값이 유사함에 따라 반드시 함유랑에 비례하지는 않는 것으로 나타났다. 또한 각 방법에 의한 계산방식을 분석하여 그 결과를 비교하였다.

• 한국재료학회지
• /
• 제27권1호
• /
• pp.25-31
• /
• 2017

This study investigates changes in the mechanical behaviors, especially hardness and indentation load-displacement curves, of thermal barrier coatings (TBCs) brought about by thermal shock. The TBCs on the Nickel-based bondcoat/superalloy was prepared with diameters of 25.4 mm and $600{\mu}m$ thickness. The results of thermal shock cycling test from $1100^{\circ}C$ of the highest temperature indicate that the thermal shock do not influence on the mechanical behavior, but a continuous decrease in porosity and increase in hardness were observed after 1200 thermal shock cycles; these changes are believed to be due to sintering of thermal barrier coating materials. The results that no degradation in the indentation load-displacement curves indicate that the coating shows good thermal shock resistance up to 1200 cycles at $1100^{\circ}C$ in air.

• 대한기계학회논문집A
• /
• 제22권2호
• /
• pp.311-320
• /
• 1998

The cryogenic fracture behaviors of austenitic stainless steel HN2 developed for nuclear fusion reactor were evaluated quantitatively by using the small punch(SP) test. The electrochemical polarization test was applied to study thermal aging degradation of HN2 steel. The X-ray diffraction(XRD) analysis was conducted to detect carbides and nitrides precipitated on the grain boundary of the heat treated HN2 steel. The mechanical properties of the HN2 steel significantly decreased with increasing time and temperature of heat treatment or with decreasing testing temperature. The integrated charge(Q) obtained from electrochemical polarization test showed a good correlation with the SP energy(ESP) obtained by means of SP tests. From the results observed in the x-ray diffraction and anodic polarization curve, it was known that the material the grain boundary. Combining SP test and electrochemical polarization test, it could be useful tools to non-destructively evaluate the cryogenic fracture behaviors and the aging degradation for cryogenic structural material.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 추계학술대회 논문집
• /
• pp.203-206
• /
• 2009

Agglomeration of catalysts is known as one of the major degradation mechanisms. Reforming of liquid fuel, which requires high temperature over $800^{\circ}C$, accelerates agglomeration of catalysts. In this work, The effects of agglomeration on catalysts activity in partial oxidation reforming conditions were investigated. Metal supported catalysts(Pt-CGO, Ru-CGO) were compared to perovskite-structured catalysts(NECS-P1, NECS-P2). High thermal stability of perovskite-structured catalysts was reported. Micro-reactor installed in electric furnace was used. its Temperature was raised from $800^{\circ}C$ to $1000^{\circ}C$ to accelerate agglomeration effect. To measure rate of agglomeration, BET analysis and CO pulse chemisorption were conducted on catalysts exposed to $1100^{\circ}C$. Metal supported catalysts showed degradation at $1000^{\circ}C$ and The rates were different according to metal supported. On the other hand perovskite-structured catalysts showed no degradation at $1000^{\circ}C$.

• Steel and Composite Structures
• /
• 제45권3호
• /
• pp.369-388
• /
• 2022

Composite effect between steel and recycled aggregate concrete (RAC) in steel reinforced-RAC (SRRAC) structures can effectively improve RAC's adverse mechanical properties due to the natural defects of recycled coarse aggregate (RCA). However, the performance of SRRAC after thermal exposure will have a great impact on the safety of the structure. In this paper, firstly, the mechanical properties of SRRAC structures after high temperatures exposure were tested, including 24 SRRAC columns and 32 SRRAC beams. Then, the change rules of beams and columns performance with the maximum temperature and replacement percentage were compared. Finally, the formulas to evaluate the residual bearing capacity of SRRAC beams and columns after exposure to high temperatures were established. The experimental results show that the maximum exposure temperature can be judged by the apparent phenomenon and mass loss ratio of RAC. After high temperatures exposure, the mechanical properties of SRRAC beams and columns change significantly, where the degradation of bearing capacity and stiffness is the most obvious. Moreover, it is found that the degradation degree of compression member is more serious than that of flexural member. The formulas of residual bearing capacity established by introducing influence coefficient of material strength agree well with the experimental results.

• 한국식품과학회지
• /
• 제24권3호
• /
• pp.232-235
• /
• 1992

2%의 MSG 용액 가열 중 pH변화에 가열온도와 초기 pH가 어떤 영향을 주는지 조사하고져, 가열온도 $100{\sim}120^{\circ}C$와 $pH2{\sim}9$의 범위에서 가열하였다. 그 결과 가열온도가 높을수록 그리고 초기 pH가 낮아지면서 MSG의 용액은 pH감소가 빨라졌으며, pH의 감소는 MSG 분해에 따른 pyroglutamic acid의 생성에 기인됨이 확인되었다. pH 감소와 가열시간의 대수값 간에는 직선관계가 있었으며 직선의 기울기에서 pH 감소속도상수를 계산하였다. pH의 감소정도(pH)는 3시간 가열 후, 초기 pH가 4일 때는 $120^{\circ}C$에서 1.2 그리고 초기 pH5와 $120^{\circ}C$에서는 0.33으로 큰 차이가 있었으며 초기 $pH6{\sim}9$에서는 감소됨이 거의 없었다. 가열 중 pH의 감소 활성화에너지는 초기 pH4에선 11.77 그리고 pH5에선 22.26kcal/mo1e 계산되었다.

• 한국화재소방학회논문지
• /
• 제23권3호
• /
• pp.103-109
• /
• 2009

콘크리트의 온도에 의한 재료적 특성에 대한 저감은 두 가지 메커니즘에 기인한다. 첫 번째 메커니즘은 온도범위에 따른 구성성분의 상변화이다. 초기 구성성분들은 온도 증가로 인해 다른 성분들로 상변화를 일으킨다. 두 번째 메커니즘은 온도에 의한 각 구성성분의 역학적 특성 변화이다. 따라서 고온에 노출된 콘크리트의 재료적 특성에 관한 모델 역시 이 두 가지 메커니즘을 함께 고려하여 제시되어야 한다. 본 연구는 위에서 언급한 두 가지 메커니즘을 고려한 고온에 노출된 콘크리트의 재료적 특성 모델을 제안하기 위한 기반연구로서, 온도범위에 따른 상변화를 고려한 경화된 시멘트 페이스트의 공극률에 대한 이론적 모델을 제시한다.

• 한국재료학회지
• /
• 제8권11호
• /
• pp.1048-1054
• /
• 1998

Pt 상부 전극 증착온도가 Pb(Zr,Ti)$O_3$(PZT) 박막의 전기적 특성에 미치는 영향에 대하여 연구하였다. Pt 상부 전극을 $200^{\circ}C$이상의 고온에서 증착하는 경우, Pt 전극의 하부에 위치한 PZT 박막은 강유전 특성이 심하게 저하되었으나, Pt 전극이 증착되지 않았던 부분은 강유전 특성이 저하되지 않았다. 이와 같은 현상이 발생된 것은 진공 chamber 내의 수증기가 Pt 상부전극의 촉매 작용에 의해 수소 원자로 분해되고, 이 분해된 수소 원자가 고온에서 Pt 하부의 PZT 박막 내로 확산해 들어가 PZT박막에 산소 공공을 만들어 내기 때문이다. Pt의 촉매 작용이 없이는 수증기의 수소 원자로의 분해가 어려우므로 Pt 전극이 덮여져 있지 않는 PZT 박막은 강유전 특성이 저하되지 않는다. 이러한 강유전 특성의 저하는 산소 분위기의 RTA(rapid thermal annealing)처리에 의해 회복이 되었다. 한편, 누설전류 특성은 Pt 상부 전극의 증착온도가 증가함에 따라 향상되는 특성을 보였다.