• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.4
• /
• pp.151-159
• /
• 2001

As huge energy transfer systems like a nuclear power plant, steam power plant and petrochemical plant are operated for a long time, mechanical properties are changed by degradation. The life time of the systems can be affected by the mechanical properties. BI(Ball Indentation) test has a potential to replace conventional fracture tests like a uniaxial tensile test, fracture toughness test, hardness test and so on. In this paper, we would like to present the ageing evaluation technique by the BI method. The four classes of the thermally aged 1Cr-!mo-0.25V specimens were prepared using an artificially accelerated aging method. Tensile tests, fracture toughness tests, hardness tests and BI tests were performed. The results of the BI tests were in good agreement with fracture characteristics by a standard fracture test method within 5%. The IDE(Indentation Deformation Energy) of a BI technique as a new parameter for evaluating a degradation was suggested and the new IDE parameter clearly depicts the degradation degree.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.171-176
• /
• 2000

As huge energy transfer systems like a nuclear power plant, steam power plant and petrochemical plant are operated for a long time, mechanical properties are changed by degradation. The life time of the systems can be affected by the mechanical properties. BI(Ball Indentation) test has a potential to replace conventional fracture tests like a uniaxial tensile test, fracture toughness test, hardness test and so on. In this paper, we would like to present the aging evaluation technique by the BI method. The four classes of the thermally aged 1Cr-1Mo-0.25V specimens were prepared using an artificially accelerated aging method. Tensile tests, fracture toughness tests, hardness tests and BI tests were performed. The results of the BI tests were in good agreement with fracture characteristics by a standard fracture test method. The IDE(Indentation Deformation Energy) of a BI technique as a new parameter for evaluating a degradation was suggested and the new IDE parameter clearly depicts the degradation degree.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.1
• /
• pp.41-51
• /
• 2004

FRP re-bar in concrete structures could be used as a substitute of steel re-bars for that cases in which aggressive environment produce high steel corrosion, or lightweight is an important design factor, or transportation cost increase significantly with the weight of the materials. But FRP fibers have only linearly elastic stress-strain behavior; whereas, steel re-bar has linear elastic behavior up to the yield point followed by large plastic deformation and strain hardening. Thus, the current FRP re-bars are not suitable concrete reinforcement where a large amount of plastic deformation prior to collapse is required. The main objectives of this study in to evaluate the tensile behavior and the fracture mode of hybrid FRP re-bar. Fracture mode of hybrid FRP re-bar is unique. The only feature common to the failure of the hybrid FRP re-bars and the composite is the random fiber fracture and multilevel fracture of sleeve fibers, and the resin laceration behavior in both the sleeve and the core areas. Also, the result of the tensile and interlaminar shear stress test results of hybrid FRP re-bar can provide its excellent tensile strength-strain and interlaminar stress-strain behavior.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.244-249
• /
• 2007

In several locations of the pressurized water reactors, dissimilar metal welds using inconel welding wires are used to join the low alloy steel nozzles to stainless steel pipes. To evaluate the integrity and design the dissimilar welds, tensile and fracture properties variations are needed. In this study, dissimilar metal welds composed of SA508 Gr.3 LAS, inconel 82/182 weld, and TP316 stainless steel were prepared by gas tungsten arc welding and shielded metal arc welding technique. Microstructures were observed using optical and electron microscopes. Different tensile and fracture properties were observed depending on the specimen sampling position at room temperature and $320^{\circ}C,$ and that was discussed based on the microstructure characteristics. It was found that the strength at the bottom of weld was greater than at the top of the weld. Also, from the test data using small punch specimen, more detailed tensile property variations were evaluated.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.14 no.4
• /
• pp.134-139
• /
• 2015

PolyJet technology is an additive manufacturing (AM) technology commonly used for modeling, prototyping, and production applications. It is one of the techniques used for 3D printing. The PolyJet technique is a process that joins materials to fabricate a product from 3D CAD data in a layer-by-layer manner. The orientation of a layer can affect the mechanical properties of the product manufactured by the PolyJet technique because of its anisotropy. In this paper, tensile and shearing tests of specimens were developed with the PolyJet technique in order to study the mechanical properties according to the orientation of a layer. The mechanical properties of the specimens were determined on the basis of true stress-strain curves from tensile and shearing tests. In addition, the tensile and shearing tests were simulated under the same conditions as those of experiment, and the experiment and simulated results were compared. Through this study, the fracture criteria could be established.

• Journal of Mechanical Science and Technology
• /
• v.18 no.8
• /
• pp.1368-1374
• /
• 2004

The remaining life estimation for the aged components in power plants as well as chemical plants are very important because mechanical properties of the components are degraded with in-service exposure time in high temperatures. Since it is difficult to take specimens from the operating components to evaluate mechanical properties of components, nondestructive techniques are needed to evaluate the degradation. In this study, test materials with several different degradation levels were prepared by isothermal aging heat treatment at $630^{\circ}C$. The DC potential drop method and destructive methods such as tensile and fracture toughness were used in order to evaluate the degradation of 1Cr-1Mo-0.25V steels. In this result, we can see that tensile strength and fracture toughness can be calculated from resistivity and it is possible to evaluate material degradation using DC potential drop method, non-destructive method.

• Journal of Korea Foundry Society
• /
• v.10 no.6
• /
• pp.503-508
• /
• 1990

The effect of interlamellar spacing on tensile behavior and fracture mode at high temperatures has been studied for unidirectionally solidified $Al-CuAl_2$ eutectic composite. The tensile properties at room temperature in $Al-CuAl_2$ eutectic composite improved as the interlamellar spacing decreased due to the constraint effects of closely spaced lamellae, while the opposite behavior was observed at high temperatures due to the annihilation of the constraint effects by phase boundary sliding. The $Al-CuAl_2$ eutectic composite exhibited brittle fracture mode below the temperature at which the reinforcing phase softened but ductile fracture mode above the temperature.

• International Journal of Naval Architecture and Ocean Engineering
• /
• v.9 no.1
• /
• pp.66-76
• /
• 2017

This paper is concerned with investigating the plastic material properties of steel plate formed by line heating method, and is aimed at implementing more rational design considering the accidental limit states such as collision or grounding. For the present study, line heating test for marine grade steel plate has been carried out with varying plate thickness and heating speed, and then microscopic examination and tensile test have been carried out. From the microscopic, it is found that the grain refined zones like ferrite and pearlite are formed all around the heat affected zone. From the tensile test results, it is seen that yield strength, tensile strength, fracture strain, hardening exponent and strength coefficient vary with plate thickness and heat input quantity. The formulae relating the material properties and heat input parameter should be, therefore, derived for the design purpose considering the accidental impact loading. This paper ends with describing the extension of the present study.

• Transactions of Materials Processing
• /
• v.29 no.2
• /
• pp.103-112
• /
• 2020

This study explores the effects of different pre-machining conditions on the deposition characteristics and mechanical properties of austenitic stainless steel samples repaired using direct energy deposition (DED). In the DED repair process, defects such as pores and cracks can occur at the interface between the substrate and deposited material. In this study, we varied the shape of the pre-machined zone for repair in order to prevent cracks from occurring at the slope surface. After repairs by the DED process, macro-scale cracks were observed in samples that had been pre-machined with elliptic and trapezoidal grooves. In addition, it was not possible to completely prevent micro-crack generation on the sloped interfaces, even in the capsule-type grooved sample. From observation of the fracture surfaces, it was found that the cracks around the inclined interface were due to a lack of fusion between the substrate and the powder material, which led to low tensile properties. The specimen with the capsule-type groove provided the highest tensile strength and elongation (respective of 46% and 571% compared to the trapezoidal grooved specimen). However, the tensile properties were degraded compared to the non-repaired specimen (as-hot rolled material). The fracture characteristics of the repaired specimens were determined by the cracks at the sloped interfaces. These cracks grew and coalesced with each other to form macro-cracks, they then coalesced with other cracks and propagated to the substrate, causing final fracture.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.05a
• /
• pp.326-330
• /
• 2004

Thermosetting matrix composites have disadvantages in terms of moulding time, repairability and manufacturing cost. Thus the high-performance thermoplastic composites to eliminate such disadvantages have been developed so far. As a result of environmental and economical concerns, there is a growing interest in the use of thermoplastic composites. However, since their mechanical properties are very sensitive to the environment such as moisture, temperature etc., those behaviors need to be studied. Particularly the temperature is a very important factor influencing the mechanical behavior of thermoplastic composites. The effect of temperature have not yet been fully quantified. Since engineering applications of reinforced composites necessitate their fracture mechanics characterization, work is in progress to investigate the fracture and related failure behavior. An approach which predicts the tensile strength was perpormed in the tensile test. The main goal of this work is to study the effect of temperature on the result of tensile test with respect to GF/PE composite. The tensile strength and failure mechanisms of GF/PE composites were investigated in the temperature range $60^{\circ}C\;to\;-50^{\circ}C$. The tensile strength increased as the fiber volume fraction ratio increased. The tensile strength showed the maximum at $-50^{\circ}C$, and it tended to decrease as the temperature increased from $-50^{\circ}C$. The major failure mechanisms was classified into the fiber matrix debonding, the fiber pull-out, the delamination and the matrix deformation.