• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.108-111
• /
• 2000

Bi2212 and Bi2223 thin films are fabricated by ion beam sputtering method. Three phases of Bi2201, Bi2212 and Bi2223 appear as stable ones in spite of the condition for thin film fabrication of Bi2212 and bi2223 compositions, depending on substrate temperature(T$\sub$sub/) and ozone pressure (PO$_3$). It is found out that these phases show similar T$\sub$sub/ and PO$_3$dependence, and that the stable regions of these phases are limited within very narrow temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.725-728
• /
• 2001

We have fabricated thin films using the DC/RF magnetron sputtering of 74wt%Ni-l8wt%Cr-4wt%Al-4wt%Cu alloy target and studied the effect of the process parameters on the electrical properties for low TCR(Temperature Coefficient of Resistance) films. In sputtering process, pressure, power and substrate temperature, are varied as controllable parameter. The films are annealed to 400$^{\circ}C$ in air and nitrogen atmosphere. The sheet resistance, TCR of the films increases with increasing annealing temperature. It abruptly increased as annealing temperature increased over 300$^{\circ}C$ in air atmosphere. From XRD, it is found that these results are due to the existence of NiO on film surface formed by annealing. As a results of them, TCR can be controlled by variation of sputter process parameter and annealing of thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.62-65
• /
• 1997

Indium nitride thin films were deposited on Si(100) substrates by reactive sputtering method. The metallic indium target was sputtered by nitrogen gas with rf sputtering equipment. The surface morphology and cross-section of the InN thin films were investigated by scanning electron microscopy. The crystal orientations were investigated by X-ray diffraction and the Hall effect were measured with van der Pauw method. The indium nitride thin film showed high Hall mobility(215$\textrm{cm}^2$/V-sec) at 5mTorr total pressure and rf power 60W.

• The Korean Journal of Ceramics
• /
• v.3 no.4
• /
• pp.257-262
• /
• 1997

Aluminum nitride(AIN) thin films were deposited on SiO$_2$/Si substrates by reactive sputtering for the application of SAW devices. The major deposition parameters such as pressure, nitrogen fraction, rf power, substrate distance were changed to find out the optimal condition for c-axis oriented thin films on an amorphous substrate. The effects of deposition parameters on the crystal structure, residual stress, and growth morphology of thin films were characterized by XRD, SEM, and TEM. The FWHM of (002) rocking curve of the films deposited at the proper condition was lower than 2.2$^{\circ}$(C=0.93$^{\circ}$). Cross-sectional TEM showed that self-aligned structure was developed just after slightly random growth at the initial stage. The frequency characteristics of test device fabricated from AIN thin films confirmed their piezoelectric property and applicability for SAW devices.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.6
• /
• pp.266-270
• /
• 2010

The effect of an Ar plasma treatment on polycarbonate substrates was investigated using $TiO_2$ coatings produced by reactive ion-beam assisted sputtering. The typical pressure used during sputtering was about $10^{-4}$ Torr. After the Ar plasma treatment, the contact angle of a water droplet was reduced from $88^{\circ}$ to $52^{\circ}$ and then further decreased to $12^{\circ}$ with the addition of oxygen into the chamber. The surface of the polycarbonate substrate hanged from hydrophobic to hydrophilic with these treatments and revealed its changing nano-scale roughness. The $TiO_2$ films on the treated surface showed various colors and periodic ordering dependant on the film thickness due to optical interference.

• Proceedings of the KIEE Conference
• /
• 1993.11a
• /
• pp.258-260
• /
• 1993

Aluminum thin films were deposited on glass substrate using DC Magnetron Sputtering. Deposition rate, specular reflectance, and resistivity were investigated as a function of the input power, pressure, substrate temperature, and deposition time. Reflectance was reduced with increasing power, also with prolonging deposition time. Topography of the surface, which influences the properties such as electromigration, was observed from scanning electron microscope (SEM) and there was a close relation between the topography and measured reflectance.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.329.1-329.1
• /
• 2014

In this paper, we report electrical, optical and structural properties of Al-doped zinc oxide (AZO) thin films deposited at different substrate temperatures and pressures. The films were prepared by radio frequency (RF) magnetron sputtering on glass substrates in argon (Ar) ambient. The X-ray diffraction analysis showed that the AZO films deposited at room temperature (RT) and 20 Pa were mostly oriented along a-axis with preferred orientation along (100) direction. There was an improvement in resistivity ($3.7{\times}10^{-3}{\Omega}-cm$) transmittance (95%) at constant substrate temperature (RT) and working pressure (20 Pa) using the Hall-effect measurement system and UV-vis spectroscopy, respectively. Our results have promising applications in low-cost transparent electronics, such as the thin-film solar cells and thin-film transistors due to favourable deposition conditions. Furthermore our film deposition method offers a procedure for preparing highly oriented (100) AZO films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.193-197
• /
• 1996

BaTiO$_3$films in pure Ar atmosphere were prepared by RF sputtering method at low substrate temperature(100$^{\circ}C$). The structural and crystallographic properties were studied with deposition conditions and annealing methodes. Deposition rates and structural properties of BaTiO$_3$ thin filles were investigated by the SEM and X-ray diffraction. The chemical composition of BaTiO$_3$ thin films grown on Si(100) wafer was studied by tole EDS and EPHA. The optimised Ar pressure and RF power were 8[mtorr] and 180[W], respectively. The thickness of BaTiO$_3$ thin films deposited at optimised conditions was ∼3400[${\AA}$], and the dielectric constant of the thin films heat-treated at 750[$^{\circ}C$] for 1[hr] was 259.

• Journal of Sensor Science and Technology
• /
• v.15 no.1
• /
• pp.71-75
• /
• 2006

ITO (Indium Tin Oxide) thin films have been fabricated by rf magnetron sputtering with a target of a mixture $In_{2}O_{3]$(90 wt%) and $SnO_{2}$ (10 wt%). ITO films were sputtered with substrate temperature from 30 to $300^{\circ}C$ and working pressure from 1 to under 0.1 m Torr. ITO thin films surface morphology and electrical properties analyzed by SEM Photographs, and X-ray diffractions patterns. The resistivity of ITO thin films was $1.8{\times}10^{-5}{\Omega}/cm$.

• The Korean Journal of Ceramics
• /
• v.4 no.4
• /
• pp.372-376
• /
• 1998

Using calcium-phosphate-powder targets with the Ca/P ratios of 1.0-1.67, hydroxyapatite ($Ca_{10}(PO_4)_6(OH)_2$, HAp) thin films with 4-7㎛ thickness were prepared on titanium metal plates by r.f. magnetron sputtering, followed an annealing at $200^{\circ}C$ for 24 hr under a high water vapor pressure using an autoclave. All the specimens were systematically characterized by XRD, FT-IR, SEM and EDS analyses. The post-annealed films were confirmed to be a nonstoichiometric oxyhydroxyapatite by XRD and FT-IR measurements.