• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.191-194
• /
• 2009

PtRu based and PtSn based ternary catalysts were prepared by a conventional impregnation method using NaBH4 as reducing agent. The alloy formation, crystalline size and chemical composition of the in-house catalysts were determined by XRD, TEM and EDX, respectively. The chemical compositions of in-house catalysts were quite similar to the nominal value and good alloy formations were also observed. Further, crystalline sizes of ternary catalysts were comparatively smaller than binary catalysts and were approximately 3.5 ~ 5.5 nm. The electrochemical measurements were carried out in the solution 1 M $H_2SO_4$ with 1 M $C_2H_5OH$ at room temperature. LSV results obtained that ternary catalysts were higher current densities and specific activities. Especially, in case of tungsten addition system, Pt5Sn4W/C have the highest specific activities values and was approximately 21.2 and 3.1 times higher than that of PtRu/C and PtSn/C electrocatalyst.

• Transactions of the Korean hydrogen and new energy society
• /
• v.19 no.5
• /
• pp.423-429
• /
• 2008

This work was carried out to improve the performance of anodic electrocatalysts in direct ethanol fuel cell(DEFC). PtRu and $Pt_5Ru_4M$(M= Ni, Sn, Mo and W) electrocatalysts were prepared by using a $NaBH_4$ reduction method. Alloy crystal structure and particle size of electrocatalysts were characterized by X-ray diffraction(XRD) and transmission electron microscopy(TEM). The XRD analysis of the electrocatalysts revealed that the face-centered cubic(fcc) peaks shifted to slightly higher diffraction angles when third metals were added. Average size of the uniform particles was observed to be approximately $3{\sim}3.5\;nm$ from the TEM image. The electrochemical measurements were carried out in the solution 1M $H_2SO_4$ and 1M $C_2H_5OH$ at room temperature. Cyclic-voltammogram results showed that $Pt_5Ru_4W$ electrocatalyst exhibited much higher current density for ethanol oxidation of $2.73\;mA/cm^2$ than PtRu electrocatalyst of $0.73\;mA/cm^2$.

• Journal of Electrochemical Science and Technology
• /
• v.6 no.3
• /
• pp.95-105
• /
• 2015

In the present work, Carbon supported Pt₁₀₀, Pt₈₀Sn₂₀, Pt₈₀Ni₂₀ and Pt₈₀Sn₁₀Ni₁₀ electrocatalysts with different atomic ratios were prepared by ethylene glycol-reduction method to study the electro-oxidation of ethanol in membraneless fuel cell. The electrocatalysts were characterized in terms of structure, morphology and composition by using XRD, TEM and EDX techniques. Transmission electron microscopy measurements revealed a decrease in the mean particle size of the catalysts for the ternary compositions. The electrocatalytic activities of Pt₁₀₀/C, Pt₈₀Sn₂₀/C, Pt₈₀Ni₂₀/C and Pt₈₀Sn₁₀Ni₁₀/C catalysts for ethanol oxidation in an acid medium were investigated by cyclic voltammetry (CV) and chronoamperometry (CA). The electrochemical results showed that addition of Ni to Pt/C and Pt-Sn/C catalysts significantly shifted the onset of ethanol and CO oxidations toward lower potentials. The single membraneless ethanol fuel cell performances of the Pt₈₀Sn₁₀Ni₁₀/C, Pt₈₀Sn₂₀/C and Pt₈₀Ni₂₀/C anode catalysts were evaluated at room temperature. Among the catalysts investigated, the power density obtained for Pt₈₀Sn₁₀Ni₁₀/C (37.77 mW/cm² ) catalyst was higher than that of Pt₈₀Sn₂₀/C (22.89 mW/cm² ) and Pt₈₀Ni₂₀/C (16.77 mW/ cm² ), using 1.0 M ethanol + 0.5 M H₂SO₄ as anode feed and 0.1 M sodium percarbonate + 0.5 M H₂SO₄ as cathode feed.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.109-114
• /
• 2008

Though ethanol can theoretically generate 12 electrons during oxidation to carbon dioxide, the complete oxidation of ethanol is hard to achieve due to the strong bond between the two carbons in its molecular structure. Therefore, development of high activity catalyst for ethanol oxidation is necessary for the commercialization of direct ethanol fuel cell. In this study, some binary and ternary electrocatalysts of PtSn/C and PtSnAu/C have been synthesized and characterized. The catalysts were fabricated with modified polyol method with the amounts of 20 wt%, where the Pt : Sn ratios in the PtSn/C were 1 : 0, 4 : 1, 3 : 1, 2 : 1, 1.5 : 1, 1 : 1, 1 : 1.5 and Pt:Sn:Au ratios in the PtSnAu/C were 5 : 5 : 0, 5 : 4 : 1, 5 : 3 : 2, 5 : 2 : 3. From the XRD and TEM analysis results, the catalysts were found to have face centered cubic structure with particle size of around $1.9{\sim}2.4\;nm$. The activity in the ethanol oxidation was examined with cyclic voltammetry and the results indicated that PtSn(1.5 : 1)/C and PtSnAu(5 : 2 : 3)/C had the highest activity in each catalyst system. Further tests with single cell were performed with those catalysts. It was found that PtSn/C(1.5 : 1) exhibited the best performance while the long term stability of PtSnAu/C(5 : 2 : 3) is better than PtSn/C(1.5 : 1).