• Journal of Technologic Dentistry
• /
• v.42 no.3
• /
• pp.234-239
• /
• 2020

Purpose: We investigated the marginal fit between abutment and metal copings according to impression technique, wax block types, and metal types. Methods: We selected the traditional impression method of using rubber impression materials and the digital impression method of using oral scanners, three types of wax blocks, and two types of metal, both of which were domestically and commercially available, were selected to produce metal copings, and the marginal fit was determined through the use of silicon replication. Results: The measurements of axial wall fit revealed that the IYV specimens had the best fit, with a mean gap of 24.11±5.95 ㎛, followed by CEV, CHV, CSS, CSV, CES, CHS, and IYS specimens (mean: 33.44±8.41 ㎛). The differences were not statistically significant. The marginal gap measurements showed that the CEV specimen had the smallest gap, 17.25±4.13 ㎛, followed by the CSV, CHV, CSS, CES, CHS, IYV, and IYS specimen (mean: 43.47±15.63 ㎛). The differences were statistically significant. Conclusion: The axial wall fit of the metal coping (VeraBond2V; Aalba Dent, Inc., Fairfield, CA, USA) produced by the lost wax technique with the traditional impression method was excellent. The marginal fit of the metal coping (VeraBond 2V) produced by wax milling with the use of an oral scanner was also excellent. The marginal fit of the metal coping was within the clinically acceptable limits in all groups.

• Elastomers and Composites
• /
• v.54 no.4
• /
• pp.359-367
• /
• 2019

Poly(2-hydroxyethyl methacrylate) (PHEMA) hydrogels modified with various co-monomers, such as N-vinyl pyrrolidone (NVP), glycidyl methacrylate (GMA), and glycerol monomethacrylate (GMMA), were prepared to investigate the effect of adding a co-monomer on the water contents, surface wettability, and tensile modulus. These polymers were synthesized by thermal- and photo-polymerization in the presence of azobisisobutyronitrile (AIBN) and diphenyl(2,4,6-trimethylbenzoyl)-phosphineoxide (TPO) as the initiators. The characteristics of the hydrogels were analyzed via FTIR and UV/Vis spectroscopies, contact angle measurements, and tensile modulus measurements with UTM. Regarding the properties of water in the hydrogels, the ratio between free to bound water was investigated using differential scanning calorimetry (DSC). The effects of adding the co-monomers on the water content, surface wettability, and tensile modulus for soft contact lenses were also investigated. In the case of p(HEMA-co-NVP) hydrogels, the increase in the equilibrium water content (EWC) was primarily due to the increase in the bound water content. For p(HEMA-co-GMMA) hydrogels, an increase in free water content was the main reason for the increased EWC. In contrast, in the case of p(HEMA-co-GMA) hydrogels, a decrease in bound water content was observed to be the main factor that reduced the EWC. Photo-polymerized PHEMA hydrogels showed enhanced surface wettability and tensile modulus as compared to those produced via thermal polymerization.

• Journal of the Institute of Electronics Engineers of Korea TE
• /
• v.39 no.2
• /
• pp.6-10
• /
• 2002

Al films (1000~4000${\AA}$)were deposited on glass and polymer(polyethersulfine) plastic substrates by DC-magnetron sputtering for plastic-based flat-panel displays. A stepped heating process was used both to improve the electrical characteristics and to diminish the thermal expansion of the polymer substrates. Following this procedure, we could succeed in sputtering Al films without any cracking or shrinkage of the polymer substrates. The treatment temperatures and deposited process of Al films were under 200$^{\circ}C$. Also, this low temperature fabrication process allows the application of plastic substrates. Scanning Electrom Microscopy, Atomic Force Microscopy, X-ray Dffractometry, and electrical measurements such as resistivity measurements were performed to investigate the properties of deposited the Al films and their reliability. 

• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.137-141
• /
• 2010

The $(1-x)La_{0.7}Sr_{0.3}MnO_3(LSMO)/xZnFe_2O_4$(ZFO) (x = 0, 0.01, 0.03, 0.06 and 0.09) composites were prepared by a conventional solid-state reaction method. We investigated the structural properties, magnetic properties and electrical transport properties of (1-x)LSMO/xZFO composites using X-ray diffraction (XRD), scanning electron microscopy (SEM), field-cooled dc magnetization and magnetoresistance (MR) measurements. The XRD and SEM results indicate that LSMO and ZFO coexist in the composites and the ZFO mostly segregates at the grain boundaries of LSMO, which agreed well with the results of the magnetic measurements. The resistivity of the samples increased by the increase of the ZFO doping level. A clear metal-to-insulator (M-I) transition was observed at 360K in pure LSMO. The introduction of ZFO further downshifted the transition temperature (350K-160K) while the transition disappeared in the sample (x = 0.09) and it presented insulating/semiconducting behavior in the measured temperature range (100K to 400K). The MR was measured in the presence of the 10kOe field. Compared with pure LSMO, the enhancement of low-field magnetoresistance (LFMR) was observed in the composites. It was clearly observed that the magnetoresistance effect of x = 0.03 was enhanced at room temperature range. These phenomena can be explained using the double-exchange (DE) mechanism, the grain boundary effect and the intrinsic transport properties together.

• Nuclear Engineering and Technology
• /
• v.53 no.9
• /
• pp.2982-2989
• /
• 2021

One of the consequences of the 475 ℃ embrittlement of duplex stainless steels is the reduction of the resistance to localized corrosion. Therefore, the detection of this type of embrittlement before the material exhibits significant loss in toughness, and corrosion resistance is important to ensure the structural integrity of critical components under corrosion threats. In this research, conductivity measurements are performed using the alternating current potential drop (ACPD) technique with using a portable four-point probe as a nondestructive evaluation (NDE) method for detecting the embrittlement in a 2507 (UNS S32750) super duplex stainless steel (SDSS) aged at 475 ℃ from as-received condition to 300 h. The electric conductivity results were compared against two electrochemical tests namely double loop electrochemical potentiokinetic reactivation (DL-EPR) and critical pitting temperature (CPT). Mechanical tests and the microstructure characterized using scanning electron microscopy (SEM) imaging are conducted to track the progress of embrittlement. It is shown that the electric conductivity correlates with the changes in impact energy, microhardness, and CPT corrosion tests result demonstrating the feasibility of the four-point probe as a possible field-deployable method for evaluating the 475 ℃ embrittlement of 2507 SDSS.

• The Journal of Advanced Prosthodontics
• /
• v.14 no.1
• /
• pp.22-31
• /
• 2022

PURPOSE. The purpose of this study was to investigate the misfit and screw preload at the implant abutment connection of implant supported fixed dental prosthesis with cantilever (ICFDP) manufactured using different digital manufacturing techniques and to compare the screw preload before and after cyclic loading. MATERIALS AND METHODS. Mandibular jaw model with four intra-foraminal implants was scanned using digital scanner. Stereolithography file was used to design a framework with nonengaging (NE) abutments and 10 mm cantilever distal to one terminal implant. Five frameworks were constructed using combined digital-conventional techniques (CAD-cast), and five frameworks were constructed using three-dimensional printing (3DP). Additional CAD-cast framework was constructed in a way that ensures passive fit (PF) to use as control. Scanning electron microscope (SEM) measured the implant abutment connection misfit. Sixty screws were used on the corresponding frameworks. Screws were torqued and pre-cyclic loading reverse torque value (RTV) was recorded. Frameworks were subjected to 200,000 loading cycles with a loading point 9 mm from the center of terminal implants adjacent to the cantilever and post-cyclic loading RTVs were recorded. RESULTS. Microscopic readings showed significant differences between frameworks. PF demonstrated the lowest measurements of 16.04 (2.6) ㎛ while CAD-cast demonstrated the highest measurements of 29.2 (3.1) ㎛. In all groups, RTVs were significantly lower than the applied torque. Post-cyclic loading RTV was significantly lower than pre-cyclic loading RTV in PF and 3DP frameworks. Differences in RTVs between the three manufacturing techniques were insignificant. CONCLUSION. Although CAD-cast and three-dimensionally printed (3DP) both produce frameworks with clinically acceptable misfit, 3DP might not be the technique of choice for maintaining screw's preload stability under an aggressive loading situation.

• Corrosion Science and Technology
• /
• v.22 no.2
• /
• pp.90-98
• /
• 2023

In this study, cobalt oxide (Co₃O₄) and cobalt-doped magnetite (CoFe₂O₄) nanoparticles were synthesized by a hydrothermal method. They were then used as corrosion inhibitors for corrosion protection of AA2024-T3 aluminum alloys. These obtained nanoparticles were characterized by x-ray diffraction, field-emission scanning electron microscopy, and Zeta potential measurements. Corrosion inhibition activities of Co₃O₄ and CoFe₂O₄ nanoparticles were determined by performing electrochemical measurements for bare AA2024-T3 aluminum alloys in 0.05 M NaCl + 0.1 M Na₂SO₄ solution containing Co₃O₄ or CoFe₂O₄ nanoparticles. Corrosion protection for AA2024-T3 aluminum alloys by a water-based epoxy with or without the synthesized Co₃O₄ or CoFe₂O₄ nanoparticles was investigated by electrochemical impedance spectroscopy during immersion in 0.1 M NaCl solution. The corrosion protection of epoxy coating deposited on the AA2024-T3 surface was improved by incorporating Co₃O₄ or CoFe₂O₄ nanoparticles in the coating. The corrosion protection performance of the epoxy coating containing CoFe₂O₄ was higher than that of the epoxy coating containing Co₃O₄.

• Tunnel and Underground Space
• /
• v.26 no.4
• /
• pp.304-315
• /
• 2016

In this study, the current horizontal stress characteristics of the Tertiary rock formations in the Pohang Basin are investigated on the basis of the in-situ rock stress measurements at depths from 75 m to 716 m of the 3 test boreholes in the Doumsan area, Pohang. The deep hydraulic fracturing stress measurement results indicated that the horizontal stress components in the test site appear far lower than the average ones by the linear fit for the data set measured from the other domestic sites. But, borehole scanning revealed clearly that lots of small and large scale borehole failures occurred due to the low strength characteristics of the existing rocks. To obtain more accurate and overall information on the horizontal stress direction, the integrated analysis combining the hydraulic fracturing stress measurement and borehole scanning data set were additionally carried out. The analysis results showed that in the upper sedimentary and the lower volcanic rock formation, the dominant orientations of the current maximum horizontal stress components were appeared in the range of $80^{\circ}{\sim}100^{\circ}$ (N80E~N80W) and $120^{\circ}{\sim}140^{\circ}$ (N60W~N40W), respectively. From this study result it was found that the maximum horizontal stress directions have a tendency to rotate in a clockwise direction as the rock formation changes with depth in the test site.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.6
• /
• pp.690-698
• /
• 2006

Statement of problems. The heat produced during polymerization of polymer-based provisional materials may cause thermal damage to the vital pulp. Purpose. This study was performed to evaluate the exotherm reaction of the polymerbased provisional materials during polymerization by differential scanning calorimetry and to compare the temperature changes of different types of resins. Material and methods. Three dimethacrylate-based materials (Protemp 3 Garant, Luxatemp Plus, Luxatemp Fluorescence) and five monomethacrylate- based material (Snap, Alike, Unifast TRAD, Duralay, Jet) were selected. Temperature changes of polymer-based provisional materials during polymerization in this study were evaluated by D.S.C Q-1000 (TA Instrument, Wilmington, DE, USA). The following three measurements were determined from the temperature versus time plot: (1) peak temperature, (2) time to reach peak temperature, (3) heat capacity. The data were statistically analyzed using one-way ANOVA and multiple comparison Bonferroni test at the significance level of 0.05. Results. The mean peak temperature was $39.5^{\circ}C({\pm}\;1.0)$. The peak temperature of the polymer-based provisional materials decreased in the following order: Duralay > Unifast TRAD, Alike > Jet > Luxatemp Plus, Protemp 3 Garant, Snap, Luxatemp Fluorescence. The mean time to reach peak temperature was 95.95 sec $({\pm}\;64.0)$. The mean time to reach peak temperature of the polymer-based provisional materials decreased in the following order: Snap, Jet > Duralay > Alike > Unifast TRAD > Luxatemp Plus, Protemp 3 Garant, Luxatemp Fluorescence. The mean heat capacity was 287.2 J/g $({\pm}\;107.68)$. The heat capacity of the polymer-based provisional materials decreased in the following order: Duralay > TRAD, Jet, Alike > Snap, Luxatemp Fluorescence, Protemp 3 Garant, Luxatemp Plus. Conclusion. The heat capacity of materials, determined by D.S.C., is a factor in determining the thermal insulating properties of restorative materials. The peak temperature of PMMA was significantly higher than others (PEMA, dimethacrylate). No significant differences were found among PEMA (Snap) and dimethacrylate (P >0.05). The time to reach peak temperature was greatest with PEMA, followed by PMMA and dimethacrylate. The heat capacity of PMMA was significantly higher than others (PEMA, dimethacrylate). No significant differences were found among PEMA and dimethacrylate (P >0.05).

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.22 no.3
• /
• pp.336-344
• /
• 2011

The purpose of this study is to analyze the radiation-pattern characteristics above 1 GHz for the electromagnetic wave radiated from multi-slot such as ventilations, etc. on the enclosure of an EUT and so to make recommendations for suitable test methods. An experimental EUT was formed by putting a comb-generator at the center of a rectangular enclosure with 4 slots, and its radiation pattern was analyzed in the frequency range of 1~6 GHz. As analysis results, multi-lobe appears above 2 GHz and the number of multi-lobes is growing as the frequency increases. And real radiated-emission measurements were performed for the experimental EUT by scanning a receiving antenna in the height of 1~4 m and tilting toward maximum radiation, as well as setting the height of a receiving antenna to the central position of the EUT which is prescribed at the present standards. The measured results are +12.8 dB in the scanning and +16.4 in the scanning and tilting compared with the present standard test method. Therefore, the latter must be revised in order to consider the radiation pattern above 1 GHz.