• Advances in concrete construction
• /
• v.3 no.4
• /
• pp.283-293
• /
• 2015

This paper presents the effects of elevated temperatures of $400^{\circ}C$ and $800^{\circ}C$ on the residual compressive strength and failure behaviour of fibre reinforced concretes and comparison is made with that of unreinforced control concrete. Two types of short fibres are used in this study e.g., steel and basalt fibres. The results show that the residual compressive strength capacity of steel fibre reinforced concrete is higher than unreinforced concrete at both elevated temperatures. The basalt fibre reinforced concrete, on the other hand, showed lower strength retention capacity than the control unreinforced concrete. However, the use of hybrid steel-basalt fibre reinforcement recovered the deficiency of basalt fibre reinforced concrete, but still slightly lower than the control and steel fibres reinforced concretes. The use of fibres reduces the spalling and explosive failure of steel, basalt and hybrid steel-basalt fibres reinforced concretes oppose to spalling in deeper regions of ordinary control concrete after exposure to above elevated temperatures. Microscopic observation of steel and basalt fibres surfaces after exposure to above elevated temperatures shows peeling of thin layer from steel surface at $800^{\circ}C$, whereas in the case of basalt fibre formation of Plagioclase mineral crystals on the surface are observed at elevated temperatures.

• Computers and Concrete
• /
• v.19 no.1
• /
• pp.79-85
• /
• 2017

This paper summarizes the experimental study of the shear behaviour of Hybrid Fibre Reinforced Concrete (HFRC) beams retrofitted by using externally bonded Glass Fibre Reinforced Polymer (GFRP) laminates. To attain the set-out objectives of the present investigation, steel fibre of 1% and polypropylene fibre of 0.30% was used for hybrid steel-polypropylene fibre reinforced concrete: whereas for hybrid glass-polypropylene fibre reinforced concrete, glass fibre by 0.03% and polypropylene fibre of 0.03% by volume of concrete was used. In this study, 9 numbers of beams were cast and tested into three groups (Group I, II & III). Each group containing 3 numbers of beams, out of which one serve as a control beam or a hybrid steel-polypropylene fibre reinforced concrete beam or a hybrid glass - polypropylene fibre reinforced concrete beam and the remaining two beams were preloaded until shear cracks appeared up to 75% of ultimate load and then preloaded beams (damaged beams) were retrofitted with GFRP laminates at shear zone in the form of strips, as one beam in vertical position and another beam in inclined position to restrict the shear cracks. Finally, the retrofitted beams were loaded until failure and test results were compared. The experimental tests have been conducted to investigate various parameters of structural performance, such as load carrying capacity, crack pattern and failure modes, load-deflection responses and ductility relations. The test results revealed that beams retrofitted using GFRP laminates considerably increased the load carrying capacity. In addition, it was found that beams retrofitted with inclined strip offers superior performance than vertical one. Comparing the test results, it was observed that hybrid steel-polypropylene fibre reinforced concrete beam retrofitted with GFRP laminates showed enhanced behaviour as compared to other tested beams.

• International Journal of Concrete Structures and Materials
• /
• v.10 no.3
• /
• pp.325-335
• /
• 2016

This paper studies the effects of steel fibre geometry and architecture on the cracking behaviour of steel fibre reinforced concrete (SFRC), with the reinforcements being four types, namely 5DH ($Dramix^{(R)}$ hooked-end), 4DH, 3DH-60 and 3DH-35, of various hooked-end steel fibres at the fibre dosage of 40 and $80kg/m^3$. The test results show that the addition of steel fibres have little effect on the workability and compressive strength of SFRC, but the ultimate tensile loads, post-cracking behaviour, residual strength and the fracture energy of SFRC are closely related to the shapes of fibres which all increased with increasing fibre content. Results also revealed that the residual tensile strength is significantly influenced by the anchorage strength rather than the number of the fibres counted on the fracture surface. The 5DH steel fibre reinforced concretes have behaved in a manner of multiple crackings and more ductile compared to 3DH and 4DH ones, and the end-hooks of 4DH and 5DH fibres partially deformed in steel fibre reinforced self-compacting concrete (SFR-SCC). In practice, 5DH fibres should be used for reinforcing high or ultra-high performance matrixes to fully utilize their high mechanical anchorage.

• Steel and Composite Structures
• /
• v.44 no.6
• /
• pp.803-816
• /
• 2022

Composite materials are effective in forming externally bonded reinforcements which find applications related to existing structures repair, attributed to their high strength-to-weight ratio and ease of installation. Among various composites, fibre reinforced polymers (FRP) have somewhat been largely accepted as a commonly utilized composite for such purposes. It is only recently that steel fibres have been considered as additional members of the FRP fibre family, intuitively termed as steel reinforced polymer (SRP). Owing to its low cost and permissibility of fibre bending at sharp corners, SRP is rapidly becoming a viable contender to other FRP systems. This paper investigates the bond behaviour of SRP-concrete joints with different bonded lengths (50, 75, 100, 150 and 300 mm) and widths (15, 30, 40, 50, and 75 mm) using single-lap shear tests. The experimental specimens contain SRP strips with a fixed density of steel fibres (0.472 cords/mm) bonded to the face of concrete prisms. The load responses were obtained and compared in terms of corresponding load and slip boundaries of the constant region and the peak loads. The failure modes of SRP composites are discussed, and the range of effective bonded length is evaluated herein. In the end, a new analytical model was proposed to estimate the SRP-concrete bond strength using a genetic algorithm, which outperforms 22 existing FRP-concrete bond strength models.

• Computers and Concrete
• /
• v.11 no.5
• /
• pp.365-382
• /
• 2013

Although shear reinforcement in beams typically consists of steel bars bent in the form of stirrups or hoops, the addition of deformed steel fibres to the concrete has been shown to enhance shear resistance and ductility in reinforced concrete beams. This paper presents a model that can be used to predict the shear strength of fibrous concrete rectangular members without stirrups. The model is an extension of the plasticity-based crack sliding model originally developed for plain concrete beams. The crack sliding model has been improved in order to take into account several aspects: the arch effect for deep beams, the post-cracking tensile strength of steel fibre reinforced concrete and its ability to control sliding along shear cracks, and the mitigation of the shear size effect due to presence of fibres. The results obtained by the model have been validated by a large set of experimental tests taken from literature, compared with several models proposed in literature, and numerical analyses are carried out showing the influence of fibres on the beam failure mode.

• Earthquakes and Structures
• /
• v.10 no.1
• /
• pp.125-139
• /
• 2016

For seismic retrofitting of masonry walls, the use of fibre reinforced cement-based mortar for bonding the fibre grids can eliminate some of the shortcomings related to the use of resin as bonding material. The results of an experimental testing program on masonry walls retrofitted with fibre reinforced mortar and fibre grids are presented in this paper. Seven squat masonry walls were tested under unidirectional lateral displacement reversals and constant axial load. Steel anchors were used to increase the effectiveness of the bond between the fibre grids and the masonry walls. Application of fibre grids on both lateral faces of the walls effectively improved the hysteretic behaviour and specimens could be loaded until slip occurred in the horizontal joint between the masonry and the bottom concrete stub. Application of the fibre grids on a single face did not effectively improve the hysteretic behaviour. Retrofitting with fibre reinforced mortar only prevented the early damage but did not effectively increase deformation capacity. When the boundaries of the cross sections were not properly confined, midplane splitting of the masonry walls occurred. Steel anchors embedded in the walls in the corners area effectively prevented this type of failure.

• Structural Engineering and Mechanics
• /
• v.76 no.4
• /
• pp.491-503
• /
• 2020

This study extends previous experimental research on the shear behaviour of macrosynthetic fibre-reinforced concrete beams and compares them to steel fibre-reinforced concrete beams with similar mechanical and geometrical properties. This work employed two fibre types: 60/0.9 (long/diameter) double hooked-end steel fibre and 60/85 monofilament polypropylene fibre. Beams were tested by shear loading covering parameters, such as two different cross-section widths, two shear-span-to-effective-depth ratios, two fibre types and using repetitions with and without transverse reinforcement. For quantitative comparison purposes, crack pattern evolution was studied along increasing loads levels. Effects were studied by photogrammetry, including influence of fibres on crack propagation in uncracked and dowel zones, influence of fibres on stirrup behaviour, and shear deformation or kinematics of critical shear cracks. The results evidenced similar effectiveness for both fibre types in controlling shear crack propagation and horizontal dowel cracking. Both fibres provided similar shear ductility and shear deflections. Consequently, the authors confirm that residual flexural tensile strengths are a convenient parameter for characterising the shear behaviour of fibre-reinforced concrete beams.

• Advances in concrete construction
• /
• v.6 no.6
• /
• pp.631-643
• /
• 2018

The focus of this paper is given to the investigation of mechanical properties of steel fibre reinforced self-compacting concrete after being exposed to fire. The research programme covered tests of two sets of beams: specimens subjected to fire and specimens not subjected to fire. The fire test was conducted in an environment mirroring one of possible real fire situations where concrete surface for an extended period of time is directly exposed to flames. Micro-cracking of concrete surface after tests was digitally catalogued. Compressive strength was tested on cube specimens. Flexural strength and equivalent flexural strength were tested according to RILEM specifications. Damages of specimens caused by spalling were assessed on a volumetric basis. A comparison of results of both sets of specimens was performed. Significant differences of all tested properties between two sets of specimens were noted and analysed. It was proved that the limit of proportionality method should not be used for testing fire damaged beams. Flexural characteristics of steel fibre reinforced self-compacting concrete were significantly influenced by fire. The influence of fire on properties of steel fibre reinforced self-compacting concrete was discussed.

• Advances in concrete construction
• /
• v.10 no.1
• /
• pp.1-11
• /
• 2020

This study intends to produce an ultra-high performance fibre reinforced concrete (UHPFRC) made with hybrid fibres (i.e., steel and polypropylene). Compressive and tensile strength characteristics of the hybrid fibres UHPFRC are considered. A total of 14 fibre-reinforced composites (FRCs) with different fibre contents or types of fibres were prepared and tested in order to determine a suitable hybrid fibre combination. The compressive and tensile strengths of each concrete at 7 days were determined. The results showed that a hybrid mix of micro-polypropylene and steel fibres exhibited good compromising performances and is the ideal reinforcement mixture in a strong, cost-effective UHPFRC. In addition, maximum compressive strength of 167 MPa was achieved for UHPFRC using 1.5% steel fibres blended with 0.5% macro-polypropylene fibres.

• Structural Engineering and Mechanics
• /
• v.66 no.5
• /
• pp.631-636
• /
• 2018

This study aims to investigate the flexural behaviour of glass fibre reinforced polymer (GFRP) laminated hybrid fibre reinforced concrete (HFRC) beams. The flexural and ductility performance of GFRP laminated HFRC beams having different proportions of polyolefin and steel fibres with 1.0% of total volume fraction were investigated. The parameters of this investigation included: load and deflection at first crack, yield, and ultimate stages, ductility and crack width. A total of seven beams of $150{\times}250mm$ in cross-section were tested in the laboratory over an effective span of 2800 mm. One reinforced concrete (RC) beam without any internal or external GFRP was taken as the reference beam. Of the remaining six beams, one beam was strengthened with GFRP, one beam with 100% steel fibres was strengthened with GFRP and four beams, each with different volume proportions of polyolefin and steel fibres (20:80, 30:70, 40:60, 50:50) were strengthened with GFRP. All the above beams were tested until failure. The experimental results show that a fibre volume proportion of 40:60 (polyolefin-steel) has significantly improved the overall performance of the tested beams.