• 구강회복응용과학지
• /
• 제23권4호
• /
• pp.283-292
• /
• 2007

Two-step or one-step bonding systems generally inhibit curing process of dual-cured core build-up resin composite for their adhesive acidity. In addition this dual-cured core build-up resin composite can be applied to dentin of pulp chamber and root at the time that complete the endodontic treatment. The purpose of this investigation was to determine the influence of sodium hypochlorite on rnicrotensile bond strength of dual-cured core build-up resin composite. Extracted human molars were horizontally sectioned with 1mm thickness using low speed diamond saw. After the sectioned specimens were divided into 8 groups, adhesive systems (Clearfil SE-Bond, Prime&Bond NT[2-step, 1-step], Adper Prompt L-Pop) were then applied with or without sodium hypochlorite pretreatment. The treated specimen was filled with dual-cured core build-up resin composite (Luxacore, DMG corp., German). Then light cured for 40 seconds and soaked in $37^{\circ}C$ water bath for 24 hours. After the treated specimen was grinded with 1mm width and measured rnicrotensile bond strength by testing machine. Additionally 8 teeth were prepared for SEM evaluation. The results were as follows. : NaOCl treated groups generally had lower rnicrotensile bond strength but did not show any difference statistically except Adper Prompt L-Pop. When the teeth were treated by NaOCl, though the difference of applied adhesive system, it had no statistically significant difference within the NaOCl treated groups except the relation of between ClearFil SE-Bond adhesive system and Adper Prompt L-Pop adhesive system. In the SEM evaluation, NaOCl treated groups presented relatively long resin tags and incomplete hybrid layer formation generally.

• KSBB Journal
• /
• 제11권6호
• /
• pp.718-725
• /
• 1996

신문고지를 Trichoderma viride로부터 분리한 en­d doglucanase, exoglucanase와 이들의 혼합분 (1:1) 으로 탈묵시킨 후 효소놓도에 따른 수율, 백색도, 및 물리적 강도를 알아 보았다. 수율은 효소의 농도 증 가에 따라 감소함을 보여 주었으며, 특히 endo-exo 혼합분(1:1)으로 처리했을 경우 더욱 낮아졌다. 이 는 endo-exo의 상호 협동작용에 대한 가수분해율의 증가 때문이라 생각된다. 백색도는 endo-exo 혼합 분(1:1)으로 처리했을 때 가장 높게 나타났으며, 최 대 값은 효소 농도 O.Smg/mL에서 나타났다. 또한 exoglucanase로 처리한 것에서는 가장 낮은 값을 보여주였다. 물리적 강도에 있어서는 exoglucanase 로 처리 했을 경우 가장 높게 나타났으며, 효소놓도 에 따라 물리적 강도가 증가함을 보여 주였다. 그리 고 endo와 endo-exo 혼합분0:1)으로 처리했을 경 우는 농도에 따라 감소함을 보여주었다. 그리고 e endoglucanase와 exoglucanase의 조합(12:1, 8:1, 4 4:1, 1:1, 1:4, 1:8, 1:12)에 있어서의 수율, 백색 도, 및 물리적 강도를 알아 보았는데, 최대 탈묵 조 건은 endoglucanase와 exoglucanase의 비가, 수율 에 있에서는 4: 1, 백색도에서는 12: 1, 인장 강도는 4 4: 1, 파열 강도는 12: 1, 그리고 인열 강도는 8:1일 때였다. 즉 endoglucanase성분이 exoglucanase성 분보다 많을 때 백색도, 불리척인 강도가 높게 나타 나는 것을 알 수 있었다. 이들 결과로부터 탈묵은 주 로 endoglucanase의 action에 주로 의존한다는 것 을 알 수 있었다 .. crude cellulase에서 exoglucan­a ase가 차지하는 비율은 600/0 (wt%) 이상이다. 그러 므로 보다 효율적인 탈묵이 이루어지기 위해서는 e exoglucanase의 action을 억제시켜주어야 할 필요 가있다.

• 공업화학
• /
• 제10권5호
• /
• pp.726-730
• /
• 1999

잉크조성분의 차이, 탈묵약품 및 열화기간에 따른 신문지의 탈묵성을 비교하였다. 잉크조성분으로 용제, 즉 대두유 30%(A), 대두유 50%(B), 광물유 45%(C) 및 아마인유 42%(D)를 각각 넣어 잉크를 제조하고 신문용지에 인쇄하였다. 신문지를 6개월 동안 자연 열화시키면서 열화기간에 따른 탈묵성을 비교하였다. 또한 탈묵약품의 차이에 따른 동일시료의 탈묵성을 비교하였다. 신문지 탈묵펄프의 백색도는 잉크조성분, 열화기간과 탈묵약품에 따라 영향을 받았다. 즉 탈묵펄프의 백색도는 열화기간의 연장에 따라 낮아지며, 광물유 잉크, 대두유 잉크(30%), 대두유 잉크(50%), 아마인유 잉크 순으로 낮아졌다. 또한 탈묵약품에 따라서는 주어진 수율에서 lipase, cellulase, 기존 화학약품 탈묵방법 순으로 백색도가 감소하였다. 주어진 백색도에서 탈묵 수율은 백색도 변화와 동일한 경향을 나타내었다. 탈묵펄프의 강도는 열화기간에 따라 1개월까지는 조금 증가하고 그 후에는 감소하거나 현상태를 유지하였다. 인쇄 잉크의 조합 즉, 광물유, 아마인유, 대두유 잉크 순으로 탈묵펄프의 제반 강도가 낮아졌다. 탈묵약품에 따라서는 lipase, 기존 화학약품, cellulase 순으로 탈묵펄프의 제반 강도가 낮아졌다.

• 공업화학
• /
• 제10권2호
• /
• pp.299-303
• /
• 1999

경제적, 환경적인 이유로 신문용지를 생산하는데 신문고지가 상당량 재이용되고 있다. 본 연구에서는 국내 외 신문고지의 열화기간에 따른 제반 성질의 변화를 조사하기 위하여 시도하였다. 시료의 백색도, 수율 및 펄프 강도를 고려하면 열화기간이 증가할수록 탈묵성이 호주산 신문고지에서 가장 우수하고, 국내 신문원지를 사용한 신문고지와 일본 신문고지는 비슷하며, 카나다산 신문원지를 사용한 신문고지에서 가장 낮았다. 국내 신문원지를 사용한 신문고지의 경우, 열화기간 90일까지는 약 83%의 수율과 백색도 50% 이상을 나타내지만 그 이후에는 급격히 감소하였다. 또한 국내 신문용지의 경우 수입된 신문용지보다 섬유의 길이는 짧지만 제반 강도적성질은 높았다. 국내 신문용지와 수입 신문용지는 전반적으로 열화기간에 따라 인장강도와 파열강도는 증가하다가 감소하였으며, 인열강도는 점차 증가하였다.

• 한국수산과학회지
• /
• 제41권4호
• /
• pp.237-242
• /
• 2008

The tunic of Styela clava(SCT) consists of a proteoglycan network. Regenerated cellulose films were prepared by solution casting and coagulation of SCT in N-methylmorpholine-N-oxide(NMMO)/$H_2O$(87/13 wt%). The crystalline structure of powdered SCT was primarily that of cellulose I. The crystalline structure of SCT films exhibited a cellulose II structure, similar to that of viscose rayon. Physical characterization of SCT films and fibers revealed an intrinsic viscosity($\eta$) of 6.35 dL/g, average molecular weight($M_w$) of 423,000 g/M, and fiber density of 1.50 $g/cm^3$ with a moisture regain and water absorption of 10.20% and 365%, respectively. The results were similar to those of cellulose films regenerated from wood pulp. Films prepared with 6 wt% SCT exhibited strong tensile strength, high water absorption, and a greater degree of elongation. Scanning electron micrographs(SEM) of film cross-sections showed a layered, sponge-like structure.

• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.499-509
• /
• 2014

Wood filler is a porous and anisotropic material having different size, shape, and aspect ratio. The use of wood fillers such as wood particle, wood flour, and wood pulp in wood plastic composites (WPCs) are growing rapidly because these wood fillers give improved strength and stiffness to WPCs. However, the wood fillers have originally poor compatibility with plastic matrix affecting the mechanical properties of WPCs. Therefore, to improve compatibility between wood and plastic, numbers of physical and chemical treatments were investigated. While the various treatments led to improved performances in WPC industries using petroleum-based plastics, full biodegradation is still issues due to increased environmental concerns. Hence, bio-based plastics such as polylactide and polyhydroxybutyrate having biodegradable characteristics are being applied to WPCs, but relatively expensive prices of existing bio-based plastics prevent further uses. As conventional processing methods, extrusion, injection, and compression moldings have been used in WPC industries, but to apply WPCs to engineered or structural places, new processing methods should be developed. As one system, co-extrusion technique was introduced to WPCs and the co-extruded WPCs having core-shell structures make the extended applications of WPCs possible.

• Current Research on Agriculture and Life Sciences
• /
• 제31권4호
• /
• pp.250-255
• /
• 2013

As a renewable nanomaterial, cellulose nanocrystal (CNC) isolated from wood grants excellent mechanical properties in developing high performance nanocomposites. This study was undertaken to compare the reinforcing efficiency of two different CNCs, i.e., cellulose nanowhiskers (CNWs) and cellulose nanofibrils (CNFs) from hardwood bleached kraft pulp (HW-BKP) as reinforcing agent in polyvinyl alcohol (PVA)-based nanocomposite. The CNWs were isolated by sulfuric acid hydrolysis while the CNFs were isolated by 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-mediated oxidation. Based on measurements using transmission electron microscopy, the individual CNWs were about $6.96{\pm}0.87nm$ wide and $178{\pm}55nm$ long, while CNFs were $7.07{\pm}0.99nm$ wide. The incorporation of CNWs and CNFs into the PVA matrix at 5% and 1% levels, respectively, resulted in the maximum tensile strength, indicating different efficiencies of these CNCs in the nanocomposites. Therefore, these results suggest a relationship between the reinforcing potential of CNCs and their physical characteristics, such as their morphology, dimensions, and aspect ratio.

• 한국응용과학기술학회지
• /
• 제27권4호
• /
• pp.508-514
• /
• 2010

Regenerated cellulose fibers were prepared from three pulps containing different degree of polymerization(DP) and $\alpha$-cellulose contents by dry-jet wet spinning technique with cellulose dope in N-methylmorpholin N-oxide (NMMO). The effect of antioxidant, n-propyl gallate (PG) on the properties of different regenerated celluloses was studied using X-ray diffraction, copper number calculation, and viscometry. The degradaqtion of regenerated cellulose from pulp containing higher DP and lower $\alpha$-cellulose content was occurred more seriously. The tensile strength and initial modulus of regenerated cellulose fiber obtained from NMMO dope with PG were higher than those of fiber obtained from NMMO dope without PG. All fibers showed the round shape cross section and typical cellulose II crystalline structure.

• Journal of Forest and Environmental Science
• /
• 제9권1호
• /
• pp.67-80
• /
• 1993

무공해 대체 펄프화법 개발의 일환으로 비교척 최근에 많은 연구가 이루어지고 있는 아세트산-물 용매 증해법을 이용하여 현사시나무와 소나무률 펄프화 하였다. 펄프 특성의 변화에서 현사시나무는 거의 모든 아세트산 충해초건에서 우수한 펄프화 경향을 보였지만 소나무는 저온에서 충해가 거의 일어나지 않았다. 현사시나무의 최적 중해조건은 중해농도 95%, 중해온도 $185^{\circ}C$, 증해시간 0.5hr이었다. 구성당 성분의 거동은 현사시나무와 소나무에서 glucose만이 소량 감소하는 반면 그외의 당성분들은 다량 용출되었다. 폐액중의 용출 아세트산 리그닌에 대한 기초척인 성질을 살펴본 결과 현사시나무의 아세트산 리그닌의 원소조성은 C가 63.88%, H가 5.45%, O가 30.67%이며 $C_9$의 formular는 $C_9H_{9.15}O_{3.24}$였고 소나무의 아세트산 리그닌의 조성온 C가 61.85%, H가 6.14%, O가 32.01% 이며 $C_9$의 formular는 $C_9H_{9.15}O_{3.50}$이었으며 두 수종의 아세트산 리그닌 중합 명균분자량은 현사시나무가 731이며 소나무는 725였다.

• 대한소아치과학회지
• /
• 제28권2호
• /
• pp.228-237
• /
• 2001

본 연구의 목적은 와동 충전시 충전재와 치질 사이에 개재되는 상아질 결합제가, 수복물에서 유리되는 불소가 와동 벽으로 침투하는 과정에 어떠한 영향을 주는지를 조사함이었고, 부가적으로 레진 강화형-글라스 아이오노머 시멘트의 접착에도 상아질 결합제를 도포 하는것이 치질과의 결합력을 강화시킬 수 있는지에 대해 평가하고자 하였다. Fuji II $LC^{(R)}$와 Dyract $AP^{(R)}$를 선정하여 상아질 결합제의 도포 여부에 따른 불소 유리량 측정과 전단 결합 강도를 비교분석하였으며, 치질 내로의 불소 침투 양상은 교환 시기에 있는 제2유구치에 Fuji II $LC^{(R)}$와 Dyract $AP^{(R)}$를 충전하고 3주내에 발거하여 EPMA로 분석하였다. 상아질 결합제는 불소 유리량을 현저하게 감소시키는 것으로 나타났으며(p<0.05) Fuji II $LC^{(R)}$의 경우 상아질 결합제의 도포가 결합강도를 증가시키지 못하였다. EPMA 분석결과 상아질 결합제는 충전재로부터 유리되어 나오는 불소가 치질 내로 확산되는 것을 방해하는 것으로 확인되었다.