• Elastomers and Composites
• /
• v.36 no.4
• /
• pp.225-236
• /
• 2001

In order to improve the properties of the copolymer and the terpolymer that was used as removal-type pressure sensitive adhesive(PSA), we synthesized quaterpolymer with the variation of the types of monomer, initiator, and solvent, and concentration, the monomer/solvent ratio, reaction temperature and time. and determined the properties of this adhesive: the viscosity, molecular weight, conversion, solid content and structure of polymer. The prepared polymer was crosslinked by changing the type of crosslinking agent and concentration, and then we investigated the characteristics or adhesive such as peel adhesion, shear adhesion, heat resistance, weathering resistance and peel adhesion to aging. The optimum performance of RA/2- EHA/MMA/2-HEMA as a PSA were obtained when benzoyl peroxide was used as an initiator with the reactant mixture consisted of 80% BA and 2-EHA, 15%, MMA, and 5% 2-HFMA. The optimum reaction temperature and time were $80^{\circ}C$ and 8 hours, respectively. For BA/2-EHA/MMA/AA, the optimum performance was obtained when the polymerization was performed at the monomer composition of 80% BA/2-EHA, 15% MMA, and 5% AA. BPO was used as initiator and the optimum reaction temperature and time were identical to those of BA/2-EHA/MMA/ 2-HEMA. Isocyanate and melamine were used to crosslink BA/2-EHA/MMA/2-HEMA and BA/2-EHA/MMA/AA, respectively. No effect on the type of cross-linking agent on the peel adhesion was observed with aging. The quarterpolymers crosslinked with melamine left residues on the counter surface after weathering resistance test, while the polymers crosslinked with isocyanate did not.

• Journal of Adhesion and Interface
• /
• v.1 no.1
• /
• pp.15-22
• /
• 2000

To prepare acrylic type pressure-sensitive adhesive, quarter polymers were synthesized from butylacrylate (BA), 2-ethylhexylacrylate (2-EHA), methyl methacrylate (MMA), 2-hydroxyethylmethacrylate (2-HEMA). The quarter polymer was identified by FT-IR. Molecular weight was measured by Gel Pearmeation Chromatograhy. Also, viscosity, solid content and peel strength were investigated. The peel strength was $160g_f/25mm$ when the volume ratio of feed monomer to solvent was 1.3:1 and the ratio was relevant to commercial usage. The pot life of adhesive was 30 s at the 50 m/min of heat treatment rate, and it indicated that the minimum drying time was 30 s. Not only weathering resistance keep up peel strength $160{\sim}180g_f/25mm$ after 1000 h, but also no residual remains.