• Architectural research
• /
• v.7 no.1
• /
• pp.49-54
• /
• 2005

Conventional studies have focused on the reduction in the water-cement ratio, the use of various admixtures, etc., to ensure the durability of reinforced concrete structures against such deterioration factors as carbonation and chloride attack. However, improvement in the concrete quality alone is not considered sufficient or realistic for meeting the recent demand for a service life of over 100 years. This study intends to improve the durability of reinforced concrete structures by improvement in the reinforcing steel, which has remained untouched due to cost problems, through subtle adjustment of the steel components to keep the cost low. As a fundamental study on the performance of Cr-bearing rebars in steel reinforced concrete structures exposed to corrosive environments, The test specimens were made by installing 8 types of rebars in concretes with a chloride ion content of 0.3, 0.6, 1.2, 2.4 and $24kg/m^3$. Corrosion accelerated curing were then conducted with them. The corrosion resistance of Cr-bearing rebars was examined by measuring crack widths, half-cell potential, corrosion area and weight loss after 155 cycles of corrosion-accelerating curing. The results of the study showed that the corrosion resistance increased as the Cr content increased regardless of the content of chloride ions, and that the Cr-bearing rebars with a Cr content of 5% and 9% showed high corrosion resistance in concretes with a chloride ion content of 1.2 and $2.4kg/m^3$, respectively.

• Computers and Concrete
• /
• v.4 no.5
• /
• pp.403-424
• /
• 2007

The investigation of corrosion effects on the tensile behavior of reinforced concrete (RC) members is very important in region prone to high corrosion conditions. In this article, an experimental study concerning corrosion effects on tensile behavior of RC members is presented. For this purpose, a comprehensive experimental program including 58 cylindrical reinforced concrete specimens under various levels of corrosion is conducted. Some of the specimens (44) are located in large tub containing water and salt (5% salt solution); an electrical supplier has been utilized for the accelerated corrosion program. Afterwards, the tensile behavior of the specimens was studied by means of the direct tension tests. For each specimen, the tension stiffening curve is plotted, and their behavior at various load levels is investigated. Average crack spacing, loss of cross-section area due to corrosion, the concrete contribution to the tensile response for different strain levels, and maximum bond stress developed at each corrosion level are studied, and their appropriate relationships are proposed. The main parameters considered in this investigation are: degree of corrosion ($C_w$), reinforcement diameter (d), reinforcement ratio (${\rho}$), clear concrete cover (c), ratio of clear concrete cover to rebar diameter (c/d), and ratio of rebar diameter to reinforcement percentage ($d/{\rho}$).

• Journal of the Korean Society of Safety
• /
• v.29 no.6
• /
• pp.87-93
• /
• 2014

In this study, the reinforced concrete rahmen bridge damaged by the chloride attack was investigated. According to the investigation, the degraded concretes on cantilever kerb and end part were intensively observed. Thus, the chloride content test and half-cell method were performed to evaluate the degraded parts. As a result, the contents of chloride on degraded parts were C and D grade. On the other hand, the half-cell potential values of rebar in degraded concrete were measured with the minor corrosion. This rebar corrosion is expected to progressing. Chloride content D grade is due to expansion pressure by corrosion of rebar and freeze-thaw by permeate water, could see progresses rapidly degradation. In order to prevent chloride attack to concrete deck caused by deicing salts, corresponding to the chloride critical concentration must maintain grade b or at least grade c. Chloride condition evaluation standard apply to evaluation of marine structure chloride attack with chloride attack by deicing salts.

• Structural Engineering and Mechanics
• /
• v.20 no.3
• /
• pp.265-277
• /
• 2005

This paper is focused on fractal analysis of the surface cracking, a new tool for safety evaluation of corroded reinforced concrete (RC) beams. Comprehensive experimental investigations, including flexural tests, coupon tests on strength evaluation of corroded concrete and rusty rebar, and pullout tests to determine bond strength between concrete and rebar were carried out on nine Corroded Reinforced Concrete Beams (CRCB) exposed to an aggressive environment for more than 10 years. In combination with test results from a previous study on CRCBs fabricated in the laboratory from accelerated methods, it is found that, for both types of beams, the surface cracking distributions are fractal in character at loading and failure stages. Fractal dimension is calculated for all specimens at different corrosion states based on fractal analysis method. Relationships between the fractal dimension and mechanical properties of corroded concrete, rebar corrosion ratio, and ductility of CRCBs are discussed in detail. It is concluded that the fractal dimension can act as a damage index and can be efficiently used to describe the corrosion state of CRCBs.

• Computers and Concrete
• /
• v.21 no.4
• /
• pp.471-484
• /
• 2018

Refined analysis depicting mass transportation and physicochemical reaction and reasonable computing load with acceptable DOFs are the two major challenges of numerical simulation for concrete durability. Mesoscopic numerical simulation for chloride diffusion considering binder, aggregate and interfacial transition zone is unable to be expended to the full structure due to huge number of DOFs. In this paper, a multiscale approach of combining both mesoscopic model including full-graded aggregate and equivalent macroscopic model was introduced. An equivalent conversion of chloride content at the Interfacial Transition Layer (ITL) connecting both models was considered. Feasibility and relative error were discussed by analytical deduction and numerical simulation. Case study clearly showed that larger analysis model in multiscale model expanded the diffusion space of chloride ion and decreased chloride content in front of rebar. Difference for single-scale simulation and multiscale approach was observed. Finally, this paper addressed some worth-noting conclusions about the chloride distribution and rebar corrosion regarding the configuration of rebar placement, rebar diameter, concrete cover and exposure period.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.751-754
• /
• 1999

Corrosion inhibitors are widely used to protect chloride-induced corrosion of reinforcement in concrete. However, the number of researches on the corrosion of reinforcement, when corrosion inhibitor is used, is not enough for actual application in the field. In addition, on corrosion of reinforcement a quantitative standard about corrosion inhibitor does not exist and the data about its influencing concrete are relatively rare. In this study, the effectiveness of rebar corrosion protection, setting time, compressive strength, chloride ion's penetration, and diffusion test were performed using with three different kinds of corrosion inhibitors.

• International Journal of Concrete Structures and Materials
• /
• v.10 no.sup3
• /
• pp.43-52
• /
• 2016

The degradation of the load-bearing capacity of reinforced concrete beams due to corrosion has a profoundly negative impact on the structural safety and integrity of a structure. The literature is limited with regard to models of bond characteristics that relate to the reinforcement corrosion percentage. In this study, uniaxial tensile tests were conducted on specimens with irregular corrosion of their reinforced concrete. The development of cracks in the corroded area was found to be dependent on the level of corrosion, and transverse cracks developed due to tensile loading. Based on this crack development, the average stress versus deformation in the rebar and concrete could be determined experimentally and numerically. The results, determined via finite element analysis, were calibrated using the experimental results. In addition, bond elements for reinforced concrete with corrosion are proposed in this paper along with a relationship between the shear stiffness and corrosion level of rebar.

• Journal of Advanced Marine Engineering and Technology
• /
• v.40 no.2
• /
• pp.107-111
• /
• 2016

This paper presents electrochemical corrosion behaviors of cement mortar specimens in the high salinity condition. Chloride ion is known as the most detrimental parameter to cause the corrosion in reinforced concrete. Increasing the concrete cover thickness is one of the corrosion protection methods against chloride ion; so, this study mainly focuses on the effects of mortar cover thickness on corrosion protection. In specimens, rebar, which was a height of 200 mm and a diameter of 10 mm, was installed at the center of the small size form. Later on, mortar was injected into the form, and 10, 20, 30, 40, and 50 mm of the different mortar cover thicknesses were selected. Potential measurements, linear polarization resistance tests, and cyclic potentiodynamic polarization tests were performed for specimens that were exposed to seawater. These results were compared with visual inspection results of rebar. The results show that an increase in the cover thickness contributes to corrosion protection. In addition, the result of electrochemical corrosion tests generally agreed with that of an autopsy visual inspection.

• Applied Chemistry for Engineering
• /
• v.9 no.6
• /
• pp.811-816
• /
• 1998

Rebar corrosion in cement mortar containing chloride ions was investigated by electrochemical AC impedance spectroscopy. Corrosion of mild steel bar was accelerated by an acceleration test equipment in short period. Impedance values obtained from AC-impedance method could be adapted to the proposed electrochemical equivalent circuit model and they were consistent with calculated values obtained by CNLS fitting method. The weight loss of rebar could be calculated by charge transfer resistance($R_2$) with time and it was close to real value.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.4
• /
• pp.194-199
• /
• 2021

In this study, rebar corrosion detection sensor was fabricated using multi-walled carbon nanotubes (MWCNTs). MWCNTs were pre-treated in the acid electrolytes to attach the carboxylic acid to the surface of MWCNTs. The fabricated sensor was attached on the surface of rebar and it detected the corrosion of steel using LCR meter with variation of capacitance. The surface morphology and electrical properties were characterized using scanning electron microscope (SEM) and electrical test equipment, respectively. To verify the corrosion detection characteristics, comparison experiment using plastic bar was performed. Moreover, mechanism of corrosion detection sensor was discussed.