• Korean Journal of Materials Research
• /
• v.17 no.11
• /
• pp.601-605
• /
• 2007

The tribological properties of acrylonitrile-butadiene rubber (NBR) filled with two kinds of carbon black filler were examined. Different types of Semi-Reinforcing Furnace (SRF), and High Abrasion Furnace (HAF) blacks were used as filler material to test the influence of carbon black particle size on the friction and wear of NBR. Results from tribological tests using a ball on disk method showed that the smaller HAF particles were more effective for reducing the wear of NBR during frictional sliding. The hardness, elastic modulus at 100% elongation, and elongation at break were measured to examine the correlation between the effects of carbon black on the mechanical and tribological properties of the NBR specimens. The wear tracks of the NBR specimens were observed with scanning electron microscopy (SEM). The wear tracks for NBR with different ratios of SRF and HAF showed clearly different abrasion patterns. Mechanisms for the friction and wear behavior of NBR with different sizes of carbon black filler were proposed using evidence from wear track observation, as well as the mechanical and tribological test results.

• Korean Journal of Materials Research
• /
• v.25 no.7
• /
• pp.322-329
• /
• 2015

The magnitude of wear should be at a minimum for numerous automobile and aeronautical components. In the current work, composites were prepared by varying the cenosphere content using the conventional stir casting method. A uniform distribution of particles was ensured with the help of scanning electron microscopy (SEM). Three major parameters were chosen from various factors that affect the wear. A wear test was conducted with a pin-on-disc apparatus; the controlling parameters were volume percentages of reinforcement of 5, 10, 15, and 20%, applied loads of 9.8, 29.42, and 49.03 N, and sliding speeds of 1.26, 2.51, and 3.77 m/s. The design of the experiments (DOE) was performed by varying the different influencing parameters using the full factorial method. An analysis of variance (ANOVA) was used to analyze the effects of the parameters on the wear rate. Using regression analysis, a response curve was obtained based on the experimental results. The parameters in the resulting curve were optimized using the Genetic Algorithm (GA). The GA results were compared with those of an alternate efficient algorithm called Neural Networks (NNs).

• Proceedings of the Korean Vacuum Society Conference
• /
• 1995.06a
• /
• pp.151-151
• /
• 1995

Nitrogen implantation process has been applied for improvement of wear resistance of Z Zircaloy-4 fuel cladding materials. Nitrogen was implanted at 120 ke V to a total do range of 1xHP ions/cm2 to 8xlO17 ions/cm2 at various temperatures of 298"C to 676"C. The m microstructure changes by nitrogen implantation were analyzed by using TEM, XRD 뻐d A AES, cmd then wear behavior was evaluated by ball-on-disc wear testings at various loads a and sliding velocity under unlubricated condition. Nitrogen implantation produced ZrNx nitride above 4.37x1017 ions!cm2 as well as heavy d dislocations, which enhanced microhardness of the implanted surface of up to 900 Hk from 2 200 Hk of unimplanted substrate. Hardness was also found to be increased with increasing i implantation temperature and enhanced up to OOOHk at 620 "C. the wear resistance was g greatly improved with increasing total ion do않 as well as implantation temperature. The effective enhancement of wear resistance at high dose and tem야ratures is believed d due to significant hardening associated with high degree of precipitation of Zr nitrides and g generation of prismatic dislocation I$\infty$ps.infty$ps.

• Korean Journal of Metals and Materials
• /
• v.50 no.2
• /
• pp.176-182
• /
• 2012

The main purpose of this study was to evaluate the endurance against Al alloy melts and wear resistance of an in-situ synthesized titanium matrix composite (TMC) sleeve for aluminum alloy die-casting. The conventional die-casting shot sleeve material was STD61 tool steel. TMCs have great thermal stability, wear and oxidation resistance. The in-situ reaction between Ti and $B_4C$ leads to two kinds of thermodynamically stable reinforcements, such as TiBw and TiCp. To evaluate the feasibility of the application to a TMCs diecasting shot sleeve, the interfacial reaction behavior was examined between Al alloys melts with TMCs and STD61 tool steel. The pin-on-disk type dry sliding wear test was also investigated for TMCs and STD61 tool steel.

• Tribology and Lubricants
• /
• v.38 no.4
• /
• pp.170-178
• /
• 2022

Mechanical surface treatment is an excellent approach widely used to modulate and improve the performance and service life of bearings, gears, and frictional joints. The main purpose of this study is to investigate and compare the effect of ultrasonic nanocrystal surface modification (UNSM) and wonder process craft (WPC) on the surface and tribological properties of SUJ2 bearing steel. The surface roughness and hardness of the untreated and treated (UNSM- and WPC-treated) specimens were measured and compared. Their tribological properties were evaluated using a micro-tribometer under grease-lubricated and dry conditions against itself. Surface hardness measurement results revealed that both the UNSM- and WPC-treated specimens had a higher hardness than that of the untreated specimen. The surface roughness of the untreated specimen was reduced after UNSM and WPC treatments. Abrasive wear mode was observed on the surface of the specimens worn under grease-lubricated conditions, while adhesive wear mode was found on the surface of the specimens worn in dry conditions. According to the tribological test results, the friction coefficient and wear rate of the untreated specimens were reduced by the application of both the UNSM and WPC treatments under grease-lubricated and dry conditions.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.17 no.5
• /
• pp.113-120
• /
• 2013

Graphite is commonly used as a solid lubricant leading to low friction coefficient and abrasion. In this study, wear behavior of sealing graphite(HK-6) at elevated temperature was evaluated. Reciprocating wear test was carried out as wear occurred graphite as a seal(HK-6) is positioned between the liner and driving shaft. Variables which are temperature, sliding speed and contact load are set. This study suggest optimized environment conditions through the wear properties of graphite.

• Tribology and Lubricants
• /
• v.38 no.3
• /
• pp.101-108
• /
• 2022

The structure and properties of tetrahedral amorphous carbon (ta-C) coatings depend on the main process parameters and bending angles of the magnetic field filter used in the filtered cathodic vacuum arc (FCVA). During the process, it is possible to effectively control the plasma flux of carbon ions incident on the substrate by controlling the arc discharge current, thereby influencing the mechanical properties of the coating film. Furthermore, we can control the size and amount of large particles mixed during carbon film formation while conforming with the bending angle of the mechanical filter mounted on the FCVA; therefore, it also influences the mechanical properties. In this study, we consider tribological characteristics for filtered bending angles of 45° and 90° as a function of arc discharge currents of 60 and 100 A, respectively. Experiment results indicate that the frictional behavior of the ta-C coating film is independent of the bending angle of the filter. However, its sliding wear behavior significantly changes according to the bending angle of the FCVA filter, unlike the effect of the discharge current. Further, upon changing the bending angle from 45° to 90°, abrasive wear gets accelerated, thereby changing the size and mixing amount of macro particles inside the coating film.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.325-332
• /
• 2003

The effect of extrusion temperature on the microstructure and mechanical properties was studied in gas atomized TEX>$Al_{81}Si_{19}$ alloy powders and their extruded bars using SEM, tensile testing and wear testing. The Si particle size of He-gas atomized powder was about 200-800 nm. Each microstructure of the extruded bars with extrusion temperature (400, 450 and 50$0^{\circ}C$) showed a homogeneous distribution of primary Si and eutectic Si particles embedded in the Al matrix and the particle size varied from 0.1 to 5.5 ${\mu}m$. With increasing extrusion temperature from 40$0^{\circ}C$ to 50$0^{\circ}C$, the ultimate tensile strength (UTS) decreased from 282 to 236 ㎫ at 300 K and the specific wear increased at all sliding speeds due to the coarse microstructure. The fracture behavior of failure in tension testing and wear testing was also studied. The UTS of extrudate at 40$0^{\circ}C$ higher than that of 50$0^{\circ}C$ because more fine Si particles in Al matrix of extrudate at 40$0^{\circ}C$ prevented crack to propagate.

• Tribology and Lubricants
• /
• v.27 no.6
• /
• pp.344-350
• /
• 2011

Friction and wear behavior of tungsten oxide nanorods (TONs) was investigated using friction force microscopy(FFM) employing colloidal probes instead of conventional sharp tips. Vertically well-ordered TONs with 40 nm diameter, 130 nm length and 100 nm pitch width were synthesized on an anodic aluminium oxide substrate using two step electrochemical anodizing processes. The colloidal probe (diameter 20 ${\mu}m$) attached at the free end of tipless cantilever was oscillated(scanned) against a stationary surface of vertically aligned TONs with various scan speeds (1.2 ${\mu}m/s$, 3.0 ${\mu}m/s$ and 6.0 ${\mu}m/s$) and sliding cycles (100, 200 and 400) under normal load of 800 nN. The friction force and wear depth decreased with the increase of the scan speed. Plastically deformed thin layers were formed and sparsely deposited on the worn nonorod surface. The lower wear rate of the TONs with the longer oscillating cycles was attributed to the decreased real contact pressure due to the increase of real contact area between the colloidal probe and the TONs.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.31-32
• /
• 2001

Recently, many of the current development in surface modification engineering are focused on multilayered coatings. Multilayered coatings have the potential to improve the tribological and corrosion properties of tools and components. By using cathodic arc deposition, $WC-Ti_{1-x}Al_xN$ multilayers were deposited on steel substrates. Wear tests of four multiplayer coatings were performed using a ball-on-disc configuration with a linear sliding speed of 0.1m/s, 5N load. The tests were carried out at room temperature in airby employing AISI 52100 steel ball ($H_v=848N$) of 11mm in diameter. Electrochemical tests were performed using the potentiodynamic and electrochemical impedance spectroscopy (EIS) measurements. The surface morphology and topography of the wear scars of tribo-element and the corroded specimen have been determined by using scanning electron spectroscopy (SEM). Also, wear mechanism was determined by using SEM coupled with EDS. Results have showed an improved wear resistance and corrosion resistance of the $WC-Ti_{1-x}Al_xN$ coatings.