• Journal of the Korea Institute of Building Construction
• /
• v.4 no.4
• /
• pp.79-86
• /
• 2004

The purpose of this study was the development of a recycling process to recover the hydraulic properties of hydration products which account for a large proportion of cementitious powder from concrete waste. This process was performed to recycle cementitious powder as recycle cement. Therefore, after the theoretical consideration of the properties of recycle process of recycled aggregates and cementitious powder, we investigated the hydraulic properties of cementitious powder under various temperature conditions in hardened mortar which was modeled on concrete waste. And we analyzed properties of chemical reactions of recycled cement with admixture materials such as Fly-Ash, Blast Furnace Slag As a result of the experiment, the most effective method to recover hydraulic properties of the cementitious powder from concrete waste was condition of burning at 700℃ for 120 minute. And it is shown that the fluidity of mortar was decreased rapidly when the burning temperature of recycle cement was increased. However, the compressive strength and fluidity were improved significantly when admixture materials such as Fly-Ash or Blast Furnace Slag was added.

• Journal of Powder Materials
• /
• v.9 no.4
• /
• pp.211-217
• /
• 2002

It is well known that the powder injection molding(PIM) process can overcome the shape limitations of traditional powder compaction, the costs of machining, the productivity limits of isostatic pressing and slip casting, and the defect and tolerance limitations of conventional casting. Increasing demands from industry for not only the dimensional accuracy nut mechanical strength in PIMed parts have had much effort focused on the investigation of mechanical properties of mechanical strength in PIMed parts have had much effort focused on the investigation of mechanical properties of sintered parts formed with high-strength metallic powders. The 17_4 PH $10\mu{m}$ were injection-molded into flat tensile specimens. Sintering of the compacts was carried out at the various temperatures ranging from 900 to $1350^{\circ}C$. Sintering behavior of the compacts and tensile properties of sintered specimens were investigated.

• Journal of the Korean Society of Food Culture
• /
• v.30 no.5
• /
• pp.650-655
• /
• 2015

Bamboo sprout powder was added to rice cake in an effort to improve the quality and functional properties of dough. The contents of crude protein and carbohydrates increased as the amount of bamboo sprout powder increased, whereas moisture contents decreased. According to increasing contents of bamboo sprout powder, total amino acid contents significantly increased. Hunter's L value decreased as contents of bamboo sprout powder increased, whereas sucrose contents increased. Addition of bamboo sprout powder to rice cake increased dietary fiber contents. Sensory scores of rice cake containing 90 g of bamboo sprout powder were the highest of all rice cakes tested. According to the results, adding bamboo sprout powder could improve the quality and sensory characteristics of rice cake.

• Journal of Dairy Science and Biotechnology
• /
• v.40 no.3
• /
• pp.134-142
• /
• 2022

Protein-enriched dairy powder is widely consumed to promote muscle synthesis. Recently, in Korea, elderly people have also begun consuming protein powder products to prevent muscle loss. However, these protein-enriched powders have poor flowability and hydration properties because of the fine particles of spray-dried milk protein powder. Therefore, in this study, the fluidized bed agglomeration process was used to solve these problems. The rheological and physical properties of milk protein isolate (MPI)/skim milk powder (SMP) mixtures were effectively improved via fluidized bed agglomeration. The particle size of the MPI/SMP mixtures significantly increased from 35.7-58 ㎛ to 118-136 ㎛, the flowability level improved from fair (21.4-26.3) to good (15.7-16.3), and the cohesiveness level changed from intermediate (1.27-1.36) to low (1.18-1.19) after fluidized bed agglomeration. In addition, the wetting time of the agglomerated MPI/SMP mixtures was effectively reduced to 4.67-58.3 s by fluidized bed agglomeration. These findings may be useful for manufacturing protein-enriched dairy powders with good instant properties.

• Ceramist
• /
• v.9 no.6
• /
• pp.42-48
• /
• 2006

The structural ceramic, such as $A1_2O_3,\;ZrO_2\;and\;Si_3N_4$ have applied as several parts of precision machines, automotives and instruments for semiconductor. The mechanical properties depended on purity, morphology and microstructure of the ceramic and its fabrication process. High purity and fine starting powder for the structural ceramic was prepared mainly by wet process and powder processing such as milling, mixing, drying and granulating strongly influenced on the fabrication process. Powder processing included powder synthesis technology is essential for ceramic manufacture. Also, the advanced mechanical treat[neat in powder processing to create nano composite powder was developed to improve several properties of ceramic materials. Innovation of powder processing will lead to improve mechanical and functional properties of the ceramics.

• Journal of the Korean Ceramic Society
• /
• v.33 no.5
• /
• pp.479-484
• /
• 1996

The tribological properties of ceramics are very important in the application to engineering ceramic parts such as mechanical seal slurry valve disc and so on. In this study the effect of graphite addition on the mechanical and tribological properties of RBSC/graphite composites were investigated. The composites were prepared by adding graphite powder to the mixture of SiC powder metallic siliconcarbon black and alumina. Bending strength water absorption friction coefficient the amount of worn out material at a certain time and maximum surface roughness(Rmax) of the prepared composites were measured and crystalline phases were examined with XRD. The composite containing 5 vol% graphite powder showed improved bending strength due to high green density and decreased friction coefficient and wear resistance. The friction coefficient and the wear resistance of the composite were increased by adding graphite powder up to 10 vol% They decreased however as increasing the amount of graphite powder more that 10vol% There was no linear relationship between the tribological properties and bending strength of the composites.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.11a
• /
• pp.77-82
• /
• 2003

The purpose of this study is development of technique to use cementitious powder as recycle cement produced from deteriorated Concrete waste which has a large quantity of calcium carbonate. Therefore, after having theoretical consideration based on the properties of high-heated concrete and concerning about neutralization of Concrete, we analysis chemical properties of ingredients of cementitious powder. After making origin cement paste, then processing the accelarated carbonation, we consider the properties of hydration and chemical properties of cementitious powder under various temperature conditions. As a result of the thermal analysis, the CaCo3 content of cementitious powder would affect decision of heat temperature to recover its hydrated ability because CaCo3 content is increased when neutralization is progressed. And as a result of XRD analysis, in case of origin powder of non-neutralized paste, CaO peak is found at 700℃. but, heat temperature to generate CaO would increase when the content of neutralized ingredients is increased. Finally, recycle cement heated at 700℃ shows the best compressive strength when the content of neutralized ingredients in recycle cement is less then 50%. However, it would be quite difficult to manage quality of recycle cement according to recycling points of various concrete waste.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.77-82
• /
• 2003

The purpose of this study is development of technique to use cementitious powder as recycle cement produced from deteriorated Concrete waste which has a large quantity of calcium carbonate. Therefore, after having theoretical consideration based on the properties of hish-heated concrete and concerning about neutralization of Concrete, we analysis chemical properties of ingredients of cementitious powder After making origin cement paste, then processing the accelerated carbonation, we consider the properties of hydration and chemical properties of cementitious powder under various temperature conditions As a result of the thermal analysis, the CacO3 content of cementitious powder would affect decision of heat temperature to recover its hydrated ability because CacO3 content is increased when neutraliTation is preBlessed. And as a result of XRD analysis. in case of origin powder of non-neutralized paste, CaO peak is found at $700^{\circ}C$. but, heat temperature to generate CaO would increase when the content of neutralized ingredients is increased. Finally, recycle cement heated at $700^{\circ}C$ shows the best compressive strength when the content of neutralized ingredients in recycle cement is less then 50%. However, it would be quite difficult to manage quality of recycle cement according to recycling points of various concrete waste.

• Journal of Powder Materials
• /
• v.9 no.3
• /
• pp.182-188
• /
• 2002

Conventional Fe-Co alloys are important soft magnetic materials that have been widely used in industry. Compared to its polycrystalline counterpart, the nanostructured materials have showed superior magnetic properties, such as higher permeability and lower coercivity due to the single domain configuration. However, magnetic properties of nanostructured materials are affected in complicated manner by their microstructure such as grain size, internal strain and crystal structure. Thus, studies on synthesis of nanostructured materials with controlled microstructure are necessary for a significant improvement in magnetic properties. In the present work, starting with two powder mixtures of Fe and Co produced by mechanical alloying (MA) and hydrogen reduction process (HRP), differences in the preparation process and in the resulting microstructural characteristics will be described for the nano-sized Fe-Co alloy particles. Moreover, we discuss the effect of the microstructure such as crystal structure and grain size of Fe-Co alloys on the magnetic properties.

• Journal of Powder Materials
• /
• v.23 no.2
• /
• pp.126-131
• /
• 2016

The recent rise in applications of thermoelectric materials has attracted interest in studies toward the fabrication of thermoelectric materials using mass production techniques. In this study, we successfully fabricate n-type $Bi_2Te_{2.7}Se_{0.3}$ material by a combination of mass production powder metallurgy techniques, gas atomization, and spark plasma sintering. In addition, to examine the effects of hydrogen reduction in the microstructure, the thermoelectric and mechanical properties are measured and analyzed. Here, almost 60% of the oxygen content of the powder are eliminated after hydrogen reduction for 4 h at $360^{\circ}C$. Micrographs of the powder show that the reduced powder had a comparatively clean surface and larger grain sizes than unreduced powder. The density of the consolidated bulk using as-atomized powder and reduced atomized powder exceeds 99%. The thermoelectric power factor of the sample prepared by reduction of powder is 20% better than that of the sample prepared using unreduced powder.