• Proceedings of the KIEE Conference
• /
• 1995.07c
• /
• pp.1058-1060
• /
• 1995

In this paper, we studied the tracking characteristics of silicone rubbers that differed in the degree of crosslinking. As the tracking method, we adopted ASTM D 2303 and Merry-Go-Round(MGR) test method. It was found that the higher the degree of crosslinking, the better tracking characteristics. In these two test methods, specimens showed similar tendency of performance variation according to the degree of crosslinking. However the degradation phenomena were very different. As for MGR method, only the color of specimens' surface changed without any erosion or tracking path on them. On the contrary, the specimens subjected to ASTM D 2303 test method showed severe erosion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.9
• /
• pp.587-592
• /
• 2015

In this study, the electrification voltage of electrostatics for silicone rubber sample($4cm{\times}4cm{\times}0.103cm$) following immersion with contaminants of 2 ml, 5 ml, 10 ml for six hours has been measured in through the applied voltage of 10 kV DC at temperature of $80^{\circ}C{\sim}110^{\circ}C$, humidity of 50%~90%. The results of this study are as follows. In case the contaminants is constant, it found that the electrification voltage of electrostatic decreased with increasing temperature and humidity to $35^{\circ}C$, 90%. In case of 2 ml of contaminants concentration, it found that the electrification voltage of electrostatic decreased with increasing temperature and humidity to $35^{\circ}C$, 50%. In case of the sample at temperature of $15^{\circ}C$ and humidity of 50%, it found that the electrification voltage of electrostatic decreased with increasing contaminants to 10 ml.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.514-517
• /
• 2003

Polymeric suspended insulators for subway and electrical track line had been designed and manufactured. The main elements to design polymeric insulators were the insulation ability and the optimal structure. To get the insulation ability, electrical and mechanical tests according to standards had done on housing rubbers and FRP cores and selected the sample with best properties as a insulator. The insulator shape and fitting parts with minimum electrical stress was simulated by FEM electrical field analysis program. The manufactured insulator set had been tested and estimated the electrical and mechanical according to ES and KS, and showed good characteristics in these tests.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1868-1869
• /
• 2005

이 논문은 반도전 실리콘 고무 표면에 코로나 방전 처리하여 이종의 실리콘 고무와의 접착 특성을 나타낸 것이다. 반도전 실리콘 고무 표면 상태를 발수성 등급에 따른 분류와 FTIR(Fourier Transform Infrared Spectroscopy)를 사용하여 평가하였다. 표면 상태 변화에 따른 반도전 실리콘 고무의 접착 특성은 T-peel test로 접착강도를 시험하였다. 실험 결과 고에너지의 코로나 방전으로 반도전 실리콘 고무의 결합쇄가 절단되었고 이 부분에 산소가 결합되어 극성 관능기를 생성하여 표면을 산화시켰다. 이러한 표면 상태 변화에 따른 접착강도는 초기 상태일 때 보다 코로나 방전 처리 후 증가하는 것을 확인 할 수 있었다. 이 논문을 통하여 코로나 방전 처리는 이종 계면의 접착 특성을 향상시킬 수 있으며, 이종 계면에서 발생하는 절연 파괴 전압을 높여 전기절연 성능을 향상시키는데 도움이 될 것이다.

• Elastomers and Composites
• /
• v.45 no.3
• /
• pp.212-216
• /
• 2010

The materials of the lithium ion battery gasket require chemical resistance to the electrolyte, electrical insulating, compression set, anti-contamination and heat resistance. To estimate suitability for rubber which has better performance to compression set than PFA, each compound were made with various rubbers, such as EPDM, NBR, FKM, FVMQ, VMQ and we checked the characteristics of each compound. Samples from each compound was deposited in Propylene Carbonate and tested for changing of Hardness and Volume during 1,000 hr with $80^{\circ}C$. EPDM and VMQ showed good performance to chemical resistance to the electrolyte, and also we could get the values over $10^{10}{\Omega}cm$ on volume resistance basis in electrical insulating. EPDM and VMQ were judged as the most suitable material.