• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.1
• /
• pp.32-38
• /
• 2014

In the present study, immersion corrosion characteristics of Zn and Al thermal spray coating with sealer for the seawater heat exchanger are experimentally investigated. Total 8 coating types of Zn and Al thermal spray coating with silicone and epoxy sealer were tested with immersion corrosion testing in $80^{\circ}C$ 3.5%w NaCl solution and compared the corrosion characteristics between each coatings. To investigate the corrosion characteristics of the specimens, AC impedance, SEM, and thermal diffusivity were acquired and analyzed. As a result, on the surface of the specimens with silicone and epoxy sealer, blister did not occurred, so the sealers might be effective at increasing the corrosion resistance of the specimens immersed in the NaCl solution.

• Restorative Dentistry and Endodontics
• /
• v.28 no.4
• /
• pp.295-302
• /
• 2003

본 연구에서는 인산 칼슘 근관 봉함재 [Apatite Root Sealer (ARS) Type I, II, III]의 세포독성을 혼합후의 시간 경과에 따라서 다른 4계열의 근관 봉함재 (Pulp Canal Sealer EWT, AH Plus, Sealapex, Ketac Endo)와 비교하여 평가하였다. 근관 봉함재를 혼합한 후 1시간, 8시간, 24시간, 48시간, 1주, 2주,4주의 기간동안 배양액을 이용하여 추출액을 얻었다. L929 쥐섬유아세포를 24시간동안 각 시간군에서 얻은 추출액과 함께 배양한 후 dimethylthiazol diphenyltetrazolium (MTT) assay와 neutral red (NR) assay를 이용하여 세포독성(%)을 평가하였다. 실험 결과 ARS Type I, II, III는 전 시간군에 걸쳐 낮은 세포독성을 보였고 (23.65-0.55%) 특히 경화 초기에 다른 계열의 근관 봉함재보다 유의성 있게 낮은 세포독성을 나타내었다. ARS Type I, II, III간의 세포독성은 각 시간군에서 유의성 있는 차이를 보이지 않았다. AH Plus와 Ketac Endo는 초기에 높은 세포독성을 보였으나 AH Plus는 8시간 이후에, Ketac Endo는 24시간 이후에 독성이 급격히 감소하여 ARS와 유의성 있는 차이를 보이지 않았다. Pulp Canal Sealer EWT와 Sealapex는 4주까지 지속적인 세포독성을 나타내었다. 그리고 MTT assay와 NR assay를 이용하여 얻은 각 근관봉함재의 세포독성은 시간 경과에 따라서 비슷한 변화 양상을 나타내었다. 인산 칼슘 근관 봉함재는 생체적합성이 우수한 재료로써 앞으로 지속적인 개발과 평가가 필요할 것으로 사료된다.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.1
• /
• pp.16-20
• /
• 2013

PURPOSE. To assess the retention of glass fiber post cemented with self-adhesive resin cement into optimum and over-prepared root canals following obturation in the presence of either eugenol (EB) or calcium hydroxide (CB)-based sealers. MATERIALS AND METHODS. Roots of extracted premolars were endodontically-treated in 5 groups (n = 10). Roots of Group 1 (control) were left with no obturation and then optimally prepared to receive endodontic dowels. Other root canals were obturated with gutta-percha in the presence of either eugenol-based (Groups 2 and 4) or calcium hydroxide-based (Groups 3 and 5) sealer. Dowel spaces were prepared with optimal diameter in Groups 2 and 3, one size larger in Groups 4 and 5. Standardized fiber posts were luted to the prepared spaces using self-adhesive resin cement and its retention was then tested on an universal testing machine. Both one-way ANOVA and Tukey's HSD comparisons (${\alpha}$=0.05) were used to identify the significance of inter-group retention differences. Scanning electron microscopy (SEM) of both optimally and over-prepared dowel spaces was also considered to figure the nature of their interior out. RESULTS. The post retention was significantly higher to the non-obturated, optimally-prepared dowel spaces of Group 1 compared to the obturated, optimally-prepared ones of Groups 2 and 3. For each dowel space diameter, root canals obturated using CB of Groups 3 and 5 showed significantly higher dowel retention compared to those obturated using EB of Groups 2 and 4. Post retention to the over-prepared dowel spaces of Groups 4 and 5 was significantly higher than that recorded for the optimally-prepared ones of Groups 1-3. SEM images revealed traces of endodontic sealer and gutta-percha on the walls of the optimally-prepared dowel spaces. CONCLUSION. Despite the adverse effect of endodontic sealers on the retention of fiber posts, the over-preparation of dowel spaces helps to improve the retention.

• Restorative Dentistry and Endodontics
• /
• v.45 no.2
• /
• pp.18.1-18.9
• /
• 2020

Objectives: The purpose of this study was to evaluate the void of root canal filling over time when a calcium silicate sealer was used in the single gutta-percha cone technique. Materials and Methods: Twenty-four J-shaped simulated root canals and twenty-four palatal root canals from extracted human maxillary molars were instrumented with ProFile Ni-Ti rotary instruments up to size 35/0.06 or size 40/0.06, respectively. Half of the canals were filled with Endoseal MTA and the other half were with AH Plus Jet using the single gutta-percha cone technique. Immediately after and 4 weeks after the root canal filling, the samples were scanned using micro-computed tomography at a resolution of 12.8 ㎛. The scanned images were reconstructed using the NRecon software and the void percentages were calculated using the CTan software, and statistically analyzed by 1-way analysis of variance, paired t-test and Tukey post hoc test. Results: After 4 weeks, there were no significant changes in the void percentages at all levels in both material groups (p > 0.05), except at the apical level of the AH Plus Jet group (p < 0.05) in the simulated root canal showing more void percentage compared to other groups. Immediately after filling the extracted human root canals, the Endoseal MTA group showed significantly less void percentage compared to the AH Plus Jet group (p < 0.05). Conclusions: Under the limitations of this study, the Endoseal MTA does not seem to reduce the voids over time.

• Restorative Dentistry and Endodontics
• /
• v.6 no.1
• /
• pp.7-16
• /
• 1980

The author observed the periodontal tissue reactions to the root canal sealers after root perforations were made intentionally in dogs. The perforations were made on 74 teeth from 7 dogs. The experiments were performed in two different modes of procedure: In Group I, the perforations were made through the root canal to the alveolar bone. In Group II, the perforations were made from site of alveolar bone to the root canals. The perforated canals in Group I were filled with gutta-percha and root canal cements; Calxyl (Calcium Hydroxide in Ringer's solution), Zinc Oxide -Eugenol cement (Z.O.E.), Kerr sealer (Rickert's paste) and AH 26 (Epoxy Resin preparations). The perforated canals in Group II were sealed with Calxyl, Z.O.E, Kerr sealer and AH26. Histologic examinations of periodontal tissue reactions were observed at various time intervals. The results were as follows; l. Cementum deposition on the perforated root surface in Group II cases showed slightly earlier than that of Group I. Healing tendency of injured alveolar bone in Group II was greater than that of Group I. 2. According to the time increase after experiment, the cementum deposition on the site of perforated dentin in Group II with intact pulp was notably thickened. Secondary dentin deposition on the root canal surface where the dentinal tubles were cut was also found in similar pattern. 3. In the cases of perforated canals sealed with Calxyl both in Group I and Group II, It revealed the earliest cementum-deposition among 4 different root canal cements. In the cases of perforated canals sealed with Kerr sealer and AH26, the cementum-deposition on the root surface was not found. 4. Proliferation of epithelium around the perforated area was first seen at 5-week cases in Group I, and at 3-week cases in Group II. 5. In all cases, dentin resorption on the site of perforated root surface was always occured.

• Restorative Dentistry and Endodontics
• /
• v.46 no.1
• /
• pp.4.1-4.16
• /
• 2021

Objectives: This study evaluated the biocompatibility and bioactive potential of NeoMTA Plus mixed as a root canal sealer in comparison with MTA Fillapex. Materials and Methods: Polyethylene tubes filled with NeoMTA Plus (n = 20), MTA Fillapex (n = 20), or nothing (control group, CG; n = 20) were inserted into the connective tissue in the dorsal subcutaneous layer of rats. After 7, 15, 30 and 60 days, the specimens were processed for paraffin embedding. The capsule thickness, collagen content, and number of inflammatory cells (ICs) and interleukin-6 (IL-6) immunolabeled cells were measured. von Kossa-positive structures were evaluated and unstained sections were analyzed under polarized light. Two-way analysis of variance was performed, followed by the post hoc Tukey test (p ≤ 0.05). Results: At 7 days, the capsules around NeoMTA Plus and MTA Fillapex had more ICs and IL-6-immunostained cells than the CG. However, at 60 days, there was no significant difference in the IC number between NeoMTA Plus and the CG (p = 0.1137) or the MTA Fillapex group (p = 0.4062), although a greater number of IL-6-immunostained cells was observed in the MTA Fillapex group (p = 0.0353). From 7 to 60 days, the capsule thickness of the NeoMTA Plus and MTA Fillapex specimens significantly decreased, concomitantly with an increase in the collagen content. The capsules around root canal sealers showed positivity to the von Kossa stain and birefringent structures. Conclusions: The NeoMTA Plus root canal sealer is biocompatible and exhibits bioactive potential.

• Restorative Dentistry and Endodontics
• /
• v.48 no.4
• /
• pp.41.1-41.17
• /
• 2023

Objectives: This scientometric and bibliometric analysis explored scientific publications related to hydraulic calcium silicate-based (HCSB) sealers used in endodontology, aiming to describe basic bibliometric indicators and analyze current research trends. Materials and Methods: A comprehensive search was conducted in Web of Science and Scopus using specific HCSB sealer and general endodontic-related terms. Basic research parameters were collected, including publication year, authorship, countries, institutions, journals, level of evidence, study design and topic of interest, title terms, author keywords, citation counts, and density. Results: In total, 498 articles published in 136 journals were retrieved for the period 2008-2023. Brazil was the leading country, and the universities of Bologna in Italy and Sao Paolo in Brazil were represented equally as leading institutions. The most frequently occurring keywords were "calcium silicate," "root canal sealer MTA-Fillapex," and "biocompatibility," while title terms such as "calcium," "sealers," "root," "canal," "silicate based," and "endodontic" occurred most often. According to the thematic map analysis, "solubility" appeared as a basic theme of concentrated research interest, and "single-cone technique" was identified as an emerging, inadequately developed theme. The co-occurrence analysis revealed 4 major clusters centered on sealers' biological and physicochemical properties, obturation techniques, retreatability, and adhesion. Conclusions: This analysis presents bibliographic features and outlines changing trends in HCSB sealer research. The research output is dominated by basic science articles scrutinizing the biological and specific physicochemical properties of commonly used HCSB sealers. Future research needs to be guided by studies with a high level of evidence that utilize innovative, sophisticated technologies.

• Restorative Dentistry and Endodontics
• /
• v.33 no.2
• /
• pp.133-140
• /
• 2008

The purpose of this study was to compare the apical micro leakage in root canal filled with Resilon by several self-etching primers and methacrylate-based root canal sealer. Seventy single-rooted human teeth were used in this study. The canals were instrumented by a crown-down manner with Gate-Glidden drills and .04 Taper Profile to ISO #40. The teeth were randomly divided into four experimental groups of 15 teeth each according to root canal filling material and self-etching primers and two control groups (positive and negative) of 5 teeth each as follows: group 1 - gutta percha and $AH26^{(R)}$ sealer: group 2 - Resilon, $RealSeal^{TM}$ primer and $RealSeal^{TM}$ sealer: group 3-Resilon, Clearfil SE $Bond^{(R)}$ primer and $RealSeal^{TM}$ sealer group 4-Resilon, $AdheSe^{(R)}$ primer and $RealSeal^{TM}$ sealer. Apical leakage was measured by a maximum length of linear dye penetration of roots sectioned longitudinally by diamond disk. Statistical analysis was performed using the One-way ANOVA followed by Scheffe's test. There were no statistical differences in the mean apical dye penetration among the groups 2, 3 and 4 of self-etching primers. And group 1, 2 and 3 had also no statistical difference in apical dye penetration. But, there was statistical difference between group 1 and 4 (p < 0.05). The group 1 showed the least dye penetration. According to the results of this study, Resilon with self-etching primer was not sealed root canal better than gutta precha with $AH26^{(R)}$ at sealing root canals. And there was no significant difference in apical leakage among the three self-etching primers.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.44 no.1
• /
• pp.20-27
• /
• 2017

This study aimed to assess microleakage of Endoseal MTA when it is used as a root canal sealer and a root canal filling material compared with conventional endodontic treatment materials Forty-two mature human permanent teeth with a single root canal were divided randomly into three experimental groups (n = 10) and two control groups (n = 6). Group A was obturated with AH $plus^{(R)}$ and gutta-percha (GP). Group E1 was obturated with Endoseal MTA and GP. Group E2 was obturated with Endoseal MTA only. The positive control group was obturated with GP only and the negative control group was obturated in the same way as the experimental groups. The samples were kept in saline solution for 24 hours and were immersed in 0.2% rhodamine B dye solution for 24 hours. Then the samples were split longitudinally and the micoleakage was assessed under a stereomicroscope. Complete microleakage was detected in all positive control group samples, whereas no microleakage was detected in the negative control group. There was no statistically significant difference between the experimental groups in the Kruskal-Wallis test. These results suggest that Endoseal MTA has potential use as a root canal sealer and a root canal filling material.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.33 no.2
• /
• pp.80-87
• /
• 2017

Purpose: The aim of this study was to assess the physical properties of a novel resin-based endodontic sealer, Any-Seal, in comparison with AH Plus Jet. Materials and Methods: Flow, radiopacity and compressive strength were examined according to ISO 6876/2001. For flow test, 0.05 mL of sealer was placed between glass plate and 100 g weight were applied. Ten minutes after mixing the sealers, the load was removed and the diameters of the compressed sealer discs were measured. For radiopacity, 10 mm diameter and 1 mm thickness sample were fabricated and took radiograph with an aluminum step-wedge and analyzed using imaging program. For compressive strength test, $4mm{\times}6mm$ cylindrical specimen was fabricated and tested after 24 hours and 1 week using Universal testing machine. Results: Both tested sealers were consistent with ISO 6876/2001 in the flow and radiopacity test. The flow values of both sealers were not significantly different (P > 0.05). AH Plus Jet had significantly higher radiopacity (P < 0.05). AH Plus Jet showed higher compressive strength at both time intervals (P < 0.05). Conclusion: Any-Seal showed low compressive strength until after 1 week, so its physical and biological aspect should be evaluated more before clinical use.