Objectives : In this study, contact angle and shore D hardness were measured, and a shark fin test was conducted after selecting five addition silicon(Blu-Mousse, BM; EXABITE II, EX; PERFECT, PF; Regisil$^{(R)}$ Rigid, RE; Silagum$^{(R)}$, SI) in order to figure out the properties of elastomeric interocclusal recording materials and reduce errors at interocclusal recording. 8) Methods : A contact angle was measured using a contact angle analyzer. After placing a drop of liquid on the surface of the specimens of interocclusal recording materials, a contact angle was photographed with a CCD camera on the equipment. In terms of a shark fin test, interocclusal recording materials were mixed for the time proposed by the manufacturer and inserted into the split ring of the Shark fin device. Twenty (20) seconds exactly, a metal rod was removed to make the materials slowly absorbed. Once they hardened, fin height was measured with a caliper after separating molds and trimming the specimens. The shore D hardness was measured with a shore D hardness tester(Model HPDSD, Hans Schmidt & Co. Gmbh, Germany) in sixty (60) minutes after fabricating specimens. In each experiment, five specimens, mean and standard deviation were calculated. A one-way ANOVA test was performed at the p>0.05 level of significance. In terms of correlation among the tests, Pearson correlation coefficient was estimated. For multiple comparison, Scheffe's test was carried out. Results : A contact angle was the highest in EX with $99.23^{\circ}$ (p<0.05) while the result of the shark fin test was the longest in RE with 5.45mm. SI was the lowest (0.27mm) with statistical significance. Among the interocclusal recording materials, significant difference was observed in terms of means (p<0.05). The shore D hardness was the highest in SI with 31.0 while RE was significantly low with 16.4 (p<0.05). Among the materials, statistically significant difference was observed in terms of means when compared to the rest materials (RE), BM, RE and SI (PF and EX) and the remaining materials (BM and SI) (p<0.05). In terms of correlations among the tests, a negative correlation occurred between shore D hardness and shark fin test(r=-0.823, p=0.000). Conclusions : According to the study above, it is necessary to understand the properties of interocclusal recording materials and consider contact angle, shark fin test and properties of shore D hardness to select appropriate materials.
Kang Z. Khor;Cheow K. Yeoh;Pei L. Teh;Thangarajan Mathanesh;Wee C. Wong
Advances in materials Research
/
제13권3호
/
pp.211-220
/
2024
Polylactic acid or polylactide (PLA) is a biodegradable thermoplastic that can be produced from renewable material to create various components for industrial purposes. In 3D printing technology, PLA is used due to its good mechanical, electrical, printing properties, environmentally friendly and non-toxic properties. However, the physical properties and excellent electrical insulation properties of PLA have limited its application. In this study, with the carbon black (CB) as filler added into PLA, the lattice spacing and morphology were investigated by using X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The physical properties of PLA-carbon composite were evaluated by using tensile test, shore D hardness test and density and voids measurement. Impedance test was conducted to investigate the electrical properties of PLA-Carbon composites. The results demonstrate that the inclusion of carbon black as filler enhances the physical properties of the PLA-carbon composites, including tensile properties, hardness, and density. The addition of carbon black also leads to improved electrical conductivity of the composites. Better enhancement toward the electrical properties of PLA-carbon composites is observed with 1wt% of carbon black in N774 grade. The N550 grade with 2wt% of carbon black shows better improvement in the physical properties of PLA-carbon composites, achieving 10.686 MPa in tensile testing, 43.330 in shore D hardness test, and a density of 1.200 g/cm3 in density measurement. The findings suggest that PLA-carbon composites have the potential for enhanced performance in various industrial applications, particularly in sectors requiring improved physical and electrical properties.
The purposes of this study were to determine the influence of midsole hardness and sole thickness of sports shoes on ball flex angle and position with increment of running velocity. The subjects employed for this study were 10 college students who did not have lower extremity injuries for the last one year and whose running pattern was rearfoot striker of normal foot. The shoes used in this study had 3 different midsole hardness of shore A 40, shore A 50, shore A 60 and 3 different sole thickness of 17cm, 19cm, 21cm. The subjects were asked to run at 3 different speed of 2.0m/sec, 3.5m/sec, 5.0m/sec and their motions were videotaped with 4 S-VHS video cameras and 2 high speed video cameras and simultaneously measured with a force platform. The following results were obtained after analysing and comparing the variables. Minimum angle of each ball flex position were increased with the increment of running velocity and shoe sole thickness(P<0.05), but mid-sole hardness did not affect minimum ball flex angle. The position which minimum angle was shown as smallest was 'D'. Midsole hardness and sole thickness did not affect time to each ball flex minimum angle, total angular displacement of ball flex angle, and total angular displacement of torsion angle(P<0.05). The position which minimum angle was appeared to be earliest was similar at walking velocity, and E and F of midfoot region at running velocity. Total angular displacement of ball flex position tended to increase as shifted to heel. It was found that running velocity had effects on ball flex angle variables, but shoe sole thickness partially affected. It would be considered that running velocity made differences between analysis variables at walking and running when designing shoes. Also, it was regarded that shoes would be developed at separated region, because ball flex angle and position was shown to be different at toe and heel region. It is necessary that midsole hardness and thickness required to functional shoes be analyzed in the further study.
가교 폴리에틸렌을 열을 가하여 노화시킨 후 구조 및 물성의 변화를 조사하였다. 가교 폴리에틸렌의 열적 산화 반응으로 카보닐 그룹이 형성됨을 X-선 광전자 분광법과 근적외선 분광법을 이용하여 확인하였다. 노화 시간이 길어질수록 1715 nm에서 관찰되는 카보닐 피이크가 정량적으로 증가하는 것을 근적외선 분광법을 이용하여 관찰하였다. 열화 시간에 따른 흡수 피이크의 선형적인 관계로부터 근적외선 분광법이 고분자 재료의 열화 과정을 감시하는데 적합한 방법임을 확인할 수 있었다. 또한 노화에 의한 가교 결합의 발생과 그에 따른 물리적 성질의 변화를 TMA, 응력-변형 시험, 쇼어 경도 측정 방법을 이용하여 관찰하였다. 노화가 진행됨에 따라 유리 전이 온도가 110에서 132$^{\circ}C$로 증가함을 관찰하였으며, 인장률은 265에서 110%로 점차 감소하고 쇼어 D 경도는 32에서 50으로 크게 증가하는 것을 관찰할 수 있었다.
In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr- 13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under $45{\mu}m$ and over $180{\mu}m$, and then they were compacted with various pressures and sintered at $1210^{\circ}C$ for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to $79l/min{\cdot}cm^2$. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.
Pahuja, Rasleen Kaur;Garg, Sandeep;Bansal, Sanjay;Dang, Rajat Harvinder
The Journal of Advanced Prosthodontics
/
제5권3호
/
pp.270-277
/
2013
PURPOSE. This study was aimed to determine the effect of two chemically distinct denture cleansers and water on the surface hardness of acrylic and silicone based soft denture liners at various time intervals. MATERIALS AND METHODS. Two commonly used commercial resilient liner material were selected based on their chemical composition (silicone- and acrylic-based soft liners) for this investigation. 120 cylindrical specimens were made of $15mm{\times}10mm$ dimensions (according to ASTM: D-2240-64T) in a custom made metal mold. All specimens were stored in artificial saliva throughout the study. Forty specimens were cleansed daily in 0.5% sodium hypochlorite solution; forty were cleansed in sodium perborate and remaining forty specimens were daily rinsed in water. Testing was done at 1 week, 1 month, 3 months and 6 months for surface hardness using a Shore A Durometer. A mean of 3 reading for each sample was subjected to one-way ANOVA, Post Hoc test and pair-t test for statistical analysis. P values of less than 0.05 were taken as statistically significant. RESULTS. Surface hardness of all the samples was significantly higher after a period of 6 months irrespective of the cleansing treatment. Minor changes were observed between control, sodium hypochlorite and sodium perborate groups with time. Greater change was observed in surface hardness of acrylic-based soft denture liners as compared to silicone-based soft liners for all groups, as time progressed. CONCLUSION. Silicone-based soft denture liners performed significantly better in all cleansing treatments than acrylic-based soft denture liners.
PURPOSE. The purpose of this study was to compare mechanical and physical properties of injection-molded thermoplastic denture base resins. MATERIALS AND METHODS. In this study, six commercially available products (VA; Valplast, LC; Lucitone, ST; Smiltone, ES; Estheshot-Bright, AC; Acrytone, WE; Weldenz) were selected from four types of thermoplastic denture base materials (Polyamide, Polyester, Acrylic resin and Polypropylene). The flexural properties and shore D hardness have been investigated and water sorption and solubility, and color stability have evaluated. RESULTS. For the flexural modulus value, ES showed the highest value and WE showed significantly lower value than all other groups (P<.05). Most of experimental groups showed weak color stability beyond the clinically acceptable range. CONCLUSION. Within the limits of this study, thermoplastic denture base resin did not show sufficient modulus to function as a denture base. In addition, all resins showed discoloration with clinical significance, and especially polyamides showed the lowest color stability.
고굴절률을 갖는 플라스틱 재료를 얻기 위하여 1,2-에틸렌디설파닐비스(2-머캅토메틸-1-에탄티올) (ESTT)을 1,2-에틸렌디설파닐비스(2-브로모메틸-1-에탄티올) (ESTB)과 티오우레아의 반응과 암모니아 용액으로 가수분해 반응을 해서 높은 수율로 새로이 합성하였고, $^1$H-NMR, $^{13}$C-NMR, FT-IR및 Mass Specooscopy 등에 의해 1.7 ppm에서 -SH, 28.4 ppm에서 -CH$_2$SH, 2540 $cm^{-1}$ /에서 -SH등의 관능기 구조를 확인하였다. 이어서, 폴리티오우레탄 (PTU)들은 디부틸틴 디라울레이트 존재하에서 ESTT와 4,4'-메틸렌비스(페놀이소시아네이트) (MDI), 톨릴렌 2,4-디이소시아네이트 (TDI), 이소포론 디이소시아네이트 (IPDI), m-자일렌디이소시아네이트 (XDI) 및 1,6-디이소시아네이토헥산 (HMDI) 등을 일정한 틀에 넣고 주형중합을 하고, FT-IR로 N=C=O의 존재를 확인하였다. 이어서, PTU 수지들의 열적, 기계적 및 광학적 성질을 살펴보기 위하여 열주사분석 (DSC)과 열중량분석 (TGA), 경도 및 굴절률 측정 등을 행하여, PTU 시편들이 DSC상에서 융점이 없고 XRD상으로 무정형임을 관찰하였다. 또, 110 $^{\circ}C$ 이상의 유리 전이 온도를 갖는 PTU 수지들은 86∼89 범위의 양호한 경도 (Shore D)를 나타냈으며, 방향족 고리를 함유하는 디이소시아네이트와 ESTT를 원료로 했던 PTU수지들의 내열성이 특별히 양호하였다. 무정형 PTU 수지들은 400∼600 m 범위의 UV-vis 광원에 의한 광투과율 들도 양호하게 나타났다. PTU 수지들은 1.60 이상의 굴절률을 보였으며, 황함량이 증가하면 굴절률도 점차 증가하는 것이 관찰되었다.
The design of sealing mechanisms of a manual pressure valve was analyzed with FE analysis for a hydrogen fuels charge and discharge system of FCEV. The damage prediction of the O-ring with respect to the material models of rubbers was calculated by the gap analysis of the backup ring and O-ring according to the internal pressure. Two kinds of the rubber material characteristic models were adopted to the O-ring. One was the linear elastic and the other was hyperelastic of Ogden $3^{rd}$ order model. The experimental data of urethane of Shore hardness 90 was utilized to the curve fitting of hyperelastic properties. It was found that the contact pattern of the backup ring was different in two models and the sealing mechanism was better in the case of the hyperelastic characteristic model.
본 연구에서는 암석 절삭 장비의 마모에 직접적인 영향을 주는 인자인 암석의 마모도(abrasiveness) 측정에 관한 연구를 수행하였다. 몇 가지 방법 중 세르샤 마모 시험(Cerchar abrasiveness test)을 통하여 암석의 마모도에 영향을 미치는 인자를 확인하고 효율적인 시험을 수행하기 위한 조건들을 연구하였다. 국내 19종 암석에 대한 시험 결과를 통하여, 세르샤 마모 지수(CAI, Cerchar Abrasiveness Index)에 영향을 미치는 암석의 역학적 물성(단축압축강도, 간접인장강도, 탄성계수, 포아송비, 공극률, 쇼어경도)과의 상관관계를 찾아보았고 X선 회절 분석을 통하여 암석의 구성 광물 중 마모도에 가장 큰 영향을 미치는 석영 함량, 등가 석영 함량과의 관계도 확인하였다. 그 결과로 암석의 입자 결합 특성보다 광물의 특성이 CAI에 영향을 더 미치는 것으로 관찰되었고, 단축압축강도와 등가 석영함량의 함수로 CAI를 예측하는 모델을 제시하였으며 핀의 경도가 커질수록 CAI값이 선형적으로 작아짐을 확인하였다. 수치해석적 연구를 통해 세르샤 마모 시험을 모사한 결과 초기 긁힘 거리에서 대부분의 마모가 발생함을 확인하였고 하중이 증가할수록 CAI값이 증가함을 확인하였다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.