• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.495-498
• /
• 2005

It was investigated the durability of the concrete to improve construction materials with polymer cement mortar in this study. With the popularity of repair and rehabilitation material, some mixtures composed of Ethylene Vinyl Acetate(EVA) was studied. Ethylene Vinyl Acetate(EVA) carried out tests to determine its properties which a include: freezing-thawing resistance test, carbonation test, and chemical resistance test. Result of freezing-thawing resistance test, mass change ratio and chemical resistance test, mass change ratio decreased of 12 and $15\~45\%$ as compared with control mortar. Carbonation depth decreased $3.7\~5.6mm$ as polymer-cement ratio increased $1\~4\%$.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.3
• /
• pp.265-271
• /
• 2014

It is strongly needed to investigate the fine sand as an alternative fine aggregate of well-graded river sand because the fine sand which is being enormously distributed in the midstream and downstream of Nakdong-River in Korea has a poor grading but good quality as a fine aggregate for concrete. Thus, the purpose of this experimental research is to evaluate the durability of concrete using the fine sand to utilize it actively as a fine aggregate. For this purpose, the concrete specimens using different fine sand were made for the specified concrete strength of 35MPa, and then their durability such as the resistance to freezing and thawing and carbonation, and drying shrinkage were evaluated. It was observed from the test results that the resistance to freezing and thawing and carbonation of concrete using the fine sand was similar to that of concrete using reference sand, but the drying shrinkage of concrete using the fine sand with small fineness was comparatively lager than that of concrete using reference sand.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.170-176
• /
• 1997

The published works on steam curing effect have been generally concentrated on the subject, "compressive strength". However a practical test for durable steam curing concrete products has not been performed in domestic. In this study, the maximum temperature of steam is considered as a major variable to investigate the freezing and thawing resistance of the steam curing concrete. All of the specimen were cured for 24 hours which included presteaming 4 hour. Finally we found that the most effective curing condition is the case of one-day and 14-day specimens after the 24 hours steam curing at $74^{\cire}C$ degree curing temperature. It is also found that the durability of one-day samples are much weaker than those of 14-day samples. Consequently, we can conclude that the samples that produced immediately after a steam curing are more possible to deteriorate from the freezing and thawing environment.vironment.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.52 no.3
• /
• pp.9-17
• /
• 2010

This study aims to evaluate a porous concrete using hwang-toh, blast furnace slag and blast furnace slag (BFS) cement instead of type I cement. The tests that were carried out to analysis the properties of porous hwang-toh BFS cement concrete included compressive strength, continuous void ratio, absorption rate, and pH value, repeated freezing and thawing test were conducted. Test results indicated that the performance in porous hwang-toh concrete are effective on the kaoline based binder materials. The pH value were shown in about 9.5 ~ 8.5. The compressive strength was increased and void ratio was decreased with increasing the kaoline based binder materials, respectively. The void ratio and compressive strength were in the range of about 21 ~ 30 %, 8 ~ 13 MPa, respectively. The increased in void ratio of more than 25 % is showed to reduce the resistance of repeated freezing and thawing. Also, the resistance of repeated freezing of thawing and the compressive strength of porous hwang-toh BFS cement concrete are independent with hwang-toh content and BFS cement amount. But, the void ratio was decreased with increasing the high volume hwang-toh contents (more than 15 %).

• Journal of The Korean Society of Agricultural Engineers
• /
• v.55 no.2
• /
• pp.65-75
• /
• 2013

In this study, the engineering characteristics of volcanic ash-cement soil mixtures and zeolite-cement soil mixtures are investigated by using unconfined compression test, freezing-thawing test, SEM and XRD analysis. The samples were mixed with volcanic ash from Mt. Baekdusan or porous zeolite, and cement as the ratios of 3.5:1, 4.0:1, 4.5:1, 5.0:1 with and without metakaolin. It is confirmed that compressive strength degraded with increasing of the amount of volcanic ash or zeolite, and increased with addition of metakaolin as a binder. Moreover, test results suggested that the mixtures provided sufficient freezing-thawing resistance. In addition, ettringite as a product of cement hydration was detected by SEM and XRD, and that possibly contributes to the strength of the mixtures.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.4
• /
• pp.153-161
• /
• 1998

Concrete structures has been deteriorated by and freezing the thawing due to temperature gap. This study was conducted to evaluate durability of concrete which are increasingly demanded recently. Therefore the research of durability must be executed for application of waste foundry sand concrete real structures. Concrete durability properties incorporating waste foundry sand was performed with the variable of W/C ratio. Sand/Waste foundry sand ratio and Air entrainment-Non air entrainment. Cylinder specimens were made and subjected to freezing and thawing cycle at -18$^{\circ}C$ and 4$^{\circ}C$. Dynamic modulus of elasticity were evaluated as F/T cycle increase. The results show that strength of concrete is increased the W/C ratio decrease, the Sand/Waste foundry sand ratio increases when the concrete contains AE agent and decreasing W/C ratio and AE concrete makes improved resistance of freezing and thawing improved. Especially, resistance of freezing and thawing is improved by Fine aggregate/Waste foundry sand ratio which is 50%, 25%, 0% in a row. Therefore it is turn out the waste foundry sand could be applied to concrete from the experiment.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.2
• /
• pp.171-175
• /
• 2010

This paper presents the experimental results of frost durability characteristics including freezing-thawing and de-icing salt scaling of the concrete for gutter of the road and marine structure. Mixtures were proportioned with the three level of water-binder ratio(W/B) and three binder compositions corresponding to Type I cement with 0%, 30% and 50% GGBS(Ground granulated blast furnace slag) replacement. Also, two different solutions of calcium chloride were used to evaluate their effect on the frost durability resistance. Specially, in case of complex of freezing and thawing with salt and carbonation, the deterioration of concrete surface is evaluated. Test results showed that the BFS30 and BFS50 mixture exhibited higher durability and lower mass loss values than those made with OPC mix and the use of GGBS can be used effectively in terms of economy and frost durability of the concrete to be in complex deterioration. Therefore, the resistance to complex deterioration with freezing-thawing was strongly influenced by the strength and the type of cement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.79-87
• /
• 2011

Concrete incorporating high volume blast-furnace slag placed in cold weather regions might be in danger of initial frost damage because dependently on the mix proportions, the setting and the hardening would be remarkably delayed. Therefore, this study investigated to effect of the degree of frost on the strength development and the resistance to freezing and thawing of the concrete incorporating blast-furnace slag when being subjected to freeze at early age. As the experimental results, the concrete incorporating blast-furnace slag attacked by initial frost damage showed the remarkable reduction of both the compressive strength development and the resistance to freezing and thawing. Especially, the resistance to freezing-thawing of the concrete incorporating high volume blast-furnace slag became much lower than that of the normal concrete.

• Resources Recycling
• /
• v.15 no.4 s.72
• /
• pp.52-59
• /
• 2006

The purpose of this study was to evaluate the effects of ground granulated blast-furnace slag on strength development and durability of ordinary portland cement concrete (OPC) with steam curing types. Main experimental variables were slag contents(0%, 10%, 30%, 50%, 70%) and curing types (standard, accelerated curing). It were performed to check the basic properties of concretes that compressive strength, rapid chloride ion permeability and chemical resistance. From the result, we have found that increasing the amount of blast-furnace slag produced concrete with increased compressive strength and permeability resistance. Rapid freezing-thawing test showed that they were good enough to protect the concrete structures and to carry out cyclic freezing and thawing. The freeze-thaw resistance of blast-furnace slag produced concretes maintained above 90% of relative dynamic modulus after 300 freezing-thawing cycles. Increasing the amount of blast-furnace slag produced concretes with increased chemical resistance.

• International Journal of Highway Engineering
• /
• v.18 no.1
• /
• pp.63-72
• /
• 2016

PURPOSES : The use of roller-compacted concrete pavement (RCCP) is an environmentally friendly method of construction that utilizes the aggregate interlock effect by means of a hydration reaction and roller compacting, demonstrating a superb structural performance with a relatively small unit water content and unit cement content. However, even if an excellent structural performance was secured through a previous study, the verification research on the environmental load and long-term durability was conducted under unsatisfactory conditions. In order to secure longterm durability, the construction of an appropriate internal air-void structure is required. In this study, a method of improving the long-term durability of RCCP will be suggested by analyzing the internal air-void structure and relevant durability of roller-compacted concrete. METHODS : The method of improving the long-term durability involves measurements of the air content, air voids, and air-spacing factor in RCCP that experiences a change in terms of the kind of air-entraining agent and chemical admixture proportions. This test should be conducted on the basis of test criteria such as ASTM C 457, 672, and KS F 2456. RESULTS : Freezing, thawing, and scaling resistance tests of roller compacted concrete without a chemical admixture showed that it was weak. However, as a result of conducting air entraining (AE) with an AE agent, a large amount of air was distributed with a range of 2~3%, and an air void spacing factor ranging from 200 to $300{\mu}m$ (close to $250{\mu}m$) coming from PCA was secured. Accordingly, the freezing and thawing resistance was improved, with a relative dynamic elastic modulus of more than 80%, and the scaling resistance was improved under the appropriate AE agent content rate. CONCLUSIONS : The long-term durability of RCCP has a direct relationship with the air-void spacing factor, and it can be secured only by ensuring the air void spacing factor through air entraining with the inclusion of an AE agent.