• Transactions on Electrical and Electronic Materials
• /
• v.12 no.4
• /
• pp.156-159
• /
• 2011

SiNx:H films have been widely used for anti-reflection coatings and passivation for crystalline silicon solar cells. In this study, SiNx:H films were deposited using high frequency (13.56 MHz) direct plasma enhanced chemical vapor deposition, and the optical and passivation properties were investigated. The radio frequency power, the spacing between the showerhead and wafer, the $NH_3/SiH_4$ ratio, the total gas flow, and the $N_2$ gas flow were changed over certain ranges for the film deposition. The thickness uniformity, the refractive index, and the minority carrier lifetime were then measured in order to study the properties of the film. The optimal deposition conditions for application to crystalline Si solar cells are determined from the results of this study.

• Journal of the Korean Vacuum Society
• /
• v.2 no.3
• /
• pp.368-373
• /
• 1993

LCVD법에 의한 박막성장장치를 제작하였다. 제작한 CO2 레이저는 CO2 : N2 : He이 1 : 1 : 8로 혼합된 가스를 사용하였으며 최대 출력은 60W였고 혼합가스의 유량이 20l/min, 방전전류 40mAdlfEo 50W의 비교적 안정된 출력을 얻을 수 있었다. 반응실의 기초 진공은 1$\times$10-6torr였으며 레이저를 기판에 수직 혹은 수평으로 조사할 수 있도록 설계하였다. 제작된 장치로 SiH4 및 NH3를 재료로 하여 실리콘 및 quartz 기판위에 silicon nitride 박막을 증착하였다. 박막 생장시 가스를 흘리는 방식보다 가스를 채워놓고 하는 방식이 낮은 레이저 출력하에서 균일한 박막을 얻는데 효율적이라는 것을 발견하였다. 출력 55W의 레이저를 실리콘 기판에 5분간 조사하였을 때 최대 두께1.5$mu extrm{m}$의 박막을 얻었으며 quartz 기판위에는 출력 4W, 조사시간 6분에서 두께가 약 1$\mu\textrm{m}$인 비교적 균질의 박막을 얻을 수 있었다. FT-IR 및 XPS 분석 결과 SiH4와 NH3의 혼합비가 1 : 12일 때 비교적 nitride화가 잘 된 박막이 얻어졌음을 알았다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.220-223
• /
• 1996

Mechanical properties of Plasma-Enhanced Chemical Vapor Deposited (PECVD) silicon nitride thin film was studied to determine the feasibility of the film as a passivation layer over the aluminum bonding areas of integrated circuit chips. Ultimate strain of the films in thicknesses of about 5 k${\AA}$ was measured using four-point bending method. The ultimate strain of these films was constant at about 0.2% regardless of residual stress. Intrinsic and residual stresses of these films were measured and compared with thermal shock and cycling test results. Comparison of the results showed that more tensile films were more susceptible to crack- induced failure.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1997.04a
• /
• pp.69-73
• /
• 1997

Microwave Plasma assisted CVD (Chemical Vapor Deposition) and DC Plasma CVD were used to prepare thin and thick diamond film, respectively. Diamond coated silicon nitride and fiee standing diamond thick film were eroded by silicon carbide particles. The velocity of the solid particle was about 220m/sec. Phase transformation and the other crack formation were investigated by using Raman spectroscopy and microscopy.

• Current Optics and Photonics
• /
• v.4 no.1
• /
• pp.81-81
• /
• 2020

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.1
• /
• pp.33-40
• /
• 1998

The composite SiO$_2$/Si$_3$N$_4$/SiO$_2$(ONO) film formed by oxidation on nitride film has been widely studied as DRAM stacked capacitor multi-dielectric films. Load lock(L/L) LPCVD system by HF cleaning is used to improve electrical capacitance and to scale down of effective thickness for memory device, but is brings a new problem. Nitride film deposited using HF cleaning shows selective deposition on poly silicon and oxide regions of capacitor. This problem is avoidable by carpeting chemical oxide using $H_2O$$_2$cleaning before nitride deposition. In this paper, we study the limit of nitride thickness for abnormal oxidation and the initial deposition time for nitride deposition dependent on underlayer materials. We proposed an advanced fabrication process for stacked capacitor in order to avoid selective deposition problem and show the usefulness of nitride deposition using L/L LPCVD system by $H_2O$$_2$cleaning. The natural oxide thickness on polysilicon monitor after HF and $H_2O$$_2$cleaning are measured 3~4$\AA$, respectively. Two substrate materials have the different initial nitride deposition times. The initial deposition time for polysilicon is nearly zero, but initial deposition time for oxide is about 60seconds. However the deposition rate is constant after initial deposition time. The limit of nitride thickness for abnormal oxidation under the HF and $H_2O$$_2$cleaning method are 60$\AA$, 48$\AA$, respectively. The results obtained in this study are useful for developing ultra thin nitride fabrication of ONO scaling and for avoiding abnormal oxidation in stacked capacitor application.

• Proceedings of the KIEE Conference
• /
• 1987.07a
• /
• pp.429-432
• /
• 1987

A new LOCOS (Local Oxidation of Silicon) process using a thin nitride film directly deposited on the silicon substrate by LPCVD has been developed in order to reduce the bird's beak length. SEM studies showed that nitride thickness of 50nm can decrease the bird's beak length down to 0.2um with 450nm field oxide. No crystalline defects are observed around the bird's beak after the Wright etch. A 30% improvement in current density was obtained when this new method was applied to MOS transistors (W/L*2.9/20.4) compared to conventional LOCOS process (bird's beak length=0.7um). Other various electrical parameters improved by this new simple LOCOS process are reported in this paper.

• Journal of the Korean Vacuum Society
• /
• v.12 no.4
• /
• pp.263-268
• /
• 2003

Precise thickness control and excellent properties of silicon nitride thin films are essential for the next-generation semiconductor and display devices. In this study, silicon nitride thin films were deposited by batch-type atomic layer deposition (ALD) method using $SiC1_4$ and $NH_3$ as the precursors at temperatures ranging from 500 to $600^{\circ}C$. Thin film deposition using a batch-type ALD reactor was a layer-by-layer atomic growth by self-limiting surface reactions, and the thickness of the deposited film can be controlled by the number of deposition cycles. The silicon nitride thin films deposited by ALD method exhibited composition, refractive index and wet etch rate similar with those of the thin films deposited by low-pressure chemical vapor deposition method at $760^{\circ}C$. The addition of pyridine mixed with precursors increased deposition rate by 50%, however, the films deposited with pyridine was readily oxidized owing to its unstable structure, which is unsuitable for the application to semiconductor or display devices.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.1
• /
• pp.44-50
• /
• 1993

In an attempt to improve the electrical characteristics of tantalum pentoxide dielectric film, silicon substrate was reacted with a nitrogen plasma to form a silicon nitride of 50.angs. and then tantalum pentoxide thin films were formed by reactive sputtering in the same chamber. Breakdown field and leakage current density were measured to be 2.9 MV/cm and 9${\times}10^{8}\;A/cm^{2}$ respectively in these films whose thickness was about 180.angs.. With annealing at rectangular waveguides with a slant grid are investigated here. In particular, 900.deg. C in oxygen ambient for 100 minutes, breakdown field and leakage current density were improved to be 4.8 MV/cm and 1.61.6${\times}10^{8}\;A/cm^{2}$ respectively. It turned out that the electrical characteristics could also be improved by oxygen plasma post-treatment and the conduction mechanism at high electric field proved to be Schottky emission in these double-layered films.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.29-33
• /
• 2000

The amorphous tungsten nitrides, WNx, film could be fabricated by reactive sputtering process. The nitrogen concentration for the amorphization ranges from 10 at% to 40at%. The amorphous $W_{67}N_{33}$ film was crystallized into low resistivity $\alpha$-tungsten phase with equiaxed grains and excess nitrogen after the rapid thermal annealing for 1min at 1273K, which was similar to the resistivity of the sputtered pure tungsten film. The excess nitrogen was depleted from $\alpha$-tungsten crystals and then segregated at $\alpha$-tungsten/poly-Si interface. The segregated nitrogen has favored the formation of the homogeneous diffusion barrier layer comprised of silicon nitride, $Si_3N_4$, nano-crystals, which undertaken the inhibition of the high resistivity tungsten silicide reaction.