• Textile Coloration and Finishing
• /
• v.23 no.3
• /
• pp.195-200
• /
• 2011

Silicone-coated fabric were treated by oxygen low temperature plasma to improve the adhesion. The surface of silicone-coated fabric was modified with gaseous plasma of several discharge power in the presence of oxygen gas at 1Torr pressure. Oxygen plasma treatment introduces oxygen-containing functional groups and micro-pittings on the silicone-coated fabric surface. The treated fabrics with oxygen low temperature plasma were measured by contact angle analyzer and XPS(X-ray photoelectron spectroscopy), and interfacial adhesion was measured by T-peel test. The surface of fabric was investigated by SEM photographs. The chemical and physical modification of the surface wettabillity by plasma treatment can increase the adhesion.

• Textile Coloration and Finishing
• /
• v.35 no.1
• /
• pp.8-19
• /
• 2023

Silicone rubber is widely used in most industries due to diverse advantages like heat stability, UV stability, durability, chemical resistance, environment friendliness, inertness and so on. But there is limitation to expand applications due to relatively weak rubber strengths such as tensile strength and tear strength, especially in fabric coating applications. The purpose of this study is to find influence of coating agent on performances of rubber and coated fabrics and their correlation according to different crosslinking densities of silicone rubbers. Addition cure type of silicones were formulated using crosslinked MQ-type silicone resin consisting of M (R₃SiO_1/2) and Q (SiO_4/2) and linear polymers. Raw materials used were; 1) linear vinyl endblocked polymers and vinyl functional MQ resin as main polymers, 2) linear silicone hydride polymers as crosslinkers, 3) platinum catalyst and 4) inhibitor to control curing speed. Rubber specimens were prepared to check mechanical strength using universal testing machine (UTM). Crosslinking density was calculated using Flory-Rhener equation using solvent swelling method. Differential scanning calorimetry (DSC) and scanning electron microscope (SEM-EDS) were used to characterize rubbers. Consequently, it was found that physical properties of silicone rubbers and coated fabrics can be expected by crosslinking density of rubbers. Silicone rubber formulations that contain 20 ~ 30 wt% of vinyl MQ resin showed strongest balanced performances.

• Proceedings of the KSR Conference
• /
• 2007.05a
• /
• pp.1511-1516
• /
• 2007

According to ISO 4589-2:2001, we studied on the fire characteristics of some gangway materials used as the interior materials of the railroad vehicles. Currently materials of the gangway used in the railroad vehicles tend to alternate PVC coated fabric mostly used in former days with synthetic rubber or silicone. Accordingly, we compared Limited Oxygen Index on them in this study. And we found that the test results of the synthetic rubber or silicone gangway are better than those of the PVC coated fabric gangway largely.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2012.03a
• /
• pp.106-106
• /
• 2012

막구조(Membrane structure)란 건축분야에서 "fabric structure" 또는 tension structure"와 같이 사용되는 용어로 코팅된 직물(coated fabrics)을 주재료로 사용하는 구조를 말한다. 특히 구조체로서 연성의 막을 이용 이것에 초기 장력을 주어 강성을 늘림으로서 외부하중에 대하여 안정된 형태를 유지하는 장점을 갖고 있다. 초기 창안된 독일의 온화한 기후에 적용되는 반면 한국이나 일본에는 60m/sec를 넘나드는 태풍의 피해와 많은 적설량을 보이는 기후적 제약으로 발달되지 못하였다. 그러나 최근 새로운 소재의 막구조 제품 개발과 구조해석 방법 및 시공기술 등이 개발되어 보편화되어지고 있는 실정이다. 막구조용 재료로 사용되는 섬유소재는 주로 Polyester직물을 기재로 한 PVC 코팅 제품으로 일반 PVC 막재는 장력이 약하고, 광선에 의한 물성이 쉽게 변화되어 내구연한이 5~15년에 불과하다. 유리섬유나 아라미드섬유 등으로 제직한 기재에 고내열 실리콘이나 PTFE 수지를 코팅한 제품은 약품에 대한 내구성이 높고 자외선에 대해서는 매우 큰 저항성을 가지기 때문에 내구연한이 10년에서 30년 까지도 향상된다. 그러나 실리콘 코팅막은 세계적으로 가장 좋은 막재로 알려졌으나 자정능력(Self Cleaning)에 문제가 발생되어 사용량이 감소 추세라고 할 수 있다. 일반적인 코팅 가공의 경우 MEK, Toluene, DMF 등과 같은 유기용제를 다량 사용함에 따라 작업환경 및 대기오염, 화재 위험 등의 문제점이 있으며 특히 가공시 잔류되는 유기용제의 심각성이 대두되고 있는 상황이다. 이와 같이 코팅 가공제 자체를 친환경적인 물질로 대체하여 각종 환경규제에 대응하고 유해 폐기물의 발생을 줄일 수 있는 코팅 가공제 및 가공기술 개발이 절실하다. 이에 본 연구에서는 Glass-Fiber, Aramid 등의 슈퍼 섬유와 고 강력 섬유 등을 이용하여 PTFE 코팅제품과 비슷한 수준의 성능을 부여하는 무용제형 실리콘 코팅 수지를 개발하고 내구성능 향상, Self Cleaning성, 난연성, 자외선 차단, 인장강도 및 인열 강도의 향상 등 다양한 기능성을 부여하는 최적의 환경 친화적 코팅 공정 기술을 개발하여 차세대 건축용 막구조 제품을 개발하고자 한다.