• 한국진공학회지
• /
• 제12권S1호
• /
• pp.21-27
• /
• 2003

Micro-arc discharge oxidation (MDO) is a cost-effective plasma electrolytic process which can be used to improve the wear and corrosion resistance of Al-alloy parts by forming a alumina coating on the component surface. However, the MDO coated Al-alloy components often exhibit relatively high friction coefficients and low wear resistance fitted with many counterface materials, additionally, the pitting corrosion for the MDO coated AI-alloy components, especially for a thinner alumina coating, often occurs in atmosphere circumstance due to the porous alumina coats. Therefore, a duplex treatment, combining a MDO coated ahumina thin layer with a TiN coating, prepared by magnetron sputtering (MS), has been investigated. The Vicker's microhardness, pin-on-disc, electrochemical measurement, salt spray, XRD and SEM tests were used to characterize and analyze the treated samples. The work demonstrates that the MDO/MS coated samples have a combination of a very low friction coefficient and good wear resistance as well as corrosion since the micro-holes on alumina coating are partly or fully covered by TiN material.

• 한국표면공학회지
• /
• 제27권1호
• /
• pp.12-18
• /
• 1994

The plasma spray process was used to deposit coatings of $ZrO_2$-8wt%Y2O3 powders on mild steel sub-strate, and the characteristics of as-deposited and heat treated coatings have been investigated. Particulary, the variations of porosity, wear resistance, thermal barrier and thermal shock resistance in $ZrO_2$-8wt% $Y_2O_3$coatings after heat treatment under vacuum circumstance have been investigated. The porosity of the coating layer was increased with increased spray distance. In the case of the arc current of 450A and at the spray distance of 50mm, it was obtained the lowest amount of porosity. After heat treatment, the amount of porosity was found to be decreased, and the wear resistance, microhardness and thermal shock resistance were im-proved. However, the thermal barrier was decreased.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 추계학술대회 논문집 학회본부
• /
• pp.243-245
• /
• 1994

We synthesized the conducting diamond-like carbon films using plasma-enhanced chemical vapor deposition and analysized its characteristics. We obtained the metal-containing diamond-like carbon films using $CH_4$, Ar gas and aluminum target. We observed the changes of electrical conductivity, microhardness and surface morphology according to $Ar/CH_4$ ratio, substrate bias and target bias. As the target bias and $Ar/CH_4$ ratio increase and the substrate bias decreases, the electrical conductivity and surface roughness increase. The increase of hardness involves decrease of the electrical conductivity. Metal-containing amorphous hydrogenated carbon films show improved adhesion on metal substrates compared to pure diamond-like carbon films and better electrical conductivity.

• 한국표면공학회지
• /
• 제34권4호
• /
• pp.289-296
• /
• 2001

Ni-P electroformed layers were investigated for developing a steam generator tube repair technology in PWRs. The effects of an additive, RPP (Reagent over Pitting Protection) and agitation on mechanical properties and microstructure of the layer were evaluated. The addition of the RPP showed to inhibit the formation of pores, to refine the grain size, and to increase the residual stress in the layer. However, the agitation of the solution during electroforming was observed to increase pores in local regions of the electroformed layer, resulting in decreasing its mechanical properties. The heat treatment of the layer at $343^{\circ}C$ for 1 hr. precipitated the very fine particles of Ni3P in the layer, which inhibited grain growth and increased microhardness.

• 한국표면공학회지
• /
• 제15권4호
• /
• pp.208-217
• /
• 1982

To study the effect of TiC coating on weight change, microhardness, wear and heat - resistance of TiC layer, chemical vapour deposition on the various substrates has been carried out with the gaseous mixture of TiCl4, toluene, and H2 in the temperature range of 900 - 1000$^{\circ}C$. The results obtained are as follows ; (1) There is a limited value of carrier and reductant H2 gas flow rate, above which deteriorate effect on the TiC depoition arises (2) Increased thickness of TiC layer was resulted with increasing temperature and time. Better deposition was obtained with stainless steels and the best results were introduced by cobalt coating of substrates. (3) Wear resistance of the TiC coated specimen improved markedly. Heat resistivity of the coated steel showed excellent result, whereas the coated stainless Steels were infer-ior to the substrate.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 춘계학술발표회 초록집
• /
• pp.62-62
• /
• 2003

A statistical evaluation method was proposed to evaluate mechanical properties by using small specimens and nano-indentation for irradiation study. The method is empirically based on nano-indentation which values are statistically treated. The nano-indentation in function of indentation depth (h) is expressed using the variation factor V(h). Statistical parameters of the indentation are given by histograms. Analytical and experimental relation between histograms of phase dimension distribution and parameters V(h) and G(h) is considered using the condition of additivity of phases' microhardness. The method is applied to estimate mechanical properties of irradiated materials.

• 대한소아치과학회지
• /
• 제32권1호
• /
• pp.144-151
• /
• 2005

현재 시판중인 대부분의 음료가 산성을 띤다는 사실은 이미 잘 알려져 있으며 이러한 산성의 음료 음용의 증가는 우려할 만한 수준으로 치아 침식증을 촉진할 것으로 생각된다. 따라서 본 연구는 어린이들이 비교적 일상적으로 쉽게 접하는 탄산음료 중 가장 보편화된 한 종을 택하여 치아와의 노출과 노출빈도에 따른 법랑질의 침식정도를 조사 분석할 목적으로 시행되었다. 탈락 시기의 건전한 유치를 발거하여 두 개의 군, 즉 magnetic stirrer에 의해 진동(agitation)을 받은 군과 그렇지 않은 군으로 나뉘었고 나뉜 군들은 또 각각 콜라에의 노출빈도에 따라 3개의 군으로 나뉘었다. 각각의 군들은 신선한 콜라에 5분씩 노출되었으며 노출 전과 후에 증류수에 의해 세척되었고 시편의 노출이 이루어지지 않는 시간에는 생리 식염수에 보관한 후, 인공적으로 침식을 유발시켰을 때 나타나는 양상을 표면미세경도측정법으로 분석하여 다음과 같은 결론을 얻었다. 1. 본 실험에 사용된 콜라의 산도는 평균 pH 2.5로서 치아 침식증을 유발하기에 충분한 수준이었다. 2. 콜라에 의한 침식유발 후의 법랑질 표면경도는 대조군에 비해 모든 시료에서 감소되었다(p<0.05). 침식유발 시간이 경과함에 따라 법랑질 표면경도는 모든 실험군에서 초기에는 급격히 낮아지다가 이후에는 그 정도가 덜해지는 양상을 보였다. 3. 법랑질을 콜라에 노출시킨 빈도가 증가함에 따라 법랑질 표면경도는 감소되었다. 4. 콜라에 진동(agitation)을 가하여 탄산가스를 증가시킨 결과 법랑질의 표면경도는 진동을 가하지 않은 군에 비해 감소되었다(p<0.05).

• 한국표면공학회지
• /
• 제20권2호
• /
• pp.49-59
• /
• 1987

The properties of $Cr_2O_3-Al_2O_3-SiO_2$ composite oxide coatings on steel surface were investigated. The results obtained were as follows: The microhardness of oxide coating layer increased with increasing heat-treatment temperature and $Cr_2O_3$ content in coating layer. The hardness showed the highest value (850Hv) treated at 700$^{\circ}C$ for $SiO_2:Al_2O_3:Cr_2O_3$=1:1:4. Increasing heat-treatment temperature, corrosion current density became lower and coating layer became denser. The corrosion current density showed the lowest value $(6.5{\times}10^{-5}\;Acm^2)$ treated at 750$^{\circ}C\;for\;SiO_2:Al_2O_3:Cr_2O_3$=1:1:3. These results were explained by protective layer which was formed during heat-treatment. The bonding between matrix and coating layer is expected to be made mechanically and chemically by the inter diffusion of Ni and Fe. The composite oxide coating was formed by softening of the binder with increasing heat-treatment temperature. The strengthening of coating layer is to be resulted from the dispersion of major oxide particles.

• Computers and Concrete
• /
• 제23권5호
• /
• pp.351-359
• /
• 2019

In this study, the calcium hydroxide, an inherent product of cement hydration, was treated using biomimetic carbonation method of incorporating stearic acid to generate the hydrophobic calcium carbonate on concrete surface. Carbonation reaction was carried out at various $CO_2$ pressure and temperatures and utilizing the Scanning Electron Microscope (SEM), chloride-ion penetration test apparatus, and compression test machine to investigate the hydrophobicity, durability, and mechanical properties of the synthesized products. Experimental results indicate that the calcium stearate may change the surface property of concrete from hydrophilicity to hydrophobicity. Increasing reaction temperature can change the particles from irregular shapes to needle-rod structures with increased shear stress and thus favorable to hydrophobicity and microhardness. The contact angle against water for the concrete surface was found to increase with increasing $CO_2$ pressure and temperature, and reached to an optimum value at around $90^{\circ}C$. The maximum static water contact angle of 128.7 degree was obtained at the $CO_2$ pressure of 2 atm and temperature of $90^{\circ}C$. It was also found that biomimetic carbonation increased the permeability, acid resistance and chloride-ion permeability of the concrete material. These unique results demonstrate that the needle-rod structures of $CaCO_3$ synthetized on concrete surface could enhance hydrophobicity, durability, and mechanical properties of concrete.

• Restorative Dentistry and Endodontics
• /
• 제16권2호
• /
• pp.126-142
• /
• 1991

The purpose of this study was to evaluate the effect of various dentin surface treatments on shear bond strength, microhardness and fracture mode before and after thermocycling. Recently extracted 75 human molars were used. The teeth were sagittal sectioned faciolingually to obtain 150 specimens. They were randomly divided into six groups. Mesial and distal dentinal surfaces of specimens were exposed by grinding and treated respectively with GC-DENTIN CONDITIONER. 10-3 solution of 4-Meta, Cleansar and Primer of GLUMA, Scotchprep of Scotchbond 2, DENTIN CONDITIONER and PRIMER A, B of ALL BOND according to the manufacturers directions. Specimens of one group were not treated. Adhesive agent of Scotchbond 2, were applied and cured on the treated dentin surfaces. After P-50 were cured on them, specimens were stored in 31c water for 24 hours before shear bond strength measurement Shear bond strength was measured in 10 specimens of each group. 10 specimens of each group were thermocycled in $20^{\circ}C$, $60^{\circ}C$,$20^{\circ}C$, $4^{\circ}C$, $20^{\circ}C$ water in order, for 30 seconds respectively, 100 times a day for 7 days. After thermocycling shear bond strength was measured. Microhardness was checked on treated dentin surface and fractured dentin surface in 10 specimens respectievly. Francture modes were observed with SEM The following results were obtained. 1. Before thermocycling. shear bond strengths in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens(P<0.01). 2. After thermocycling. shear bond strengths in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of AIL BOND were significantly higher than those in specimens not: treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta(P<0.01). Shear bond strengths in the specimens treated with GC-DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens except those treated with Scotchprep of Srotchbond 2(P<0.01). 3. Shear bond strengths after thermocycling were reduced in the specimens not treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta and were increased in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2, without significance, compared with those before thermocycling. In the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, shear bond strengths after thermocycling were significantly increased, compared with those before thermocycling(P<0.01). 4. Microhardnesses in the fractured surfaces after shear bond strength measurement were significantly increased in the specimens treated with 10-3 solution of 4-Meta and significantly decreased in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, compared with those in the treated dentin surfaces(P<0.01). 5. In the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of ALL BOND, cohesive fracture modes were observed more than adhesive fracture modes.