• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.387-392
• /
• 2005

For the production of further functional bio-degradable plastic(polybutylene succinate:PBS) with $TiO_{2}$ as photocatalyst, which shows the decomposition of detrimental organic compound and pollutant under ultraviolet irradiation, we attempted to prepare $TiO_{2}$ coatings on PBS substrate by HVOF and plasma spraying techniques under various conditions. The microstructures of coatings were characterized with SEM and XRD analysis, and the photocatalytic efficiency of coatings was evaluated through the photo degradation of gaseous acetaldehyde. The effects of primary particle size and spraying parameters on the formation behavior, photo catalytic performance and mechanical characteristics of the coatings have been investigated. The results indicated that with respect to both the HVOF sprayed $P_{200}$ and $P_{30}$ coatings, the high anatase ratio off 100% can be achieved regardless of fuel gas pressure. On the other hand, the HVOF sprayed $P_{7}$ coating exhibited largely decreased anatase ratio (from 100% to 49.1%) with increasing the fuel gas pressure, which may be attributed to the much higher susceptibility to heat of 7nm agglomerated powder. In terms of photocatalytic efficiency, HVOF sprayed $P_{200}$ and $P_{30}$ coatings seem to predominate as compared to that of plasma sprayed $P_{200}$ coatings owing to the higher anatase ratio. However, the HVOF sprayed $P_{7}$ coatings didn't show the photo catalytic activity, which may result from the extremely small reaction surface area to the photo-catalytic activity and low anatase ratio. Such functional PBS with new roles is expected to cosiderably contribute to the reduction of aggravated environmel problem.

• Journal of Welding and Joining
• /
• 제17권6호
• /
• pp.62-69
• /
• 1999

The advantages of Thermal sprayed coatings as a replacement for cast iron liners are reduced weight, better heat transfer and reduced cost. One of the most important performance attributes of a cylinder bore coating is its wear resistance, since it must survive the abrasive sliding of both the piston rings and the piston skirt. In this study, composite powders were prepared by ball milling of Al-13Si-3Mg(wt%) alloy with SiC particles. The concentrations of SiC were 40 and 60wt%. The composite powders were sprayed using Metco-9MB plasma torch. Plasma sprayed coatings were heat-treated at 500℃ for 3 hours. The wear resistances of the plasma sprayed coatings were found to improve with heat treatment and superior to the commercially available G.C.I.(gray cast iron). AlSiMg-40SiC heat-treated coatings showed the best wear resistance in this study.

• Journal of Welding and Joining
• /
• 제20권1호
• /
• pp.76-82
• /
• 2002

In these days, many advanced nations have enforced import restrictions against things emitting electromagnetic wave which has report that it is so harmful. In general, electromagnetic wave is composed of electric wave and magnetic wave. The reflection of electromagnetic wave is mainly reflected by conductive materials and the magnetism loss is generated by magnetic ferrite. The magnetism loss of ferrite is separated by eddy current loss, residual magnetism loss and hysteresis loss. Thermal sprayed coating is intended to manufacture because of simple processes and high efficient electromagnetic wave shielding. The high efficient thermal sprayed coatings were made from the magnetic ferrite materials that characterizes absorption of electromagnetic wave, and the electric conductive materials that characterize emitting of electromagnetic wave. This study was manufactured thermal sprayed coatings to improve absorption-efficiency, and measured the electromagnetic wave shielding efficiency. As the experimental results, high electromagnetic wave shield efficiency was obtained at wave frequency 2GHz to thermal sprayed ferrite coatings manufactured by size distribution range of spray powders, $38~88\mu\textrm{m}$.

• 한국건축시공학회지
• /
• 제21권6호
• /
• pp.519-527
• /
• 2021

본 연구에서는 기존의 전자기파 차폐 성능이 없는 콘크리트를 대상으로 아크 금속용사 공법을 적용하여 전자기파 차폐성능을 확보하고자 한다. 이를 위해 금속 코팅의 두께에 전기적 특성을 평가하기 위해서 8 종류의(Cu, CuAl, CuNi, CuZn, Al, Zn, ZnAl, AlMg) 금속들을 두께 100, 200 및 500㎛의 금속 코팅으로 제작하여 4pin-probe로 표면에서의 전기전도도를 측정하였고, KS C 0304에 의거하여 전자기파 차폐 성능 시험을 실시하였다. 금속 코팅 시험 결과를 토대로 전자기파 차폐를 위한 최적의 금속 코팅 두께 200㎛를 제안하였으며, 이를 300×300×100mm 콘크리트 시험체에 용사하여 전자기파 차폐 성능을 분석한 결과 목표 성능 1GHz에서 80dB의 전자기파 차폐 성능이 확보됨을 확인하였다. 하지만 부착 강도의 경우 최대 1.11MPa로 목표 성능 대비 74% 이하로 확인되어 추후 콘크리트 표면에 미세한 요철을 형성하여 부착 성능을 향상시키는 연구가 필요할 것으로 판단된다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1999년도 추계학술발표강연 및 논문개요집
• /
• pp.125-125
• /
• 1999

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1998년도 특별강연 및 추계학술발표 개요집
• /
• pp.253-256
• /
• 1998

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1997년도 특별강연 및 추계학술발표 개요집
• /
• pp.116-118
• /
• 1997

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1994년도 특별강연 및 춘계학술발표 개요집
• /
• pp.167-170
• /
• 1994

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2000년도 추계학술발표회 초록집
• /
• pp.20-21
• /
• 2000

• 한국분말재료학회지
• /
• 제18권3호
• /
• pp.226-237
• /
• 2011

W-ZrC and W-HfC composite powders were fabricated by the Plasma Alloying & Spheroidization (PAS) method and the powders were sprayed into hybrid coating layers by using Low Vacuum Plasma Spray (LVPS) process, respectively. Microstructure, mechanical properties, and ablation characteristics of the fabricated coating layers were investigated. The LVPS process led to successful production of W-Carbide hybrid coatings, approximately 400 ${\mu}M$ or above in thickness. As the substrate preheating temperature increased from $870^{\circ}C$ to $917^{\circ}C$, the hardness of the W-ZrC coating layer increased due to decreased porosity. Vickers hardness showed higher value (about 108.4 HV) in W-ZrC hybrid coating material compared to that of W-HfC while adhesive strength was found to be similar in both coating layers. The plasma torch test revealed good ablation resistance of the W-Carbide hybrid coating layers. The relatively high performance W-ZrC coating layer at the elevated temperature is thought to be attributed to both the strengthening effect of ZrC particle remained in the layer and the formation of ZrO2 phase with high temperature stability.