• Journal of the Korean Wood Science and Technology
• /
• 제23권3호
• /
• pp.66-72
• /
• 1995

The rate of fixation of the components were evaluated in CCA-Type B and CCFZ-treated radiata pine sapwood by quantitative analysis of solution expressed from the treated wood. The leaching characteristics of radiata pine blocks treated with CCA-Type B and CCFZ were also evaluated by the AWPA standard leaching test. Both fixation and leaching charactersistics of CCA-Type B were compared with CCA-Type C treated wood samples. The rate of CCA-Type B fixation was a little faster than that of CCFZ. However, significant amounts of arsenic was unfixed in the CCA-Type B treated samples and consequently leached. These significant quantities of arsenic liberated from the CCA-Type B treated wood during service may pose some environmental concerns. Arsenic was no longer detectable from CCA-Type C treated samples when fixation was complete, even though the fixation of CCA-Type C was slower in some degree than CCA-Type B. In summary, it could be said that CCFZ was much safer preservative than CCA-Type B by the criterion based on the relative hazard assessed by absolute amount of unfixed element present in the treated wood. Also the decision that CCA preservative has to move from Type B to Type C should be made sooner or later for continuous use of CCA preservative in the future.

• Journal of the Korean Wood Science and Technology
• /
• 제25권2호
• /
• pp.67-74
• /
• 1997

A relationship between drying resistance and moisture content was found for 24, 27 and 30mm thick boards, and 45, 51 and 57mm thick dimensions of Japanese larch. Dahurian larch and radiata pine in order to modify the kiln schedule by using time schedules. The amount of drying resistance for Dahurian larch lumber was the highest, and radiata pine lumber was the lowest, on the basis of the same moisture content range. Drying resistance increased curvilinearly as moisture content decreased, and was higher for thicker lumber than for thinner lumber, at a given moisture content. Combined drying resistance for the three board thicknesses and the three dimension thicknesses showed a comparatively strong for radiata pine and a Japanese larch, while a weak correlation for Dahurian larch as a function of two independent variables, thickness and moisture content of lumber, respectively.

• Journal of the Korean Wood Science and Technology
• /
• 제32권1호
• /
• pp.45-51
• /
• 2004

본 연구는 두께 24 mm 뉴질랜드산 라디아타 소나무 단판의 마이크로파-열풍 복합 건조특성을 파악하기 위하여 수행되었다. 단판을 100℃ 열풍과 복합한 마이크로파 건조한 결과 함수율 160%에서 0%까지 건조하는데 7.5분이 소요되었다. 이 건조속도는 100℃ 열풍만으로 건조한 경우에 비하여 약 3배 정도 높은 수준이었다. 그러나 과도한 마이크로파 출력이 가해지면 탄흔이 남는 문제가 발생하였다. 그러므로 최적의 건조조건을 결정하기 위해서는 다양한 규격과 수종의 단판에 대한 마이크로파 건조특성의 파악이 요구됨을 알 수 있었다.

• Plant Biotechnology Reports
• /
• 제5권2호
• /
• pp.177-186
• /
• 2011

This study describes for the first time in Pinus genus a plant regeneration system via a combined pathway of somatic embryogenesis and organogenesis from immature seeds of radiata pine. Somatic embryos were obtained from embryogenic line 2162 of Pinus radiata D. Don on EDM basal medium containing $60{\mu}M$ ABA and 6% sucrose. The explants used for organogenesis experiments were either freshly collected somatic embryos or somatic embryos germinated for 1 week. Germination medium was half-strength LP medium, supplemented with 0.2% activated charcoal. Different induction periods and BA concentrations were assayed for shoot induction. After induction treatments, explants were elongated on the same medium used for germination stage. Rooting medium was quarter-strength LP medium supplemented with three different auxin treatments: $1.5mg\;L^{-1}$ 1-naphthalene acetic acid (NAA), $1.5mg\;L^{-1}$ indole-3-butyric acid (IBA) and $1mg\;L^{-1}$ IBA with $0.5mg\;L^{-1}$ NAA (MIX). The effect of the photon flux ($120mmol\;m^{-2}\;s^{-1}$ and darkness) in the first week of the explants in the rooting media was also tested. This methodology could offer an alternative to overcome some problems associated with somatic embryogenesis such as the seasonality of embryogenic tissue (ET) initiation or a low embryo production from the ET, a particularly important issue in the case of genetically transformed ETs.

• 한국가구학회지
• /
• 제16권2호
• /
• pp.59-65
• /
• 2005

As physical condition of students improves, there is a need to develop human body-friendly desk and chair for students. In this study, desks and chairs were manufactured with curved veneer lamination under high frequency heating and pressing, using ten wood species such as Japanese red pine, Korean pine, pitch pine, Japanese larch, yellow poplar, black locust, oak, radiata pine, beech, and birch. The performance of these products were evaluated. The results obtained were summarized as follows; With high frequency heating, the turned lamination of veneers with full size sheet ($3{\times}6\;feet$) prepared by rotary lathe peeling was successfully applied for making the members of desk top, leg frames of desk and chair. Bending strengths of desk tops were relatively greater for yellow poplar, black locust and red pine, which were similar to those of beech and birch. Bending strengths of desk legs were classified into greater species group (red pine, yellow poplar, larch) and lower species group (radiata pine, Korean pine, pitch pine). Compressive strengths of chair legs in parallel direction to the lamination were greater in black locust and larch. On the other hand, differences between outer and inner gap at the top and drawer bottom of desk top were rather larger for the laminations of birch and beech, and less for those of yellow poplar and pitch pine, showing greater stability of open drawer space. In results, yellow poplar, larch, pitch pine and red pine showed good appearance and strength properties at the curved veneer lamination. Accordingly, it was believed that these domestic woods were able to substitute for birch which was being imported for the use of veneer-laminates type furniture.

• 한국산림과학회지
• /
• 제86권1호
• /
• pp.1-8
• /
• 1997

뉴질랜드 북섬의 다우지역에서 라디아타소나무 유묘생장이 일련의 주요 잡초종과의 경쟁으로 인하여 감소함을 계량화(計量化)하기 위하여 계획된 실험의 2차년도 결과이다. 라디아타소나무 유묘(1/0)들을 각각 잡초제거구와 활엽성초본, 목초, broom, pampas, buddleia, gorse와 함께 생육시켰다. 양료와 수분공급은 각 요인에 관수와 시비, 무관수와 무시비로 다양화하였다. 식재 21개월 후 라디아타소나무 유묘의 재적생장량은 잡초제거구와 gorse와 함께 생육된 구에서 최대였고 buddleia나 pampas와 함께 생육된 곳에서는 최소였다. 유묘생장에 대한 잡초의 영향이 수분이나 양료 경쟁에 의해 조정된다는 증거가 없었다. 유묘를 능가하여 치솟는 키크고 빨리 자라는 종(broom, buddleia, pampas)들이 유묘 생장에 가장 큰 영향력을 갖고 있고 그 영향력의 크기는 유묘 위에 뒤덮는 정도와 상관관계가 있었다. 이것은 피음 혹은 광경쟁이 아마도 중요한 인자임을 암시해 주고 있다.

• Journal of the Korean Wood Science and Technology
• /
• 제31권1호
• /
• pp.46-51
• /
• 2003

본 연구는 라디에타소나무 제재목의 균 변색을 제거하기 위한 표백처리의 사용 가능성을 조사하기 위하여 수행하였다. 염소계 표백제인 아염소산나트륨과 차아염소산나트륨은 표백조건(약제농도, 처리온도, 처리시간)의 조절에 따라 만족할만한 변색제거 효과를 얻을 수 있었다. 비염소계 표백제인 과산화수소는 표백조건의 조절만으로는 변색제거가 불가능하였으나 규산나트륨과 수산화나트륨을 활성제로 첨가하는 경우에는 염소계 표백제보다 탁월한 변색제거 효과를 나타내었다. 그러나 활성제 첨가에 따라 재색의 녹색화 문제가 발생하였는데, 앞으로 이러한 문제점을 해결하기 위한 연구가 진행되어야 할 것이다. 또한, 앞으로 본 연구를 통해 개발된 변색제거 방법의 현장 적용을 위한 후속 연구도 필요하다고 본다.

• Environmental Analysis Health and Toxicology
• /
• 제23권3호
• /
• pp.187-194
• /
• 2008

국내에서 목질계 바이오매스는 유망한 재생가능한 자원이다. Fast pyrolysis을 통한 radiata pine 톱밥의 bio-oil의 전환은 벤치스케일의 유동층 반응기을 이용하였다. 이 실험에서 얻어진 bio-oil은 주로 산, 페놀, 알킬페놀 등을 포함하고 있었고. 세포생존율실험, comet assay, 물벼룩 급성유영저해실험을 이용하여 각각 세포독성, 유전독성 및 생태독성을 평가하였다. Bio-oil의 액상부분은 타르 부분보다 세포독성과 유전독성이 더 높게 나타났고, 반면 타르부분은 액상부분에 비해 생태독성이 높게 나타났다. 본 연구에서 얻어진 결과를 통해 pyrolysis 생성물에 대한 다양한 독성영향을 확인할 수 있었으나, 보다 다양한 독성 지표의 적용이 필요할 것으로 보인다.

• Journal of the Korean Wood Science and Technology
• /
• 제25권1호
• /
• pp.23-27
• /
• 1997

Alkali-soluble extracts were prepared from barks of Japanese larch(Larix leptolepis). Siberian larch(Larix gmelineii) and Radiata pine(Pinus radiata) The effect of various factors, such as particle size, liquor ratio, extraction temperature, and reaction time, on the extracts yield was investigated. Particle sizes affected the alkali-soluble extracts; the finer the particle size, the higher extracts and extract efficiency. High temperature and high liquor ratio were more effective. In the range of 0.25% to 1% NaOH concentration, alkali extracts were increased with the increasing alkali concentration. However, extract yields were leveled off above 0.5% alkali concentration. Extractions with NaHCO3 were almost equivalent to those of NaOH extraction. 1% NaOH and 1% NaHCO3 resulted in the highest yields of alkaline extracts. Extracts from Japanese larch were lower than those from Siberian larch and Radiata pine barks. Siberian larch bark was the best raw material for tannin adhesives, because its extractive yield was higher than those of the other barks. Concerning pH of alkaline media during extraction, small increases of the extract yields were resulted at range of pH 7 to pH 9, while a large increases from pH 9.0 to pH 12. This phenomenon is attributed to higher alkalinity.

• 한국가구학회지
• /
• 제19권2호
• /
• pp.116-123
• /
• 2008

Kiln schedule development was based on two schedule phases, the first being to determine the maximum safe kiln temperature during the check prone initial stage of drying, with the second stage determining how to accelerate drying once the danger of checking had passed. This was achieved by using 38 mm thick boards which were pre-screened for susceptibility to internal checking, and then drying matched sample boards over a range of kiln temperatures. Research has shown that below 50% MC there is no further risk of internal checking. However, difference in drying rate due to board width and the increased occurrence of wet patches in wide boards means that it is essential to modify the basic schedule according to the maximum board width. A condition of 52/40 $^{\circ}C$ was selected for the checking-free initial kiln drying step and a 5-step kiln-schedule dried the boards from 109% to 8% MC for 72.5 hours without internal checking.