• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.151-152
• /
• 2002

An oxidized surface layer was intentionally formed on a sputtered $MoS_2$ film by introducing oxygen gas in the final stage of sputtering process. The film showed longer life than the normal Ar-sputtered film when the surface layer was slightly oxidized. A XPS analysis revealed co-existence of $MoS_2$ and $MoO_3$ in the surface layer. suggesting that the existence of some amount of oxides in the surface layer had beneficial effect. A confusing result was obtained: the life was much shorter than normal Ar-sputtered film when the film was exposed to $O_2$ environment for 1 minute after normal Ar-sputtering, although almost no oxide was detected in XPS analysis.

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.2
• /
• pp.93-96
• /
• 2017

The structural, electrical and optical properties of Ti thin films fabricated by dual magnetron sputtering were investigated under various film thicknesses. The fabricated Ti thin films exhibited uniform surfaces, crystallinity, various grain sizes, and with various film thicknesses. Also, the crystallinity and grain size of the Ti thin films increased with the increase of film thickness. The electrical properties of Ti thin films improved with the increase of film thickness. The results showed that the performance of TCO-less DSSC critically depended on the film thickness of the Ti working electrodes, due to the conductivity of Ti thin film. However, the maximum conversion efficiency of TCO-less DSSC was exhibited at the condition of 100 nm thickness due to the surface scattering of photons caused by the variation of grain size.

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.1049-1052
• /
• 2003

This study shows the change of the structural characteristic of AIN thin film deposition with the change of the deposition conditions such as Ar/$N_2$ gas ratio, operating pressure in chamber, and the distance between substrate and target in RF Magnetron Sputtering. The orientation and surface roughness of AIN thin film are studied by using XRD and AFM and the thickness is measured by using STYLUS PROFILER. While we can not identify the orientation of the thin film deposited in Ar only, we can obtain the (100) orientation of the thin film with the addition of $N_2$ to Ar. Especially the thin film deposited at 10% of Ar/$N_2$ gas ratio appears to be the most (100) oriented. The (100) orientation of thin film becomes weaker as the operating pressure becomes higher. The further distance between substrate and target is stronger the (100) orientation of the thin film is. The (100) orientation becomes weaker and (002) orientation starts to appear as the distance is shorter.

• Korean Journal of Metals and Materials
• /
• v.49 no.2
• /
• pp.192-196
• /
• 2011

The multi-layered thin film with an ITO/Ag/ITO structure was produced on PET by using magnetron reactive sputtering method. First, 30 nm of ITO thin film was coated on PET by using normal temperature process. Then 20-52 nm of the Ag thin film was coated. Lastly, 30 nm of ITO thin film was coated on Ag layer. The sample of the 20 nm Ag thin film showed more than 70% transmission and a $2.7{\Omega}/{\Box}$ sheet resistance. When compared to the existing single-layered transparent conducting thin film, multi-layered film was found to be superior with about $5{\Omega}/{\Box}$ less sheet resistance. However, since the Ag layer became thinner, the band gap energy needs to be increased to more than 3.5 eV.

• Korean Journal of Materials Research
• /
• v.13 no.3
• /
• pp.185-190
• /
• 2003

Titanium dioxide films were prepared by RF sputtering method on glass for various oxygen partial pressures at power 270 W. The crystal structure, photocatalytic property and the hydrophilicity of $TiO_2$thin film the deposition conditions were investigated. Crystallized anatase phase was observed in $TiO_2$film deposited at the ratio of oxygen partial pressure 10% and 20% for 2 hrs. As the increase of deposition time, the grain size and void size of $TiO_2$film have increased and also $V_2$films have been good crystallinity. The ultraviolet-visible light absorption of $TiO_2$films was increased with increasing of deposition time and occured chiefly at the wavelength between 280 and 340 nm. The absorption band was shifted to a longer wave length as deposition time increased. Water contact angle on the X$TiO_2$film of anatase structure was decreased with increasing ultraviolet illumination time and became lower than $11^{\circ}$ from $83^{\circ}$. When hydrophilic $TiO_2$film changed by enough ultraviolet illumination was stored in the dark, the film surface gradually turned to hydrophobic state.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.10 no.12
• /
• pp.2251-2257
• /
• 2006

We fabricated ZnO thin film successfully by using RF magnetron sputtering and investigated its potential for being utilized as the key material of piezoelectric device with the characterization of ZnO thin film such as such as crystallinity, surface morphology, c-axis orientation, film density. In thin study, $Ar/O_2$ gas ratio is fixed 70/30, RF power 125W, working pressure 8mTorr, distance between substrate and target 70mm, but the substrate temperature is varied from room temperature to $400^{\circ}C$. The relative intensity ($I_{(002)}/I_{(100)}$) or (002) peak in ZnO thin film deposited at $300^{\circ}$ was exhibited as 94%, then its FWHM was $0.571^{\circ}C$. Also, from the surface morphology evaluated by SEM and AFM, the film deposited at $300^{\circ}C$ showed uniform particle shape and excellent surface roughness of 4.08 m. The tendency of ZnO thin film density was exhibited to be denser with increasing substrate temperature but slightly decreased at near $400^{\circ}C$.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.4
• /
• pp.261-265
• /
• 2003

The heat treatment process of thin film microbatteries manufacturing processes has several Problems. This study, without heat treatment, considered the characteristics of $LiCoO_2$ thin films deposited by bais sputtering method inducing the structural change of the thin film. The properties of deposited $LiCoO_2$ thin films such as crystal structure, morphology, and discharge capacity were observed by various analysis methods. Among $LiCoO_2$ thin films deposited by substrate bias $voltage(V_b)$, the one deposited by substrate bias voltage of -50V had the highest initial discharge capacity of about $60{\mu}Ah/cm^2{\mu}m.$ We confirmed that $LiCoO_2$ thin film could be used as cathode material of lithium thin film microbatteries without annealing.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.11a
• /
• pp.171-177
• /
• 2001

The adhesion enhancement from inserting a RF bias-sputtered Cr layer between Cu and polyimide (PI) has been studied. The RF bias power applied in this study was ranged from 0 to 400 W. Without the RF bias, the peel strength, which measures the adhesion strength, was nearly o g/mm. As the RF power was increased, the peel strength rose up to ~130 g/mm at 200 W, which remained constant with further increase of the RF bias power. Cross-sectional transmission electron microscopy(TEM) was used to investigate the interfacial reaction between the Cr film and PI substrate during the bias sputtering. The Cr/PI interface without the application of RF dais showed a clean, sharp interface while the RF raised Cr/PI interface had about 10~30 nm thick atomistically mixed interlayer between the metal film and PI substrate. This interlayer appeared to have resulted from the implantation of high energy adatoms during the RF bias sputtering of Cr film. This mixed layer serves as an interlocking layer, which enhances adhesion between the metal and PI layers.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.32.1-32.1
• /
• 2011

Ultra thin tantalum nitride (TaNx) films with various thicknesses (10 nm to 40 nm) have been deposited by rf magnetron sputtering technique on glass substrates. The as deposited films were systematically characterized by several analytical techniques such as X-ray diffraction, X-ray photoelectron spectroscopy, field emission scanning electron microscopy, atomic force microscopy, UV-Vis-NIR double beam spectrophotometer and four point probe method. From the XRD results, the as deposited films are in amorphous nature, irrespective of the film thicknesses. The films composition was changed greatly with increasing the film thickness. SEM micrographs exhibited the densely pack microstructure, and homogeneous surface covered by small size grains at lower thickness deposited films. The surface roughness of the films was linearly increases with increasing the films thickness, consequently the transmittance decreased. The absorption edge was shifted towards higher wavelength as the film thickness increases.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.725-728
• /
• 2001

We have fabricated thin films using the DC/RF magnetron sputtering of 74wt%Ni-l8wt%Cr-4wt%Al-4wt%Cu alloy target and studied the effect of the process parameters on the electrical properties for low TCR(Temperature Coefficient of Resistance) films. In sputtering process, pressure, power and substrate temperature, are varied as controllable parameter. The films are annealed to 400$^{\circ}C$ in air and nitrogen atmosphere. The sheet resistance, TCR of the films increases with increasing annealing temperature. It abruptly increased as annealing temperature increased over 300$^{\circ}C$ in air atmosphere. From XRD, it is found that these results are due to the existence of NiO on film surface formed by annealing. As a results of them, TCR can be controlled by variation of sputter process parameter and annealing of thin film.