• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.354-357
• /
• 2009

The effect of texture of an extruded OFHC Cu rod on its sliding wear has been explored. Disk specimens with three different orientations were machined from the Cu rod for the wear test; surfaces of the disk were perpendicular ($0^{\circ}$), inclined with a specific angle ($45^{\circ}$), and parallel ($90^{\circ}$) to the extrusion axis of the rod. The texture was analyzed using an X-ray goniometer by measuring {111}, {200}, and {220} pole figures of each specimen. The analyzed texture was correlated with wear-test results of the Cu specimen. Dry sliding wear tests were performed at room temperature using a pin-on-disk wear tester against an Al2O3 ball. Applied load, sliding distance, sliding speed were fixed as 20 N, 200 m, and 0.5 m/sec, respectively. The $45^{\circ}$-inclined (to the extrusion axis) disk specimen showed the lowest wear resistance with the least data scatters. It has been found that distribution of cube texture strongly influences wear rate of the extruded Cu rod.

• Tribology and Lubricants
• /
• 제17권5호
• /
• pp.380-385
• /
• 2001

In nuclear power steam generators, high flow rates can induce vibration of the tubes resulting in fretting wear damage due to contacts between the tubes and their supports. In this paper the fretting wear tests and the sliding wear tests were performed using the steam generator tube materials of Inconel 600 and 690 against STS 304. Sliding tests with the pin-on-disk type tribometer were done under various applied loads and sliding speeds at air environment. Fretting tests were done under various vibrating amplitudes and applied normal loads. From the results of sliding and fretting wear tests, the wear of Inconel 600 and 690 can be predictable using the work rate model. Depending on normal loads and vibrating amplitudes, distinctively different wear mechanisms and often drastically different wear rates can occur. It was found the results that the wear coefficients for Inconel 600 and 690 were 262.3$\times$10$\^$-15/Pa$\^$-1/ and 209.2$\times$10$\^$-15/Pa$\^$-1/, respectively. This study shows that Inconel 690 can provide much better wear resistance than Inconel 600 in air.

• 제어로봇시스템학회논문지
• /
• 제16권3호
• /
• pp.256-263
• /
• 2010

The paper proposes a sensorless speed control strategy for a PMSM (Permanent Magnet Synchronous Motor) based on a new SMO (Sliding Mode Observer), which substitutes a signum function with a sigmoid function. To apply robust sensorless control of PMSM against parameter fluctuations and disturbance, the high speed SMO is proposed, which estimates the rotor position and angular velocity from the back EMF. The low-pass filter and additional position compensation of the rotor are used to reduce the chattering problem commonly found in sliding mode observer with signum function, which becomes possible by applying the sigmoid function with the control of a switching function. Also the proposed sliding mode observer with the sigmoid function has better efficiency than the conventional sliding mode observer since it adjusts the observer gain by variable boundary layer and estimates the stator resistance. The stability of the proposed sliding mode observer is verified by the Lyapunov second method in determining the observer gain. The validity of the proposed high speed PMSM sensorless velocity control has been demonstrated by real experiments.

• 한국주조공학회지
• /
• 제20권6호
• /
• pp.377-385
• /
• 2000

Al matrix composites as the most promising MMCs can be expected to be excellent engineering materials in the nearest future. So as to improve material properties of composite, many manufacturing processes have been developed. Among them, squeeze casting process which offers fine microstructure and near-net-shape is one of the most successful MMCs manufacturing processes. But, in case of with subsieve size particles (under 44 ${\mu}m$), it is very difficult to homogeneously distribute particles in matrix of Al matrix composite by various casting processes, including squeeze casting used so far. Duplex process which was developed in previous study was used to distribute the particle of subsieve size more homogeneously in matrix of Al matrix composite. Microstructures, wear and heat resistance characterization of Al-Si-Cu-Mg-(Ni)/SiCp manufactured by duplex process were examined to clarify the effect of manufacturing conditions, particle size of reinforcement and alloying elements. Al matrix composites reinforced with SiCp(10 ${\mu}m$) have the lowest wear amount among composites reinforced with 3 ${\mu}m$, 5 ${\mu}m$ and 10 ${\mu}m$ SiCp. The wear amount of Al matrix composites with 10 wt.% SiCp(3, 5, 10 ${\mu}m$) was decreased according to the increase of the sliding speed because abrasive wear takes place at high sliding speed of 4m/s and worn debris with block type occurs at low sliding speed of 1m/s. As for heat resistance, it is made clear that remarkable heat resistance property can be obtained by addition of Ni element in Al matrix composites.

• 한국재료학회지
• /
• 제8권10호
• /
• pp.969-974
• /
• 1998

Fe 계 합금의 적층결함에너지를 감소시키는 거승로 알려진 vanadium이 Fe-20Cr-1.7C-1Si합금의 미세조직과 고온 마모저항성에 미치는 영향에 대하여 조사하였다. Fe-20Cr-1.7C-1Si-xV (x=0, 1, 3, 6, 10wt.%)조성에서 오스테나이트 기지상을 유지하면서 첨기될 수 있는 V의 최대 첨가량은 약 3wt.%이었으며 오스테나이트 기지상을 갖는 합금은 상온에서 낮은 적층결함에너지와 $\gamma->\alpha$ 변형유기 상변태에 의해 페라이트 합금보다 높은 마모저항성을 보인 것으로 생각된다.$225^{\circ}C$에서 $\alpha$ 생성량도 많은 것으로 보다 V은 Fe-20Cr-1.7C-1Si 합금의 온도에 따른 적층결함에너지 증가율를 억제하고 Md온도도 증가시킴으로써 고온 마모저항성을 증가시키는 것으로 생각된다.

• 열처리공학회지
• /
• 제16권3호
• /
• pp.134-140
• /
• 2003

Effects of cryogenic treatment and tempering temperature on the amount of retained austenite, hardness and wear properties has been investigated using alloy tool steel, STD 11. Cryogenic treatments were performed at the temperatures of $-100^{\circ}C$, $-150^{\circ}C$ and $-196^{\circ}C$, and tempering were performed at $200^{\circ}C$ and $530^{\circ}C$. It was shown that lower hardness value was obtained on high temperature ($530^{\circ}C$) tempering even after cryogenic treatment. And retained austenite was not entirely transformed to martensite after cryogenic treatment even at $-196^{\circ}C$, which was not consistent with the belief that $-80^{\circ}C$ was sufficient to entirely transform any austenite retained in the quenched microstructure. Austenite retained in cryogenic treated condition was completely transformed to martensite only after tempering at $530^{\circ}C$. As far as wear test conditions in this investigation, it was found that cryogenic treatments improved the sliding wear resistance, but improvement of wear resistance was not directly related with retained austenite contents. And it was found that predominent wear mechanisms of STD 11 steel were oxidation wear and adhesive wear In sliding wear conditions.

• 대한설비공학회:학술대회논문집
• /
• 대한설비공학회 2006년도 하계학술발표대회 논문집
• /
• pp.1075-1080
• /
• 2006

Purpose of this study is proposal of estimating method about window thermal performance that based on KS F 2278 'Test method of thermal resistance for windows and doors' due to material composition of PVC frame window. First step of this study is research of present state about material composition of PVC frame window. Second is selection of main effective elements about window thermal resistance. For example, composition of Glazing, Frame area ratio of total window area, frame width, opening type, area of heat transfer and so on. Third is multiple regression analysis about thermal performance of PVC frame window due to main effective elements. It produces equations of multiple regression analysis due to opening type. Case of sliding window is $Y=0.149+0.034X_g+0.248X_{far}$, 4track sliding is $Y=0.584+0.175X_g+1.355X_{far}-0.008X_{fw}$, Tilt & Turn window is $Y=-0.161+0.076X_g+0.576X_{far}+0.0008X_{fw}$.

• 한국철도학회논문집
• /
• 제15권3호
• /
• pp.237-243
• /
• 2012

3차원 유한요소법을 이용하여 엔드코일 효과를 고려한 SRM의 자계해석을 수행하였다. 고정자 극 형상에 따른 자계특성의 비교를 통하여 제안된 형상에서 자계특성이 향상됨을 확인하였다. 해석한 자계특성을 적용하여 철도부하에 대한 PI 제어기와 슬라이딩모드 제어기의 속도제어를 수행하였다. 속도 제어 시뮬레이션은 Matlab-Simulink를 사용하여 구현되었으며 부하 가변 조건에서 슬라이딩모드 제어기가 PI 제어기에 비해 더 우수한 과도응답 및 정상상태응답을 나타냄을 확인하였다.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 1996년도 한국자동제어학술회의논문집(국내학술편); 포항공과대학교, 포항; 24-26 Oct. 1996
• /
• pp.1253-1256
• /
• 1996

In this paper, a new nonlinear feedback linearization control scheme for induction motors is developed. The control scheme employs a fuzzy nonlinear identification scheme based on fuzzy basis function expansion to adoptively compensate the parameter variations, i.e. rotor resistance, mutual and self inductance etc. An important feature of the proposed control scheme is to incorporate the sliding mode controller into the scheme to speed up convergence rate. Simulation tests show the robust behavior of the proposed controller in the presence of the parameter uncertainties of the machine.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 2010년도 추계 학술발표회
• /
• pp.293-302
• /
• 2010

2 types of geogrids and geotextiles was used to evaluate shear behaviors after installation damage test. Shear behaviors were compared after installation damage test and coefficient of resistance to direct sliding($f_{ds}$) was estimated by theoretical shear analysis. Shear strength of damaged geogrid decreased under high normal stress of 150kPa and shear strength of geotextile decreased with increasing normal stress. It is seen that $f_{ds}$ values after installation damage decreased than before installation damage through comparison calculated $f_{ds}$ by direct theoretical shear analysis. $f_{ds}$ values to be calculated by theoretical shear analysis were changed with before and after installation damage.