• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.627-632
• /
• 1995

W-Cu composites utilize the high electrical conductivity of copper and arc erosion resistance of tungsten to provide properties better suited to electrical contact applications than either tungsten or copper alone. W-Cu composite materials were milled in an attritor with an impeller speed of 300rpm for various milling times. The milled powders were compacted at 300MPa into cylinders, 16m in diameter, and approximately 4m high. Sintering was performed in dry H$_2$at temperature ranging from 1200$^{\circ}C$ to 1400$^{\circ}C$. Samples were sectioned and were polished for scanning electron microscopy (SEM) of microstructures. Homogeneous W-Cu composites were formed after 10 hours mechanical alloying and could be attained 99% density at 1330$^{\circ}C$. As mechanical alloying time increased, Fe-concentration was increased linearly. Intermetallic compound formation interupted the growth of W particles Increased hardness.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.3
• /
• pp.118-123
• /
• 2006

Degradation of polymer electrolyte membrane fuel cell (PEMFC) that is facilitated by on/off cycles is one of the most important issues for commercialization of fuel cell vehicles. When a PEMFC stack is shut down, residual hydrogen and induce high voltage equivalent to open circuit voltage to the cathode side that might cause sintering of Pt catalyst and facilitate formation of hydrogen peroxide at the anode side that might decompose $Nafionc\'{A}$ membrane. In this study, degradation of PEMFC exposed to repetitive on/off cycles was investigated by measuring i-V characteristics, ac impedance, cyclic voltammograms, gas leak, cross-sectional SEM images, and TEM images. To prevent degradation of PEMFC caused by the residual gases, hydrogen was removed from anode gas channel by gas-purging and by using a dummy resistance, that were found to be a very effective method.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.66 no.7
• /
• pp.1141-1148
• /
• 2017

Generally, a thermistor made by sintering a metal oxide is widely used to measure the ambient temperature. This thermistor is widely used not only for industrial use but also for medical use because of its excellent sensitivity, durability, temperature change characteristics and low cost. In particular, the normal body temperature is 36.9 degrees relative to the armpit temperature, and it is most closely related to the circulating blood flow. Previous studies have shown that body temperature changes during biomechanical changes and body temperature changes by anomalous signs or illnesses. Therefore, in this study, we propose a Lock-In-Amp design to detect minute temperature changes of clothing and thermistor wired by a preacher as a method to regularly measure body temperature in daily life. Especially, it is designed to measure the minute resistance change of the thermistor according to body temperature change even in a low-cost microprocessor environment by using a micro-processor-based Lock-In-Amp, and a jacquard and the thermistor is arranged so as to be close to the side, so that the reference body temperature can be easily measured. The temperature was measured and stored in real time using short-range wireless communication for non - restraint temperature monitoring. A baby vest was made to verify its performance through temperature experiments for infants. The measurement of infant body temperature through the existing skin sensor or thermometer has limitations in monitoring infant body temperature for a long time without restriction. However, it can be overcome by using the embroidery fabric based micro temperature monitoring wireless monitoring device proposed in this study.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.5
• /
• pp.221-225
• /
• 2001

The effect of $Al_2O_3+Y_2O_3$ additives on fracture toughness of ${\beta}-SiC-TiB_2$ composites by hot-pressed sintering was investigated. The ${\beta}-SiC-TiB_2$ ceramic composites were hot-press sintered and pressureless-annealed by adding 16, 20, 24 wt% ${\beta}-SiC-TiB_2$(6:4 wt%) powder as a liquid forming additives at low temperature(1800 $^{\circ}C$) for 4 h. Phase analysis of composites by XRD revealed mostly of ${\alpha}$-SiC(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$). The relative density was over 95-88 % of the theoretical density, and the porosity increased with increasing $Al_2O_3+Y_2O_3$ contents because of the increasing tendency of pore formation. The fracture toughness showed the highest value of 5.88 MPa${\cdot}m^{1/2}$ for composites added with 20 wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity showed the lowest value of $5.22{\times}10^{-4}\;{\Omega}\;{\cdot}\;cm$ for composite added with 20 wt% $Al_2O_3+Y_2O_3$ additives at room temperature, and was all positive temperature coefficeint resistance(PTCR) against temperature up to 900 $^{\circ}C$.

• Proceedings of the KIEE Conference
• /
• 2007.11a
• /
• pp.124-125
• /
• 2007

The composites were fabricated $\beta$-SiC and $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at $1,650[^{\circ}C]$ for 4 hours. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[MPa], 54.60 [GPa] and 2.84[GPa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. The electrical resistivity showed the lowest value of 0.012[${\Omega}{\cdot}cm$] for 16[wt%] at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from 25[$^{\circ}C$] to 700[$^{\circ}C$].

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.4
• /
• pp.181-184
• /
• 2017

Multilayer ceramics in which piezoelectric layers of $0.90Pb(Zr_{0.48}Ti_{0.52})O_3-0.05Pb(Mn_{1/3}Sb_{2/3})O_3-0.05Pb(Zn_{1/3}Nb_{2/3})O_3$ (0.90PZT-0.05PMS-0.05PZN) stack alternately with silver electrode layers were prepared by an advanced low-temperature co-fired ceramic (LTCC) method. The electrical properties and bonding strength of the multilayers were associated with the interface morphologies between the piezoelectric and silver-electrode layers. Usually, the inner silver electrodes are fabricated by sintering silver paste in multi-layer stacks. To improve the interface bonding strength, piezoelectric powders of 0.90PZT-0.05PMS-0.05PZN with an average particle size of $23{\mu}m$ were added to silver paste to form a gradient interface. SEM observation indicated clear interfaces in multilayer ceramics without powder addition. With the increase of piezoelectric powder addition in the silver paste, gradient interfaces were successfully obtained. The multilayer ceramics with gradient interfaces present greater bonding strength as well as excellent piezoelectric properties for 30~40 wt% of added powder. On the other hand, over addition greatly increased the resistance of the inner silver electrodes, leading to a piezoelectric behavior like that of bulk ceramics in multilayers.

• Korean Journal of Metals and Materials
• /
• v.48 no.7
• /
• pp.625-629
• /
• 2010

This study investigates the effects of porosity on the thermal stability and the thermal shock resistance of a porous nozzle used for blowing an inert gas. The samples of $Al_2O_3-SiO_2-ZrO_2$ system, which had the apparent porosity of 16~30% and bulk density of $2.6{\sim}3.2g/cm^3$, were prepared by adding different graphite contents (5, 10, 20 wt%) as a pore-forming agent. The thermal shock test was conducted at ${\Delta}T=500$, 1000, and $1400^{\circ}C$ also and the thermal stability was also carried out at 1550, 1600, and $1650^{\circ}C$ for 5 hrs. The specimen contained 10 wt% graphite had uniform pore size distribution, whereas the specimen with 20 wt% graphite showed non-uniform pore size distribution. As a result of thermal shock test, the specimen containing 10 wt% graphite appears to have higher mechanical strength than the other specimens (5, 20 wt% graphite). Both the 5 wt% and 20 wt% graphite specimens developed a non-uniform pore size distribution and cracks that were generated by intensive thermal stress.

• Industry Promotion Research
• /
• v.6 no.4
• /
• pp.1-9
• /
• 2021

The purpose of this study is to manufacture lightweight aggregates for recycling water treatment sludge, to identify the physical properties of the aggregates, and present a method of utilizing the manufactured lightweight aggregates. The chemical composition and thermal properties were examined via a raw materials analysis. The aggregate examined here was fired by the rapid sintering method and the single-particle density and water absorption rate were measured. Water treatment sludge has high ignition loss and high fire resistance. When 30wt% of purified sludge was added, the single-particle density of the aggregates was in the range of 0.8~1.2g/cm³ at a temperature of 1,150~1,200℃. At temperatures of 1200℃ or higher, ultra-light aggregates having a single-particle density of 0.8 or less could be produced. When applied to concrete by replacing the general aggregate in the concrete, a specimen having strength values of 200 to 450 kgf/cm² on 28 days was obtained, and when applied as a filter material, the performance was equal to or higher than that of ordinary sand.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.35 no.3
• /
• pp.292-296
• /
• 2022

(La_0.5Nd_0.2Sr_0.3)MnO₃ specimens were prepared by a solid-state reaction. In all specimens, X-ray diffraction patterns of an orthorhombic structure were shown. The fracture surfaces of (La_0.5Nd_0.2Sr_0.3)MnO₃ specimens showed a transgranular fracture pattern be possibly due to La ions (0.122 nm) as a perovskite A-site dopant substituting for Nd ions (0.115 nm) having a small ionic radius. The full-width at half maximum (FWHM) of the Mn 2p XPS spectra showed a value greater than that [8] of the single valence state, which is believed to be due to the overlapping of Mn²⁺, Mn³⁺, and Mn⁴⁺ ions. The dependence of Mn 2p spectra on the Mn³⁺/Mn⁴⁺ ratio according to sintering time was not observed. Electrical resistivity resulted in the minimum value of 100.7 Ω-cm for the specimen sintered for 9 hours. All specimens show a typical negative temperature coefficient of resistance (NTCR) characteristics. In the 9-hour sintered specimen, TCR, activation energy, and B25/65-value were -1.24%/℃, 0.19 eV, and 2,445 K, respectively.

• The Journal of Korean Academy of Prosthodontics
• /
• v.60 no.3
• /
• pp.293-300
• /
• 2022

Various materials and restorative options have been introduced recently with growing interest in esthetic dental treatment in modern society. Zirconia is especially known for its biocompatibility as well as remarkable toughness and resistance to wear, but it is limited in its use for esthetically focused treatment in anterior region for its white opacity. Lately the development of different kinds of zirconium blocks, such as colored block, clear block, and multi-layered block, allowed more extensive use of zirconia as a treatment option. This report describes a case, in which a prosthetic crown maxillary anterior region was stained with a combination of various coloring liquids before sintering to reproduce natural-looking color scheme in final restoration. The case was reported as the utilization of coloring liquid on monolithic zirconia crown could achieve esthetically satisfying prosthesis for both dentist and patient.