Pb0.5Sr0.5TiO3 (PST) thin films were fabricated by the alkoxide-based sol-gel process using spin-coating method on Pt/Ti/SiO2/Si substrate. The PST films annealed from 500C to 650C for 1h show a perovskite phase and dense microstructure with a smooth surface. The grain size and dielectric constant of PST films increases with the increase in annealing temperature, which reduces the SiO2 equivalent thickness of the PST film. The crystallinity or internal strain in the PST thin films analyzed from the diffraction-peak widths correlate well with the decrease in the dielectric losses. The dielectric constants and dielectric loss (%) of the PST films annealed at 650c (teq : 0.89 nm) were 549 and 0.21%, respectively.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.3
• /
• pp.465-470
• /
• 2006

Coating are needed on ophthalmic lenses to enhance both the mechanical durability of the relatively soft plastic surface and the optical performance of lenses. Organic-inorganic hybrid materials as molar ratio of 3-glycidoxypropyltrimethoxysilane(GPTS), methyltrimethoxysilane(MTMS) and tetraethyl orthosilicate(TEOS) were used to improve the surface characteristics and the optical properties on allyl diglycol carbonate lenses. Coating for these plastics were at $140^{\circ}C$ for 4hrs, applied using the sol-grl process flow-coating technique. The coated lens properties of transmittance, adhesion, pencil hardness, abrasion resistance, hot water resistance and chemical resistance were investigated. The optimum properties was obtained when the ratio of GPTS : MTMS : TEOS was 1:1:2, respectively.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.485-490
• /
• 2007

Hard coating was made on a polycarbonate plate using a sol-gel process with a melamine derivative and silicates, and examined as potential substitutes for automobile glass. Methylated poly(melamine-co-formaldehyde), tetraethoxysilane, and phenyltriethoxysilane were used to form a coating solution. The coatings on the polycarbonate plate were deposited using a sol-gel process. Poly(methyl methacrylate) was coated on the surface of polycarbonate in order to improve adhesion property. The optimum conditions and formulation to obtain excellent physical properties of the coating were determined. Adding the melamine derivative to the coating solution, the pencil hardness of the coating was improved. The hardness of a 3H class pencil, excellent abrasion resistance, and surface uniformity were found in the coated polycarbonate surface.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.5
• /
• pp.741-744
• /
• 2002

Single phase of multicomponent oxide ZrTiO4 film could be prepared through surface sol-gel route simply by coating the mixture of 100 mM zirconium butoxide and titanium butoxide on $Pt/Ti/SiO_2Si(100)$ substrate, following pyro lysis at $450^{\circ}C$, and annealing it at 770 $^{\circ}C.$ The dielectric constant of the film was reduced as the film thickness decreased due to of the interfacial effects caused by layer/electrode and a few voids inside the multilayer. However, the dielectric property was independent of applied dc bias sweeps voltage (-2 to +2 V).The dielectric constant of bulk film, 31.9, estimated using series-connected capacitor model was independent of film thickness and frequency in the measurement range, but theoretical interfacial thickness, ti, was dependent on the frequency. It reached a saturated ti value, $6.9{\AA}$, at high frequency by extraction of some capacitance component formed at low frequency range. The dielectric constant of bulk ZrTiO4 pellet-shaped material was 33.7 and very stable with frequency promising as good applicable devices.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.233-233
• /
• 2006

[ $Y_{2}O_{2}S:Eu$ ], a red phosphor, coated with silica nanoparticles or nanocomposites composed of silica nanoparticles and polymeric materials such as PMMA and PVP was prepared via sol-gel process. Samples were prepared from four different methods coded P1, P2, P3, and P4. P1 includes a conventional sol-gel process and a dip-coating method while P2 has the same procedure with P1 except that nanocomposites containing both silica nanoparticles and polymer prepared by sol-gel process were used as coating materials. In P3 method, phosphors were dispersed in a solution containing silica precursor, i.e., TEOS and then polymerization was performed to coat onto the phosphors surface while P4 followed the same procedure with P3 except that a solution containing both TEOS and organic monomer were used in preparing coating materials. Among various coating methods examined in this study, uniform coating of phosphor could be achieved by using method P4, i.e., phosphor surface coating in a solution containing hydrophobic monomer and TEOS. Furthermore, $Y_{2}O_{2}S:Eu$ red phosphor coated with nanocomposite composed of PMMA matrix and silica nanoparticles exhibited enhanced PL intensity and long-term stability.

• Journal of the Korean Ceramic Society
• /
• v.33 no.4
• /
• pp.432-440
• /
• 1996

ZrO2 gel was prepared under pH 10 alkaline condition by sol-gel process and was investigated as a function of calcination temperature and effect of calcination temperature on cobalt adsorption capacity. The ZrO2 powder prepared by sol-gel process was calcined at 600, 800, 1000, 1200, 140$0^{\circ}C$ and analyzed by X-ray diffractometry. SEM specific surface area by BET nitrogen adsorption FT-IR and TG-DTA technique. It was shown that cobalt adsorption capacity of ZrO2 prepared under pH 10 alkaline condition and then calcined at $600^{\circ}C$ in high temperature was determined to be larger than that of ZrO2 at various calcination temperature. The specific surface area of ZrO2 calcined at $600^{\circ}C$ was 24.03m2/g and cobalt adsorption capacity at 25$0^{\circ}C$ high-temperature water was 0.16m-eq/g.

• Journal of Powder Materials
• /
• v.12 no.3
• /
• pp.220-224
• /
• 2005

Boehmite (AlOOH) powder with uniform pore size and high specific surface area were synthesized via sol-gel method using metal salts, $Al_2(SO_4)_3$ and $NaAlO_2$. During these synthetic process, the effects of the aging time were investigated to determine the optimal synthetic conditions of boehmite. X-ray diffraction, BET, Raman/IR, and scanning electron microscopy techniques were used for the characterization of the powder. Boehmite gel synthesized at the first stage of the experimental procedure transformed to crystalline boehmite phase after aging for 6 hours. The specific surface area of the crystalline boehmite showed a maximum value, $350m^2/g$, at aging time of 72 hours. The pore size of the boehmite increased with increasing aging time and the boehmite with average pore diameter of 3.6 nm was obtained at aging time of 96 hours.

• Electrical & Electronic Materials
• /
• v.7 no.2
• /
• pp.152-156
• /
• 1994

The rapid thermal annealing effects of Sol-Gel derived ferroelectric PZT thin films were investigated. It was found that rapid thermal annealing(RTA) of spin coated thin films on silicon typically >$800^{\circ}C$ for about 1 min. was changed to the perovskite phase. Rapid thermally annealed films recorded maximum remanent polarization of about 5 .mu.C/cm$^{2}$, coercive field of around 30kV/cm. The switching time for polarization reversal was about 220ns. The films of RTA process showed smooth surface, and high breakdown voltages of over 1 MV/cm and resistivity of $1{\times}{10^12}$ .ohm.cm at 1 MV/cm. It was verified that the polarization reversal of the PZT film was varied partially with applying the multiple short pulse.

• Carbon letters
• /
• v.10 no.2
• /
• pp.123-130
• /
• 2009

Multi-elements doped $TiO_2$ was prepared as a new photocatalyst in order to decrease the band gap of $TiO_2$ by sol-gel process which can provide the large active sites of $TiO_2$. Multi-elements were doped by using a single precursor, tetraethylammonium tetrafluoroborate (TEATFB). By the benefit of large specific surface area of $TiO_2$ prepared by sol-gel process, catalysts showed initial fast removal of dye. The photoactivity showed that the doped catalysts significantly promote the light reactivity than undoped $TiO_2$. The commendable photoactivity of prepared catalysts is predominantly attributable to the doping of anions which may reduce the band gap.

• The Journal of Korea Institute of Information, Electronics, and Communication Technology
• /
• v.1 no.2
• /
• pp.27-32
• /
• 2008

A current research basically diverted towards an increase in the operational output with the minimization of the materials used, which ultimately scaled down the dimensions of ceramic electronic components. In this direction the nano-technology pave the revolutionary changes in particular the electronic industries. The applications of nano-sized particles or nano-sized materials are hence, playing a significant role for various purposes. The PZT(lead, zirconium, titanium) based ceramics which, are reported to be ferroelectric materials have their important applications in the areas of surface acoustic waves (SAW), filters, infrared detectors, actuators, ferroelectric random access memory, speakers, electronic switches etc. Moreover, these PZT materials possess the large electro mechanical coupling factor, large spontaneous polarization, low dielectric loss and low internal stress etc. Hence, keeping in view the unique properties of PZT piezoelectric ceramics we also tried to synthesize indigenously the small sized PZT ceramic powder in the laboratory by using the modified sol-gel approach. In this paper, propyl alcohol based sol-gel method was used for preparation of PZT piezoelectric ceramic. The powder obtained by this sol-gel process was calcined and sintering to reach a pyrochlore-free crystal phase. The characterization of synthesized material was carried out by the XRD analysis and the surface morphology was determined by high resolution scanning electron microscopy.