• Resources Recycling
• /
• v.21 no.6
• /
• pp.65-73
• /
• 2012

Selective catalytic reduction(SCR) catalysts are obtained from de-NOx system of thermoelectric power plant. A process was developed for valuable metals such as vanadium and tungsten recovery from spent SCR catalyst by using soda roasting followed by water leaching. Spent SCR catalyst having $V_2O_5$(1.23 mass %) and $WO_3$(7.73 mass %). For getting soluble metal forms of the targeted metals like vanadium and tungsten soda roasting process was implemented. In soda roasting process, sodium carbonate added 5 equivalent ratio at roasted temperature $850^{\circ}C$ with 120 min roasted time for $544{\mu}m$ particle size of spent SCR catalyst. After soda roasting process moved to water leaching for roasted spent catalyst. Before leaching process the roasted spent catalyst was grinded up to $-45{\mu}m$ size. The leaching time is 30 min at $40^{\circ}C$ temperature, 10 % pulp density. The final leaching efficiency obtained 46 % of vanadium and 92 % of tungsten from present process.

• Resources Recycling
• /
• v.29 no.5
• /
• pp.48-54
• /
• 2020

Sulphuric acid (H₂SO₄) leaching and hydrolysis were experimented for the recovery of titanum dioxide (TiO₂) from the water-leached residue followed by soda-roasting spent SCR catalysts. Sulphuric acid leaching of Ti was carried out with leachate concentration (4~8 M) and the others were fixed (temp.: 70 ℃, leaching time: 3 hrs, slurry density: 100 g/L, stirring speed: 500 rpm). For recovering of Ti from the leaching solution, hydrolysis precipitation was conducted at 100 ℃ for 2 hours in various mixing ratio (leached solution:distilled water) of 1:9 to 5:5. The maximum leachability was reached to 95.2 % in 6 M H₂SO₄ leachate. on the other hand, the leachability of Si decreased dramatically 91.7 to 3.0 % with an increase of H₂SO₄ concentration. Hydrolysis precipitation of Ti was proceeded with leaching solution of 8 M H₂SO₄ with the lowest content of Si. The yield of precipitation increased proportionally with a dilution ratio of leaching solution. Moreover, it increased generally by adding 0.2 g TiO₂ as a precipitation seed to the diluted leaching solution. Ultimately, 99.8 % of TiO₂ can be recovered with the purity of 99.46 % from the 1:9 diluted solution.

• Resources Recycling
• /
• v.29 no.3
• /
• pp.61-74
• /
• 2020

This study was conducted to improve the recycling process of waste fluorescent lamp, and investigate the possibility of using the waste fluorescent lamp glass as a raw material for glass beads, the leaching method of rare earth from the waste phosphor powder, and the possibility of solvent extraction of rare earth from the rare earth leaching solution. The waste phosphor contained 28.9% yttrium oxide, 3.46% cerium oxide, 1.95% europium oxide, 1.76% terbium oxide, and 1.43% lanthanum oxide. As a result of the trial production of glass beads using waste fluorescent lamp glass, it was judged that the production yield and quality were excellent, so that waste fluorescent lamp glass could be used as a raw material for glass beads. The soda roasted waste phosphor was leached in water and thereby the aqueous solution was blown with CO₂ to drop the pH to about 7, Then, Al, Si and residual N₂CO₃ were dissolved, and NaAlCO₃(OH)₂ and SiO₂ were precipitated in the aqueous solution. In the solvent extraction of cyanex272-hydrochloric acid, cyanex272-sulfuric acid, D2EHPA-hydrochloric acid, D2EHPA-sulfuric acid, Ionquest290-hydrochloric acid, Ionquest290-sulfuric acid, p507-hydrochloric acid using xylene as a diluent, the extraction yield of Y, Eu, Ce, La, and Tb are close to 100%. However, in this conditions, the difference in extraction yield for each element, that is, selectivity is 16% or less.