• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.2
• /
• pp.88-95
• /
• 1994

In order to compare mechanical properties of ausformed martensite with those of marformed martemsite in Fe-30%Ni-0.1%C alloy and to investigate their strengthening mechanisms, ausformed martensite and marformed martensite were prepared by ausforming treatment and marforming treatment respectively. The microstructures were observed and the quantities of retained austenite, hardness, yield strength, ultimate tensile strength and elongation were examined. The strength of ausformed martensite was mainly increased because of the lattice defects inherited from austenite. The ductility of ausformed martensite was constant at the rate of 7-8% by ductile matrix formation of the retained austenite in spite of the increase in strength. The strength of marformed martensite was increased by the increment in dislocation density, the crossing of transformation twin with deformation twin and the mutual crossing of deformation twin. The ductility of mar formed martensite was slightly lower than that of ausformed martensite, but the strength of mar formed martensite was prominently higher.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.90-91
• /
• 2020

Utilization of upgraded fine fly ash in cement-based materials has been proved by many researchers as an effective method to improve compressive strength of cement based materials at early ages. The addition of fine fly ash has introduced dilution effect, enhanced pozzolanic reaction effect, nucleation effect and physical filling effect into cement-fly ash system. In this study, an integrated reaction model is adpoted to quantify the contributions from cement hydration and pozzolanic reaction to compressive strength. A modified model related to the physical filling effect is utilized to calculate the compressive strength increment considering the gradual dissolution of fly ash particles. Via combination of these two parts, a numerical model has been proposed to predict the compressive strength development of fine fly ash mortar considering fly ash fineness. The reliability of the model is validated through good agreement with the experimental results from previous articles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.425-428
• /
• 1996

Treeing deterioration which is one of the main cause of breakdown in insulating materials is affected by temperature, applied voltage and frequency. In this study, GN was introduced to improve impact strength of DGEBA/MDA system and the temperature dependence of AC treeing deterioration in this system was investigated. Dielectric breakdown strength decreased with the increment of temperature. As temperature increased, the growth rate of tree Increased.

• Journal of the Korea Institute of Building Construction
• /
• v.7 no.4
• /
• pp.145-151
• /
• 2007

In this paper, tests are carried out in order to investigate the strength development of concrete under various binder types, W/B and curing temperature ranged from $5{\sim}20^{\circ}C$. Fly ash and blast furnace slag were incorporated by as much as 30%, respectively. Strength development of concrete are estimated using Logistic model and strength ratio of concrete at 28days to that at early age are also investigated. According to experimental results, it is found that good agreements are obtained between measured values and calculated ones using logistic model below $20^{\circ}C$. Strength ratio of concrete at 28days to that at early age increases in case W/B decreases and curing temperature increases. Tables and graphs for strength ratio of concrete are provided in this paper. It is capable of obtaining and predicting the periods to attain design strength by considering increment factor of strength easily with the table and graphs presented in this paper. This paper presents the reference data to decide removal time of form, time to reach target strength and strength inspection of remicon whether the test specimens meet the specified criteria of compressive strength. Multi regression models with respect to the relationship between 7days compressive strength and 28 days compressive strength depending on W/B and admixture types are presented.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.215-218
• /
• 1995

This paper presents an experimental study on the strength and deformation of concrete-filled circular steel short columns. Six specimens of concrete-filled circular short columns were tested under concentric compressive load. For comparsion, three specimens of circular steel short columns were also loaded to failure. The ultimate strength, ductility, and confinement mechanism of columns were compared. In the comparison, the effect of witch-thickness ratio and concrete compressive strength on the behavior of colimns were examed. As a result, the axial load verse axial average strain relationship of concrete-filled circular steel columns was very stable, because of interactions between the concrete and steel, the strength are 13% and 30% larger than the strength extimated by simply superimposed method of the concrete and steel. The ratio of the circumferential to longitudinal strain increment, both measured on the steel suface, was 0.28 up to the longitudinal strain of 0.1%, increases from 0.3 to 0.8 between the strain of 0.1% to 0.3%, and 0.8 beyond the strain of 0.3%

• Journal of the Korean Society of Environmental Restoration Technology
• /
• v.7 no.2
• /
• pp.46-51
• /
• 2004

In this paper, reinforcement of soil shear strength by bamboo(substitute materials simulating a root system) are evaluated by soil strength parameters(apparent cohesion(c) and internal friction angle(tan${\Phi}$)), using simple shear tester which clearly depicts shear deformation and controls soil suction. The results show that the internal friction angle does not change under various soil suction conditions but the apparent cohesion, which reach a peak in suction of 45cm$H_2O$ near critical capillary head, is effected by soil suction. And the reinforcement of soil strength by bamboo are expressed by apparent cohesion more than internal friction angle. In addition the increment of apparent cohesion by bamboo reached a peak in suction 45cm$H_2O$ too.

• Journal of the Korean Geotechnical Society
• /
• v.35 no.3
• /
• pp.25-35
• /
• 2019

A laboratory test on uniaxial compressive strength was carried out by making 640 specimens in total, which were divided into two groups by their curing time of 7 and 28 days for 3 water content conditions of a water content at 100% saturation level and 10% and 20% increased water content from the state with clay, sand and gravel mixed grounds of 20 ground conditions of 4 types of stabilizer mixing conditions which were 8%, 10%, 12%, 14%, to understand laboratory strength characteristics for strength design of deep mixing ground. In case of clayey grounds, although the strength increased depending on the increase of stabilizer content, it showed to be analogous regardless of the curing time. And the impact on the strength development of deep mixing specimen according to water content was considered to be comparatively little compared to other grounds. For sandy grounds, the strength increment amount clearly showed to increase as stabilizer content increased, and also the increase of water content was determined to be decreasing the strength increment effect. For gravel mixed grounds, at 14% or over of stabilizer content, the effect on strength development was big making a large increase in strength, but compared to sandy grounds, the strength ratio depending on the curing time showed to be small.

• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.738-746
• /
• 1997

MgO clinker and two kinds of dolomite clinkers with different microstructures and CaO contents were used as starting materials, and the effects of Fe2O3 addition on the properties of MgO and dolomite were investigated in the range of 2 to 8 wt% of Fe2O3 content. Secondary phases contributed to densification of MgO-Fe2O3 and dolomite-Fe2O3 were magnesioferrite and dicalciumferrite, respectively. Sinterabilities of MgO-Fe2O3 and dolomite-Fe2O3 were directly proportional to the amount of secondary phases. Also, sinterability of dolomite itself was dependent on the microstructure of starting material including distribution of CaO and MgO as well as the addition amount of Fe2O3. The flexural strength of MgO-Fe2O3 content was almost constant. The hydration resistance of dolomite with large size of MgO and discontinuous distribution of CaO was higher than that of dolomite with small size of MgO and continuous distribution of CaO. Also, the minimum content of Fe2O3 to prevent they hydration of dolomite was about 4wt%. As increasing Fe2O3 content, the penetration resistance of MgO-Fe2O3 was improved by the increment of magnesioferrite. On the other hand, the penetration resistance of dolomite-Fe2O3 was decreased because of the increment of dicalciumferrite having low melting point.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.702-708
• /
• 2003

Cement paste, mortar or concrete specimens, substituting the content of Portland cement with fly ash up to 50 wt%, were prepared to investigate the effect of fly ash on the temperature, free lime content and strength etc. of mortar/concrete. Being compared with the concrete made of ordinary Portland cement, temperature increment of the concrete containing 50 wt% fly ash reduced, according to appropriate conversion formulae, to about 45％ at the 7 days curing time: the temperature increment of the former amounted to 33.4$^{\circ}C$, while that of the latter only to 18.7$^{\circ}C$. On the other hand, it is better to control the content of fly ash in the cement that is used for reinforced concrete not to exceed 30 wt％. In this study, more than 28 days curing time is necessary in order that the strength of concrete made of fly ash cement will be higher than that of pure Portland cement. In addition, 28-days concrete strength higher than 360 kg/$\textrm{cm}^2$ could be easily achieved even with 50 wt% fly ash cement.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.3 no.4
• /
• pp.163-171
• /
• 1999

In this study, we executed fundamental experiment to investigate properties of accelerated carbonation with changing chloride content of concrete used sea sand in order to examine durability. So we obtained the results of following properties of mechanics, durability, concrete with sea sand, determined concrete w/C 30%, 40%, 50%, and fine aggregate 40% and changing containing chloride 0, 0.3, 0.6, $0.9kg/m^3$ by the experiment of accelerated neutralization. The results of this study as follows: 1) As result of changing chloride content of concrete used sea sand augmented in stages $0.3kg/m^3$, accelerated carbonation was increased as increment chloride content. The increment depth was decreased as it went long term age. It was shown the chloride content effected increment of carbonation depth in concrete 2) As a result of changing W/C of concrete used sea sand augmented in stages 10% at a time from 30% to 50%, accelerated carbonation depth of concrete was increased as W/C ratio. 3) As the carbonation concrete used sea sand, compressive strength between 8 weeks and accelerated carbonation depth of 1 weeks, 2 weeks, 4 weeks, 8 weeks was inversion proportion.