• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.5
• /
• pp.556-575
• /
• 2001

For the improvement of denture fitness of changed residual ridge, denture liner can be used. Denture liner should be very stable physically in various environments of the mouth as well as be bonded strongly with denture resin. In this study. the specimens bonded with four kinds of soft denture liner and three kinds of hard denture liner were used to test the physical properties of the liners. All experimental groups were stored in $37{\pm}1^{\circ}C$ distilled water for 24hours, followed by thermocycling between $15^{\circ}C$ and $45^{\circ}C$ with 15 second dwell time. 1000, 2000, 3000 cycles of thermocycling were excuted and physical properties were measured by Instron Universal Testing Machine. The obtained results were as follows : 1. In tensile bond test of sea liners, it was shown that both of $Molloplast-B^{(R)}$ specimens before and after thermocycling had the highest tensile strength, and in case of hard liners, Dura-Liner $II^{(R)}$ specimen had the highest tensile strength before and after thermocycling. Depending on thermocycling, $Soft-Relining^{(R)}$, $Denture-Relining^{(R)}$, $Molloplast-B^{(R)}$, $Coe-Soft^{(R)}$ and $Kooliner^{(R)}$ specimen showed significant difference(p<0.05). 2. In strain test of soft liners, it was shown that $Molloplast-B^{(R)}$ specimen before thermocycling and the $Coe-Soft^{(R)}$ after thermocycling showed highest results, and in case of hard liners, the Dura-Liner $II^{(R)}$ specimen before and after thermocycling had the highest result. Depending on thormocycling, $Denture-Relining^{(R)}$, $Molloplast-B^{(R)}$ and Dura-Liner $II^{(R)}$ specimen showed significant difference(p<0.05). 3. In maximum distance test of soft liners. the $Molloplast-B^{(R)}$ specimen before thermocycling and the $Coe-Soft^{(R)}$ after thermocycling showed highest results. and in case of hard liners, the Dura-Liner $II^{(R)}$ specimen before and after thermocycling showed highest result. Depending on thermocycling, $Denture-Relining^{(R)}$, $Molloplast-B^{(R)}$ specimens showed significant difference(p<0.05). 4. In elasticity test of soft liners, the $Molloplast-B^{(R)}$ specimen before and after thermocycling showed highest result. and in case of hard liners, the Dura-Liner $II^{(R)}$ specimen before thermocycling and the $Tokuso-Rebase^{(R)}$ after thermocycling showed highest results. Depending on thermocycling, $Soft-Relining^{(R)}$ $Molloplast-B^{(R)}$ specimens showed significant difference (p<0.05).

• The Journal of Korean Academy of Prosthodontics
• /
• v.54 no.1
• /
• pp.49-56
• /
• 2016

Excessive occlusal wear can result in unacceptable damage to the residual teeth structure, anterior guidance and masticatory function. An 86-year-old man presented with worn dentition and anterior deep bite due to loss of the posterior support. Two implants covered by Korean national health insurance, fixed partial denture and direct composite resin were used to restore the dentition, instead of removable prosthesis. The occlusal vertical dimension was increased by 2 mm in the premolar area and shortened dental arch concept was applied. This treatment was a less expensive alternative to full-mouth rehabilitation with positive esthetic and functional outcomes after 7 months of follow-up.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2006.05a
• /
• pp.90-94
• /
• 2006

The waste solution discharged from the LCD manufacturing process contains acids like nitric, acetic and phosphoric acid and metal ions such as Al, Mo and other impurities. It is important to removal of impurities to tess than 1ppm in phosphoric acid to reuse as an etchant because the residual impurities even in sub-ppm concentration in semiconductor materials play a major role on the electronic properties. In this study, we have been clearly established that a mixed system of solvent extraction, diffusion dialysis and ion-exchange technique, which made individually the most of characteristics is developed to commercialize in an efficient system for recovering the high-purity phosphoric acid. By applying vacuum evaporation, the yield of the process are almost 99% removal of nitric acid and acetic acid was achieved. And by applying the solvent extraction method with tri-octyl phosphate(TOP) as an extractant, the removal of acetic and nitric acid from the acid mixture was achieved effectively at the ratio O/A=1/3 with four stages and the stripping of nitric acid from organic phase is attained at a ration of O/A=1 with six stages by distilled water. About 97% and 76% removal of Al and Mo were achieved by diffusion dialysis. Essentially complete less than 1ppm removal of Al, Mo by using ion exchange ion resin and purification of the phosphoric acid was obtain.

• The Journal of Korean Academy of Prosthodontics
• /
• v.59 no.3
• /
• pp.319-332
• /
• 2021

With the rapid development of aesthetic ceramic materials and resin adhesives, the transition from metal ceramic crown to all-ceramic restoration is being actively carried out. When making porcelain restorations, the advantages can be maximized only when appropriate forms and techniques are used. Recently, an esthetic partial-coverage restoration method with supra-gingival margins was introduced by applying a minimally invasive tooth removal method that preserves enamel as much as possible and enhances adhesion efficiency. Through this, various advantages such as minimization of tooth structure removal and ease of excess cement removal can be obtained. In addition, since this manufacturing method does not require cord packing, it is possible to save time for impression taking and reduce patient discomfort. Furthermore, the margins can be clearly obtained without the intervention of gingival fluid or blood, making it possible to manufacture more accurate restorations. In the following cases of patients with partial tooth defects, esthetic ceramic partial-coverage restorations with supra-gingival margin was applied using minimally invasive tooth preparation method according to the concept of adhesive dentistry. Therefore, unnecessary tooth abutment preparation was prevented and residual tooth structure could be preserved as much as possible. After delivery of the ceramic partial-coverage restorations, favorable outcome was obtained.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.37 no.1
• /
• pp.1-15
• /
• 2021

Additive manufacturing (AM) for dental materials can produce more complex forms than conventional manufacturing methods. Compared to milling processing, AM consumes less equipment and materials, making sustainability an advantage. AM can be categorized into 7 types. Polymers made by vat polymerization are the most suitable material for AM due to superior mechanical properties and internal fit compared to conventional self-polymerizing methods. However, polymers are mainly used as provisional restoration due to their relatively low mechanical strength. Metal AM uses powder bed fusion methods and has higher fracture toughness and density than castings, but has higher residual stress, which requires research on post-processing methods to remove them. AM for ceramic use vat polymerization of materials mixed with ceramic powder and resin polymer. The ceramic materials for AM needs complex post-processing such as debinding of polymer and sintering. The low mechanical strength and volumetric accuracy of the products made by AM must be improved to be commercialized. AM requires more research to find the most suitable fabrication process conditions, as the mechanical properties and surface of any material will vary depending on the processing condition.

• Journal of the Korean Wood Science and Technology
• /
• v.30 no.2
• /
• pp.172-179
• /
• 2002

In this study, two materials treated with a flame retardant were examined for their fire resistance. The first, MDF (medium density fiberboard) was overlaid by an oak sliced veneer, which was either treated by soaking in a 6wt.% solution of flame retardant chemicals (pentabromine-chlorinated paraffin) or non-treated and then was coated with either a flame retardant polyurethane coating or with a common polyurethane coating. The second material, Pinus koraiensis penal was either treated by a spray treatment using a flame retardant solution or non-treated and then was coated with either a flame retardant polyurethane coating or with a common polyurethane coating. Pentabromine-chorinated paraffin chemicals were added (6 part of urethane resin) as the flame retardant chemicals in the polyurethane coatings. In the fire resistance test, the th𝜃(℃·min) decreased with the flame retardant treatment or/and the flame retardant coatings, compared to the untreated sample Weight loss (%) decreased with the flame retardant treatment or/and the flame retardant coatings. The ignition time (sec.) increased and the residual flame time (sec.) decreased with the flame retardant treatment or/and flame retardant coatings. Therefore, the flame retardant treatment or/and flame retardant polyurethane coatings have excellent incombustibility.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.1
• /
• pp.17-25
• /
• 2013

Thermal storage technology used for indoor heating and cooling to maintain a constant temperature for a long period of time has an advantage of raising energy use efficiency. This, the phase changing material, which utilizes heat storage properties of the substances, capsulizes substances that melt at a constant temperature. This is applied to construction materials to block or save energy due to heat storage and heat protection during the process in which substances melt or freeze according to the indoor or outdoor temperature. The micro-encapsulation method is used to create thermal storage from phase changing material. This method can be broadly classified in 3 ways: chemical method, physical and chemical method and physical and mechanical method. In the physical and chemical method, a wet process using the micro-encapsulation process utilized. This process emulsifies the core material in a solvent then coats the monomer polymer on the wall of the emulsion to harden it. In this process, a surfactant is utilized to enhance the performance of the emulsion of the core material and the coating of the wall monomer. The performance of the micro-encapsulation, especially the coating thickness of the wall material and the uniformity of the coating, is largely dependent on the characteristics of the surfactant. This research compares the performance of the micro-capsules and heat storage for product according to molecular mass and concentration of the surfactant, SSMA (sulfonated styrene-maleic anhydride), when it comes to micro-encapsulation through interfacial polymerization, in which Dodecan-1 is transformed to melamin resin, a heat storage material using phase changing properties. In addition, the thickness of the micro-encapsulation wall material and residual melamine were reduced by adjusting the concentration of melamin resin microcapsules.

• Applied Biological Chemistry
• /
• v.15 no.2
• /
• pp.111-142
• /
• 1972

An experimental Chung-Kook-Jang was prepared using the strain Bacillus subtilis sp. isolated by the author Samples were taken in 12 hrs interval during the fermentation and the oligopeptides were separated by the method of molecular sieving using the ion exchange resin column of Dowex-50. Only the X-16 fraction of oligopeptides was taken and the components of oligopeptides were developed in two dimensional thin layer chromatograms. The each peptide spot was eluted and each peptide was isolated. The pattern and kinds of amino acids, and N and C-terminal amino acids were studied. Fourteen different oligopeptides could be detected by the two dimensional thin layer chromatography, all of which were consisted of $4{\sim}9$ kinds of amino acids. No dipeptides and no tripeptides could be found. The N and C-terminal amino acids and the residual component amino acids of all these 14 peptides could be summarized as the follows. [P]-I. Pro (Cys Ala Asp Trp Ile Val) Glu [P]-II. Val (His Arg Glu Thr Ala Met) Asp [P]-III. Glu (Cys Lys Asp Thr Met) Ala [P]-IV. Glu(His Ser Ala) Met) [P]-V. Ile (Cys Asp Arg Gly Pro T.p Phe) His [P]-VI. Gly(Asp ser) Lys [P]-VII. Thr(Pro Tyr Phe) Asp [P]-VIII. Phe(Tyr Leu Ile) Val [P]-IX. Trp (Phelle) Thr [P]-X. Ile (Arg Leu) Phe [P]-XI. Asp (Lys His Ser Gly Glu Pro) Ala [P]-XII. Glu (Cys Asp Gly) Ser [P]-XIII. Ala (Arg Tyr) Glu [P]-XIV. Met (Glu Ala) His It appears that the protease of the Bacillus subtilis K-27 syrain has rather wider range of specificity than proteases of Aspergoillus soya, pepsin, chymotrypsin, and trypsin.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.4
• /
• pp.595-603
• /
• 2005

Incomplete removal of bacteria contaminated dentin or enamel associated with caries is a potential problem in restorative dentistry Secondary or residual caries, pulpal inflammation and hypersensitivity may result from bacteria left after the initial preparation, especially if an adequate seal against microleakage is not obtained. A possible solution to eliminate residual bacteria left in a cavity preparation would be to treat the cavity with cavity disinfectant wash. But a potential problem with using a cavity disinfectant with dentin bonding agents could be their interference with the ability of the resin to bond to the tooth micromechanically. The purpose of this study was to evaluate the effect of 2% chlorhexidine containing cavity disinfectant ($Consepsis^{(R)}$) on shear bond strength and microleakage of dentin bonding agents, $Adper ^{TM}$ $Scotchbond^{TM}$ Multi-Purpose, $Adper^{TM}$ Single Bond and $Adper^{TM}\;Prompt^{TM}\; L-Pop^{TM}$ Sixty and sixty sound human third molar teeth, respectively, were used for shear bond strength and microleakage test. For experimental group, cavity disinfectant was applied before dentin bonding agents, and was not applied for the control group. The result from the this study can be summarized as follows ; 1. Use of 2% chlorhexidine containing cavity disinfectant($Consepsis^{(R)}$) does not significantly affect the shear bond strength of dentin bonding agents. 2. Use of 2% chlorhexidine containing cavity disinfectant($Consepsis^{(R)}$) does not significantly affect the microleakage of dentin bonding agents.

• The korean journal of orthodontics
• /
• v.34 no.4 s.105
• /
• pp.325-332
• /
• 2004

A self-etching primer that combines the etchant and primer in one chemical compound saves time and should be mote cost-effective to the clinician and patient. The purpose of this study was to evaluate the clinical effectiveness of a self-etching primer by measuring shear bond strengths according to various conditions and observing adhesive failure patterns. For this Investigation, 120 upper and lower premolars extracted for orthodontic purposes were used and randomly divided into six groups of twenty teeth each. Human premolars were embedded in a metal cylinder with orthodontic resin. Metal brackets and ceramic brackets were bonded with XT primer and self-etching primer by means of XT adhesive. Upon curing, plasma arc light and visible light were used. After bonding, the shear bond strength was tested by Instron universal testing machine, and the amount of residual adhesive that remained on the tooth after debonding was measured by stereoscope and assessed with an adhesive remnant index. The results were as fellows: 1. When brackets were bonded, if other conditions remained the same, there was no significant difference in shear bond strength due to the type of primer - either self-etching primer or XT primer. 2. When metal brackets were bonded, there was no significant difference in shear bond strength according to the source of light - plasma arc light or visible light - and type of primer. 3. There was a very significant difference in shear bond strength according to the type of brackets - metal or ceramic brackets. The shear bond strength of ceramic brackets was stronger than metal brackets. 4. When the adhesive failure patterns of metal brackets bonded with self-etching primer were observed by using the adhesive remnant index, the bond failure of the metal bracket occurred more frequently at the bracket-adhesive. The failure of the ceramic bracket, however, occurred more frequently at the enamel-adhesive interface. The adhesive failure patterns of metal brackets bonded with XT primer observed the same patterns. The above results suggest that self-etching primer can be clinically useful for bonding the brackets without fear of a decrease in shear bond strength.