• Journal of the Korean Wood Science and Technology
• /
• v.29 no.1
• /
• pp.22-30
• /
• 2001

Composites with various layer constructions involving the ratio of S/P were produced from wood strands(S) and particles(P) (Cryptomeria japonica D.Don) to measure various Young's moduli and anisotropy by ultrasonics. As a result, static Young's moduli of composites were almost same as dynamic Young's moduli obtained from natural frequency. However, these were smaller than those evaluated from ultrasonic wave propagation velocity. The differences between propagation velocity of the parallel(${\parallel}$) and perpendicular(${\bot}$) in-plane direction resulted in a tendency of anisotropy. The tendency of anisotropy was larger in three-layer constructions than in seven-layer constructions. The differences of strand surface layers showed larger values than those of particle surface layers. Also, composites with higher weight ratio of strand had a tendency to propagate rapidly in each direction. In contrast to these results, the propagation velocity in the thickness direction had a tendency to propagate rapidly in composites with particle surface layers and the lower weight ratio of strand.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.3
• /
• pp.1-8
• /
• 2000

To develop the technology of producing structural board from low grade materials, an attempt was made to produce strand/particle composites from split wood strand(S) and particle(P) of (Cryptomeria japonica D. Don), which changed the layer construction and the ratio of S/P. The influence of layer construction on board properties was determined, focusing on the number and alignment of the S layers. The effect of weight ratio of S/P (3:7, 1:1, 7:3) on mechanical properties was also discussed on seven layered panel. Mechanical properties were determined from static bending tests to give parallel and perpendicular modulus of rupture (MOR) and modulus of elasticity (MOE), and the internal bond (IB) strength. In general, the surface strand layers contributed to the MOR and MOE. The parallel MOR and MOE values were the largest for the single layered S panel (only Slayers: S1), but the perpendicular MOR and MOE was the smallest. Perpendicular MOR and MOE were the largest for seven layered composite that had two cross oriented strand layers (SPSPSPS: SP7). Specimens retained more than half of their MOE and MOR after two hours in boiling water and one hour soaking. IB was the largest for the panel having only P layers, however, differences in IB strength were not identified among the other multi-layered composite panels thus the effect of layer construction on IB strength was small. Thickness swelling (TS) and surface roughness were smaller for the composite having P layers on the surface than for those having S layers. The addition of strands did not enhance the mechanical properties (MOR, MOE, IB). TS values for the panels, with which the S/P ratio was over than 1:1, was the similar to the value for the single layered S panels.