• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1102-1107
• /
• 1999

SiC-Si3N4 composites were prepared by mixing $\alpha$-Si3N4 powder to $\alpha$-SiC powder in the range of 10 to 30 vol% with 10vol% interval. 6wg% Al2O3 and 6wt% Y2O3 were respectively added as sintering aids. Hot pressing was performed at 1,80$0^{\circ}C$ for 1 hour with 25 MPa pressure. In the case of adding 20vol% of $\alpha$-Si3N4 powder the relative density to theoretical value and the flexural strength were 99.1% and 34,420 MPa respectively and the worn amount was 2.09$\times$10-3 mm2 which were the highest values in the all range of he composition. Although the composite containig 10 vol% of $\alpha$-Si3N4 powder showed the highest fracture toughness(KIC) of 4.65MN/m3/2 the reduction of the wear resistance in this composite is likely to be affected by the homogeneity and the uniformity of the grain coalescence and growth during the sintering process.

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.89-96
• /
• 2003

The recent trend of miniaturization and high performance of vehicle engines has put an urgent necessity for the development of valve seats which can operate under more severe conditions. In order to develope valve seat material that has the most excellent wear resistance at operating temperature of engine through improvement of the progress of work. the effects of mixing ratio of the milled powder on sintered and Cu-infiltrated properties of sintered valve seats have been studied. The resultant radial crushing strength and hardness of sintered specimens were gradually increased with increasement of volume of milled powders. It is because increasement of sintering density by increasing of surface diffusion. The hardness of Cu-infiltrated specimens became lower than that of the commercial powders as the increasement of volume of milled powders. It was due to the decrease of the amount of the martensite. By results of this research, It has been found that martensite is formed around of the Cu-infiltrated site and the decrease of the amount of the martensite is due to decrease of the amount of the Cu-infiltrated site by the decrease of gas channel.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.9
• /
• pp.89-95
• /
• 2001

Ceramic tool has to equip with not only high toughness and strength but also low thermal expansion and good thermal conductivity which leads to the high thermal shock resistance. These characteristics make it have longer tool life under thermal stress condition. In this study, commercial Si$_3$N$_4$ceramic cutting tool and home-made SiC based ceramic cutting tools which have different sintering time and chemical composition are tested under various cutting speed and the feed rate increase, the cutting force and the flank wear growth ratio increase, too. The performance of home-made SiC based ceramic cutting tool shows the possibility to be a new ceramic tool.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.97-98
• /
• 2006

Gas-permeable metal die materials are developed using tool steel powder, packed in a mold having the insertion of orthogonally arrayed polymer wires. Linear gas-permeable channels in orthogonal array are thus developed by the burning out of the polymer wires, which yield a microstructure with wear resistance value and air permeability much larger than those of the conventional gas-permeable die material.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.6
• /
• pp.2612-2617
• /
• 2013

This study aims to develop hair cutter with zirconia($ZrO_2$) material whose machinability, corrosion resistance, wear resistance and bio-compatibility are excellent by comparing iron hair cutter. Ultra-thin zirconia cutter with the thickness of 0.253mm is manufactured through the optimization of design, molding, sintering, grinding and grinding process. With observation result of cutter specimen by use of scanning electron microscope(SEM), formability and process of cutting face are shown to be good. It is also evaluated with sufficient merchantability by cutting test results. The cutter process technology of thin zirconia can be utilized at the development of high value-added beauty appliances like razor, beauty-razor and eye brows-razor for woman by use of study result.

• Laser Solutions
• /
• v.12 no.4
• /
• pp.12-16
• /
• 2009

The engineering ceramic is one of the materials advantageous in various conditions with high strength, endurance at high temperature, abrasion resistance and corrosion resistance, etc. However, due to high strength and high brittleness, ceramic incurs high costs and long time on finishing process required after sintering. So a process for obtaining wanted measurements of them has been studied using the high temperature which makes ceramics softened and heat affected recently. This study makes an estimate of laser-assisted machining (LAM) if an economically practical process for manufacturing precision silicon nitride ceramic parts using laser beam. In this study, mechanical properties of silicon nitride at high temperature were observed. And during the LAM, it was observed that cutting force and tool wear were reduced and oxidation of machined surface was increased according to a increase of laser power.

• Journal of Powder Materials
• /
• v.24 no.3
• /
• pp.235-241
• /
• 2017

Titanium alloys have high specific strength, excellent corrosion and wear resistance, as well as high heat-resistant strength compared to conventional steel materials. As intermetallic compounds based on Ti, TiAl alloys are becoming increasingly popular in the aerospace field because these alloys have low density and high creep properties. In spite of those advantages, the low ductility at room temperature and difficult machining performance of TiAl and $Ti_3Al$ materials has limited their potential applications. Titanium powder can be used in such cases for weight and cost reduction. Herein, pre-forms of Ti-Al-xMn powder alloys are fabricated by compression forming. In this process, Ti powder is added to Al and Mn powders and compressed, and the resulting mixture is subjected to various sintering temperature and holding times. The density of the powder-sintered specimens is measured and evaluated by correlation with phase formation, Mn addition, Kirkendall void, etc. Strong Al-Mn reactions can restrain Kirkendall void formation in Ti-Al-xMn powder alloys and result in increased density of the powder alloys. The effect of Al-Mn reactions and microstructural changes as well as Mn addition on the high-temperature compression properties are also analyzed for the Ti-Al-xMn powder alloys.

• Journal of Powder Materials
• /
• v.18 no.3
• /
• pp.290-296
• /
• 2011

Titanium carbonitride is more perspective materials compared to titanium carbide. It can be used in tool industry and special products because of its higher strength, abrasive wear-resistance and especially its strong chemical stability at high temperatures. We produced STS+TiCxNy composite by the spark plasma sintering for higher strength and studied the characteristics. The planar and cross-sectional microstructures of the specimens were observed by scanning electron microscopy. Characterizations of the carbon and nitride phases on the surface of composite were carried out using an X-ray diffractometer. During annealing TiCxNy particles diffusion into STS 430 was observed. After annealing, sintering isolations between particles were formed. It causes decreasing of mechanical strength. In addition when annealing temperature was increased hardness increased. Heterogeneous distribution of alloying elements particles was observed. After annealing composites, highest value of hardness was 738.1 MHV.

• Journal of Powder Materials
• /
• v.29 no.5
• /
• pp.424-431
• /
• 2022

3Y-TZP ceramics obtained by doping 3 mol.% of Y₂O₃ to ZrO₂ to stabilize the phase transition are widely used in the engineering ceramic industry due to their excellent mechanical properties such as high strength, fracture toughness, and wear resistance. An additional increase in mechanical properties is possible by manufacturing a composite in which a high-hardness material such as oxide or carbide is added to the 3Y-TZP matrix. In this study, composite powder was prepared by dispersing a designated percentage of WC in the 3Y-TZP matrix, and the results were compared after manufacturing the composite using the different processes of spark plasma sintering and HP. The difference between the densification behavior and porosity with the process mechanism was investigated. The correlation between the process conditions and phase formation was examined based on the crystalline phase formation behavior. Changes to the microstructure according to the process conditions were compared using field-emission scanning electron microscopy. The toughness-strengthening mechanism of the composite with densification and phase formation was also investigated.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.721-725
• /
• 1998

In this study solid-phase sintered silicon caribide samples composed of SiC powder having boron and car-bon black as additives were prepared by pressureless sintering at $1950^{\circ}C$. The bending strength the frac-ture toughness and the specific werar rate of the samples were examined and the micro structures of the broken and the worn surface were observed by SEM to understand the relationship between the tri-bological charcteristics and the micro structure. Additionally the relationship between the micro struc-tures and the tribological characteristics of the samples for the frictional opponents SiC and $Al_{2}O_{3}$ pins were investigated Conclusions are as follows ; 1. The specific were rate of the samples for the SiC pin was larger than that for the $Al_{2}O_{3}$ pin. HOwever the specific wear rate for the $Al_{2}O_{3}$ pin was increased about 6,45 times as that for the SiC pin under the load increasing. 2. The specific wear rate of the SiC pin was larger than that of the $Al_{2}O_{3}$ pin. owever the specific wear rate of the $Al_{2}O_{3}$ pin was increased about 4 times as that of the SiC pin under the load increasing 3. The micro stucture of the worn surface showed a flat face without cracks in the case that the frictional opponents has the low friction coefficient but in the case of without cracks in the case that the frictional opponents has the low friction coefficient but in the case of the high friction coefficient the micro structure of the worn surface showed an uneven face having spread-ed cracks. 4. The tribological characteristics of thesolid-phase sintered SiC samples was similar to that of li-quid-phase sintered ones when the pin having the high friction coefficient was used.