• Elastomers and Composites
• /
• v.33 no.2
• /
• pp.103-109
• /
• 1998

The determination method of successful operation conditions to control the temperature and pressure in autoclave after non-taping vulcanization process was represented. Heat and mass balances were constructed to predict the mass flow rates of air, steam, and condensed water into or from autoclave when the temperature and pressure in the autoclave were to be controlled in the desired profiles. The balance equations were solved by appropriate mathematics, and the solution was applied to an autoclave system where the temperature and pressure were linearly decreased. The resulting solutions were illustrated in graphs.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.189-192
• /
• 1998

The mechanical properties of alkali resistance (AR) glass fiber reinforced cement(GFRC) under different curing conditions were investigated in this study. The specimens were formed by extrusion process, and then steam cured and autoclaved. An autoclaved specimen showed the elastic-brittle behavior up to 4% of fiber volume fraction. However, it was found that the fracture behavior for cured specimen was changed to the elastic-plastic with crack branches fracture at greater than 3 vol.% of fiber.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.04a
• /
• pp.203-208
• /
• 1994

These tests were conducted to get a device high strength concrete products in factory using admixtures for high strength concrete. The superplasticzer was used to compensate low slump of base concrete keeping its slump up about $6\pm1cm$. To examine the property for strength revelation of concrete using admixtures for high strength concrete, steam and standard curing were compared each other. Test results show that admixtures for high strength concrete is effective in steam curing and compressive strength 500kgf/$\textrm{cm}^2$ is obtained at one day, 650kgf/$\textrm{cm}^2$ at 28days as added to concrete at the ratio of 10-15%, and 740kgf/$\textrm{cm}^2$ at the ratio of 30%. Therefore admixtures for high strength concrete is effective in steam curing and make it possible to get high strength concrete using only steam curing not using autoclave curing.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.437-442
• /
• 1998

In order to investigate the mechanical properties of several fibers for reinforced cement these speciments with 2wol% of ARG and organic fibers were formed by vacuum extrusion process. After steam curing and autoclaving the flexural strength and the elastic modulus of FRC were measured. It was found that the ARG-FRC showed the elastic-brittle fracture behavior in both steam cured and autoclaved condition. And also the steam cured PP and PVA-FRC had elstic-plastic behavior but their ductility were reduced and changed to the elastic-brittle after autoclaving This change in mechanical behavior was found to be related to the thermal stablity of thes organic fibers.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.545-548
• /
• 2006

This study has been carried out to examine the properties of concrete according to replacement ratio and curing method of fly ash, in order to increase utilization of it. As the result of experiments, the 7 days of early age strength presented around 20MPa, up to 20% of replacement ratio, which is almost the same strength as non-replacement. However, when the replacement ratio was 30%, the strength was decreased to 16MPa, as 20% reduction compared to the non-replacement condition. In 365 days of long term aging, the strength was 5% higher, up to 20% of the replacement ratio, due to the pozzolanic reaction of fly ash. When the replacement ratio was 30%, it presented similar strength development as the non-replacement condition. Steam curing and autoclave curing increased the short age strength, regardless of the replacement ratio of fly ash; however, they don't have an effect on increasing the 365 days of long term strength. Water curing showed high strength development after 28 days, 51.81MPa, which is around 30% higher than air curing, 38.9MPa, steam curing, 38.6MPa, and autoclave curing, 39MPa. Therefore, water curing was examined as one of the very effective curing methods for developing long term strength of concrete.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.3
• /
• pp.37-42
• /
• 1997

This study was carried out to track the heated-air flows within the tree disk through measuring the distribution of wood temperatures during explosing the 7.5mm-thick Japanese cedar disk and to investigate the effects of the time for the first explosion cycle and the number of explosion cycles on the improvement of permeability of tree disk. If the tree disk are explosed when the temperatures of the shell and core of it are not equilibrium yet, all of the inflated airs in the shell after explosion don't flow out toward the autoclave and some of them flow into the core of which the air pressures are lower than those of the shell. It is very effective for the improvement of permeability of tree disk to make the first explosion cycle when the temperatures of the shell and the core equilibrate at the setting temperature of steam in the autoclave. The more tree disks were explosed under the same conditions of first explosion, the more their permeabilities were improved.

• Restorative Dentistry and Endodontics
• /
• v.33 no.1
• /
• pp.54-65
• /
• 2008

The purpose of this study was to determine the effect of sodium hypochlorite and steam autoclaving on the cyclic fatigue of nickel-titanium endodontic files. Two types of files with a .06 taper and #30 were used, $K3^{(R)}$ (SybronEndo, Glendora, California, USA) and Hero $642^{(R)}$(Micro-Mega, BesanCon, France). The files were divided into 6 experimental groups containing 10 files each group depending the soaking time in 6% sodium hypochlorite solution and number of cycles of steam autoclave. After sterilization, a cyclic fatigue test was performed on each file, and the fracture time was recorded in seconds. The control group underwent the cyclic fatigue test only. After the test, the surface characteristics of the files were observed using scanning electron microscopy (SEM). All groups containing the Hero 64~ files showed a similar cyclic fatigue fracture time. However, the cyclic fatigue fracture time with the $K3^{(R)}$ files was significantly shorter in groups which were treated with sodium hypochlorite than in the control group (P < 0.05), SEM revealed both Hero $642^{(R)}$ and $K3^{(R)}$ files to have significant corrosion on the file surface in groups treated with sodium hypochlorite, compared with the sharp and regular blades of the control group. $K3^{(R)}$ files showed more corrosion than the Hero $642^{(R)}$ files. Bluntness of the blades of the $K3^{(R)}$ file was observed in groups treated with steam autoclave. Although there was no obvious destruction on the surface of steam autoclaved Hero $642^{(R)}$ files, slight bluntness was observed. Sterilizing with a steam autoclave is much less destructive to $K3^{(R)}$ files than sodium hypochlorite. The longer time exposed to sodium hypochlorite, the more destructive pattern was shown on the blades of the files. Therefore, when using sodium hypochlorite solution, the exposure time should be as short as possible in order to prevent corrosion and increase the cyclic fatigue fracture time.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.1 no.1
• /
• pp.9-19
• /
• 1981

Using superplasticizer or the methods of autoclave curing is the most typical and practical of the ways to make high strength concrete. In this study the high strength concrete piles by way of centrifugal forming and hand compacting, are put to the freezing and thawing test after the process of autoclave curing, water curing after steam curing, or stand water curing. And the relation of such piles to durability, the rate of strength decrease, and the rate of weight variation is shown. The durability of those test piles throughout freezing and thawing test proves to be comparatively sufficient in the above-mentioned curings when the piles contain a proper quantity of air. But it is also acknowledged that without A.E agent, the high strength concrete piles of autoclave curing is higher than those of the other curing in strength, but lower in modulus of dynamic elasticity and their durability factor after the test is much lower.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.2
• /
• pp.9-18
• /
• 2004

This study was carried out to find the efficient methods for preventing resin exudation from spruce board during high temperature environment service.In the dry-air oven test, in-use temperature related to resin exudation of 110℃ could be obtained by the appropriate kiln drying without any special treatment, and the in-use temperature of the radio-frequency/vacuum (RF/V)-dried boards was about 20℃ higher than that of the conventional kiln-dried boards.In the autoclave test, resin exudation was not found from any board dried in the conventional kiln and in the RF/V kiln after the low pressure steam explosion (SE) treating, while for the control resin exudations were more severe in the autoclave test above 130℃ than in the dry-air oven test. It, therefore, would be suggested that resin exudation during high temperature service condition can be prevented more effectively by super-heated steaming green boards than by high-temperature drying boards with low moisture.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.137-142
• /
• 1997

From the results of study on the electrical characteristics of heat-generation mortar used graphite as fine aggregates is summerized as following. The primary purpose of this study is the mixing ratio of graphite (35%, 50%/Sg), curing conditions (autoclave, steam, surface, underwater) and shape change (length, section of the electric heat-generation mortar). In case of the test condition with the steam curing condition appearance to most excellent heat-generation reproducibility. And temperature a coefficient of electric heat-generation mortar change from is in inverse proportion to the temperature a coefficient of direct proportion as the ratio of graphite mixing increased.