• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.6
• /
• pp.367-373
• /
• 2023

600 MPa-grade deformed bar samples were manufactured by conventional hot rolling and subsequent Tempcore heat treatment processes. Considering the short-time water quenching step of the Tempcore process for hot-rolled steel, it is inevitable that the temperature profile of the deformed bar depends strongly on its position throughout the sample thickness. As a result, its microstructure can be easily divided into two regions, the surface and the core regions. The former is expected to have a fresh martensite microstructure under rapid cooling conditions, but self-tempering occurs due to the intense heat flow from the hot core region after the process. The latter is generally known to exhibit a mixed microstructure of ferrite and pearlite due to its slow cooling rate. In this study, detailed microstructural evolutions were examined through the thickness direction. The large variation of the microstructure through the thickness direction in the deformed bar samples is partly due to the easy carbon diffusion from the limited additions of alloying elements.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.5
• /
• pp.543-547
• /
• 2015

The cooling process referred to as Tempcore has been applied to produce a high-strength rebar. Excellent rebar with strength and weldability can be manufactured from mild steel without the addition of alloying elements by using the Tempcore process. However, there are limitations to evaluating the effect of various chemical compositions and cooling conditions within a site facility. In this study, we developed an apparatus to simulate the Tempcore process and obtained microstructures with a hardened surface layer, an intermediate region and a soft inner core. The experimental apparatus has been equipped with a cooler set that is the same as the site facility and consists of a pump line that supplies pressure of 12-13 bar and flow rate of up to $50m^3/h$. In accordance with the simulation result of steel grade SD400 that requires more than 400 MPa of yield strength, both the hardened area ratio and the hardness with respect to each cooling depth were found to agree well with the product.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.157-161
• /
• 2009

The corrosion resistance of reinforcing bar was studied to endure the marine environment during shipment. The red rust on the surface did not damage the adherence in the concrete structures, especially in highly alkaline environment, but made the consumer doubt of the quality. The passivation process by alkalization of the quenching water in the tempcore process failed to endure the long shipping period. The ceramic coating by sol-gel process improved the corrosion resistance without damaging the mechanical properties and adherence between concrete and reinfiorcing bar. Optimal concentration of the coating solution and coating temperature were tested. No additional energy was necessary for the coating process by spraying during cooling process, resulting simplified process and low cost. Salt spray test, cyclic corrosion test and atmospheric test were employed to confirm the resistance. The corrosion rates were presented by rating number and polarization resistance. The coating layer was examined by FIB, XRD and SEM etc.