• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.165-172
• /
• 2012

In this study, the physical, mechanical, structural, and environmental performances based on field measured data were evaluated to check the suitability of concrete for ecological preservation and cultivation of a hydrophilic environment. More specifically, the study is focused on developing an environmentally friendly functional concrete with river ecology restoration and natural river early formation capabilities. The mechanical performance evaluation results showed that the increase in mix rate of the PVA (Poly Vinyl Alcohol) reinforcement fibers and silica fume caused an increase in the strength. The optimal mix rate was found to be 0.05 volume % PVA fiber and approximately 10% silica fume. The frost resistance evaluation showed that superior performance was gained when 0.05 volume % PVA fiber and 15% silica fume was mixed simultaneously. In the structural performance evaluation, the bending strength was improved by 47.7% compared to plain concrete when mixed with 0.05 volume % PVA fiber. The flexural toughness also saw significant improvement. The environmental monitoring of field performance showed that grasses germinated most rapidly, but the growth of red poppies, a plant that germinates in the spring, was most active with passing of time. Coverage measurements in all of the monitoring locations found favorable coverage of over 95% after 12 weeks. The study results showed that the environmentally friendly functional concrete had outstanding environmental performance.

• Tunnel and Underground Space
• /
• v.17 no.4
• /
• pp.266-284
• /
• 2007

Recently, many efforts have been made to construct the first unlined tunnel, without in-situ concrete lining, in Korea. However, the lack of reliability in the performance of shotcrete as permanent tunnel support prevented from its realization. Shotcrete has been regarded to have significant problems in field application and long term performance because of unsatisfactory strength level and durability compared to those of European countries. In this study, the high strength shotcrete satisfying compressive strength over 40 MPa and flexural strength over 4.5 MPa was developed from optimized mix design. The type of accelerators and the amount of silica fume were selected as the main factors in mixing process and the analyses were carried out up to the elapsed time of 2 years. In order to evaluate the short term durability of shotcrete, an array of laboratory test consisting of freeze-thaw, carbonation chloride penetration and permeability test was performed. For long-term durability tests, specimens have been put in an operated highway tunnel to expose them to the similar environment when they are actually used as an unlined tunnel support. From the strength and durability tests, it was found that only alkali-free based accelerator satisfied the target strength of this study and also, the developed shotcrete showed very high performance in its durability.

• International Journal of Highway Engineering
• /
• v.19 no.6
• /
• pp.129-137
• /
• 2017

PURPOSES : The purpose of this study is to develop bridge deck concrete materials based on ordinary Portland cement concrete, and to evaluate the applicability of the developed materials through material properties tests. METHODS : For field implementation, raw material (cement, fine aggregate, and coarse aggregate) properties, fresh concrete properties (slump and air content), strength (compressive, flexural and bond strength) gain, and durability (freeze-thaw resistance, scaling resistance, and rapid chloride penetrating resistance) performance were evaluated in the laboratory. RESULTS : For the selected binder content of $410kg/m^3$, W/B = 0.42, and S/a = 0.48, the following material performance results were obtained. Considering the capacity of the deck finisher, a minimum slump of 150 mm was required. At least 6 % of air content was obtained to resist freeze-thaw damage. In terms of strength, 51.28 MPa of compressive strength, 7.41 MPa of flexural strength, and 2.56 MPa of bond strength at 28 days after construction were obtained. A total of 94.9 % of the relative dynamic modulus of elasticity after 300 cycles of freeze-thaw resistance testing and $0.0056kg/m^2$ of weight loss in a scaling resistance test were measured. However, in a chloride ion penetration resistance test, the result of 3,356 Coulomb, which exceeds the threshold value of the standard specification (1000 Coulomb at 56 days) was observed. CONCLUSIONS : Instead of using high-performance modified bridge deck materials such as latex or silica fume, we developed an optimum mix design based on ordinary Portland cement concrete. A test construction was carried out at ramp bridge B (bridge length = 111 m) in Gim Jai City. Immediately after the concrete was poured, the curing compound was applied, and then wet mat curing was applied for 28 days. Considering the fact that cracks did not occur during the monitoring period, the applicability of the developed material is considered to be high.