• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.4
• /
• pp.427-434
• /
• 2004

Ferritic stainless steel is recently used in high temperature structures because of its good properties of thermal fatigue resistance, corrosion resistance, and low price. Tensile and low-cycle fatigue (LCF) tests on 429EM stainless steel used in exhaust manifold were performed at several temperatures from room temperature to 80$0^{\circ}C$. Elastic Modulus, yield strength, and ultimate tensile strength monotonically decreased when temperature increased. Cyclic hardening occurred considerably during the most part of the fatigue life. Dynamic strain aging was observed in 200~50$0^{\circ}C$, which affects the cyclic hardening behavior. Among the fatigue parameters such as plastic strain amplitude, stress amplitude, and plastic strain energy density (PSED), PSED was a proper fatigue parameter since it maintained at a constant value during LCF deformation even though cyclic hardening occurs considerably. A phenomenological life prediction model using PSED was proposed considering the influence of temperature on fatigue life.

• Journal of Mechanical Science and Technology
• /
• v.19 no.6
• /
• pp.1229-1242
• /
• 2005

When natural rubber is used for a long period of time, it becomes aged; it usually becomes hardened and loses its damping capability. This aging process affects not only the material property but also the (fatigue) life of natural rubber. In this paper the aging effects on the material property and the fatigue life were experimentally investigated. In addition, several fatigue life prediction equations for natural rubber were proposed. In order to investigate the aging effects on the material property, the load-stretch ratio curves were plotted from the results of the tensile test, the compression test and the simple shear test for virgin and heat-aged rubber specimens. Rubber specimens were heat-aged in an oven at a temperature ranging from $50^{\circ}C$ to $90^{\circ}C$ for a period ranging from 2 days to 16 days. In order to investigate the aging effects on the fatigue life, fatigue tests were conducted for differently heat-aged hourglass-shaped and simple shear specimens. Moreover, finite element simulations were conducted for the specimens to calculate physical quantities occurring in the specimens such as the maximum value of the effective stress, the strain energy density, the first invariant of the Cauchy-Green deformation tensor and the maximum principal nominal strain. Then, four fatigue life prediction equations based on one of the physical quantities could be obtained by fitting the equations to the test data. Finally, the fatigue life of a rubber bush used in an automobile was predicted by using the prediction equations, and it was compared with the test data of the bush to evaluate the reliability of those equations.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.6
• /
• pp.95-102
• /
• 2021

Elastometic bearings using flexible rubber materials have recently been widely applied for seismic retrofit of bridges. However, due to various factors, the aging of the rubber material progresses, which causes the shear stiffness change of the bearing, which affects the seismic performance of the bridge. For natural rubber, accelerated heat aging test was performed with variables of heating temperatures and exposure time to analyze shear characteristics. As aging progresses (i.e. increase of temperature and exposure time), the maximum shear stress and shear strain decrease. Also, the shear stiffness is greatly increased at the same shear strain. This means that the rubber material is hardened, implying that the seismic performance of the elastomeric bearing becomes poor.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1978.06a
• /
• pp.116.3-117
• /
• 1978

• Earthquakes and Structures
• /
• v.6 no.2
• /
• pp.127-140
• /
• 2014

Laminated rubber bearing is very popular base isolation of earthquake engineering pertaining to the passive structural vibration control technologies. Rubber used in fabricating NRB and LRB can be easily attacked by various environmental factors such as oxygen, heat, light, dynamic strain, and organic liquids. Among these factors, this study carried out thermal aging test to investigate the effect of thermal aging on the mechanical properties of laminated rubber bearings in accelerated exposure condition of $70^{\circ}C$ temperature for 168 hours. The compressive-shear test was carried out to identify the variation of compressive and shear properties of the rubber bearings before and after thermal aging. In contrast to tensile strength and elongation tests, the hardness of rubber materials showed the increasing tendency dependent on exposure temperature and period. Based on the test results, the property changes of rubber bearing mainly aged by heat are quantitatively presented.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.630-636
• /
• 1994

The changes in adhesion interface between rubber compound and brass plated steel cord after various aging treatments were studied by using an Auger electron spectrometer and a scanning electron microscope. After thermal aging, partial oxidation and additional growth of adhesion layer were observed. The adhesion layer and brass were partially removed after humid aging. With dynamic aging the adhesion layer was destroyed and the corrosion of steel core was proceeded. The changes in adhesion interface were discussed in terms of the adhesion properties determined from the stress-strain experiments.

• Journal of Powder Materials
• /
• v.13 no.3 s.56
• /
• pp.172-177
• /
• 2006

Aging characteristics and mechanical properties of commercial 7xxx series Al composites were investigated from viewpoint of ceramic contents. After sintering process, sintered densities of blended and composite powder were 95 and 97%, respectively. Each part was solution-treated at $475^{\circ}C$ for 60 min and aged $175^{\circ}C$. And two-step aging was also performed form $120^{\circ}C$ to $175^{\circ}C$. The aging behavior of the sintered composite pow-der was different from that of sintered blended powder. The peak aging time of the composite was rapid as well due to strain. Before aging, mechanical properties of sintered composite powder was significantly higher than that of sintered blended powder. These increments of properties were directly affected by ceramic particles. However, after aging, incremental rate of mechanical properties was slowed in the composite.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.1
• /
• pp.11-16
• /
• 2007

The fatigue properties of Ti-Ni shape memory alloy wires were investigated. In Ni-rich Ti-Ni shape memory alloys, $Ti_3Ni_4$ precipitates formed by aging treatments are believed to vary the shape memory and mechanical properties. In this study, the effect of aging temperature and aging time on shape memory properties and fatigue life were investigated using Ti-50.9 at% Ni alloy wires. The specimens were solution-treated at 1073 K for 3.6 ks followed by aging at 573 K, 673 K and 773 K for periods between 3.6 ks and 3600 ks. It was found that the fatigue life under a constant stress decreased with increasing aging temperature. When the specimens were aged at 573 K for periods between 36 ks and 360 ks, superior shape memory and fatigue properties were obtained. The fatigue life also decreased when the test temperature and strain amplitude increased. It was concluded that the fatigue life exhibited a linear relationship with the critical stress for slip.

• YAKHAK HOEJI
• /
• v.36 no.5
• /
• pp.460-468
• /
• 1992

Several bichemical parameters related to free radicals were estimated in senile-prone (P) and resistant(R) strains of male senescence-accelerated mice(SAM) at 2, 5 and 11 months of age. The superoxide generation was increased with age in SAM-R/1 and SAM-P/2. Compared to SAM-R/1, more generation of superoxide was significantly noted in the SAM-P/2 liver. The activities of Cu/Zn-superoxide dismutase and catalase were decreased during aging and these activities in SAM-P/2 were significantly lower than in SAM-R/l liver. The activities of glutathione S-transferase were varied with aging, whereas SAM-P/2 showed lower levels compared to SAM-R/l. The gradual decreases of glutathione, protein bound-SH and nonprotein bound-SH contents were noted with increasing age. SAM-P/2 liver contained lesser amounts of glutathione and nonprotein bound-SH compared to SAM-R. In conclusion, superoxide generation was increased whereas the antioxidant enzyme activities were decreased during aging in SAM-R/1. In addition, SAM-P/2 strain showed more superoxide generation and less antioxidant enzyme activities than SAM-R/1 in the liver, thus we assume that these factors might accelerate the senescence of SAM-P/2 strain.

• Journal of Applied Reliability
• /
• v.6 no.2
• /
• pp.135-150
• /
• 2006

Rubber material properties and lifetime evaluation are very important in design procedure to assure the safety and reliability of the rubber components. This paper discusses the failure mechanism and material tests were carried out to predict the useful lifetime of NBR and EPDM for compression motor, which is used in refrigerator component. The heat-aging process leads not only to mechanical properties change but also to chemical structure change so called degradation. In order to investigate the aging effects on the material properties, the accelerated test were carried out. The stress-strain curves were plotted from the results of the tensile test for virgin and heat-aged rubber specimens. The rubber specimens were heat-aged in an oven at the temperature ranging from $70^{\circ}C\;to\;100^{\circ}C$ for a period ranging from 1 to 180 days. Compression set results changes as the threshold are used for assessment of the useful life and time to threshold value were plotted against reciprocal of absolute temperature to give the Arrhenius plot. By using the compression set test, several useful lifetime prediction equations for rubber material were proposed.