• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.71.1-71.1
• /
• 2000

• 한국재료학회지
• /
• 제12권9호
• /
• pp.691-695
• /
• 2002

A low temperature anode-supported tubular solid oxide fuel cell was developed. The anode-supported tube was fabricated using extrusion process. Then the electrolyte layer and the cathode layer were coated onto the anode tube by slurry dipping process, subsequently. The anode tube and electrolyte were co-fired at $140^{\circ}C$, and the cathode was sintered at $1200^{\circ}C$. The thickness and gas permeability of the electrolyte depended on the number of coating and the slurry concentration. Anode-supported tube was satisfied with SOFC requirements, related to electrical conductivity, pore structure, and gas diffusion limitations. At operating temperature of $800^{\circ}C$, open circuit voltage of the cell with gastight and dense electrolyte layer was 1.1 V and the cell showed a good performance of 450 mW/$\textrm{cm}^2$.

• 전기화학회지
• /
• 제7권2호
• /
• pp.94-99
• /
• 2004

연료극 지지체 평관형 고체산화물 연료전지(SOFC)의 셀 전력밀도를 증가시키기 위하여 압출법에 의하여 제조하고 그 특성을 연구하였다. 연료극 지지체로써 Ni/YSZ($8mol\%$ yttria stabilized zirconia) cermet는 기공율 $50.6\%,\;0.23{\mu}m$의 기공크기를 나타내었다. 지지체에서의 Ni의 분포는 균일하였으며 전자전도 경로로써의 Ni의 연결성은 양호하였다. 지지체에 YSZ전해질과 복합 공기극층인 $LSM((La_{0.85}Sr_{0.15})_{0.9}MnO_3)/YSZ$ 복합층, LSM, LSCF $(La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_3)$층이 슬러리 디핑법에 의하여 코팅 및 소결된 연료극 지지체식 평관형 고체산화물 연료전지 단위전지의 성능은 $800^{\circ}C$에서 $300mW/cm^2(0.6V,\;500mA/cm^2)$의 성능을 나타내었다. 임피던스 분석에 의하여 평관형 셀의 전기화학적 분극저항을 평가하고 연료측의 가습에 따라 분극저항이 감소되어 성능이 향상됨을 알 수 있었다 슬러리 디핑법으로 LSM이 코팅된 SUS430 금속연결재를 $Ar+10\%\;H_2$에서 소결하였으며, $750^{\circ}C$에서 면저항의 측정할 결과, 초기에는 $148m{\Omega}cm^2$를 나타내었으며, 450시간 경과 후에 $43m{\Omega}cm^2$의 낮은 면저항을 유지하였다. 반면에 동일한 조건으로 LSM이 코팅된 Fecralloy는 높은 면저항을 나타내었다.

• 유체기계공업학회:학술대회논문집
• /
• 유체기계공업학회 2001년도 유체기계 연구개발 발표회 논문집
• /
• pp.373-380
• /
• 2001

Solid Oxide Fuel Cells (SOFCs) have received considerable attention because of the advantages of high effiiciency, low pollution, cogeneration application and excellent integration with simplified reformer In this paper, we reported development of anode-tubular SOFC by wet process. For making tubular cell, Ni-cermet YSZ anode tube was fabricated using extrusion process, and YSZ electrolyte layer and LSM-YSZ composite, LSM, LSCF cathode layer were coated onto the anode supported tube using slurry dipping process and sintered by co-firing process. By using this tubular cell, we fabricated single cell consisted of the various cathode layers and 4 cell stack with an effective area of $75 cm^2$ per single cell, and evaluated their performance characteristics.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 하계학술대회 논문집 D
• /
• pp.1547-1549
• /
• 1999

As a preliminary experiment for the development of anode-supported tubular cell with proper porosity, we have investigated the anode substrate and the electrolyte-coated anode tube. The anode substrate was manufactured as a function of carbon content in the range of 20 to 50 vol.%. As the caron content increased, the porosity of the anode substrate increased slightly and the carbon content with proper porosity was obtained at 30 vol.%. The anode tube was fabricated by extrusion process and the electrolyte layer was coated on the anode tube by slurry dipping process. The anode-supported tube was cofired successfully. Their sintered property and microstructure were examined and the porosity of the anode tube was 35%. From the gas permeation test, the anode tube was found to be porous enough for gas supply. On the other hand, the anode-supported tube with electrolyte layer indicated a very low gas permeation rate. This means that the coated electrolyte was dense. Based upon these experimental results. we will fabricate and test the anode-supported tubular cell.

• 한국세라믹학회지
• /
• 제29권8호
• /
• pp.601-608
• /
• 1992

We investigated the influence of several processes, including the preparation of slurry and preform and the heat-treatment of the preform, on the properties of composites to fabricate the carbon-fiber reinforced glass composites having good mechanical properties. Cerander was determined to be the best binder among Cerander, Rhoplex and Elvacite 2045 by the dipping test and the binder within a preform could be completely eliminatd by burning out the specimen under 10-6 Torr at 400$^{\circ}C$ for more than 1h. The fracture behavior of a composite was largely dependent on the uniformity of carbon-fiber distribution within the composite and the heat-treatment condition of the composite. The higher the glass content, the more difficult to obtain uniform distribution of carbon-fiber. As the hot-pressing temperature increased, the densification process of the composite and the formation of pore due to oxidation of carbon fiber occurred competitively. But, above 1000$^{\circ}C$ the latter played a predominant role. We could fabricated the densest 15 vol.% carbon-fiber-content glass composite having the highest toughness and flexural strength of 250 MPa by hot-pressing under 15 MPa at 900$^{\circ}C$ for 30 min.