• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 제5회 압연심포지엄 신 시장 개척을 위한 압연기술
• /
• pp.63-71
• /
• 2004

Recently, a sheet forming process of Mg alloys is highlighted again due to increasing demand for Mg wrought alloys in the applications of casings of mobile electronics and outer-skins of light-weight transportation. Microstructure control is essential for the enhancement of workability and formability of Mg alloy sheets. In this research, AZ31 Mg alloy sheets were prepared by hot rolling process and the rolling condition dependency of the microstructure and texture evolution was studied by employing a conventional rolling mill as well as an asymmetric rolling mill. When rolled through multiple passes with a small reduction per pass, fine-grained and homogeneous microstructure evolved by repetitive dynamic and static recrystallization. With higher rolling temperature, dynamic recrystallization was initiated in lower reduction. However with increasing reduction per pass, deformation was locallized in band-like regions, which provided favorable nucleation sites f3r dynamic recrystallization. Through post annealing process, the microstructures could be transformed to more equiaxed and homogeneous grain structures. Textures of the rolled sheets were characterized by $\{0002\}$ basal plane textures and retained even after post annealing. On the other hand, asymmetrically rolled and subsequently annealed sheets exhibited unique annealing texture, where $\{0002\}$ orientation was rotated to some extent to the rolling direction and its intensity was reduced.

• Progress in Superconductivity
• /
• 제5권2호
• /
• pp.124-127
• /
• 2004

Many of research efforts have been focused on the improvement of critical current density (Jc) of silver-sheathed Bi-2223 tapes far practical applications. In this study, the transformation of Bi-2212 phase was investigated, which was transformed to orthorhombic from tetragonal through pre-annealing during powder packing and drawing process. The relationship between hardness of Bi-2212 orthorhombic phase and workability of Bi-2223/Ag tape was investigated. Bi-2223 superconducting wires with 55 filaments were fabricated by stacking and drawing process with different heat-treatment histories. Before rolling process, round wires were pre-annealing at 76$0^{\circ}C$ and in a low oxygen partial pressure. We confirmed that pre-annealing step was to transform to Bi-2212 orthorhombic structure from Bi-2212 tetragonal structure and to reduce the formation of second phases. However the breakages were created at Ag-alloy clad during rolling for pre-annealed Bi-22231Ag tapes. Several pre-annealing scenarios were introduced to reduce the breakages during rolling process. Microstructure and critical current density of pre-annealed Bi-2223 superconducting tapes were investigated. We could achieve proper pre-annealing conditions for Ag-alloy clad Bi-2223 superconducting tapes.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.80-81
• /
• 2009

Ti-6Al-4V alloy has been widely used for aerospace and power generation applications because of low density and attractive mechanical and corrosion resistant properties. However, the titanium alloy bolt is generally manufactured by cutting and rolling because of their poor workability. In order to achieve the mass production of titanium alloy bolts, it needs to be solved some manufacturing problems such as the sticking between workpiece and dies, the formation of the forming defects during the forging and so on. In this study, the manufacturing technology of titanium alloy bolts using warm forging process was introduced. The aim of present work is to develop a warm forging technology for high strength Ti-6Al-4V bolts.

• 한국초전도ㆍ저온공학회논문지
• /
• 제5권1호
• /
• pp.31-34
• /
• 2003

Bi-2223 superconducting wires with 55 filaments were fabricated by stacking, drawing process with different heat-treatment histories. Two kinds of powders were prepared. One was pre-annealed at 760-820 $^{\circ}C$ and low oxygen partial pressure, and the other was only calcined state. Before rolling process, round wires were pre-annealed at 760 -820 $^{\circ}C$ and in a low oxygen partial pressure. We confirmed that pre-annealing step was to transform Bi-2212 orthorhombic structure from Bi-2212 tetragonal structure and to reduce the formation of second phases at superconducting wire. However Bi-2223 phases were formed at higher pre-annealing temperature. Bi-2223 conductor was needed frequently annealing at low temperature because pre-annealing at precursor powder brought about decrease in workability. We could achieve highest Je of 6500 A/$\textrm{cm}^2$ at the tape using Bi-2212 orthorhombic phase by introduced slightly overheating at the 1st sintering process.

• 한국도로학회논문집
• /
• 제17권6호
• /
• pp.55-63
• /
• 2015

PURPOSES : The objective of this study is to investigate the properties of recycled asphalt binders with five different rejuvenators, in order to evaluate the applicability of the recycled asphalt binders compared with the original asphalt binder. METHODS : In order to simulate recycled asphalt binders, fresh asphalt binders are aged by various Superpave aging procedures, such as the rolling thin-film oven (RTFO) and the pressure aging vessel (PAV). Then, selected rejuvenators are added to the aged asphalt binders in the amount of 5%, 10%, and 15%. The asphalt binder properties are evaluated by the dynamic shear rheometer (DSR), the rotational viscometer (RV), and the bending beam rheometer (BBR). In this study, AP-5 (penetration grade 60-80, PG 64-16) asphalt binder is used. A total of five types of rejuvenators are employed. RESULTS AND CONCLUSIONS : When considering aged asphalt without a new asphalt binder, it seems that the percentage of rejuvenator used in Korea is a bit too low, and that it fails to possess the characteristics of the original binder. From the current practice of evaluating the properties of recycled binder based on penetration ratio only, the amount of rejuvenator required is similar for the long-term-aged binder, but is excessive for the longest-term aged binder, causing deterioration of workability and stiffness of the recycled binder.

• 전기화학회지
• /
• 제3권4호
• /
• pp.204-210
• /
• 2000

용융아연 도금 강판 제조시 용융아연 도금 bath중의 알루미늄 농도를 조절하는 것은 매우 중요하다 본 연구의 목적은 용융아연 도금욕 중 알루미늄 농도를 신속하게 측정할 수 있는 센서 개발을 위한 기초 data를 제공하는 것이다. $CaF_2$고체전해질과 3가지 종류의 참조극을 사용하여 $460^{\circ}C\~500^{\circ}C$의 순수한 용융아연 bath에서 불소포텐샬을 측정하였다. 용융 아연 중 알루미늄의 농도를 측정하기 위하여 다음과 같은 불소 이온 농담전지 센서를 구성하였다. $$(-)W|Zn-Al,\;AlF_3|CaF_2|Bi,BiF_3|W(+)$$ 알루미늄의 농도가 $0.984wt\%$이하인 Zn-Al bath의 온도를 $460\pm10^{\circ}C$로 유지하고 상기의 알루미늄 농도 센서를 이용하여 기전력을 측정하였다. 측정된 기전력 값으로부터 최소 자승 회귀분석법을 이용하여, 다음과 같은 알루미늄 농도와 기전력과의 관계식을 얻었다. $$E/mV=56.795log[\%Al]+1881.7\;R=0.9704$$,$$0.026wt\%{\leq}[\%Al]{\leq}0.984wt\%$$