• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.2
• /
• pp.119-130
• /
• 2007

Purpose: This investigation was designed to estimate the flexure strength, density, and microstructure of the colored and uncolored zirconia oxide ceramics for fixed partial denture. Material and Methods: LAVATM All Ceramic(3M-ESPE, USA), Cercon Smart Ceramic(Dentsply, USA), and Z-match Ceramic(DentAim, Korea) were used for this study. All specimen was fabricated by ASTM C1161. After preparing $25{\times}2{\times}1.5mm$ of rectangular column and sitting rectangular column on universal test machine (UTM), external supporting point distance is 20.0 mm, internal supporting point distance is 10.0 mm. Specimen was loaded with 0.2 mm/min of cross head speed until fracture and at the time of broken of specimen, measuring loading value with PC software. Results: The results were obtained as follows: 1. Flexure strength of uncolored zirconia was higher than that of colored zirconia. 2. In uncolored zirconia, flexure strength of LAVATM Ceramic was more higher than the other ceramics, and it showed statistical difference between LAVATM Ceramic and Cercon Smart Ceramic (P<0.05). 3. In colored zirconia, flexure strength of LAVATM Ceramic was more higher than the other ceramics too, but they did not show statistical difference (p>0.05). 4. In Weibull analysis, Characterastic strength was showed highest value to uncolored LAVATM Ceramic and lowest value to Z-match ceramic, and Weibull modulus(m) of uncolored zirconia was higher than that of colored zirconia. 5. In XRD analysis, all group except Z-match showed high peak of t-ZrO2 but they did not show m-ZrO2. Colored zirconia group showed lower peak of t-ZrO2 than that of uncolored zirconia group.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.2
• /
• pp.157-170
• /
• 2007

Purpose: This investigation was designed to determine the translucency and color stability of various core ceramics for all-ceramic restoration using the CIE $L^*a^*b^*$ system. Material and Methods: IPS e.max Press ceramic(Ivoclar-Vivadent, Liechtenstein), $LAVA^{TM}$ All Ceramic(3M-Espe, Germany), Cercon Smart Ceramic(Dentsply, Germany), and Z-match Ceramic(DentAim, Korea) were used for this study. For the specimens of zirconia oxide ceramics, the as-sintered cylindrical blanks($11.0{\times}25.0mm$) were machined into the shape of a disk(0.4, 0.8, 1.5 mm in thickness, 10 mm in diameters) with a diamond grind machine. The IPS e.max Press specimens ($0.8{\times}10mm$) were fabricated using the "lost wax" technique. CIE $L^*a^*b^*$ coordinates and light transmission were recorded for each specimen with a spectrophotometer(CM-2600d, Minolta, Japan). Color differences were calculated using the equation, ${\Delta}E^*ab=[({\Delta}L^*)2+({\Delta}a^*)2+({\Delta}b^*)2]1/2$. Results: The results were obtained as follows: 1. The most translucent group was IPS e.max Press ceramic that is a glass-ceramic, and $Lava^{TM}$ and Z-match ceramic were more translucent than Cercon Smart ceramic in zirconia ceramic group. 2. In the all groups, there was no significant translucent change after 6 times heat-treatments required to make a final restoration. 3. Colored zirconia was showed more yellowish and dark than uncolored zirconia. 4. After heat-pressing, IPS e.max Press ceramic was showed high ${\Delta}E^*ab$ value(4.1 of eM1, 6.8 of eM2) that means to be more whiter than before heat-pressing. However, there was no color change after additive heat treatments for final restoration. 5. In the colored zirconia groups, there was no significant color change after some heat-treatments required to make a final restoration.