• 한국기계가공학회지
• /
• 제11권5호
• /
• pp.13-20
• /
• 2012

In order to clarify the effect of overload on crack growth behaviors, fatigue tests for overload were carried out for round plain specimens of SM45C steel. In the experiment, typical semi-elliptical crack shape was found and further crack growth behaviors were tested. Using three types of single overload fatigue tests, Crack growth retardation phenomenon were examined. The growth rate of surface crack(da/dN) during retardation period was analyzed in terms of ${\Delta}K$ and ${\Delta}K_{eff}$. On the growth rate of surface crack analyzed by ${\Delta}K$, the dependence of overload stress levels appears. However, on the growth rate by ${\Delta}K_{eff}$ obtained by Willenborg analysis, there is a non-liner relationship between da/dN and ${\Delta}K_{eff}$ with narrow scatter band.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.1508-1512
• /
• 2003

In this study, retardation behavior of fatigue crack under single overloading of the mixed mode state was experimentally investigated. To produce single overload in the mixed mode I+II state, the compact tension shear (CTS) specimen and loading device were used. The propagation tests for fatigue crack were performed under mode I and mixed-mode loading overloading afterwards. We examined the observed deformation aspects, the variation of fatigue life and crack propagation rate, and the aspects of retardation behavior from tests. The retardation effect of mixed-mode single overload on fatigue crack propagation behavior was smaller than that of mode I single overload. Also the loading modes of variable and constant amplitude loads have influence on the retardation behavior of fatigue cracks.

• 한국기계가공학회지
• /
• 제11권4호
• /
• pp.82-89
• /
• 2012

In order to clarify the effect of overload on crack growth behaviors, fatigue tests for overload were carried out for round plain specimens of SM45C steel. In the experiment, typical semi-elliptical crack shape was found and further crack growth behaviors were tested. Using three types of single overload fatigue tests, Crack growth retardation phenomenon were examined. The growth rate of surface crack(da/dN) during retardation period was analyzed in terms of ${\Delta}K$ and ${\Delta}K_{eff}$. On the growth rate of surface crack analyzed by ${\Delta}K$, the dependence of overload stress levels appears. However, on the growth rate by ${\Delta}K_{eff}$ obtained by Willenborg analysis, there is a liner relationship between da/dN and ${\Delta}K_{eff}$ with narrow scatter band.

• 대한조선학회논문집
• /
• 제40권3호
• /
• pp.45-53
• /
• 2003

Ships and ocean structures are subjected to random loads caused by irregular waves. The irregularity of amplitude from random loading affects on fatigue crack growth and fatigue life. However the effects of irregularity of loading on fatigue including random loading have not been explained exactly. Therefore in this paper crack growth tests on DENT specimens under constant-amplitude loading including a single tensile overload are conducted to investigate the effect of overload on crack growth rate. The size of plastic zone and crack growth rate before and after a single tensile overloading are measured using ESPI system. Crack growth retardation model that is characterized by crack growth length and the size of plastic zone was proposed and compared with test result. From the research, the validity of proposed model is examined on crack growth retardation, and consequently fatigue life.

• 폴리머
• /
• 제34권3호
• /
• pp.220-225
• /
• 2010

폴리에테르설폰(PES) 필름의 주사슬 연신에 의한 광학 특성 변화와 보상 필름으로 사용 환경온도에 따른 이들의 특성변화를 살펴보았다. 아울러 연신 및 열처리가 필름의 광학 특성 및 치수안정성에 미치는 영향을 함께 확인하였다. PES는 연신에 의하여 광학용 보상 필름으로 사용이 가능할 정도의 $R_e$ 값과 $R_{th}$ 값을 얻을 수 있었으며 이러한 값들은 반복적인 사용 환경 온도에 따라 변화되며 이를 최소화하기 위하여 열처리 공정이 필요함을 알 수 있었다. 연신된 PES 필름은 사용온도가 증가됨에 따라 연신에 의한 주사슬의 수축이 발생되며 그 이후 고유 특성인 열팽창이 일어나며, 연신에 의한 주사슬 배향에 의하여 열팽창계수는 다소 감소함을 알 수 있었다. 필름의 열처리는 열팽창계수에는 크게 영향을 미치지 않는 반면 열수축을 현저하게 감소시킴을 확인하였다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1997년도 추계학술대회 논문집
• /
• pp.829-832
• /
• 1997

It is difficult to explain the effects of complex variable loading experienced by the machine and the structure only with the studies of the single-overload itself. Hence, it is thought that the variation of overload-holding time are required to explain the effects more clearly. The effects of the overload were analyzed by means of the crack retardation, and the fractography on retardation zone. A characteristic of the fractography on retardation zone was that striation distribution did not appear due to decreased crack driving force. Rotary bending fatigue tests were performed with the circular shaft which has two hole defects.

• 대한기계학회논문집
• /
• 제14권5호
• /
• pp.1193-1199
• /
• 1990

본 연구에서는 가공경화지수 (n)가 서로 다른 몇가지 재료를 선택하고 과대하 중의 비 (%PL)를 달리하는 단일 과대하중 피로 시험을 행하여 재료의 가공경화지수가 피로 균열 진파의 지연거동에 미치는 영향과 아울러 균열닫힘현상과의 관계를 구명하였다.

• 한국안전학회지
• /
• 제7권2호
• /
• pp.47-56
• /
• 1992

The retardation effect of fatigue crack propagation after cyclic overloading seems to be affected by strain hardening exponent. Namely, for the material with high values of n, the delay effect is found to be severe. We proposed a modified crack retardation equation which may apply the retardation of fatigue crack growth after a cyclic overloading, as (da/dN)'$_{cyc}$=($\mu$n＋λ)B $\Delta$ $K^{q}$ /[(1－ $R_{eff}$) $K_{cf}$ －$\Delta$K]. where, $R_{eff}$ is effective stress ratio [＝( $K_{min}$－K, os)/( $K_{max}$－ $K_{res}$)] The constants $\mu$＝－0.5 and λ＝0.6, and the values are found to be identical for materials such as aluminum (A 1060), steel (SS 34), brass ( $B_{s}$ SIB) and stainless steel (SUS 304) used in this investigation. (SUS 304) used in this investigation.ation.n.n.

• Current Optics and Photonics
• /
• 제5권1호
• /
• pp.45-51
• /
• 2021

The effect of the out-of-plane retardation (Rth) of a substrate film on the viewing-angle dependence of transmittance (TR) in a display device was investigated. When the polarization state of input light deviates from the transmission axis of the polarizer, Rth of the substrate film induces inhomogeneous viewing-angle dependence of TR. The inhomogeneity of TR gets worse for greater values of of Rth. The inhomogeneous TR profile can be eliminated by inserting compensation films, which convert the input polarization state to the linear polarization state parallel to the transmission axis of the polarizer.

• 한국지하수토양환경학회:학술대회논문집
• /
• 한국지하수토양환경학회 1998년도 총회 및 춘계 학술발표회 논문집
• /
• pp.43-49
• /
• 1998

Retardation effect of heavy metals in soils caused by adsorption onto the surfaces of solids particles is well known phenomena. The adsorption of metal ions has been recognized more strong in clay mineral and organic matter contents rather than sands and gravels. In this study, we investigated the retardation effect in two sandy soils by conducting batch and column tests. The column tests were conducted to obtain the relationship between concentration and time known as breakthrough curve (BTC). We applied pulse type injection of ZnCl$_2$solution on the inlet boundary and monitored the effluent concentration at the exit boundary under steady state condition using EC-meter and ICP-AES. Batch test consisted of an equilibrium procedure for fine fractions collected from two sandy soils for various initial ZnCl$_2$concentrations, and analysis of Zn ions in equilibrated solution using ICP-AES. The results of column test showed that i) the peak concentration of Zn analyzed by ICP was far less than that detected by EC-meter for both soils and ii) travel times for peak concentration were more less identical for two different monitoring techniques. The first result can be explained by ion exchange between Zn and other cations initially present in the soil particles since ICP analysis showed a significant amount of Ca, Mg ions in the effluent. From the second result, we found that retardation effect was not present in these soils due to strong cation exchange capacity of Zn ion over other cations since we did not apply a solution containing more adsorptive cations such as Al. The result of batch test also showed high distribution coefficients (K$_{d}$) for two soils supporting the dominant ion exchange phenomena. Based on the retardation factor obtained from the Kd, we predicted the BTC using CDE model and compared with the BTC of Zn concentration obtained from ICP The predicted BTC, however, disagreed with the monitored in terms of travel time and magnitude of the peak concentrations. The only way to describe the prominent decrease of Zn ion was to introduce decay or sink coefficient in the CDE model to account for irreversible decrease of Zn ions in liquid phase.e.