• Journal of Sensor Science and Technology
• /
• v.17 no.6
• /
• pp.437-446
• /
• 2008

Single crystalline ${ZnIn_2}{Se_4}$ layers were grown on thoroughly etched semi-insulating GaAs (100) substrate at $400^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating ${ZnIn_2}{Se_4}$ source at $630^{\circ}C$. The crystalline structure of the single crystalline thick films was investigated by the photoluminescence (PL) and Double crystalline X-ray rocking curve (DCRC). The carrier density and mobility of ${ZnIn_2}{Se_4}$ single crystalline thick films measured from Hall effect by van der Pauw method are $9.41{\times}10^{16}cm^{-3}$ and $292cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the ${ZnIn_2}{Se_4}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)$=1.8622 eV-$(5.23{\times}10^{-4}eV/K)T^2$/(T+775.5 K). After the as-grown ${ZnIn_2}{Se_4}$ single crystalline thick films was annealed in Zn-, Se-, and In-atmospheres, the origin of point defects of ${ZnIn_2}{Se_4}$ single crystalline thick films has been investigated by the photoluminescence (PL) at 10 K. The native defects of $V_{Zn}$, $V_{Se}$, $Zn_{int}$, and $Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Se-atmosphere converted ${ZnIn_2}{Se_4}$ single crystalline thick films to an optical p-type. Also, we confirmed that In in ${ZnIn_2}{Se_4}$/GaAs did not form the native defects because In in ${ZnIn_2}{Se_4}$ single crystalline thick films existed in the form of stable bonds.

• Journal of Sensor Science and Technology
• /
• v.14 no.2
• /
• pp.131-135
• /
• 2005

This paper describes the ohmic contact formation of single crystalline 3C-SiC thin films heteroepitaxially grown on Si(001) wafers. In this work, a TiW (Titanium-tungsten) film as a contact matieral was deposited by RF magnetron sputter and annealed with the vacuum and RTA (rapid thermal anneal) process respectively. Contact resistivities between the TiW film and the n-type 3C-SiC substrate were measured by the C-TLM (circular transmission line model) method. The contact phases and interface the TiW/3C-SiC were evaulated with XRD (X-ray diffraction), SEM (scanning electron microscope) and AES (Auger electron spectroscopy) depth-profiles, respectively. The TiW film annealed at $1000^{\circ}C$ for 45 sec with the RTA play am important role in formation of ohmic contact with the 3C-SiC substrate and the contact resistance is less than $4.62{\times}10^{-4}{\Omega}{\cdot}cm^{2}$. Moreover, the inter-diffusion at TiW/3C-SiC interface was not generated during before and after annealing, and kept stable state. Therefore, the ohmic contact formation technology of single crystalline 3C-SiC using the TiW film is very suitable for high temperature MEMS applications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.259-259
• /
• 2015

Single crystalline indium-tin-oxide (ITO) nanowires (NWs) were grown by sputtering method. A thin Ni film of 5 nm was deposited before ITO sputtering. Thermal treatment forms Ni nanoparticles, which act as templates to diffuse Ni into the sputtered ITO layer to grow single crystalline ITO NWs. This Ni diffusion through an ITO NW was investigated by transmission electron microscope to observe the Ni-tip sitting on a single crystalline ITO NW. Meanwhile, a single crystalline ITO structure was found at bottom and body part of a single ITO NW without remaining of Ni atoms. This indicates the Ni atoms diffuse through the oxygen vacancies of ITO structure. Rapid thermal process (RTP) applied to generate an initial stage of a formation of Ni nanoparticles with variation in time periods to demonstrate the existence of an optimum condition to initiate ITO NW growth. Modulation in ITO sputtering condition was applied to verify the ITO NW growth or the ITO film growth. The Ni-assisted grown ITO layer has an improved electrical conductivity while maintaining a similar transmittance value to that of a single ITO layer. Electrically conductive and optically transparent nanowire-coated surface morphology would provide a great opportunity for various photoelectric devices.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.4
• /
• pp.533-537
• /
• 2007

This paper describes the heteroepitaxial growth of single-crystalline 3C-SiC (cubic silicon carbide) thin films on Si (100) wafers by atmospheric pressure chemical vapor deposition (APCVD) at 1350 oC for micro/nanoelectromechanical system (M/NEMS) applications, in which hexamethyldisilane (HMDS, Si2(CH3)6) was used as a safe organosilane single-source precursor. The HMDS flow rate was 0.5 sccm and the H2 carrier gas flow rate was 2.5 slm. The HMDS flow rate was important in obtaing a mirror-like crystalline surface. The growth rate of the 3C-SiC film in this work was 4.3 μm/h. A 3C-SiC epitaxial film grown on the Si (100) substrate was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), reflection high energy electron diffraction (RHEED), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and Raman scattering, respectively. These results show that the main chemical components of the grown film were single-crystalline 3C-SiC layers. The 3C-SiC film had a very good crystal quality without twins, defects or dislocations, and a very low residual stress.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.3
• /
• pp.281-286
• /
• 2002

In odder to investigate the magnetic properties of CoCr-based bilayered thin films on kind of underlayer, we introduced amorphous Si layer to Co-Cr(-Ta) magnetic layer as underlayer. First, we prepared CoCr and CoCrTa single layer using the Facing Targets Sputtering system to investigate theirs properties. It was revealed that with increasing the film thickness of CoCr, CoCrTa single layer, crystalline orientation and perpendicular coercivity was improved. The CoCrTa thin film showed bettor crystalline and magnetic characteristics than CoCr thin film. As a result of investigating magnetic properties of CoCr and CoCrTa magnetic layer on introducing the Si underlayer, perpendicular coercivity and saturation magnetization of CoCr/Si and CoCrTa/Si bilayered thin film were decreased due to the increased grain size and diffusion of Si atoms to magnetic layer. And they showed constant with increasing the film thickness of Si thin film. However, in case of CoCrTa/Si bilayered thin film, in-plane coercivity was controlled low at about 250Oe. The c-axis orientations of CoCr/si and CoCrTa/Si bilayered thin film showed a good crystalline characteristics as about $2^{\circ}$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.2
• /
• pp.98-102
• /
• 2010

This paper describes that single crystalline 3C-SiC (cubic silicon carbide) thin films have been deposited on carbonized Si(100) substrates using hexamethyldisilane (HMDS, $Si_2(CH_3){_6}$) as a safe organosilane single precursor and a nonflammable mixture of Ar and $H_2$ gas as the carrier gas by APCVD at $1280^{\circ}C$. The deposition was performed under various conditions to determine the optimized growth condition. The crystallinity of the 3C-SiC thin film was analyzed by XRD (X-ray diffraction). The surface morphology was also observed by AFM (atomic force microscopy) and voids between SiC and Si interfaces were measured by SEM (scanning electron microscopy). Finally, residual strain and hall mobility was investigated by surface profiler and hall measurement, respectively. From these results, the single crystalline 3C-SiC film had a good crystal quality without defects due to viods, a low residual stress, a very low roughness.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.219-219
• /
• 2010

Silicides have been commonly used in the Si technology due to the compatibility with Si. Recently the silicide has been applied in solar cells [1] and nanoscale interconnects [2]. The modulation of Ni silicide phase is an important issue to satisfy the needs. The excellent electric-conductive nickel monosilicide (NiSi) nanowire has proven the low resistive nanoscale interconnects. Otherwise the Ni disilicide (NiSi2) provides a template to grow a crystalline Si film above it by the little lattice mismatch of 0.4% between Si and NiSi2. We present the formation of Ni silicide phases performed by the single deposition and the co-deposition methods. The co-deposition of Ni and Si provides a stable Ni silicide phase at a reduced processing temperature comparing to the single deposition method. It also discusses the Schottky contact formation between the Ni silicide and the grown crystalline Si film for the solar cell application.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.6-9
• /
• 2008

We have investigated the MOD process successfully for the fabrication of the YBCO thick film on the $LaAlO_3$(001) single crystalline substrate. The cracking problem in YBCO thick film, a serious problem in the conventional TFA-MOD method, could be overcome with a careful control of precursor materials. Thus coating solution was prepared for the YBCO thick film by using fluorine-free precursor material. The precursor solutions were coated on the LAO(001) single crystalline substrate using the dip coating method, calcined at the temperature up to $500^{\circ}C$, and fired at various high temperatures for 2 h in a reduced oxygen atmosphere. Optimally processed YBCO thick film exhibited high critical current($I_c$) over 200 A/cm-width at 77K in self-field.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.120-121
• /
• 2009

Single crystalline $ZnIn_2Se_4$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $400^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating, $ZnIn_2Se_4$ source at $630^{\circ}C$. After the as-grown $ZnIn_2Se_4$ single crystalline thin films was annealed in Zn-, Se-, and In-atmospheres, the origin of point defects of $ZnIn_2Se_4$single crystalline thin films has been investigated by the photoluminescence(PL) at 10 K The native defects of $V_{Zn}$, $V_{Se}$, $Zn_{int}$ and $Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Se-atmosphere converted $ZnIn_2Se_4$ single crystalline thin films to an optical p-type. Also, we confirmed that In in $ZnIn_2Se_4$/GaAs did not form the native defects because In in $ZnIn_2Se_4$ single crystalline thin films existed in the form of stable bonds.

• Progress in Superconductivity
• /
• v.4 no.1
• /
• pp.14-18
• /
• 2002

We had succeeded to grow bulk sing1e crystals of La／sub 2-x／Sr／sub x／$CuO_4$by the traveling solvent floating zone method (TSFZ), and to prepare La／sub 2-x／Sr／sub x／CuO$_4$single-crystalline thick films on the Zn-doped La$_2$$CuO_4$ substrate by new liquid phase epitaxial technique using an infrared heating furnace (IR-LPE). In this paper, Ireview growth of bulk single crystals and single-crystalline thick films of La／sub 2-x／Sr／sub x／$CuO_4$, and discuss on their device properties to develop high speed integrated electronic devices.