• Journal of the Korean Electrochemical Society
• /
• v.1 no.1
• /
• pp.45-51
• /
• 1998

[ $AB_2-type$ ] alloy, one kind of hydrogen storage alloys used as an anode of Ni-MH batteries, has large discharge capacity but has remaining problems regarding initial activation, cycle life and self-discharge. This study investigates the effects of Cr-addition and fluorination after La-addition on $Zr_{0.7}Ti_{0.3}V_{0.4}Mn_{0.4}Ni_{1.2}$, composition $AB_2-type$ alloy. EPMA and SEM surface analysis techniques were used and the crystal structure was characterized by XRD analysis. In addition, electrodes were fabricated out of the alloys and characterized by constant current cycling test, electrochemical impedance spectroscopy and potentiodynamic polarization. Cr-addition was found to be effective to cycle life and self-discharge but ineffective to initial activation due to formation of stable oxide film on surface. Fluorination after La-addition to the alloys improved initial activation remarkably due to formation of highly reactive particles on surface.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.386-390
• /
• 2016

The surface of carbon nanotubes (CNTs) was modified by fluorination and applied to conductive materials to improve the energy efficiency of a capacitive desalination (CDI) electrode. CNTs were fluorinated at room temperature with a mixed gas of fluorine and nitrogen, and activated carbon based CDI electrodes were then prepared by adding 0-0.5 wt% of untreated CNTs or fluorinated CNTs with respect to the activated carbon. Fluorinated CNTs showed improved dispersibility in the electrode and also slurry as compared to untreated CNTs, which was confirmed by the zeta potential and scanning electron microscopy. Fluorinated CNTs added electrodes showed higher desalination efficiency but lower energy consumption than those of using untreated CNTs added electrodes. This was attributed to the decrease in the resistance of CDI electrodes due to the improved dispersibility of CNTs by fluorination.

• Applied Chemistry for Engineering
• /
• v.26 no.1
• /
• pp.92-98
• /
• 2015

In this study, phenol-based activated carbons (ACs) were fluorinated at various fluorine partial pressures (0.01~0.03 MPa) and the $Cr^{6+}$ ion adsorption of fluorinated ACs was investigated. According to BET and XPS results, the specific surface area and total pore volume of fluorinated ACs increased by 24.7 and 55.8%, respectively, and fluorine functional groups were introduced to AC surface. The most optimized condition of $Cr^{6+}$ ion adsorption was confirmed at the fluorine partial pressure of 0.02 MPa. And also the removal efficiency of $Cr^{6+}$ ion was up to 98% at 300 mg/L of the initial concentration, and these results showed an approximately three-fold increase compared to that of using untreated ACs. Furthermore, the $Cr^{6+}$ ion adsorption of fluorinated ACs was completed in less than 30 min in contrast with untreated ACs, which was expected to be an increase of the affinity between $Cr^{6+}$ ions and ACs surfaces by fluorination.

• Applied Chemistry for Engineering
• /
• v.29 no.6
• /
• pp.677-681
• /
• 2018

In this study, the carbon block was prepared using the fluorinated coke and binder pitch by molding compression to increase its density. After fluorination, it is confirmed that the fluorine element on the coke surface was introduced up to 24.14 at% using XPS analysis. The wettability between the fluorinated coke and binder pitch was evaluated according to the reaction temperature. From the result of contact-angle tests, it can be found that the wettability was improved up to 64.7% as more fluorine atoms were introduced on the surface of cokes. Also, the density of the carbon block with the highest amount of fluorine increased with 6.8% compared to that of using the carbon block prepared by the untreated cokes.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.04a
• /
• pp.434-435
• /
• 2003

Physicochemical properties of a polymer surface significantly affect adhesion, wetting, and dyeing properties. In recent years, low temperature plasma technology has been widely used for surface modification of polymers. Surface fluorination by low temperature plasma treatment has been employed to improve the water and oily repellency of textile fabrics. However, very few results have been reported on soil release properties of the oxygen plasma treated textile fabrics. (omitted)

• Polymer(Korea)
• /
• v.39 no.2
• /
• pp.338-345
• /
• 2015

Poly(phenylene oxide) (PPO) and polyether imide (PEI) were sulfonated and aminated to create sulfonated poly(phenylene oxide) (SPPO) and aminated polyether imide (APEI), respectively. Characterization of the SPPO and APEI were performed via measurements of FTIR, thermogravimetry (TGA), swelling degree, ion exchange capacity (IEC), and ion conductivity. Next, the surfaces of these membranes were modified by surface fluorination at room temperature. The surface fluorinated SPPO and APEI membranes underwent characterization again for the mentioned measurements to determine any differences. The 3 types of bi-polar membranes were prepared by varying the IEC of the APEI at a fixed SPPO IEC value, which were applied to the low and high NaCl concentration of feed solution at the different current density, respectively. The hypochlorite concentration derived from the surface fluorinated membranes was dependent on the IEC of the APEI and ranged from 491 to 692 ppm at $80mA/m^2$. At low current density of $5mA/m^2$, the hypochlorite concentrations ranged from 18 to 28 ppm for the 4 hrs surface fluorinated membranes and their durability increased greatly.

• Applied Chemistry for Engineering
• /
• v.21 no.4
• /
• pp.475-478
• /
• 2010

Fluorinated polymeric membranes were prepared by direct surface modification of PDMS with fluorine gas ($50{\sim}2000\;{\mu}mol/mol$ in nitrogen). The formed fluorinated polymeric membranes were characterized by FT-IR spectroscopy, GC (Gas chromatography), atomic force microscopy, and scanning electron microscopy. Direct fluorination resulted in the change of permeability and selectivity of various gases (pure gases such as $CO_2$, $O_2$, $N_2$, $C_2H_4$, mixture of He, Ne, Kr, Xe) through PDMS membranes. Fluorination resulted in the maximum 50% increase of selectivity through PDMS membrane.

• Carbon letters
• /
• v.13 no.3
• /
• pp.178-181
• /
• 2012

In this work, we synthesized superhydrophobic coatings by chemical surface functionalization of multi-walled carbon nanotubes (MWCNTs). This was accomplished through the radical polymerization of 3-(trimethoxysilyl) propyl methacrylate modified MWCNTs and fluoro acrylate/methyl methacrylate. The chemical compositions and microstructures of the prepared MWCNT surface were investigated using X-ray photoelectron spectroscopy, Fourier transform infrared spectrometry, and scanning electron microscopy, respectively. The wettability of the MWCNTs surface was determined through contact angle assessments in different liquids. The resulting surface exhibited a water contact angle of $157.7^{\circ}$, which is clear evidence of its superhydrophobicity. The 3D MWCNT networks and the low surface energy of the -C-C- and -C-F- groups play important roles in creating the superhydrophobic surface of the MWCNTs.

• Membrane Journal
• /
• v.18 no.1
• /
• pp.75-83
• /
• 2008

In this research, the research for enhancing the stability at the mechanical strength and thermal stability and high power through the Direct Fluorination of the Polyethylene (PE, Asahi) for secondary battery was conducted. The surface of according to the fluorine gas exposure time and constructional change were observed through the scanning electron microscope image, and the contact angle. The mechanical property was confirmed through the tensile strength and surface hydrophilic property experiment. Charge and discharge experiment, the lifetime property, and the overcharge test were performed in order to confirm the electrochemical characteristic of produced and we confirmed at the high power that the stability about a temperature was improved.

• Polymer(Korea)
• /
• v.33 no.6
• /
• pp.537-543
• /
• 2009

The direct fluorination of polymers is a heterogeneous reaction using the mixture of $F_2$ and inert gas. In general, the resulting fluorinated polymers have good barrier property chemical stability similar to those of the fluoro-polymers, and could be prepared from the simple process. In this study, the polysulfone dense films were surface fluorinated using the direct fluorination technique and gas permeability and selectivity of the prepared membranes were measured with varying both $F_2$ concentration and reaction time. The introduction of $F_2$ was confirmed by X-ray photoelectron spectroscopy (XPS), water contact angles, and atomic force microscopy (AFM). As the $F_2$ increased, the permeability decreased while the selectivities for $O_2$, $CO_2$, and He gases relative to $N_2$ increased.