• 소성∙가공
• /
• 제20권1호
• /
• pp.64-72
• /
• 2011

In this study, we have investigated bonding of metal and plastic parts with single planar interface. This is facilitated by surface processing of aluminum sheet, which consists of slitting and punching, followed by insert-molding of polybuthylelne terephthalate(PBT). An injection mold has been built to fabricate specimen. After processing of the specimen, tensile and bending shear adhesion tests have been fulfilled according to KS M3734 and KS M3723, respectively. We also have conducted simulation of tensile and bending shear adhesion tests. Based on the tests results, the proposed bonding method outperforms existing methods based on adhesion.

• 대한기계학회논문집A
• /
• 제33권6호
• /
• pp.560-567
• /
• 2009

This paper was designed to estimate the adhesion strength of galvannealed coatings on steel sheets. The adhesion strength were evaluated using single lap - shear tests where the lap joint was bonded by structural adhesive. Tests were performed for overlap length of 5mm, 10mm and 15 mm and three directions (0, 45, 90) of steel sheets used as the adherend of the overlap joint. After the tests, FE simulations of the single lap-shear test were also carried out to observe the stress distribution in the interface between the adhesive and the coated sheet. The results showed that the joint failure loads obtained from the tensile tests of bonded single lap-joints were the same, regardless of overlap lengths and directions of steel sheets. Also, the failure of galvannealed coatings greatly depended on shear stress distribution in the interface and the value was about 30MPa.

• Corrosion Science and Technology
• /
• 제13권5호
• /
• pp.186-194
• /
• 2014

Establishment of adhesion strength measurement procedure for marine epoxy coatings was conducted in order to ensure reliability of the test results. It was found that (1) the increase in thickness of the substrates would induce increase of pull-off strength. Especially, the increase in adhesion strength with the substrate thickness increment was attributed to the transition of stress mode to the pure tensile mode excluding bending effect. (2) The longer curing time, the higher pull-off strength. It may be due to higher cross-linking density of the coating (3) The pull-off strength increases as coating thickness increases due to the diminishment of bending effect (4) The longer drying time after water immersion, the higher pull-off strength. It may be due to the evaporation of water molecule at the coating-substrate interface.

• Elastomers and Composites
• /
• 제49권3호
• /
• pp.245-252
• /
• 2014

폴리올, 이소시아네이트, 2-HEMA 및 기타 아크릴레이트 단량체들로부터 제조된 폴리우레탄 접착제의 FT-IR측정과 물성을 검토하였다. 폴리우레탄 접착제의 연화점, 점도, 접착강도 및 기계적 물성들이 각각 링과볼법, Brookfield 점도계 및 만능시험기를 이용하여 검토되었다. 실험 결과에 의하면 PPG 함량 및 부틸아크릴레이트 함량이 증가함에 따라 연화점, 접착강도, 인장강도 및 100% modulus 값 등은 감소하는 것을 보여준다. 하지만 2-HEMA 및 MDI량이 증가할수록 인장강도 및 100% modulus값 등은 증가하였으며 점도와 NCO함량 등도 또한 증가하였다.

• 공업화학
• /
• 제10권3호
• /
• pp.450-455
• /
• 1999

말레산 무수물 (MA)과 diethylene glycol (DEG)을 반응시켜 볼포화기가 도입된 에스테르형 디올 (UD)을 제조한 다음 이를 로진과 MA를 반응시켜 얻은 rosin maleic anhydride adduct (RMA) 또는 2-hydroxyethylmethacrylate (HEMA)가 도입된 RMA (RMA-HEMA)와 각각 반응시켜 rosin (UPMR) 및 RMA-HEMA 변성 불포화 폴리에스테르 (UPMRH)를 각각 제조하였다. 이를 가교제로 스티렌 또는 메틸메타아크릴레이트(MMA)로 가교시킨 후 내용매성과 인장강도 및 접착특성을 측정하였다. 가교제로 스티렌을 사용하는 경우가 MMA를 사용한 것에 비해 내용메성과 인장강도가 증가하였다. 또한 UPMRH의 경우가 UPMR에 비해 내용매성이 우수하였고 인장강도도 증가되었다. 한편 T-peel test로 측정한 계면접착력에 있어서 UPMR의 경우 가교제로 스티렌 및 MMA를 사용하는 경우는 1.61과 3.02 MPa인 반면 UPMRH의 경우는 2.32와 3.89 MPa로 HEMA가 도입됨에 따라 계면접착력이 증가되었다.

• 접착 및 계면
• /
• 제20권1호
• /
• pp.15-22
• /
• 2019

Polybutadiene diol (PBD)과 isophorone diisocyanate (IPDI)의 반응을 통하여 이관능 우레탄 아크릴레이트 올리고머 (PB-UAO)를 합성하고, 여기에 삼관능 아크릴레이트 모노머 (Tris(2- acryloyloxyethyl) isocyanurate (TAOEIC), 또는 Trimethylolpropane triacrylate (TMPTA) 또는 Pentaerythritol triacrylate(PETA)), 단관능 아크릴레이트 모노머 (Stearyl Acrylate) 그리고 광개시제를 혼합한 후 이형필름 위에 코팅하고 자외선 경화를 통하여 감압 점착 필름을 제조하였다. 삼관능 아크릴레이트 모노머의 구조 및 함량에 따른 감압 점착제의 박리강도, 인장강도, 신율, 열안정성 및 흡습 특성의 변화를 고찰하였다. 삼관능 아크릴레이트 모노머의 함량이 증가할수록, 그리고 분자량이 작을수록 감압 점착 필름의 박리강도, 연신율 및 흡습율은 감소하는 경향을 보였으며, 인장강도 및 열안정성은 증가하는 것을 확인하였다.

• 대한치과보철학회지
• /
• 제37권2호
• /
• pp.200-211
• /
• 1999

For many years permanent soft denture liners has been widely used in dental practice directly or indirectly because of its function in absorbing and distributing the impact force. However, it reveals problems such as lack of permanency and decreased bond strength in long term use. The purpose of this study is to measure the bond strength and failure between denture base resin and several permanent liners. Lucitone 199 was used as denture base resin with soft acrylic liners (Triad, Tokuso Rebase) and silicone elastomers (Tokuyama, Ufi Gel C) bonded to measure the tensile strength before and after thermocycling. The thermocycling was done in 2000 cycles at $5^{\circ}C,\;26^{\circ}C\;and\;55^{\circ}C$ and the measured tensile strength values before and after thermocycling were compared. The mode of failure was investigated in the separated specimens. The results are as follows. 1. As to tensile strength, the strongest material is Tokuso Rebase followed by Triad, Tokuyama, Ufi Gel C in before thermocycling and the order of Triad, Tokuso Rebase, Tokuyama, Ufi Gel C in after thermocycling state. There was significant difference between the values of Triad, Tokuso Rebase and Tokuyama, Ufi Gel C(p<0.05). 2. As to degree of displacement, Ufi Gel C showed most displacement with or without thermo-cycling treatment and also the difference was significant with the other materials(p<0.05). 3. As to comparisons before and after thermocycling, Tokuso Rebase and Tokuyama showed significant difference in bond strength, whereas Triad and Tokuso Rebase showed significant difference in the degree of displacement(p<0.05). 4. In debonded specimens, Triad and Ufi Gel C showed adhesion failure and Tokuyama showed cohesion failure. Both failures were observed in Tokuso Rebase with adhesion failure up to 70%. The results of this study showed that degree of bond strength between permanent soft denture liner and denture base resin were variable. There was a significant difference between soft acrylics and silicone elastomers with regard to bond strength. Further research in improving bond strength of widely used silicone elastomers and in developing the method of measuring bond strength between denture base resin and the lining materials is needed.

• 한국산학기술학회논문지
• /
• 제22권1호
• /
• pp.74-80
• /
• 2021

본 연구는 최근 전력화가 완료되어 양산이 진행 중인 K5 방독면에 대한 공정품질 수준을 평가하기 위하여 통계적 공정관리 기법을 활용하여 양산 단계 및 로트 별 분석을 수행하였다. 렌즈의 접착강도는 K5방독면의 기술적 요구사항 중 유일하게 생산 공정 간 평가하는 항목으로, 초도 및 2차 양산간 획득된 고무안면부와 렌즈 사이의 접착정도를 측정한 시험결과를 바탕으로 기술통계 및 통계적 공정관리 기법을 적용하여 분석하였다. 기술통계 분석결과에 따르면 초도 양산 대비 2차 양산 공정에 대한 결과가 더 좋음을 나타내고 있었다. 통계적 공정관리 기법인 관리도 분석과 공정능력지수에 대한 양산 단계 별 분석결과, 공정품질 수준 또한 양산이 진행됨에 따라 향상되고 있음을 확인 할 수 있었다. 이는 공정이 점차 안정화 되고 업무 숙련도에 의해 개선이 되고 있음을 보여주고 있었다. 이에 초도 및 2차 양산 간 획득된 성능시험 결과를 바탕으로 향후 3차 양산을 위한 기초자료로서 활용하고자 한다. 더불어 린6시그마의 DMAIC[Define(정의)-Measure(측정)-Analyze(분석)-Improve(개선)-Control(관리)] 방법론을 통해서 K5방독면의 품질향상 등의 목표달성을 수행할 예정이다.

• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2003년도 학술발표논문집
• /
• pp.391-394
• /
• 2003

Effects of the polymer-binder ratio and slag content on the properties of combined wet/dry-cured polymer-modified mortars using granulated blast-furnace slag are examined. Results shows that the flexural, compressive, tensile and adhesion in tension strengths of polymer-modified mortar using the slag tend to increase with increasing slag content, and is inclined to increase with increasing polymer-binder ratio. In particular, the polymer-modified mortars with slag content of 40% provide about 20% higher tensile strength than unmodified mortars. Such high strength development is attributed to the high tensile strength of polymer and the improved bond between cement hydrates and aggregates because of the addition of polymer.

• Elastomers and Composites
• /
• 제39권4호
• /
• pp.294-300
• /
• 2004

혼합폐플라스틱과 폐타이어분말을 혼합하여 복합체를 구성하고 그 기계적인 물성을 조사하였다. 수지-고무분말 사이의 계면접착력을 증대시키고자 두 요소와 친화성을 가질 것으로 예상되는 trans-octylene rubber(TOR)를 소량 첨가하였다. 고무분말의 투입량이 많아질수록 인장강도와 압축강도는 플라스틱자체보다 저하되었으며 파단신장률과 충격강도는 증가되었다. 상용화제 TOR이 첨가되면 인장강도와 충격강도 및 압축강도는 크게 향상되었으나 신장률은 변화가 없었다. 이러한 물성의 변화는 TOR의 화학적인 이중성에 기인한다고 여겨진다.