• Journal of the Korean Wood Science and Technology
• /
• v.47 no.5
• /
• pp.547-556
• /
• 2019

Thinned, small larch logs have small diameters and no value-added final use, except as wood chips, pallets, or fuel wood, which are products with very low economic value; however, their mechanical strength is suitable for structural applications. In this study, small larch logs were sawed, dried, and cut into square timbers (with a $90mm{\times}90mm$ cross section) that were laterally glued to form core panels used to manufacture cross-laminated timber (CLT) wall panels. The surface and back of these core panels were covered with 12-mm-thick structural plywood panels, used as cross bands to obtain three-ply CLT wall panels. This attachment procedure was conducted in two different ways: gluing and pressing (CGCLT) or gluing and nailing (NGCLT). The size of the as-manufactured CLT panels was $1,220mm{\times}2,440mm$, the same as that of the plywood panels. The final wall panels were tested under lateral shear force in accordance with KS F 2154. As the lateral load resistance test required $2,440mm{\times}2,440mm$ specimens, two CLT wall panels had to be attached in parallel. In addition, the final CLT panels had tongued and grooved edges to allow parallel joints between adjacent pieces. For comparison, conventional light-frame timber shear walls and midply wall systems were also tested under the same conditions. Shear walls with edge nail spacing of 150 mm and 100 mm, the midply wall system, and the fabricated CGCLT and NGCLT wall panels exhibited maximum lateral resistances of 6.1 kN/m (100%), 9.7 kN/m (158%), 16.9 kN/m (274%), 29.6 kN/m (482%), and 35.8 kN/m (582%), respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.3
• /
• pp.184-191
• /
• 2009

In the southern part of the Korean Peninsula including Jeju-island, the production amount of domestic cedar has increased gradually. However, their low qualities, expected to be caused by the low density and frequent knots, have restricted their practical utilization as the high value-added products. In this study, it is aimed to look for the new uses of domestic cedar and to examine the applicability for lamination lumbers of structural glued laminated timber (glulam). Above all, machine stress ratings for individual sawn lumbers confirmed that modulus of elasticity (MOE) of cedar lumber was lower than that of other common softwood species in Korea. On the other hand, cedar lumbers have enough stiffness to manufacture the structural glulam in accordance with Korean Industrial Standard (KS). The bonding strength and durability also met the KS limitation. Nevertheless, from the result of bending tests for cedar glulam, it was shown that the modulus of elasticity (MOE) did not meet the KS limitation. Therefore, it was concluded that additional researches were needed for reinforcing the stiffness of cedar glulam.

• Coupled systems mechanics
• /
• v.9 no.2
• /
• pp.147-161
• /
• 2020

Constructive merging of "basic" systems of different behavior creates hybrid systems. In doing so, the structural elements are grouped according to the behavior in carrying the load into a geometric order that provides sufficient load and structure functionality and optimization of the material consumption. Applicable in all materializations and logical geometric forms is a transparent system suitable for the optimization of load-bearing structures. Research by individual authors gave insight into suitable system constellations from the aspect of load capacity and the approximatemethod of estimating the participation of partialstiffnesswithin the rigidity ofthe hybrid system. The obtained terms will continue to be the basisfor our own research of the influence of variable parameters on the behavior of hybrid systemsformed of glued laminated girder and cable of different geometric shapes. Previous research has shown that by applying the strut-type hybrid systems can increase the load capacity and reduce the deformability ofthe free girder.The implemented parametric analysis pointsto the basic parameterin the behavior of these systems-the rigidity ofindividual elements and the overallstiffnessofthe system.The basic idea ofpre-stressing is that, in the load system or individual load-bearing element, prior to application of the exploitation load, artificially challenge the forcesthatshould optimize the finalsystembehaviorin the overall load. Pre-stressing is possible only if the supporting system orsystem's element possesssufficientstrength orstiffness, orreaction to the imposed forces of pre-stressing. In this paper will be presented own research of the relationship of partial stiffness of strut-type hybrid systemsofdifferentgeometric forms.Conducted parametric analysisofhybridsystemswithandwithoutpre-stressing, and on the example of the glulam-steel strut-type hybrid system under realistic conditions of change in the moisture content ofthe wooden girder,resulted in accurate expressions and diagramssuitable for application in practice.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.3 no.2
• /
• pp.199-204
• /
• 1999

A recent application of advanced composite materials, primarily fiber-reinforced plastic (FRP) composites, in structures is the reinforcement of conventional structural materials, such as concrete and glued-laminated timber (glulam), to increase their performance. In particular, the construction of large-scale glulam structures usually requires members with large depths and to significantly increase the stiffness and strength of glulam, the members can be reinforced with FRP at top and bottom surfaces. In this paper, glulam beams reinforced with GFRP strip are tested under 2-point bending and results are compared with numerical solution using layer-wise beam theory.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.6
• /
• pp.13-22
• /
• 2007

This study was carried out to scrutinize possibility of manufacturing pitch pine (Pinus rigida) glued laminated timber in order to add values of pitch pine trees. Also, it was investigated to improve bending performance of pitch pine glulam. Pitch pine was imported as one of major plantation species in Korean peninsula. Machine stress rated grades of pitch pine lumber mostly ranged between E7 and E9. which grades were more or less inferior to producing high quality glulam. However, the adhesive properties between pitch pine and pitch pine, and between pitch pine and Japanese larch (Larix kaempferi Carr.), such as shear bond strength, wood failure rate and de-lamination rate of bonded layer submerged in cold and boiling water, were higher than Korean Standard criteria. These properties are essential for manufacturing glulam with single species or multiple species. The modulus of rupture (MOR) of pitch pine glulam exceeded the criterion of Korean Standard for glulam strength grade but modulus of elasticity (MOE) was lower than the criterion. On the other hand, the bending performances (MOR and MOE) were improved 20 percent by mixing with Japanese larch laminar. It is effective to arrange higher quality Japanese larch laminar at the outer layer of glulam for improving bending performances. In conclusion, it is possible to use low quality pitch pine as laminar of structural glulam for adding values of pitch pine.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.1
• /
• pp.40-47
• /
• 2016

Instead of metal connector generally used on the structural glued laminated timber rahmen joints, the GFRP reinforced laminated plates combining veneer and GFRP (Glass Fiber Reinforced Plastic) and bonded type GFRP rod were used as the connectors. As a result of moment resistance performance evaluation on the joint part applied with these connectors, the yield moment of specimen using the GFRP reinforced laminated plates and GFRP rod pin was measured 4 % lower in comparison to the specimen (Type-1) using the metal connectors, but the initial rotational stiffness was measured 29% higher. Also, the yield moment and rotational stiffness of the specimen using the GFRP-reinforced laminated plates and wood (Eucalyptus marginata) pin showed were measured 11% and 56% higher in comparison to the Type-1 specimen, showing the best performance. It was also confirmed through the failure shape and perfect elasto-plasticity analysis that it showed ductility behavior, not brittle fracture, from the shear resisting force by the pin and the bonding strength increased and the unification of member was carried out. On the other hand, in case of the specimen bonded with GFRP rod, it was impossible to measure the bonding performance or it was measured very low due to poor bonding.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.6
• /
• pp.791-806
• /
• 2020

In this study, a block shear strength test was conducted to compare and analyze the strength and failure mode on the glued laminated timber, CLT, and Ply-lam CLT, which are mainly used for the construction of wood construction as engineering wood. Through this, the Ply-lam CLT manufacturing conditions for optimum production, such as the type of lamina, plywood, adhesive, and layer composition, were investigated. The results are as follow. Through block shear strength test, it showed high strength in the order of glued laminated timber, Ply-lam CLT and CLT. In particular, the shear strength of Ply-lam CLT, which is made of a composite structure of larch plywood and larch lamina, passed 7.1 N/㎟, which is a Korean industrial standards for block shear strength of structural glued laminated timber. In addition, in this study, there was no different in shear strength according to the adhesive type used for glulam, CLT, and Ply-lam CLT adhesion. However, in the case of Ply-lam CLT, the difference in shear strength of Ply-lam CLT was shown according to the type of lamina and plywood. The results showed high strength in the order of Larix kaempferi > Mixed light hardwood ≒ Pinus densiflora, sieb, et, Zucc plywood. The optimal configuration of Ply-lam CLT is when larch plywood and larch lamina are used, and it is decided that the adhesive can be used by selecting PRF and PUR according to the application. The results of block shear strength failure mode by type of wood based materials were analyzed. The failure mode showed shear parallel-to-grain for glulam, rolling shear for CLT, and shear parallel-to-grain and rolling for ply-lam CLT. This is closely related to shear strength results and is decided to indicate higher shear strength in Ply-lam CLT than in CLT due to rolling shear.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.1 s.129
• /
• pp.87-96
• /
• 2005

This study was carried out to evaluate the shear bond strength and adhesive bond durability of structural glued laminated timber (glulam) manufactured with mixed species lumber of Korean red pine, Korean pine and Japanese larch, using resorcinol adhesive and water-based polymeric-isocyanate adhesive (WPI). Each board used as a glulam lamina was graded by visual inspection. The visual lumber grade of the all species was very low due to the large size and number of knots and the steep slope of grain. In view of the results, appropriate pruning, sawing and drying processes might be needed to produce high grade lamina lumber with small knot size and drying defect free. Shear bond strength of every tested glulam specimen ranged between 7.9 and $9.9N/mm^2$, and much higher than the Korean Standard (KS) for glulam shear bond strength, $7.1N/mm^2$. There was not much shear bond strength difference between wood/resorcinol and wood/WPI. The resorcinol adhesive bond durability exceeded KS requirements. However, delamination on the end-grain surfaces of WPI glulam submerged in both room temperature and boiling water severely occurred, and its durability did not meet KS requirements. Further investigations may be required, and special care should be taken, to ensure long service life of WPI glulam used for exterior application. Results of this study are expected to be useful for improvement of mechanical properties and structural performance of mixed species glulam.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.3
• /
• pp.213-220
• /
• 2018

In order to use Pitch pine (Pinus rigida Miller) as the material of the structural glued laminated timber, the effect of the amount of resin exudation due to storage time after the planning and the knot of the lamina were evaluated on the bonding properties of the glued board with resorcinol resin. For Pitch pine that was dried at high temperature ($120{\sim}95^{\circ}C$) and low temperature ($65{\sim}50^{\circ}C$), the flat sawn(tangential section) showed higher amount of resin exudation than the quarter sawn(radial section). And the low temperature drying wood showed higher resin exudation than the high temperature drying wood. The low and high temperature drying wood showed the highest amount of resin exudation on the 3rd day and 7th day, respectively and they were gradually decreased. However, there were no significant differences from 15 to 90 days. Adhesion performances were low until 2~3 days with high exudation of resin, but there were no significant differences after 15 days. Both high temperature and low temperature drying woods satisfied the Korean standard regardless of the storage time. The adhesive strengths of the laminating parts including knots were higher than those of KS criteria, but the wood failures were not satisfied the KS standard. Adhesive performances according to the laminating combinations (quarter sawn + quarter sawn, flat sawn + flat sawn, quarter sawn + flat sawn) were better than those of KS criteria in all laminating combinations in both high temperature and low temperature drying woods.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.4
• /
• pp.446-455
• /
• 2015

Based on comparative studies on standards and grading procedures of machine graded lumber in Korea and other countries, this study proposed a procedure of determining the grade classification and design strengths of domestic machine graded lumber. Differences between machine stress rated lumber and E-rated laminations were detailed in order to clarify the need for the procedure improvement. To this improvement the use of average MOE requirement for grading was introduced instead of the fixed minimum MOE requirement which is currently used in the Korean standards. It was found that the fixed minimum MOE requirement method was easier for an inspector to grade but, less efficient as a strength predictor than the average MOE requirement method. The advantage of average MOE requirement method is statistically MOR-MOE regression-based MOR prediction and highly efficient in quality control though it requires a computer-aided operation system in an initial setup. A major weakness of the current Korean grading system was found that different strength characteristics depending on wood species were not reflected on the grade classification and the tabulated allowable design stress. The proposed procedures were developed taking advantages of respective merits of both methods and based on MOR-MOE regression analysis. Through this procedure, the grades of machine stress rated lumber should be revised to become interchangeable with E-rated lamination, which would be beneficial to the cost competitiveness of domestic machine graded lumber and glued laminated timber industry.